CN107158965A - A kind of air filting material - Google Patents
A kind of air filting material Download PDFInfo
- Publication number
- CN107158965A CN107158965A CN201710440242.6A CN201710440242A CN107158965A CN 107158965 A CN107158965 A CN 107158965A CN 201710440242 A CN201710440242 A CN 201710440242A CN 107158965 A CN107158965 A CN 107158965A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- raw material
- fibre
- air filting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of air filtration, a kind of air filting material is disclosed, is characterized in that:It is made up of the raw material below according to parts by weight:50 100 parts of bacteria cellulose fibre, 2 10 parts of zinc oxide, 2 10 parts of activated carbon, 35 parts of potassium dihydrogen phosphate, 30 50 parts of glass bead, 2 10 parts of Sodium Polyacrylate, 2 10 parts of aluminum silicon powder of oxidation, 35 parts of tetra oxygen furyl.Including the raw material composition according to parts by weight:35 parts of 10 20 parts of bamboo fibre, 10 20 parts of wood fibre and isopropanol.Solve and filtered using non-woven cotton more than existing filtering material, filter effect is general, in the case where present PM2.5 is often exceeded, original filtering material is difficult the problem of playing use.
Description
Technical field
Concretely it is a kind of air filting material the present invention relates to field of air filtration.
Background technology
A set of independent air processing system that VMC is made up of supply air system and exhaust system, it is divided into duct type
VMC and without two kinds of pipeline VMC.Duct type VMC is made up of new blower fan and pipe fitting, passes through new blower fan
Clean room outer space conductance enters interior, is discharged room air by pipeline;Without pipeline VMC by Fresh air handling units into, equally by
New blower fan clean room outer space conductance enters interior, while being discharged foul indoor air by breathing treasured.Comparatively duct type fresh air
System is used because quantities is more suitable for greatly industrial or large area Office Area, and without pipeline VMC because easy for installation,
It is more suitable for family to use.
Air pollution has been listed in one of the pollution greatly of the world three, and harm and influence are all very big, suck low quality air
It is easy to infringement healthy, induces various diseases.Air is filtered using filtering material, particularly made in VMC
Extremely popularized with filtering material filtering.
Filtered more than existing filtering material using non-woven cotton, filter effect is general, in the frequent exceeded feelings of present PM2.5
Under condition, original filtering material is difficult to play use.
Accordingly, it would be desirable to a kind of simple in construction, it is possible to increase VMC filter effect, it is greatly reduced and pours into air
A kind of air filting material of PM2.5 contents.
The content of the invention
The present invention using non-woven cotton for being filtered more than existing filtering material, and filter effect is general, is passed through in present PM2.5
In the case of Chang Chaobiao, original filtering material is difficult that there is provided a kind of air filting material the problem of playing use.
The present invention solves above-mentioned technical problem, and the technical scheme of use is, a kind of air filting material, by below according to weight
Measure the raw material composition of part:50-100 parts of bacteria cellulose fibre, 2-10 parts of zinc oxide, 2-10 parts of activated carbon, potassium dihydrogen phosphate 3-5
Part, 30-50 parts of glass bead, 2-10 parts of Sodium Polyacrylate, 2-10 parts of aluminum silicon powder of oxidation, 3-5 parts of tetra oxygen furyl.
Optionally, it is made up of the raw material below according to parts by weight:60-90 parts of bacteria cellulose fibre, 3-8 parts of zinc oxide,
3-8 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, 32-48 parts of glass bead, 3-8 parts of Sodium Polyacrylate, oxidation 3-8 parts of aluminum silicon powder,
3-5 parts of tetra oxygen furyl.
Further, it is made up of the raw material below according to parts by weight:65-85 parts of bacteria cellulose fibre, zinc oxide 4-7
Part, 4-7 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, 35-45 parts of glass bead, 4-7 parts of Sodium Polyacrylate, oxidation aluminum silicon powder 4-7
Part, 3-5 parts of tetra oxygen furyl.
Further, it is made up of the raw material below according to parts by weight:70-80 parts of bacteria cellulose fibre, zinc oxide 5-7
Part, 5-7 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, 38-42 parts of glass bead, 5-7 parts of Sodium Polyacrylate, oxidation aluminum silicon powder 5-7
Part, 3-5 parts of tetra oxygen furyl.
