CN107182806A - A kind of anti-corrosive antibacterial sheep bed and its preparation method and application - Google Patents
A kind of anti-corrosive antibacterial sheep bed and its preparation method and application Download PDFInfo
- Publication number
- CN107182806A CN107182806A CN201710392378.4A CN201710392378A CN107182806A CN 107182806 A CN107182806 A CN 107182806A CN 201710392378 A CN201710392378 A CN 201710392378A CN 107182806 A CN107182806 A CN 107182806A
- Authority
- CN
- China
- Prior art keywords
- parts
- sheep
- sheep bed
- corrosive antibacterial
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of anti-corrosive antibacterial sheep bed, including following raw material：Polypropylene, polystyrene, natural rubber, polymer coupler, calyx meto, burnt ochre, plant protein powder, antioxidant, auxiliary agent and filler；The material rate is 10 25 parts of 18 40 parts of polypropylene, 30 42 parts of polystyrene, 12 18 parts of natural rubber, 0.5 5 parts of polymer coupler, 0.2 1.0 parts of calyx meto, 0.1 0.6 parts of burnt ochre, 6 10 parts of plant protein powder, 0.3 1.5 parts of antioxidant, 59 parts of auxiliary agent and filler, present invention also offers the preparation method of sheep bed, including：The synthesis step of base resin, the opening steps and extrusion process of organic molecule chain；A kind of application of the anti-corrosive antibacterial sheep bed of the present invention in milch goat cultivates, can reduce the probability that sheep hoof infects staphylococcus aureus, and the probability of sheep hoof infection staphylococcus aureus is reduced to 0.2 1.2%.
Description
Technical field
The invention belongs to livestock-raising field of mechanical technique, it is related to a kind of anti-corrosive antibacterial sheep bed, and in particular to a kind of anti-corrosion
Antibacterial sheep bed and its preparation method and application.
Background technology
For a long time, traditional flock of sheep raise many using field Continous grazing mode, but forage grass and feed transformation efficiency is low,
The speed of growth is slow, and economic benefit is low, and destruction ecological environment, in recent years, industrial artificial rearing sheep in pens occurs only, and sheep bed is all adopted
The crack formula sheep bed with spacing is followed closely into bamboo chip or batten.Just occurred various types of plastics sheep bed in recent years, this scale,
Intensive farm has strict demand to the health of feed lot, if clearing up sheep manure not in time, makes that the smell is awful, and causes bacterium to grow
It is raw.Present a variety of industrial sheep raising facilities, most of simpler and cruder, utilization ratio is low, is not easily cleaned and sweeps, other facilities
Although multiple functional, cost of equipment is excessive, it is difficult to promote.There is following major defect in existing sheep bed：
（1）Existing sheep bed, service life is short；
（2）Existing sheep bed, oxygen transmission rate is low；
（3）Existing sheep bed, tensile strength is low, the high easy fracture of fragility；
（4）Existing sheep bed, the effect for improving lactation amount is limited；
（5）Existing sheep bed, it is impossible to prevent the foot rot of milch goat, the effect of suppression staphylococcus aureus not good；
（6）The preparation method of existing sheep bed, very complicated, it is not easy to operate.
The content of the invention
The present invention is not enough for more than, and the technical problems to be solved by the invention are to provide a kind of synthesis anti-corrosive antibacterial sheep bed
Preparation method.The present invention can realize following goal of the invention：
The anti-corrosive antibacterial sheep bed of the present invention, high with intensity, quality is good, and service life is strong, and oxygen transmission rate is high, it is possible to increase milch goat
Lactation amount, the effect with potent suppression staphylococcus aureus, the preparation method technique of sheep of the present invention bed is simple, easily behaviour
Make.
In order to solve the above technical problems, using following technical scheme：
A kind of anti-corrosive antibacterial sheep bed, including following raw material：Polypropylene, polystyrene, natural rubber, polymer coupler, bitter leaves
Perfume, burnt ochre, plant protein powder, antioxidant, auxiliary agent and filler；The raw material, by weight, ratio are polypropylene 18-40
Part, 30-42 parts of polystyrene, 12-18 parts of natural rubber, 0.5-5 parts of polymer coupler, 0.2-1.0 parts of calyx meto, burnt ochre
10-25 parts of 0.1-0.6 parts, 6-10 parts of plant protein powder, 0.3-1.5 parts of antioxidant, 5-9 parts of auxiliary agent and filler.
