CN107160525B - A kind of processing method of solid wood bathroom cabinet cabinet plate - Google Patents
A kind of processing method of solid wood bathroom cabinet cabinet plate Download PDFInfo
- Publication number
- CN107160525B CN107160525B CN201710553480.8A CN201710553480A CN107160525B CN 107160525 B CN107160525 B CN 107160525B CN 201710553480 A CN201710553480 A CN 201710553480A CN 107160525 B CN107160525 B CN 107160525B
- Authority
- CN
- China
- Prior art keywords
- solid wood
- parts
- wood board
- paint
- cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of processing methods of solid wood bathroom cabinet cabinet plate, it is related to sanitary ware processing technique field, mainly include the following steps: the paint coating of (1) hot melt, (2) curing of coatings, (3) sawing sheet cabinet plate, (4) waterproof edge sealing, (5) assembly hole are reserved.The present invention carries out roller coating to solid wood board to make hot melt paint by oneself, to form coating in plate surface, the coating not only has the service performances such as excellent waterproofness, wearability, corrosion resistance, anti-flammability, the solid wood board moisture content of coat inside can also be made to maintain stable state, moisture or volatilization moisture are not absorbed with the variation of external environment, with the optimum state set when guaranteeing that solid wood board moisture content is constantly in processing, to extend the service life of solid wood bathroom cabinet cabinet plate.
Description
Technical field:
The present invention relates to sanitary ware processing technique fields, and in particular to a kind of processing method of solid wood bathroom cabinet cabinet plate.
Background technique:
Bathroom cabinet belongs to one of common sanitary ware, is mainly made of cabinet body, table top and bathroom mirror.Cabinet body presses processed plate
Type is divided into solid wood, glued board, density board, particieboard etc., and wherein solid wood cabinet body is deep with the characteristic of its natural environmental-protective is consumed
Person likes.
It is substrate that the material of solid wood bathroom cabinet, which is with the solid wood after distillation dehydration, is process by water-proof treatment technology
Cabinet body.Why flourishing long time solid wood material is, from color analysis, is its natural wood true qualities, not only natural but also without chemical contamination,
It is the fashion selection of health, meets the psychological needs that people from modern metropolitan cities advocates the Nature.But the maximum defect of solid wood cabinet body be as
Fruit local environment is excessively dry, then is easy dry and cracked.Therefore, need to balance its waterproof and performance of keeping humidity when solid wood cabinet body is processed,
Its local environment cannot excessively humidity can not be dried excessively.
Summary of the invention:
Technical problem to be solved by the present invention lies in provide one kind to have both Waterproof Breathable effect with science adjusting solid wood board
The processing method of the solid wood bathroom cabinet cabinet plate of material water content.
The following technical solution is employed for the technical problems to be solved by the invention to realize:
A kind of processing method of solid wood bathroom cabinet cabinet plate, mainly includes the following steps:
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 5-10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
The hot melt paint is made of the raw material of following parts by weight: 35-40 parts of thermosetting acrylic resin, methyl-etherified trimerization
15-20 parts of melamine resin, 5-10 parts of PVC paste resin, 1-5 parts of molecular sieve micro mist, 1-5 parts of asparatate, N- isopropyl
0.5-3 parts of acrylamide, 0.5-3 parts of glycidyl methacrylate, 0.1-1 parts of hydrolysis of polymaleic anhydride, hexamethylol three
0.1-1 parts of poly cyanamid pregnancy ether, 0.1-1 parts of superfine powder of polytetrafluoroethylene, 0.01-0.05 parts of methylol ferrocene;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
The specific preparation method of the hot melt paint includes the following steps:
1. thermosetting acrylic resin, asparatate and n-isopropyl acrylamide are sufficiently mixed, and in hot pressing temperature
Hot pressing 3-5min under 135-145 DEG C of degree, hot pressing pressure 0.05MPa, gained mixture are transferred to sealing and standing in -15 DEG C of environment immediately
3-5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 10-15min, it is sweet to add Glycidyl methacrylate
Grease and methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 30-60min to get modified molecular screen micro mist;
3. hydrolysis of polymaleic anhydride and hexamethylolmelamine pregnancy ether are added into PVC paste resin, it is sufficiently mixed
After conjunction under microwave frequency 2450MHz, output power 700W microwave treatment 5-10min to get modified polyvinyl chloride paste resin;
4. by modified heat convertible acrylic resin, methyl-etherified melamine resin, modified polyvinyl chloride paste resin, modified point
It is sent into kneading machine after son sieve micro mist and superfine powder of polytetrafluoroethylene mixing, 3-5min is kneaded under molten condition, and through nature
It is cooled to room temperature to get hot melt paint.
