CN107157762A - 一种石墨烯艾炙贴的制造方法 - Google Patents
一种石墨烯艾炙贴的制造方法 Download PDFInfo
- Publication number
- CN107157762A CN107157762A CN201710546662.2A CN201710546662A CN107157762A CN 107157762 A CN107157762 A CN 107157762A CN 201710546662 A CN201710546662 A CN 201710546662A CN 107157762 A CN107157762 A CN 107157762A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixed liquor
- graphene
- obtains
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种石墨烯艾炙贴的制造方法，具体为以特殊工艺烧结远红外陶瓷；以石墨为原材料通过预氧化、浓硫酸及高锰酸钾氧化、过氧化氢终氧化等三个阶段获得充分氧化的氧化石墨，再通过强还原剂的维生素C获得无害且有保健作用的石墨烯粉末，又填充热炙效果最佳的陈放3年‑5年的陈艾叶末而最终获得。本发明的石墨烯艾炙贴成本低、使用方便、持续时间长、效果显著、可循环使用。
Description
技术领域
本发明涉及药用品领域，尤其涉及一种石墨烯艾炙贴的制造方法。
背景技术
艾灸：中医针灸疗法中的灸法。点燃用艾叶制成的艾炷、艾条为主，熏烤人体的穴位以达到保健治病的一种自然疗法。艾灸产生于中国远古时代，因为它的作用机理和针疗有相近之处，并且与针疗有相辅相成的治疗作用，通常针、灸并用，故称为针灸。是用艾叶制成的艾灸材料产生的艾热刺激体表穴位或特定部位，通过激发经气的活动来调整人体紊乱的生理生化功能，从而达到防病治病目的的一种治疗方法。
但现有技术中真正有效的艾灸主要通过有多年经验的人手动操作，方便快捷的艾炙贴多为艾叶与胶片的机械结合，效果不好，且没有配套的热、磁作用，同时易伤害皮肤，生效时间短且持续性差，同时有些制作成本高的艾炙贴无法循环使用也造成了极大的浪费。
针对现有技术中的这些问题，市场上亟待一种成本低、使用方便、持续时间长、效果显著、可循环使用的艾炙贴。
发明内容
为解决现有技术中存在的上述缺陷，本发明旨在提供一种成本低、使用方便、持续时间长、效果显著、可循环使用的石墨烯艾炙贴的制造方法。
为了实现上述发明目的，本发明采用以下技术方案：一种制造石墨烯艾炙贴的方法，包括以下步骤：
1）无纺布包制备
①采用网孔间隙0.1mm-0.2mm的单层无纺布编织成内含两层空间的布包，所述两层空间分别为第一空间和第二空间；
2）远红外陶瓷珠制备
①按重量份准备氯化镁11份-13份、次氯酸锆25份-30份、硫酸铝铵65份-70份、四氯化硅55份-60份、四氯化钛70份-75份、三氯化钇2份-3份、三氯化铝1份-2份，混合并搅拌均匀作为添加物；
②将石英25份-30份、长石35份-40份、滑石5份-8份分别煅烧制成熟料；
③按重量份将高岭土10份-15份、黑电气石2份-3份、稀土0.3份-0.5份与粘合剂混合、造粒、烘干，烧制成陶粒；
④将步骤③获得的陶粒、步骤②获得的熟料、步骤①获得的添加物混合并搅拌均匀，经过550℃-600℃、保温1h-2h，800℃-850℃、保温1h-2h，1350℃-1400℃，保温2h-3h的工艺烧结成陶瓷坯；
⑤将陶瓷坯机械破碎并研磨成直径2.5mm-4mm的陶瓷球，该陶瓷球即为所需远红外陶瓷珠；