Optionally, it is made up of the raw material below according to parts by weight:75 parts of bacteria cellulose fibre, 67 parts of zinc oxide, activity
6 parts of charcoal, 4 parts of potassium dihydrogen phosphate, 40 parts of glass bead, 6 parts of Sodium Polyacrylate, 6 parts of aluminum silicon powder of oxidation, 4 parts of tetra oxygen furyl.
Optionally, in addition to according to the raw material of parts by weight constitute:10-20 parts of bamboo fibre, 10-20 parts of wood fibre and isopropyl
3-5 parts of alcohol.
Optionally, including according to the raw material of parts by weight constitute:12-18 parts of bamboo fibre, 12-18 parts of wood fibre and isopropanol
3-5 parts.
Optionally, including according to the raw material of parts by weight constitute:4 parts of 15 parts of bamboo fibre, 15 parts of wood fibre and isopropanol.
The purpose so designed is, because glass bead is mixed with zinc oxide, after being handled by potassium dihydrogen phosphate again with
Activated carbon is blended in processing and can significantly improve the mechanical strength of product provides skeleton structure for filtering material, serves support
Effect, and glass bead layer can play certain filter effect.
Meanwhile, the cellulose banding beamwidth as made from bacteriocin is 70-80nm, and it is directly far smaller than glass fibre, changed
Work fiber and string, can be difficult that the clean material filtered is filtered by other filtering materials with highly-breathable,
It is greatly reduced and imports indoor PM2.5 contents.
Beneficial effects of the present invention are at least one below:
1. being mixed by glass bead with zinc oxide, being blended in processing with activated carbon again after being handled by potassium dihydrogen phosphate can
Skeleton structure is provided to significantly improve the mechanical strength of product as filtering material, supporting role, and glass bead layer is served
Certain filter effect can be played.
2. being 70-80nm by the cellulose banding beamwidth as made from bacteriocin, it is directly far smaller than glass fibre, changed
Work fiber and string, can be difficult that the clean material filtered is filtered by other filtering materials with highly-breathable,
It is greatly reduced and imports indoor PM2.5 contents.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments to the present invention
It is described in further detail.It should be appreciated that specific embodiment described herein is used only for explaining the present invention, limit is not used to
The fixed present invention.
Embodiment 1
Filter membrane is made from the filtering material of non-woven cotton material, is put into VMC, opens VMC and is changed
PM2.5 values at gas, statistics VMC air outlet, statistics, labeled as A.
Embodiment 2
A kind of air filting material, is made up of the raw material below according to parts by weight:Including 50 parts of bacteria cellulose fibre, oxygen
Change 2 parts of zinc, 2 parts of activated carbon, 3 parts of potassium dihydrogen phosphate, 30 parts of glass bead, 2 parts of Sodium Polyacrylate, 2 parts of aluminum silicon powder of oxidation, four oxygen
3 parts of furans.
Filter membrane is made from the filtering material, is put into VMC, opens VMC and is taken a breath, count fresh air
PM2.5 values at system air outlet, statistics, labeled as B.
Embodiment 3
A kind of air filting material, is made up of the raw material below according to parts by weight:Including 100 parts of bacteria cellulose fibre,
10 parts of zinc oxide, 10 parts of activated carbon, 5 parts of potassium dihydrogen phosphate, 50 parts of glass bead, 10 parts of Sodium Polyacrylate, oxidation aluminum silicon powder 10
Part, 5 parts of tetra oxygen furyl.
Filter membrane is made from the filtering material, is put into VMC, opens VMC and is taken a breath, count fresh air
PM2.5 values at system air outlet, statistics, labeled as C.
Embodiment 4
A kind of air filting material, is made up of the raw material below according to parts by weight:75 parts of bacteria cellulose fibre, zinc oxide
67 parts, 6 parts of activated carbon, 4 parts of potassium dihydrogen phosphate, 40 parts of glass bead, 6 parts of Sodium Polyacrylate, oxidation 6 parts of aluminum silicon powder, four oxygen furans
Mutter 4 parts.
Filter membrane is made from the filtering material, is put into VMC, opens VMC and is taken a breath, count fresh air
PM2.5 values at system air outlet, statistics, labeled as D.
