CN107189630A - Water tank of stand ironing machine with anti-corrosion insulation performance - Google Patents
Water tank of stand ironing machine with anti-corrosion insulation performance Download PDFInfo
- Publication number
- CN107189630A CN107189630A CN201710478682.0A CN201710478682A CN107189630A CN 107189630 A CN107189630 A CN 107189630A CN 201710478682 A CN201710478682 A CN 201710478682A CN 107189630 A CN107189630 A CN 107189630A
- Authority
- CN
- China
- Prior art keywords
- corrosion
- water tank
- ironing machine
- insulation performance
- corrosion insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water tank of stand ironing machine with anti-corrosion insulation performance, including：Tank body and the anti-corrosion insulating layer being arranged on the tank body inwall, the anti-corrosion insulating layer are made by brushing after anti-corrosion insulation coating, then through drying.The water tank of stand ironing machine with anti-corrosion insulation performance of the present invention, anti-corrosion insulating layer is provided with tank inner wall, it has good antibacterial, anticorrosion, waterproof, anti-wear performance, corrosion of the water in water tank of stand ironing machine to tank inner wall can effectively be suppressed, the water in water tank of stand ironing machine is set to keep cleaning, so that the using effect of Garment Steamer Machine is can guarantee that, while the service life of water tank of stand ironing machine can also be improved, and anti-corrosion insulating layer also has good insulating properties, can improve the security performance of water tank of stand ironing machine.The water tank of stand ironing machine safety durable with anti-corrosion insulation performance of the present invention, waterproof anti-corrosion performance is superior, can keep the cleaning of the water in water tank, using effect is good, service life is long.
Description
Technical field
The present invention relates to Garment Steamer Machine equipment technical field, especially a kind of water tank of stand ironing machine with anti-corrosion insulation performance.
Background technology
Garment Steamer Machine is also hanging flatiron, vertical iron, can exactly hang the machine of pressing and cloth.Garment Steamer Machine passes through interior
The scorching hot water vapour that portion is produced constantly contacts clothes and cloth, reaches the purpose of softening clothes and fabric fibre tissue, and passes through
" drawing ", " pressure ", the smooth clothes of action and cloth of " spray ", make clothes and cloth intact.Water tank of stand ironing machine is Garment Steamer Machine
One of core composition, water tank contains clear water, for producing steam.Present water tank of stand ironing machine after long-term use, in water tank
Wall tends to corrosion, shortens water tank service life, can also pollute the water in water tank, influences the using effect of Garment Steamer Machine.Water
The chamber interior wall microorganism that reason is mainly in water body that is corroded easily corrodes tank inner wall, and water body in itself also can be to tank inner wall
Cause to corrode.And present water tank of stand ironing machine insulating properties are generally poor, easily cause potential safety hazard.So needing a kind of tool now
There is good corrosion-resistant and good insulating water tank of stand ironing machine.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, the technical problem to be solved by the present invention is that providing a kind of with anti-corrosion
The water tank of stand ironing machine of insulating properties.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of hanging with anti-corrosion insulation performance
Machine water tank, including：Tank body and the anti-corrosion insulating layer being arranged on the tank body inwall, the anti-corrosion insulating layer pass through
Brush after anti-corrosion insulation coating, then be made through drying；
The anti-corrosion insulation coating includes the raw material of following parts by weight：
Preferably, the anti-corrosion insulation coating includes the raw material of following parts by weight：
Preferably, the anti-corrosion insulation coating includes the raw material of following parts by weight：
Preferably, the film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester-imide tree
One or more mixtures in fat, aldehyde ketone resin.
Preferably, the organic solvent is one or more in paint naphtha, toluene, dimethylbenzene, n-butanol
Mixture.
Preferably, the pigment includes zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum
One or more mixtures in powder, calcium carbonate, barium sulfate, mica powder and diatomite.
Preferably, the auxiliary agent include coalescents, corrosion inhibiter, dispersant, heat stabilizer, thickener in one kind or
A variety of mixtures.
Preferably, the thickener is oxypropyl trimethyl TMOS.
Preferably, the curing agent is epoxylite curing agent.
Preferably, the bamboo fibre powder is the polished obtained fine powder of bamboo fibre.
Beneficial effects of the present invention：Set on the water tank of stand ironing machine with anti-corrosion insulation performance of the present invention, tank inner wall
There is anti-corrosion insulating layer, it has good antibacterial, anticorrosion, waterproof, anti-wear performance, can effectively suppress the water in water tank of stand ironing machine
Corrosion to tank inner wall, makes the water in water tank of stand ironing machine keep cleaning, so as to can guarantee that the using effect of Garment Steamer Machine, also simultaneously
The service life of water tank of stand ironing machine can be improved, and anti-corrosion insulating layer also has good insulating properties, can improve water tank of stand ironing machine
Security performance.The water tank of stand ironing machine safety durable with anti-corrosion insulation performance of the present invention, waterproof anti-corrosion performance is superior, energy
The cleaning of the water in water tank is kept, using effect is good, service life is long.