The molecular sieve micro mist is made by molecular screen primary powder is preprocessed, preprocess method are as follows: by molecular screen primary powder
2-3h is roasted at 450-500 DEG C, after naturally cool to addition stearyl alcohol and glutamic acid after 120-130 DEG C, and at 120-130 DEG C
15-30min is ground in lower heat preservation, continues cooled to room temperature, deionized water is added dropwise into gained mixture under stirring, drips
10-15min is stood after finishing, is filtered, gained filter residue is sent into freeze drier, and dry obtained solid is made micro- through micronizer
Powder is to get molecular sieve micro mist.
The molecular screen primary powder, stearyl alcohol, glutamic acid and deionized water mass ratio be 3-5:0.1-1:0.1-1:10-
20。
The beneficial effects of the present invention are: the present invention carries out roller coating to solid wood board to make hot melt paint by oneself, in plate surface
Coating is formed, which not only has the service performances such as excellent waterproofness, wearability, corrosion resistance, anti-flammability, moreover it is possible to make to apply
Solid wood board moisture content inside layer maintains stable state, does not absorb moisture or volatilization moisture with the variation of external environment,
With the optimum state set when guaranteeing that solid wood board moisture content is constantly in processing, to extend the use of solid wood bathroom cabinet cabinet plate
Service life avoids it from the phenomenon that moisture absorption mildew or season cracking occur.
Specific embodiment:
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 35g thermosetting acrylic resin, 3g asparatate and 1g n-isopropyl acrylamide are sufficiently mixed, and
The hot pressing 5min under 135-145 DEG C of hot pressing temperature, hot pressing pressure 0.05MPa, gained mixture are transferred to close in -15 DEG C of environment immediately
Envelope stands 5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. 5g molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 10min, 0.5g Glycidyl methacrylate is added
Glyceride and 0.02g methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 30min to get modified molecular screen micro mist;
3. 0.3g hydrolysis of polymaleic anhydride and 0.3g hexamethylolmelamine six are added into 5g PVC paste resin
Methyl ether, after being sufficiently mixed under microwave frequency 2450MHz, output power 700W microwave treatment 10min to get modified polyvinyl chloride
Paste resin;
4. by modified heat convertible acrylic resin, 15g methyl-etherified melamine resin, modified polyvinyl chloride paste resin, changing
Property molecular sieve micro mist and 0.3g superfine powder of polytetrafluoroethylene mixing after be sent into kneading machine in, 5min is kneaded under molten condition, and
Through cooled to room temperature to get hot melt paint.
The preparation of molecular sieve micro mist: 5g molecular screen primary powder is roasted into 2h at 450-500 DEG C, after naturally cool to 120-
0.3g stearyl alcohol and 0.3g glutamic acid are added after 130 DEG C, and the heat preservation grinding 30min at 120-130 DEG C, continue to naturally cool to
15g deionized water is added dropwise into gained mixture, 15min is stood after being added dropwise for room temperature under stirring, filter, and gained filter residue is sent
Enter in freeze drier, micro mist is made through micronizer to get molecular sieve micro mist in dry obtained solid.