The raw material, by weight, ratio are preferably 20-35 parts of polypropylene, 35-40 parts of polystyrene, natural rubber 15-
18 parts, it is 0.9-4 parts of polymer coupler, 0.2-0.6 parts of calyx meto, 0.1-0.5 parts of burnt ochre, 8-10 parts of plant protein powder, anti-
12-20 parts of 0.5-1.2 parts of oxidant, 6-8 parts of auxiliary agent and filler；The plant protein powder, including starch acetate, walnut powder,
Lotus nut starch, purple sweet potato powder, black bean powder, millet powder.
The auxiliary agent, including modifying agent, crosslinking agent, glue class, lubricant, vegetable colour, its ratio are 1-2:3:2:2:
0.5-3。
The natural rubber, density is 0.95-0.99g/cm3, and refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；Institute
Burnt ochre is stated, free iron content is not less than 30%, and fineness is 400 mesh.
The polymer coupler, preferably apple anhydride dehydration；The glue class, preferably guar gum；The lubrication
Agent, is fully refined paraffin wax；
The filler is chitosan with montmorillonite, wollastonite, kaolin, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and
Any one or several group in alpha-cellulose, gas-phase silica, lithopone.
A kind of preparation method of anti-corrosive antibacterial sheep bed, comprises the following steps：Synthesis step, the organic molecule chain of base resin
Opening steps and extrusion process.
The synthesis step of the base resin, includes the preparation of dispersion liquid, the preparation of the dispersion liquid is into mixed liquor
Add polymer coupler quality, temperature be 170-200 DEG C, pressure be 2-6MPa under mix 30-45min.
The opening of the organic molecule chain, to add crosslinking agent, low-grade fever 25-40min so that organic molecule chain is from each other
Open.
The extrusion process step, for the spiral shell for being 25-40 with draw ratio under the conditions of 255-270 DEG C of temperature by the mixture
Bar extruder is extruded.
A kind of application of anti-corrosive antibacterial sheep bed in milch goat cultivates, can reduce the general of sheep hoof infection staphylococcus aureus
Rate, the probability of sheep hoof infection staphylococcus aureus is reduced to 0.2-1.2%.
The present invention uses above technical scheme, compared with prior art, with advantages below：
（1）The sheep bed of the present invention, service life is long, and service life is up to 25.1-30.5, and the common pp sheep bed of control group is 15.2
Year；
（2）The sheep bed of the present invention, tensile strength is high, and tensile strength is up to 102.5-114.6MPa, and the common pp sheep bed of control group is
89.4MPa；
（3）The sheep bed of the present invention, oxygen transmission rate is high, and oxygen transmission rate is 92-102cm3.m/m2Mpa24h20 DEG C of 65%RH (0.025mm),
The common pp sheep bed of control group is 88cm3.m/m2Mpa24h20 DEG C of 65%RH (0.025mm)；
（4）Sheep bed prepared by the present invention, can improve the lactation amount of milch goat, and milch goat is raised on the anti-corrosive antibacterial sheep bed of the present invention
After supporting 100 days, lactation amount increase rate is 3.8-9.4%, and control group is 2.0%；
（5）Sheep bed prepared by the present invention, substantially reduces the incidence of milch goat foot rot, anti-corrosive antibacterial of the milch goat in the present invention
After being raised 100 days on sheep bed, foot rot incidence is reduced to 0.9-3.4%, and control group is 5.2%；
（6）Sheep bed prepared by the present invention, can substantially reduce the probability that sheep hoof infects staphylococcus aureus, milch goat is in the present invention
Anti-corrosive antibacterial sheep bed on raise 100 days after, sheep hoof infection staphylococcus aureus probability be reduced to 0.2-1.2%, control group is
6.1%。
Embodiment
A kind of anti-corrosive antibacterial sheep bed of embodiment 1
By weight, including following component：
40 parts of polypropylene, 42 parts of polystyrene, 18 parts of natural rubber, 5 parts of polymer coupler, 1.0 parts of calyx meto, burnt ochre
25 parts of 0.6 part, 10 parts of plant protein powder, 1.5 parts of antioxidant, 9 parts of auxiliary agent and filler；
The plant protein powder, including starch acetate, walnut powder, lotus nut starch, purple sweet potato powder, black bean powder, millet powder and cation
Starch.