3）石墨烯粉末制备
①准备石墨粉，置于550℃-600℃有氧环境内，保持3h-3.5h，获得预氧化石墨；
②将步骤①获得的预氧化石墨缓慢沉入盛放有浓度为98%的浓硫酸中，获得第一混合液；
③在步骤②获得的第一混合液中缓慢添加原石墨总质量5倍-6倍的高锰酸钾粉末，并采用玻璃棒缓慢搅拌，持续2h-3h，获得第二混合液；
④将盛放有第二混合液的容器缓慢放入冰水浴桶中，保持容器开口处在冰水液水平面上方，并在容器内放置水银温度计；
⑤在第二混合液内缓慢滴加纯净水，加入速度控制在容器内液体温度不高于40℃，滴加总体积为第二混合液总体积的2倍-2.5倍，获得第三混合液；
⑥在第三混合液内滴加体积分数3%-5%的过氧化氢水溶液，至第三混合液内不再有气泡产生，滤除液体，获得充分氧化的氧化石墨；
⑦将步骤⑥获得的氧化石墨浸入纯净水中，缓慢加热至50℃-60℃，持续加入维生素C粉末，至反应完结，滤除液体，将固含物研磨成粉，获得石墨烯粉末；
4）艾炙贴制备
①将新鲜艾叶陈放3年-5年，获得陈艾；
②将陈艾机械粉碎为尺寸0.5mm-2mm的碎末，然后与3）中步骤⑦获得的石墨烯粉末混合均匀，填充进第二空间；
③在第一空间内部填装2）中步骤⑤获得的远红外陶瓷珠；
④在第一空间远离第二空间的外表面粘贴矩形胶片，即获得所需石墨烯艾炙贴。
与现有技术相比较，由于采用了上述技术方案，本发明具有以下优点：采用价格低廉的石墨为原料，再采用特殊工艺的三次氧化加维生素还原的氧化还原法制备的石墨烯粉末纯度优于市售石墨烯，同时由于基材的方向性均一、三次氧化均为大气均匀氧化或液体浸润氧化，使得生成的石墨烯粉末的均匀性及热、磁性能相当稳定而可靠（石墨烯对高周波磁场具有极好适应性，同时能引导磁力线的方向）；远红外陶瓷珠通过加热进行能量转换，它通过吸收电磁波产生共振，又将共振产生的动能转化成热能蓄存起来，热能则激发了远红外线，而这种远红外线波长正好与人体高分子蛋白的振动频率一致，可在人体组织内生热，产生生理、生物效应，可以起到温经散寒、活血化瘀、软坚散结，恢复经络通畅的目的，达到扶正祛邪、补虚泻实、调节脏腑功能，行气活血、消肿止痛、祛风除湿、治病强身保健之目的；选用陈艾是根据大量研究表明，新艾其中的挥发油没有完全挥发掉，不仅不能达到治疗效果，而且可能对人体产生一定的危害，而陈艾其艾油已经完全挥发掉，不会对人体造成危害，而且渗透力好；新艾施灸有灼痛感，而陈艾施灸则相对柔和灸感明显效果好；陈艾灸热“温而不燥，润能通经”，远红外陶瓷珠放热过程中，陈艾末释放的热力温和，能穿透皮肤，直达深部，经久不消，功效强劲；由于有石墨烯粉末的存在，陈艾的受热更加均匀，同时远红外陶瓷珠释放的远红外线经粉末状石墨烯散射后获得了更好的穿透性，由于远红外陶瓷珠只需要吸收机械能，即随着人体运动自然生热，生效时间极长；由于石墨烯及远红外陶瓷珠物理化学性质稳定可以撕去胶片、燃烧去除陈艾叶，成本高且制作难度大的石墨烯粉末和远红外陶瓷珠可重复再利用。
具体实施方式
实施例1
一种制造石墨烯艾炙贴的方法，包括以下步骤：
1）无纺布包制备
①采用网孔间隙0.2mm的单层无纺布编织成内含两层空间的布包，所述两层空间分别为第一空间和第二空间；
2）远红外陶瓷珠制备
①按重量份准备氯化镁12份、次氯酸锆28份、硫酸铝铵68份、四氯化硅58份、四氯化钛72份、三氯化钇2.5份、三氯化铝1.5份，混合并搅拌均匀作为添加物；
②将石英28份、长石38份、滑石6份分别煅烧制成熟料；
③按重量份将高岭土12份、黑电气石2.5份、稀土0.4份与粘合剂混合、造粒、烘干，烧制成陶粒；