Embodiment
The present invention is described in further detail below, to make those skilled in the art being capable of evidence with reference to specification word
To implement.
It should be appreciated that such as " having ", "comprising" and " comprising " term used herein do not allot one or many
The presence or addition of individual other elements or its combination.
A kind of water tank of stand ironing machine with anti-corrosion insulation performance of the present embodiment, including：Tank body and it is arranged at described
Anti-corrosion insulating layer on tank body inwall, the anti-corrosion insulating layer is made by brushing after anti-corrosion insulation coating, then through drying；
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Wherein, the addition of cajaput oils and camphorated oil can make obtained coating have good antibacterial effect, bamboo fibre powder
Addition can improve the antibacterial antiseptic property of obtained coating, and cajaput oils, camphorated oil, bamboo fibre powder can be in Water in Water Tanks bodies
The microorganisms such as bacterium play good inhibiting effect, so as to suppress corrosion of the water body to tank inner wall, and cajaput oils, camphor
Oil, the addition of bamboo fibre powder can also make obtained anti-corrosion insulating layer have faint scent, so that the steaming of the water formation in water tank
Vapour also has certain faint scent, and the experience effect of user can be improved with the vapor ironing clothes.P-hydroxybenzoic acid first
Ester can play stronger inhibitory action to microorganisms such as the bacteriums in Water in Water Tanks body, so as to suppress water body to tank inner wall
It is corrosion-damaged, improve the Corrosion Protection of obtained anti-corrosion insulating layer.The addition of polyureas can improve obtained anti-corrosion insulating layer
Waterproof, anticorrosion and anti-wear performance.Glass fiber powder can improve the hardness and ageing-resistant performance of obtained anti-corrosion insulating layer；Nanometer
Zirconia powder can strengthen the surface flatness and anti-wear performance of obtained anti-corrosion insulating layer, can improve its water resistance；Nano oxygen
Changing zinc powder makes to be more uniformly distributed and fine and close inside obtained anti-corrosion insulating layer, can improve its waterproof and Corrosion Protection.By by jade
Set oil, camphorated oil, bamboo fibre powder, methyl p-hydroxybenzoate, polyureas, glass fiber powder, nano oxidized zirconium powder, nano zine oxide
Powder compounding use, coordinates anti-corrosion insulating layer made from other raw materials, and it has good antibacterial, anticorrosion, waterproof, wearability
Can, it can effectively suppress corrosion of the water in water tank of stand ironing machine to tank inner wall, the water in water tank of stand ironing machine is kept cleaning, so that
Ensure the using effect of Garment Steamer Machine, while the service life of water tank of stand ironing machine can also be improved.In addition, being base-material by film-forming resin
Obtained anti-corrosion insulating layer has good insulating properties, so as to improve the security performance of water tank of stand ironing machine.
The preparation method of the anti-corrosion insulation coating of water tank of stand ironing machine with anti-corrosion insulation performance of the invention given below,
It comprises the following steps：
1) film-forming resin organic solvent is added in reactor, it is 50-70 DEG C to control temperature, stirs 1-3h；
2) silicone acrylic emulsion, polyureas, glass fiber powder, pigment, nano oxidized zirconium powder, nano zine oxide are added into reactor
Powder, it is 40-50 DEG C to control temperature；Stir 0.5-1.5h；
3) bamboo fibre powder, cajaput oils, camphorated oil, methyl p-hydroxybenzoate are added into reactor, it is 30- to control temperature
45℃；Stir 0.5-1h；
4) auxiliary agent and curing agent are added into reactor, it is 30-40 DEG C to control temperature；10-45min is stirred, anti-corrosion is obtained
Coatings.
The preparation method of the anti-corrosion insulating layer of water tank of stand ironing machine with anti-corrosion insulation performance of the invention given below：
1) dried after being cleaned to water tank of stand ironing machine inner wall surface；
2) anti-corrosion insulation paint brush will be coated in as made from the above method on water tank of stand ironing machine inwall, brush 2-5 all over (every
1-2h is brushed one time), form anti-corrosion insulating layer on water tank of stand ironing machine inwall after it is spontaneously dried.
Embodiment given below, is illustrated to the water tank of stand ironing machine with anti-corrosion insulation performance to the present invention, but
It is that technical scheme is not limited to this.
Embodiment 1
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Embodiment 2
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Embodiment 3
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Embodiment 4
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Embodiment 5
The anti-corrosion insulation coating includes the raw material of following parts by weight：
The film-forming resin is epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone tree
One or more mixtures in fat.The organic solvent is one kind in paint naphtha, toluene, dimethylbenzene, n-butanol
Or a variety of mixtures.The pigment include zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder,
One or more mixtures in calcium carbonate, barium sulfate, mica powder and diatomite.The auxiliary agent includes coalescents, inhibition
One or more mixtures in agent, dispersant, heat stabilizer, thickener.The thickener is oxypropyl trimethyl epoxide silicon
Alkane.The curing agent is epoxylite curing agent.The bamboo fibre powder is the polished obtained nanoscale of bamboo fibre or Asia
Nano level fine powder.