Embodiment 2
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 40g thermosetting acrylic resin, 5g asparatate and 2g n-isopropyl acrylamide are sufficiently mixed, and
The hot pressing 5min under 135-145 DEG C of hot pressing temperature, hot pressing pressure 0.05MPa, gained mixture are transferred to close in -15 DEG C of environment immediately
Envelope stands 5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. 5g molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 15min, 0.5g Glycidyl methacrylate is added
Glyceride and 0.03g methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 1h to get modified molecular screen micro mist;
3. 0.5g hydrolysis of polymaleic anhydride and 0.5g hexamethylolmelamine six are added into 10g PVC paste resin
Methyl ether, after being sufficiently mixed under microwave frequency 2450MHz, output power 700W microwave treatment 10min to get modified polyvinyl chloride
Paste resin;
4. by modified heat convertible acrylic resin, 20g methyl-etherified melamine resin, modified polyvinyl chloride paste resin, changing
Property molecular sieve micro mist and 0.5g superfine powder of polytetrafluoroethylene mixing after be sent into kneading machine in, 5min is kneaded under molten condition, and
Through cooled to room temperature to get hot melt paint.
The preparation of molecular sieve micro mist: 3g molecular screen primary powder is roasted into 2h at 450-500 DEG C, after naturally cool to 120-
0.2g stearyl alcohol and 0.1g glutamic acid are added after 130 DEG C, and the heat preservation grinding 30min at 120-130 DEG C, continue to naturally cool to
10g deionized water is added dropwise into gained mixture, 10min is stood after being added dropwise for room temperature under stirring, filter, and gained filter residue is sent
Enter in freeze drier, micro mist is made through micronizer to get molecular sieve micro mist in dry obtained solid.
Reference examples 1
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 40g thermosetting acrylic resin, 5g asparatate and 2g n-isopropyl acrylamide are sufficiently mixed, and
The hot pressing 5min under 135-145 DEG C of hot pressing temperature, hot pressing pressure 0.05MPa, gained mixture are transferred to close in -15 DEG C of environment immediately
Envelope stands 5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. 5g molecular screen primary powder is warming up to 110-120 DEG C of heat preservation grinding 15min, 0.5g Glycidyl methacrylate is added
Glyceride and 0.03g methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 1h to get modified molecular screen original powder;
3. 0.5g hydrolysis of polymaleic anhydride and 0.5g hexamethylolmelamine six are added into 10g PVC paste resin
Methyl ether, after being sufficiently mixed under microwave frequency 2450MHz, output power 700W microwave treatment 10min to get modified polyvinyl chloride
Paste resin;
4. by modified heat convertible acrylic resin, 20g methyl-etherified melamine resin, modified polyvinyl chloride paste resin, changing
Property molecular screen primary powder and 0.5g superfine powder of polytetrafluoroethylene mixing after be sent into kneading machine in, 5min is kneaded under molten condition, and
Through cooled to room temperature to get hot melt paint.
Reference examples 2
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 40g thermosetting acrylic resin, 5g asparatate and 2g n-isopropyl acrylamide are sufficiently mixed, and
The hot pressing 5min under 135-145 DEG C of hot pressing temperature, hot pressing pressure 0.05MPa, gained mixture are transferred to close in -15 DEG C of environment immediately
Envelope stands 5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. 0.5g hydrolysis of polymaleic anhydride and 0.5g hexamethylolmelamine six are added into 10g PVC paste resin
Methyl ether, after being sufficiently mixed under microwave frequency 2450MHz, output power 700W microwave treatment 10min to get modified polyvinyl chloride
Paste resin;
3. modified heat convertible acrylic resin, 20g methyl-etherified melamine resin, modified polyvinyl chloride are pasted resin, 5g
It is sent into kneading machine after molecular sieve micro mist and the mixing of 0.5g superfine powder of polytetrafluoroethylene, 5min is kneaded under molten condition, and pass through
Cooled to room temperature is to get hot melt paint.