④将步骤③获得的陶粒、步骤②获得的熟料、步骤①获得的添加物混合并搅拌均匀，经过580℃、保温1.5h，820℃、保温1.5h，1380℃，保温2.5h的工艺烧结成陶瓷坯；
⑤将陶瓷坯机械破碎并研磨成直径3mm的陶瓷球，该陶瓷球即为所需远红外陶瓷珠；
3）石墨烯粉末制备
①准备石墨粉，置于580℃有氧环境内，保持3.5h，获得预氧化石墨；
②将步骤①获得的预氧化石墨缓慢沉入盛放有浓度为98%的浓硫酸中，获得第一混合液；
③在步骤②获得的第一混合液中缓慢添加原石墨总质量5.5倍的高锰酸钾粉末，并采用玻璃棒缓慢搅拌，持续2.5h，获得第二混合液；
④将盛放有第二混合液的容器缓慢放入冰水浴桶中，保持容器开口处在冰水液水平面上方，并在容器内放置水银温度计；
⑤在第二混合液内缓慢滴加纯净水，加入速度控制在容器内液体温度不高于40℃，滴加总体积为第二混合液总体积的2.2倍，获得第三混合液；
⑥在第三混合液内滴加体积分数4%的过氧化氢水溶液，至第三混合液内不再有气泡产生，滤除液体，获得充分氧化的氧化石墨；
⑦将步骤⑥获得的氧化石墨浸入纯净水中，缓慢加热至55℃，持续加入维生素C粉末，至反应完结，滤除液体，将固含物研磨成粉，获得石墨烯粉末；
4）艾炙贴制备
①将新鲜艾叶陈放3年-5年，获得陈艾；
②将陈艾机械粉碎为尺寸0.5mm-2mm的碎末，然后与3）中步骤⑦获得的石墨烯粉末混合均匀，填充进第二空间；
③在第一空间内部填装2）中步骤⑤获得的远红外陶瓷珠；
④在第一空间远离第二空间的外表面粘贴矩形胶片，即获得所需石墨烯艾炙贴。
实施例2
整体与实施例1一致，差异之处在于：
一种制造石墨烯艾炙贴的方法，包括以下步骤：
1）无纺布包制备
①采用网孔间隙0.1mm的单层无纺布编织成内含两层空间的布包，所述两层空间分别为第一空间和第二空间；
2）远红外陶瓷珠制备
①按重量份准备氯化镁11份、次氯酸锆25份、硫酸铝铵65份、四氯化硅55份、四氯化钛70份、三氯化钇2份、三氯化铝1份，混合并搅拌均匀作为添加物；
②将石英25份、长石35份、滑石5份分别煅烧制成熟料；
③按重量份将高岭土10份份、黑电气石2份、稀土0.3份与粘合剂混合、造粒、烘干，烧制成陶粒；
④将步骤③获得的陶粒、步骤②获得的熟料、步骤①获得的添加物混合并搅拌均匀，经过550℃、保温1h，800℃、保温1h，1350℃、保温2h的工艺烧结成陶瓷坯；
⑤将陶瓷坯机械破碎并研磨成直径2.5mm的陶瓷球，该陶瓷球即为所需远红外陶瓷珠；
3）石墨烯粉末制备
①准备石墨粉，置于550℃有氧环境内，保持3h，获得预氧化石墨；
③在步骤②获得的第一混合液中缓慢添加原石墨总质量5倍的高锰酸钾粉末，并采用玻璃棒缓慢搅拌，持续2h，获得第二混合液；
⑤在第二混合液内缓慢滴加纯净水，加入速度控制在容器内液体温度不高于40℃，滴加总体积为第二混合液总体积的2倍，获得第三混合液；
⑥在第三混合液内滴加体积分数3%的过氧化氢水溶液，至第三混合液内不再有气泡产生，滤除液体，获得充分氧化的氧化石墨；
⑦将步骤⑥获得的氧化石墨浸入纯净水中，缓慢加热至50℃，持续加入维生素C粉末，至反应完结，滤除液体，将固含物研磨成粉，获得石墨烯粉末；
实施例3
整体与实施例1一致，差异之处在于：
2）远红外陶瓷珠制备
①按重量份准备氯化镁13份、次氯酸锆30份、硫酸铝铵70份、四氯化硅60份、四氯化钛75份、三氯化钇3份、三氯化铝2份，混合并搅拌均匀作为添加物；
②将石英30份、长石40份、滑石8份分别煅烧制成熟料；
③按重量份将高岭土15份、黑电气石3份、稀土0.5份与粘合剂混合、造粒、烘干，烧制成陶粒；
④将步骤③获得的陶粒、步骤②获得的熟料、步骤①获得的添加物混合并搅拌均匀，经过600℃、保温2h， 850℃、保温2h， 1400℃、保温3h的工艺烧结成陶瓷坯；