The auxiliary agent, including modifying agent, crosslinking agent, glue class, lubricant, vegetable colour, its ratio are 2:3:2:2:3.
The natural rubber, density is 0.95-0.99g/cm3, and refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；Institute
Burnt ochre is stated, free iron content is not less than 30%, and fineness is 400 mesh.
The polymer coupler, preferably apple anhydride dehydration；The glue class, preferably guar gum；The lubrication
Agent, is fully refined paraffin wax；
The filler, is chitosan and wollastonite, kaolin, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and alpha fibre
The group of element.
A kind of anti-corrosive antibacterial sheep bed of embodiment 2
By weight, including following component：
18 parts of polypropylene, 30 parts of polystyrene, 12 parts of natural rubber, 0.5 part of polymer coupler, 0.2 part of calyx meto, burnt ochre
10 parts of 0.1 part, 6 parts of plant protein powder, 0.3 part of antioxidant, 5 parts of auxiliary agent and filler.
The plant protein powder, is starch acetate, walnut powder, lotus nut starch, purple sweet potato powder, black bean powder, millet powder and buckwheat
Powder.
The auxiliary agent, including modifying agent, crosslinking agent, glue class, lubricant, vegetable colour, its ratio are 1:3:2:2:0.5.
The natural rubber, density is 0.95-0.99g/cm3, and refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；Institute
Burnt ochre is stated, free iron content is not less than 30%, and fineness is 400 mesh.
The polymer coupler, preferably apple anhydride dehydration；The glue class, preferably guar gum；The lubrication
Agent, is fully refined paraffin wax；
The filler, is the group of chitosan and montmorillonite, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and alpha-cellulose.
A kind of anti-corrosive antibacterial sheep bed of embodiment 3
By weight, including following component：
20 parts of polypropylene, 35 parts of polystyrene, 15 parts of natural rubber, 0.9 part of polymer coupler, 0.2 part of calyx meto, burnt ochre
12 parts of 0.1 part, 8 parts of plant protein powder, 0.5 part of antioxidant, 6 parts of auxiliary agent and filler；
The plant protein powder, is starch acetate, walnut powder, lotus nut starch, purple sweet potato powder, black bean powder, millet powder and corn flour；
The auxiliary agent, including modifying agent, crosslinking agent, glue class, lubricant, vegetable colour, its ratio are 1.4:3:2:2:2.6.
The natural rubber, density is 0.95-0.99g/cm3, and refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；Institute
Burnt ochre is stated, free iron content is not less than 30%, and fineness is 400 mesh.
The polymer coupler, preferably apple anhydride dehydration；The glue class, preferably guar gum；The lubrication
Agent, is fully refined paraffin wax；
The filler is chitosan with montmorillonite, wollastonite, kaolin, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and
The group of alpha-cellulose, gas-phase silica.
A kind of anti-corrosive antibacterial sheep bed of embodiment 4
By weight, including following component：
35 parts of polypropylene, 40 parts of polystyrene, 18 parts of natural rubber, 4 parts of polymer coupler, 0.6 part of calyx meto, burnt ochre
20 parts of 0.5 part, 10 parts of plant protein powder, 1.2 parts of antioxidant, 8 parts of auxiliary agent and filler；
The plant protein powder, is starch acetate, walnut powder, lotus nut starch, purple sweet potato powder, black bean powder, millet powder and corn flour；
The auxiliary agent, including modifying agent, crosslinking agent, glue class, lubricant, vegetable colour, its ratio are 1.4:3:2:2:2.6.
The natural rubber, density is 0.95-0.99g/cm3, and refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；Institute
Burnt ochre is stated, free iron content is not less than 30%, and fineness is 400 mesh.