Anti-corrosion insulating layer model is made in the anti-corrosion insulation coating that above-mentioned 5 embodiments are obtained, and performance test is carried out respectively,
Test event includes：Outward appearance, pencil hardness, wearability, anticorrosive property, impermeability, weatherability, insulating properties.The test of outward appearance
Method：Whether its visual surface is smooth homogeneous.The method of testing of pencil hardness：The pencil of various hardness is used in same level
After core is polished and measured object angle at 45 °, forms it into 300mm with 500g power, checks whether there is scratch and peeling.Wearability (RCA)
Method of testing：Firm demand 175g/cm2, index is not show-through 100 times.Anticorrosive property test here include acid resistance and
Alkali resistance is tested, acid proof method of testing：Enter to soak after 48h observes its state, 2h to be restored for 5% hydrochloric acid solution in concentration and do
Cross cut test；The method of testing of alkali resistance：It is to soak 24h in 5% sodium hydroxide solution in concentration, observes its state, it is to be restored
Cross cut test is done after 2h.The method of testing of weatherability：Be placed in the water of temperature 60 C and soak, determine after 48h outward appearance and
Adhesive force.Test result is as shown in table 1 below：
Table 1
Anti-corrosion insulation coating application made from above-mentioned 5 embodiments is formed in the water tank of stand ironing machine inwall of same model again
Anti-corrosion insulating layer, and performance test is carried out to 5 water tank of stand ironing machine；From same model a water tank of stand ironing machine as right
Ratio, the uncoated anti-corrosion insulating layer of water tank of stand ironing machine inwall of comparative example.By 5 water tank of stand ironing machine and the Garment Steamer Machine of comparative example
After water tank is used 3 months, whether observation tank inner wall gets rusty, whether the water that whether produces in obvious evidence of corrosion, water tank is limpid.
Result is observed to find：Above-mentioned 5 water tank of stand ironing machine inwalls do not get rusty, limpid without the water in obvious evidence of corrosion, water tank；Contrast
There is a large amount of rusty stains, evidence of corrosion substantially in the water tank of stand ironing machine of example, and the water in water tank occurs muddy.
As can be seen here, anti-corrosion insulating layer made from anti-corrosion insulation coating of the invention, with good anticorrosion, waterproof,
Weather resistance and insulating properties.The anti-corrosion insulating layer can be internally formed good protection to water tank of stand ironing machine.
Although embodiment of the present invention is disclosed as above, it is not restricted in specification and embodiment listed
With.It can be applied to various suitable the field of the invention completely., can be easily for those skilled in the art
Realize other modification.Therefore under the universal limited without departing substantially from claim and equivalency range, the present invention is not limited
In specific details.
Claims (10)
1. a kind of water tank of stand ironing machine with anti-corrosion insulation performance, it is characterised in that including：Tank body and it is arranged at the water
Anti-corrosion insulating layer in case inner body wall, the anti-corrosion insulating layer is made by brushing after anti-corrosion insulation coating, then through drying；
The anti-corrosion insulation coating includes the raw material of following parts by weight：
2. the water tank of stand ironing machine according to claim 1 with anti-corrosion insulation performance, it is characterised in that the anti-corrosion insulation
Coating includes the raw material of following parts by weight：
3. the water tank of stand ironing machine according to claim 1 with anti-corrosion insulation performance, it is characterised in that the anti-corrosion insulation
Coating includes the raw material of following parts by weight：
4. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, it is characterised in that
The film-forming resin is one in epoxy resin, organic siliconresin, polyester acrylate resin, polyester imine resin, aldehyde ketone resin
Plant or a variety of mixtures.
5. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, it is characterised in that
The organic solvent is one or more mixtures in paint naphtha, toluene, dimethylbenzene, n-butanol.
6. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, it is characterised in that
The pigment includes zinc yellow, zinc powder, trbasic zinc phosphate, aluminium powder, micaceous iron oxide, zinc oxide, talcum powder, calcium carbonate, barium sulfate, cloud
One or more mixtures in female powder and diatomite.
7. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, it is characterised in that
The auxiliary agent includes one or more mixtures in coalescents, corrosion inhibiter, dispersant, heat stabilizer, thickener.
8. the water tank of stand ironing machine according to claim 7 with anti-corrosion insulation performance, it is characterised in that the thickener is
Oxypropyl trimethyl TMOS.
9. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, it is characterised in that
The curing agent is epoxylite curing agent.
10. the water tank of stand ironing machine with anti-corrosion insulation performance according to any one in claim 1-3, its feature exists
In the bamboo fibre powder is the polished obtained fine powder of bamboo fibre.