⑤将陶瓷坯机械破碎并研磨成直径4mm的陶瓷球，该陶瓷球即为所需远红外陶瓷珠；
3）石墨烯粉末制备
①准备石墨粉，置于600℃有氧环境内，保持3.5h，获得预氧化石墨；
③在步骤②获得的第一混合液中缓慢添加原石墨总质量6倍的高锰酸钾粉末，并采用玻璃棒缓慢搅拌，持续3h，获得第二混合液；
⑤在第二混合液内缓慢滴加纯净水，加入速度控制在容器内液体温度不高于40℃，滴加总体积为第二混合液总体积的2.5倍，获得第三混合液；
⑥在第三混合液内滴加体积分数5%的过氧化氢水溶液，至第三混合液内不再有气泡产生，滤除液体，获得充分氧化的氧化石墨；
⑦将步骤⑥获得的氧化石墨浸入纯净水中，缓慢加热至60℃，持续加入维生素C粉末，至反应完结，滤除液体，将固含物研磨成粉，获得石墨烯粉末；
对所公开的实施例的上述说明，仅为了使本领域专业技术人员能够实现或使用本发明。对这些实施例的多种修改对本领域的专业技术人员来说将是显而易见的，本文中所定义的一般原理可以在不脱离本发明的精神或范围的情况下，在其它实施例中实现。因此，本发明将不会被限制于本文所示的这些实施例，而是要符合与本文所公开的原理和新颖特点相一致的最宽的范围。
Claims (1)
1.一种制造石墨烯艾炙贴的方法，其特征在于包括以下步骤：
1）无纺布包制备
①采用网孔间隙0.1mm-0.2mm的单层无纺布编织成内含两层空间的布包，所述两层空间分别为第一空间和第二空间；
2）远红外陶瓷珠制备
①按重量份准备氯化镁11份-13份、次氯酸锆25份-30份、硫酸铝铵65份-70份、四氯化硅55份-60份、四氯化钛70份-75份、三氯化钇2份-3份、三氯化铝1份-2份，混合并搅拌均匀作为添加物；
②将石英25份-30份、长石35份-40份、滑石5份-8份分别煅烧制成熟料；
③按重量份将高岭土10份-15份、黑电气石2份-3份、稀土0.3份-0.5份与粘合剂混合、造粒、烘干，烧制成陶粒；
④将步骤③获得的陶粒、步骤②获得的熟料、步骤①获得的添加物混合并搅拌均匀，经过550℃-600℃、保温1h-2h，800℃-850℃、保温1h-2h，1350℃-1400℃，保温2h-3h的工艺烧结成陶瓷坯；
⑤将陶瓷坯机械破碎并研磨成直径2.5mm-4mm的陶瓷球，该陶瓷球即为所需远红外陶瓷珠；
3）石墨烯粉末制备
①准备石墨粉，置于550℃-600℃有氧环境内，保持3h-3.5h，获得预氧化石墨；
②将步骤①获得的预氧化石墨缓慢沉入盛放有浓度为98%的浓硫酸中，获得第一混合液；
③在步骤②获得的第一混合液中缓慢添加原石墨总质量5倍-6倍的高锰酸钾粉末，并采用玻璃棒缓慢搅拌，持续2h-3h，获得第二混合液；
④将盛放有第二混合液的容器缓慢放入冰水浴桶中，保持容器开口处在冰水液水平面上方，并在容器内放置水银温度计；
⑤在第二混合液内缓慢滴加纯净水，加入速度控制在容器内液体温度不高于40℃，滴加总体积为第二混合液总体积的2倍-2.5倍，获得第三混合液；
⑥在第三混合液内滴加体积分数3%-5%的过氧化氢水溶液，至第三混合液内不再有气泡产生，滤除液体，获得充分氧化的氧化石墨；
⑦将步骤⑥获得的氧化石墨浸入纯净水中，缓慢加热至50℃-60℃，持续加入维生素C粉末，至反应完结，滤除液体，将固含物研磨成粉，获得石墨烯粉末；
4）艾炙贴制备
①将新鲜艾叶陈放3年-5年，获得陈艾；
②将陈艾机械粉碎为尺寸0.5mm-2mm的碎末，然后与3）中步骤⑦获得的石墨烯粉末混合均匀，填充进第二空间；
③在第一空间内部填装2）中步骤⑤获得的远红外陶瓷珠；
④在第一空间远离第二空间的外表面粘贴矩形胶片，即获得所需石墨烯艾炙贴。