The polymer coupler, preferably apple anhydride dehydration；The glue class, preferably guar gum；The lubrication
Agent, is fully refined paraffin wax；
The filler is chitosan with montmorillonite, wollastonite, kaolin, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and
The group of alpha-cellulose, gas-phase silica.
A kind of performance detection of the 1-4 of the embodiment of the present invention of embodiment 5 anti-corrosive antibacterial sheep bed
Related performance test, test result such as table 1 are carried out to a kind of 1-4 of embodiment of the present invention anti-corrosive antibacterial sheep bed：
The result that table 1 is tested
Wherein, the unit of oxygen transmission rate is cm3.m/m2Mpa24h20 DEG C of 65%RH (0.025mm) pressure application
As shown in Table 1,1-4 of embodiment of the present invention anti-corrosive antibacterial sheep bed is longer than the service life of common pp sheep bed, strong in tension
It is all better than common pp sheep bed on degree and oxygen transmission rate；Specially：
The sheep bed of the present invention, service life is long, and service life is up to 25.1-30.5, and the common pp sheep bed of control group is 15.2；
The sheep bed of the present invention, tensile strength is high, and tensile strength is up to 102.5-114.6MPa, and the common pp sheep bed of control group is
89.4MPa；
The sheep bed of the present invention, oxygen transmission rate is high, and oxygen transmission rate is 92-102cm3.m/m2Mpa24h20 DEG C of 65%RH (0.025mm), control
The common pp sheep bed of group is 88cm3.m/m2Mpa24h20 DEG C of 65%RH (0.025mm).
A kind of anti-corrosive antibacterial sheep bed preparation method of embodiment 6
Comprise the following steps：
（1）The synthesis of base resin
A, according to the formula rate described in embodiment 3 or 4 weigh following raw material：Calyx meto, burnt ochre, plant protein powder, antioxygen
Agent, polymer coupler, modifying agent and vegetable colour, to calyx meto, burnt ochre, plant protein powder, antioxidant, modifying agent
With the deionized water completely of addition in vegetable colour, the addition of complete deionized water is the 50-60% of above-mentioned raw materials gross weight,
It is stirred vigorously, prepares mixed liquor；
B, dispersion liquid preparation：One of the polymer coupler quality of formula rate described in embodiment is added into the mixed liquor
Half, it is 170-200 DEG C in temperature, pressure is under 2-6MPa, mixes 30-45min, and the dispersion liquid stablized does dispersion liquid
It is dry to water content 7-15%, obtain base resin.
（2）The opening of organic molecule chain
With step（1）Carry out simultaneously, following raw material is weighed according to the formula rate described in embodiment 3 or 4：Polypropylene, polyphenyl second
Alkene, natural rubber, crosslinking agent, glue class, lubricant, by the polypropylene weighed, polystyrene, natural rubber, glue class and lubrication
Agent is well mixed, and adds crosslinking agent, and low-grade fever 25-40min so that organic molecule chain is opened from each other obtains mixture A；
（3）The preparation of head product
Mixture A in step a base resin, step b is mixed, 180-200 DEG C is heated to, constant temperature is kept, while stirring
Remaining polymer coupler is added, continues constant temperature stirring 10min, obtains mixture B.
（4）Extrusion process
The screw extruder extrusion process for being 25-40 with draw ratio under the conditions of 255-270 DEG C of temperature by mixture B, is obtained
Raw material C.
（5）Moulding
Raw material C is subjected to pressing plate, pipe processing is squeezed, combination obtains the sheep bed of the present invention.
A kind of preparation methods of anti-corrosive antibacterial sheep bed of embodiment 7-21
The present embodiment 7-11 is that on the basis of embodiment 6, the preparation condition of dispersion liquid is 180 DEG C, 2.5MPa, the kind of crosslinking agent
Class is polyepoxy compound, and embodiment 7-11 only changes extruder draw ratio, carries out single factor analysis, prepares a kind of anti-corrosion and resists
Bacterium sheep bed, is specifically changed into：
The experiment that 12 pairs of embodiment anti-corrosive antibacterial sheep bed of the invention is carried out
Specially：10000 milch goat composition test groups are randomly selected, in certain brand sheep bed and the anti-corrosive antibacterial sheep bed of the present invention
It is upper to raise 100 days, lactation amount, foot rot are carried out to it and occurs the number of elements that number of elements, milch goat sheep hoof infect staphylococcus aureus
Keep track of and data statistics processing is carried out to the initial data, lactation amount increase rate, foot rot incidence and milk are calculated respectively
Goat sheep hoof infects the probability of staphylococcus aureus, and the data after test result processing are shown in Table 3.