The preparation of molecular sieve micro mist: 3g molecular screen primary powder is roasted into 2h at 450-500 DEG C, after naturally cool to 120-
0.2g stearyl alcohol and 0.1g glutamic acid are added after 130 DEG C, and the heat preservation grinding 30min at 120-130 DEG C, continue to naturally cool to
10g deionized water is added dropwise into gained mixture, 10min is stood after being added dropwise for room temperature under stirring, filter, and gained filter residue is sent
Enter in freeze drier, micro mist is made through micronizer to get molecular sieve micro mist in dry obtained solid.
Reference examples 3
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 40g thermosetting acrylic resin, 5g asparatate and 2g n-isopropyl acrylamide are sufficiently mixed, and
The hot pressing 5min under 135-145 DEG C of hot pressing temperature, hot pressing pressure 0.05MPa, gained mixture are transferred to close in -15 DEG C of environment immediately
Envelope stands 5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. 5g molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 15min, 0.5g Glycidyl methacrylate is added
Glyceride and 0.03g methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 1h to get modified molecular screen micro mist;
3. by modified heat convertible acrylic resin, 20g methyl-etherified melamine resin, 10g PVC paste resin, modification
It is sent into kneading machine after molecular sieve micro mist and the mixing of 0.5g superfine powder of polytetrafluoroethylene, 5min is kneaded under molten condition, and pass through
Cooled to room temperature is to get hot melt paint.
The preparation of molecular sieve micro mist: 3g molecular screen primary powder is roasted into 2h at 450-500 DEG C, after naturally cool to 120-
0.2g stearyl alcohol and 0.1g glutamic acid are added after 130 DEG C, and the heat preservation grinding 30min at 120-130 DEG C, continue to naturally cool to
10g deionized water is added dropwise into gained mixture, 10min is stood after being added dropwise for room temperature under stirring, filter, and gained filter residue is sent
Enter in freeze drier, micro mist is made through micronizer to get molecular sieve micro mist in dry obtained solid.
Reference examples 4
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-
The heating rate of 10 DEG C/min is warming up to 60-70 DEG C of preheating 10min, then the two-sided roller of hot melt paint is carried out to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-
Spontaneous curing in 60% environment;
(3) sawing sheet cabinet plate: carrying out sawing sheet to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body,
Obtain bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw works
Accessory.
Heat the preparation of paint:
1. 5g molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 15min, 0.5g Glycidyl methacrylate is added
Glyceride and 0.03g methylol ferrocene continue in 110-120 DEG C of heat preservation grinding 1h to get modified molecular screen micro mist;
2. 0.5g hydrolysis of polymaleic anhydride and 0.5g hexamethylolmelamine six are added into 10g PVC paste resin
Methyl ether, after being sufficiently mixed under microwave frequency 2450MHz, output power 700W microwave treatment 10min to get modified polyvinyl chloride
Paste resin;
3. 40g thermosetting acrylic resin, 20g methyl-etherified melamine resin, modified polyvinyl chloride are pasted resin, modification
It is sent into kneading machine after molecular sieve micro mist and the mixing of 0.5g superfine powder of polytetrafluoroethylene, 5min is kneaded under molten condition, and pass through
Cooled to room temperature is to get hot melt paint.
The preparation of molecular sieve micro mist: 3g molecular screen primary powder is roasted into 2h at 450-500 DEG C, after naturally cool to 120-
0.2g stearyl alcohol and 0.1g glutamic acid are added after 130 DEG C, and the heat preservation grinding 30min at 120-130 DEG C, continue to naturally cool to
10g deionized water is added dropwise into gained mixture, 10min is stood after being added dropwise for room temperature under stirring, filter, and gained filter residue is sent
Enter in freeze drier, micro mist is made through micronizer to get molecular sieve micro mist in dry obtained solid.
Embodiment 3
Respectively to embodiment 1, embodiment 2, reference examples 1, reference examples 2, reference examples 3, the made solid wood bathroom cabinet cabinet of reference examples 4
The service performance of plate is tested, and the reference examples 5 of no roller coating hot melt paint are arranged, and the results are shown in Table 1.