Embodiment 5
A kind of air filting material, is made up of the raw material below according to parts by weight:75 parts of bacteria cellulose fibre, zinc oxide
67 parts, 6 parts of activated carbon, 4 parts of potassium dihydrogen phosphate, 40 parts of glass bead, 6 parts of Sodium Polyacrylate, oxidation 6 parts of aluminum silicon powder, four oxygen furans
Mutter 4 parts.Also include constituting according to the raw material of parts by weight:4 parts of 15 parts of bamboo fibre, 15 parts of wood fibre and isopropanol.
Filter membrane is made from the filtering material, is put into VMC, opens VMC and is taken a breath, count fresh air
PM2.5 values at system air outlet, statistics, labeled as E.
Embodiment 5
Contrast marker A~E data, are made following table:
Project | A groups | B groups | C groups | D groups | E groups |
PM2.5 values | 58 | 9 | 8 | 7 | 5 |
It can be obtained by contrasting 5 groups of experimental datas, VMC filter membrane made from the filtering material provided by the present invention,
It is significantly larger than existing non-woven cotton filtering material for PM2.5 filter effects, it is every that World Health Organization requires that PM2.5 standard values should be less than
10 micrograms of cubic meter, existing non-woven cotton filtration of material result is every cubic metre of 58 microgram, although meets national standard and is less than and often stands
The square microgram of rice 75, but with a certain distance from the requirement from World Health Organization still has.
The B groups of VMC filter membrane made from the filtering material that the present invention is provided are contrasted simultaneously to E group data, can obtain E
Assemble more best than obtained filter membrane filter effect.
Claims (8)
1. a kind of air filting material, it is characterised in that:It is made up of the raw material below according to parts by weight:Bacteria cellulose fibre
50-100 parts, 2-10 parts of zinc oxide, 2-10 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, 30-50 parts of glass bead, Sodium Polyacrylate
2-10 parts, oxidation 2-10 parts of aluminum silicon powder, 3-5 parts of tetra oxygen furyl.
2. a kind of air filting material according to claim 1, it is characterised in that:By below according to the raw material group of parts by weight
Into:60-90 parts of bacteria cellulose fibre, 3-8 parts of zinc oxide, 3-8 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, glass bead 32-
48 parts, 3-8 parts of Sodium Polyacrylate, oxidation 3-8 parts of aluminum silicon powder, 3-5 parts of tetra oxygen furyl.
3. a kind of air filting material according to claim 1, it is characterised in that:By below according to the raw material group of parts by weight
Into:65-85 parts of bacteria cellulose fibre, 4-7 parts of zinc oxide, 4-7 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, glass bead 35-
45 parts, 4-7 parts of Sodium Polyacrylate, oxidation 4-7 parts of aluminum silicon powder, 3-5 parts of tetra oxygen furyl.
4. a kind of air filting material according to claim 1, it is characterised in that:By below according to the raw material group of parts by weight
Into:70-80 parts of bacteria cellulose fibre, 5-7 parts of zinc oxide, 5-7 parts of activated carbon, 3-5 parts of potassium dihydrogen phosphate, glass bead 38-
42 parts, 5-7 parts of Sodium Polyacrylate, oxidation 5-7 parts of aluminum silicon powder, 3-5 parts of tetra oxygen furyl.
5. a kind of air filting material according to claim 1, it is characterised in that:By below according to the raw material group of parts by weight
Into:75 parts of bacteria cellulose fibre, 67 parts of zinc oxide, 6 parts of activated carbon, 4 parts of potassium dihydrogen phosphate, 40 parts of glass bead, polypropylene
Sour 6 parts of sodium, 6 parts of aluminum silicon powder of oxidation, 4 parts of tetra oxygen furyl.
6. a kind of air filting material according to claim 1, it is characterised in that:Also include the raw material group according to parts by weight
Into:3-5 parts of 10-20 parts of bamboo fibre, 10-20 parts of wood fibre and isopropanol.
7. a kind of air filting material according to claim 6, it is characterised in that:Including the raw material group according to parts by weight
Into:3-5 parts of 12-18 parts of bamboo fibre, 12-18 parts of wood fibre and isopropanol.
8. a kind of air filting material according to claim 6, it is characterised in that:Including the raw material group according to parts by weight
Into:4 parts of 15 parts of bamboo fibre, 15 parts of wood fibre and isopropanol.