The result that table 3 is tested
As a result show, test group the present invention anti-corrosive antibacterial sheep bed on raise 100 days after, lactation amount, foot rot occur number of elements,
The number of elements of milch goat sheep hoof infection staphylococcus aureus is compared certain the brand sheep for getting up commercially available and all accordingly changed, lactation amount
Increase, foot rot occurs number of elements, the number of elements of milch goat sheep hoof infection staphylococcus aureus and then decreased.Wherein, it is real
It is more preferably embodiment to apply example 10.
The present embodiment 13-16 is that on the basis of embodiment 6, the preparation condition of dispersion liquid is 180 DEG C, 2.5MPa, extrusion
Machine draw ratio is 35, and embodiment 13-16 only changes the species of crosslinking agent, carries out single factor analysis, prepares a kind of anti-corrosive antibacterial sheep
Bed, is specifically changed into：
The experiment that 17 pairs of embodiment anti-corrosive antibacterial sheep bed of the invention is carried out
Specially：10000 milch goat composition test groups are randomly selected, in certain brand sheep bed and the anti-corrosive antibacterial sheep bed of the present invention
It is upper to raise 100 days, lactation amount, foot rot are carried out to it and occurs the number of elements that number of elements, milch goat sheep hoof infect staphylococcus aureus
Keep track of and data statistics processing is carried out to the initial data, lactation amount increase rate, foot rot incidence and milk are calculated respectively
Goat sheep hoof infects the probability of staphylococcus aureus, and the data after test result processing are shown in Table 4.
The result that table 4 is tested
As a result show, test group the present invention anti-corrosive antibacterial sheep bed on raise 100 days after, lactation amount, foot rot occur number of elements,
The number of elements of milch goat sheep hoof infection staphylococcus aureus is compared certain the brand sheep for getting up commercially available and all accordingly changed, lactation amount
Increase, foot rot occurs number of elements, the number of elements of milch goat sheep hoof infection staphylococcus aureus and then decreased.Wherein, it is real
It is more preferably embodiment to apply example 15.
The present embodiment 18-21 is that on the basis of embodiment 6, the species of crosslinking agent is polyepoxy compound, extruder
Draw ratio is 35, and embodiment 18-21 only changes the preparation condition of dispersion liquid, carries out single factor analysis, prepares a kind of anti-corrosive antibacterial
Sheep bed, is specifically changed into：
The experiment that 22 pairs of embodiment anti-corrosive antibacterial sheep bed of the invention is carried out
Specially：10000 milch goat composition test groups are randomly selected, in certain brand sheep bed and the anti-corrosive antibacterial sheep bed of the present invention
It is upper to raise 100 days, lactation amount, foot rot are carried out to it and occurs the number of elements that number of elements, milch goat sheep hoof infect staphylococcus aureus
Keep track of and data statistics processing is carried out to the initial data, lactation amount increase rate, foot rot incidence and milk are calculated respectively
Goat sheep hoof infects the probability of staphylococcus aureus, and the data after test result processing are shown in Table 5.
The result that table 5 is tested
As a result show, test group the present invention anti-corrosive antibacterial sheep bed on raise 100 days after, lactation amount, foot rot occur number of elements,
The number of elements of milch goat sheep hoof infection staphylococcus aureus is compared certain the brand sheep for getting up commercially available and all accordingly changed, lactation amount
Increase, foot rot occurs number of elements, the number of elements of milch goat sheep hoof infection staphylococcus aureus and then decreased.Wherein, it is real
It is more preferably embodiment to apply example 20.
