CN107186091A - The process for stamping of sheet metal - Google Patents
The process for stamping of sheet metal Download PDFInfo
- Publication number
- CN107186091A CN107186091A CN201710414215.1A CN201710414215A CN107186091A CN 107186091 A CN107186091 A CN 107186091A CN 201710414215 A CN201710414215 A CN 201710414215A CN 107186091 A CN107186091 A CN 107186091A
- Authority
- CN
- China
- Prior art keywords
- parts
- sheet metal
- applicator
- coats
- petropols
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of process for stamping of sheet metal, it includes heating pending sheet metal, and coats one layer of applicator A being mixed by following parts by weight:30 parts~40 parts of lube base oil, Petropols are 5 parts~10 parts, 0.5 part~1 part of 1 part~5 parts of ox-hide cream and magnesium silicate;Then precooling, and coating one layer of applicator B being mixed by following parts by weight again:30 parts~40 parts of lube base oil, Petropols are 5 parts~10 parts, 0.5 part~1 part of 1 part~5 parts of clay and silica;Sheet metal is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.Pending sheet metal is first heated using the principle expanded with heat and contract with cold and coats specific applicator A, then cooled down again and coat specific applicator B, so that the problem of rhegma or cut occur during overcoming existing metallic plate punching by the present invention.
Description
Technical field
The present invention relates to mechanical spare and accessory parts processing technique field, especially a kind of sheet metal.
Background technology
It is more and more extensive with the application of sheet metal, and the quality of sheet metal and its process for stamping are closely related, because
This, people also increasingly pay close attention to for its process for stamping.At present, when implementing punch process to sheet metal, often easily go out
The phenomenon of existing rhegma or cut.How this phenomenon that metallic plate punching process occur is overcome into current metallic plate punching
Technology is badly in need of the technical problem solved.
The content of the invention
It is an object of the invention to provide a kind of process for stamping of sheet metal, it can solve existing metallic plate punching
During the problem of there is rhegma or cut.
In order to solve the above-mentioned technical problem, the technical solution adopted in the present invention is:
It comprises the following steps:
A. pending sheet metal is heated to 50 DEG C~60 DEG C, then coats one layer of applicator A on its surface;Wherein, institute
Applicator A is stated to be mixed by following parts by weight:30 parts~40 parts of lube base oil, Petropols be 5 parts~10 parts,
0.5 part~1 part of 1 part~5 parts of ox-hide cream and magnesium silicate;
B. the sheet metal handled by step A is cooled to 0 DEG C~5 DEG C in advance, then coats one layer of applicator B on its surface again;
Wherein, the applicator B is mixed by following parts by weight:30 parts~40 parts of lube base oil, Petropols are 5 parts
0.5 part~1 part of~10 parts, 1 part~5 parts of clay and silica;
C. the sheet metal handled by step B is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.
By adopting the above-described technical solution, the present invention has following remarkable result compared with prior art:
Pending sheet metal is first heated using the principle expanded with heat and contract with cold and coats specific applicator A, then by the present invention
Cool down again and coat specific applicator B, and by above way make the surface of sheet metal fully absorb above-mentioned applicator A and
Applicator B, and make that there is the effect interpenetrated between applicator A and applicator B, so as to overcome existing metallic plate punching
During the problem of there is rhegma or cut;In addition, due to having stronger attachment respectively in above-mentioned applicator A and applicator B
Power so that sheet metal is not in the phenomenon dispersed in punching course.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described, and protection scope of the present invention is not only limited to
In following examples.
The process for stamping of embodiment 1 --- sheet metal
It comprises the following steps:
A. pending sheet metal is heated to 50 DEG C, then coats one layer of applicator A on its surface;Wherein, the coating
Thing A is mixed by following parts by weight:30 parts of lube base oil, Petropols are 5 parts, 1 part of ox-hide cream and silicic acid
0.5 part of magnesium;
B. the sheet metal handled by step A is cooled to 0 DEG C in advance, then coats one layer of applicator B on its surface again;Wherein,
The applicator B is mixed by following parts by weight:30 parts of lube base oil, Petropols are 5 parts, 1 part of clay with
And 0.5 part of silica;
C. the sheet metal handled by step B is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.
According to the process for stamping of the present embodiment, in product of the sheet metal in punching course and after punch forming, split
Damage or the probability of cut appearance is only 1%;And in punching course, do not occurring what sheet metal surface attachment dispersed
Phenomenon.
The process for stamping of embodiment 2 --- sheet metal
It comprises the following steps:
A. pending sheet metal is heated to 60 DEG C, then coats one layer of applicator A on its surface;Wherein, the coating
Thing A is mixed by following parts by weight:40 parts of lube base oil, Petropols are 10 parts, 5 parts of ox-hide cream and silicic acid
1 part of magnesium;
B. the sheet metal handled by step A is cooled to 5 DEG C in advance, then coats one layer of applicator B on its surface again;Wherein,
The applicator B is mixed by following parts by weight:40 parts of lube base oil, Petropols are 10 parts, 5 parts of clay with
And silica 1 part;
C. the sheet metal handled by step B is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.
According to the process for stamping of the present embodiment, in product of the sheet metal in punching course and after punch forming, split
Damage or the probability of cut appearance is only 1%;And in punching course, do not occurring what sheet metal surface attachment dispersed
Phenomenon.
The process for stamping of embodiment 3 --- sheet metal
It comprises the following steps:
A. pending sheet metal is heated to 58 DEG C, then coats one layer of applicator A on its surface;Wherein, the coating
Thing A is mixed by following parts by weight:36 parts of lube base oil, Petropols are 7 parts, 4 parts of ox-hide cream and silicic acid
0.7 part of magnesium;
B. the sheet metal handled by step A is cooled to 2 DEG C in advance, then coats one layer of applicator B on its surface again;Wherein,
The applicator B is mixed by following parts by weight:36 parts of lube base oil, Petropols are 7 parts, 4 parts of clay with
And 0.7 part of silica;
C. the sheet metal handled by step B is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.
According to the process for stamping of the present embodiment, in product of the sheet metal in punching course and after punch forming, split
Damage or the probability of cut appearance is only 1%;And in punching course, do not occurring what sheet metal surface attachment dispersed
Phenomenon.
Claims (1)
1. a kind of process for stamping of sheet metal, it is characterised in that comprise the following steps:
A. pending sheet metal is heated to 50 DEG C~60 DEG C, then coats one layer of applicator A on its surface;Wherein, institute
Applicator A is stated to be mixed by following parts by weight:30 parts~40 parts of lube base oil, Petropols be 5 parts~10 parts,
0.5 part~1 part of 1 part~5 parts of ox-hide cream and magnesium silicate;
B. the sheet metal handled by step A is cooled to 0 DEG C~5 DEG C in advance, then coats one layer of applicator B on its surface again;
Wherein, the applicator B is mixed by following parts by weight:30 parts~40 parts of lube base oil, Petropols are 5 parts
0.5 part~1 part of~10 parts, 1 part~5 parts of clay and silica;
C. the sheet metal handled by step B is put into mould, punching press is carried out by the pressure-activated dynamic compressor of setting.