The service performance of the made solid wood bathroom cabinet cabinet plate of 1 embodiment of the present invention of table
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of processing method of solid wood bathroom cabinet cabinet plate, it is characterised in that: mainly include the following steps:
(1) hot melt paint coating: the solid wood board after distillation dehydration is sent into paint line, and by solid wood board with 5-10
DEG C/heating rate of min is warming up to 60-70 DEG C of preheating 5-10min, then carries out the two-sided roller of hot melt paint to preheating solid wood board
It applies, the coating layer thickness formed after solidifying is made to reach 50-60 μm;
The hot melt paint is made of the raw material of following parts by weight: 35-40 parts of thermosetting acrylic resin, methyl-etherified melamine
15-20 parts of resin, 5-10 parts of PVC paste resin, 1-5 parts of molecular sieve micro mist, 1-5 parts of asparatate, N- isopropyl propylene
0.5-3 parts of amide, 0.5-3 parts of glycidyl methacrylate, 0.1-1 parts of hydrolysis of polymaleic anhydride, hexamethylol melamine
0.1-1 parts of amine pregnancy ether, 0.1-1 parts of superfine powder of polytetrafluoroethylene, 0.01-0.05 parts of methylol ferrocene;
(2) curing of coatings: the solid wood board that above-mentioned roller coating is heated well to paint is placed in 25-30 DEG C of temperature, relative humidity 55-60%
Spontaneous curing in environment;
(3) sawing sheet cabinet plate: sawing sheet is carried out to solid wood board obtained by above-mentioned processing according to the design size of bathroom cabinet cabinet body, is obtained
Bathroom cabinet plate;
(4) edge sealing processing waterproof edge sealing: is carried out to the cabinet plate after sawing sheet using PUR waterproof edge sealing technology;
(5) assembly hole is reserved: to through waterproof edge sealing, treated that cabinet plate reserves assembly hole, inside setting assembling screw, which works, matches
Part;
The specific preparation method of the hot melt paint includes the following steps:
1. thermosetting acrylic resin, asparatate and n-isopropyl acrylamide are sufficiently mixed, and in hot pressing temperature
135-145 DEG C, hot pressing 3-5min under hot pressing pressure 0.05MPa, gained mixture are transferred to sealing and standing 3- in -15 DEG C of environment immediately
5h, then the powder of granularity 0.05-0.1mm is made to get modified heat convertible acrylic resin through pulverizer;
2. molecular sieve micro mist is warming up to 110-120 DEG C of heat preservation grinding 10-15min, glycidyl methacrylate is added
With methylol ferrocene, continue in 110-120 DEG C of heat preservation grinding 30-60min to get modified molecular screen micro mist;
3. hydrolysis of polymaleic anhydride and hexamethylolmelamine pregnancy ether are added into PVC paste resin, after being sufficiently mixed
Microwave treatment 5-10min pastes resin to get modified polyvinyl chloride under microwave frequency 2450MHz, output power 700W;
4. modified heat convertible acrylic resin, methyl-etherified melamine resin, modified polyvinyl chloride are pasted resin, modified molecular screen
It is sent into kneading machine after micro mist and superfine powder of polytetrafluoroethylene mixing, 3-5min is kneaded under molten condition, and through natural cooling
To room temperature to get hot melt paint;
The molecular sieve micro mist be by molecular screen primary powder it is preprocessed be made, preprocess method are as follows: by molecular screen primary powder in
2-3h is roasted at 450-500 DEG C, after naturally cool to addition stearyl alcohol and glutamic acid after 120-130 DEG C, and at 120-130 DEG C
Heat preservation grinding 15-30min, continues cooled to room temperature, deionized water is added dropwise into gained mixture under stirring, is added dropwise
After stand 10-15min, filter, gained filter residue is sent into freeze drier, and dry obtained solid is made micro- through micronizer
Powder is to get molecular sieve micro mist.
2. the processing method of solid wood bathroom cabinet cabinet plate according to claim 1, it is characterised in that: the molecular screen primary powder,
The mass ratio of stearyl alcohol, glutamic acid and deionized water is 3-5:0.1-1:0.1-1:10-20.