Unless otherwise indicated, the percentage employed in the present invention is percetage by weight, ratio of the present invention,
For mass ratio.
Finally it should be noted that：The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although the present invention is described in detail with reference to the foregoing embodiments, for those skilled in the art, it still can be with
Technical scheme described in foregoing embodiments is modified, or equivalent substitution is carried out to which part technical characteristic.It is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements made etc., should be included in the guarantor of the present invention
Within the scope of shield.
Claims (10)
1. a kind of anti-corrosive antibacterial sheep bed, it is characterised in that including following raw material：Polypropylene, polystyrene, natural rubber, high score
Sub- coupling agent, calyx meto, burnt ochre, plant protein powder, antioxidant, auxiliary agent and filler；The raw material, by weight, ratio
For 18-40 parts of polypropylene, 30-42 parts of polystyrene, 12-18 parts of natural rubber, 0.5-5 parts of polymer coupler, calyx meto
0.2-1.0 parts, 0.1-0.6 parts of burnt ochre, 6-10 parts of plant protein powder, 0.3-1.5 parts of antioxidant, 5-9 parts of auxiliary agent and filler
10-25 parts.
2. a kind of anti-corrosive antibacterial sheep bed according to claim 1, it is characterised in that the raw material, by weight, ratio is excellent
Elect 20-35 parts of polypropylene, 35-40 parts of polystyrene, 15-18 parts of natural rubber, 0.9-4 parts of polymer coupler, calyx meto as
0.2-0.6 parts, 0.1-0.5 parts of burnt ochre, 8-10 parts of plant protein powder, 0.5-1.2 parts of antioxidant, 6-8 parts of auxiliary agent and filler
12-20 parts；The plant protein powder, including starch acetate, walnut powder, lotus nut starch, purple sweet potato powder, black bean powder, millet powder.
3. a kind of anti-corrosive antibacterial sheep bed according to claim 1, it is characterised in that the auxiliary agent, including modifying agent, crosslinking
Agent, glue class, lubricant, vegetable colour, its ratio are 1-2:3:2:2:0.5-3.
4. a kind of anti-corrosive antibacterial sheep bed according to claim 1, it is characterised in that the natural rubber, density is 0.95-
0.99g/cm3, refractive index is 1.534, and modulus of elasticity is 1-3.5MPa；The burnt ochre, free iron content is not less than 30%, carefully
Spend for 400 mesh.
5. a kind of anti-corrosive antibacterial sheep bed according to claim 3, it is characterised in that the polymer coupler, is preferably
Apple anhydride dehydration；The glue class, preferably guar gum；The lubricant, is fully refined paraffin wax；
The filler is chitosan with montmorillonite, wollastonite, kaolin, talcum powder, bismuth loess, modified alta-mud, titanium dioxide and
Any one or several group in alpha-cellulose, gas-phase silica, lithopone.
6. a kind of preparation method of anti-corrosive antibacterial sheep bed, it is characterised in that comprise the following steps：The synthesis step of base resin,
The opening steps and extrusion process of organic molecule chain.
7. the preparation method of a kind of anti-corrosive antibacterial sheep bed according to claim 6, it is characterised in that the base resin
Synthesis step, includes the preparation of dispersion liquid, the preparation of the dispersion liquid is the addition polymer coupler quality into mixed liquor,
Temperature be 170-200 DEG C, pressure be 2-6MPa under mix 30-45min.
8. a kind of preparation method of anti-corrosive antibacterial sheep bed according to claim 6, it is characterised in that the organic molecule chain
Opening, for add crosslinking agent, low-grade fever 25-40min so that organic molecule chain is opened from each other.
9. a kind of preparation method of anti-corrosive antibacterial sheep bed according to claim 6, it is characterised in that the extrusion process step
Suddenly, for be 25-40 with draw ratio under the conditions of 255-270 DEG C of temperature by the mixture screw extruder extrude.
10. application of a kind of anti-corrosive antibacterial sheep bed in milch goat cultivates, it is characterised in that the golden yellow Portugal of sheep hoof infection can be reduced
The probability of grape coccus, the probability of sheep hoof infection staphylococcus aureus is reduced to 0.2-1.2%.