CN107151387A - A kind of hard plastics display screen of tablet personal computer - Google Patents
A kind of hard plastics display screen of tablet personal computer Download PDFInfo
- Publication number
- CN107151387A CN107151387A CN201710507400.5A CN201710507400A CN107151387A CN 107151387 A CN107151387 A CN 107151387A CN 201710507400 A CN201710507400 A CN 201710507400A CN 107151387 A CN107151387 A CN 107151387A
- Authority
- CN
- China
- Prior art keywords
- hard
- personal computer
- tablet personal
- display screen
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hard plastics display screen of tablet personal computer, including hard plastic matrix, the hard plastic matrix lower surface adheres to one layer of rupture pressure disc, hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, and inorganic the admixture plates the film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made；The present invention can replace the strengthened glass of heavy fragility, make tablet personal computer screen lighter more tough.Hard plastic hardness is up to 9H, than the 4H of general plastic cement, is higher by as many as twice.Although strengthened glass is heavy frangible, because of hard scratch resistance, into the protective glass of wisdom device；The present invention plates special organic and inorganic the admixture plates the film on plastic cement top layer, can solve the problem of general plastic cement hardness is not enough.Inorganic ceramic is hard heat-resisting, and organic polymer light weight is soft, and the admixture plates the film combines both specialities, and after being processed on plastic cement top layer, hard plastic will possess the hardness of strengthened glass, and weight only has glass half less than the resistance to degree of falling is even more glass twice.
Description
Technical field
The invention belongs to tablet personal computer screen material field, more particularly to a kind of hard plastics of tablet personal computer are shown
Screen.
Background technology
Tablet personal computer is also portable computer, is a kind of small-sized, PC for being convenient for carrying, using touch-screen as basic
Input equipment.The touch-screen that it possesses allows user to carry out operation rather than traditional keyboard by stylus or digital pen
Or mouse.User can be real by the real keyboard of the soft keyboard on built-in handwriting recognition, screen, speech recognition or one
Now input causes tablet personal computer screen to be related to tabular mostly.
Glass material has the disadvantage that as tablet personal computer screen：（1）Glass material is frangible, and hardness is relatively low, and drop resistant
Beat ability；（2）Glass material heavier-weight so that increased burden in the overall weight increase of tablet personal computer, carrying process；
（3）The wearability of glass material is poor, and nowadays tablet personal computer almost one is touched based on capacitance plate, is entered after prolonged use,
Tablet personal computer screen is easily scratched；（4）Glass material easily leaves fingerprint etc..
The content of the invention
The invention provides a kind of hard plastics display screen of tablet personal computer, to solve the problems of the prior art.
To achieve these goals, the present invention uses following technical scheme：
A kind of hard plastics display screen of tablet personal computer, it is characterised in that：Including hard plastic matrix, the hard plastic
Matrix lower surface adheres to one layer of rupture pressure disc, and the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, institute
It is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made to state inorganic the admixture plates the film.
Further, the hard plastic matrix is made up of the raw material of following weight parts：Polyvinyl chloride 10-20, resin 10-
20th, polypropylene 150-170, aluminosilicate powder 10-12, sodium carbonate 2-3, ammonium dihydrogen phosphate 0.3-0.5, lauryl sodium sulfate
0.6-0.7, isocyanuric acid three-glycidyl ester 0.5-0.6, tetramethylol methane 3-4, polyethyleneimine 2-4, ethylene are double stearic
Acid amides 1-2, polybenzimidazoles 4-6, tetrahydrofurfuryl carbinol 1-2, stabilizer 1-3.
It is preferred that, the hard plastic matrix is made up of the raw material of following weight parts：Polyvinyl chloride 15, resin 15, poly- third
Alkene 160, aluminosilicate powder 11, sodium carbonate 2, ammonium dihydrogen phosphate 0.4, lauryl sodium sulfate 0.7, isocyanuric acid three shrink sweet
Grease 0.6, tetramethylol methane 4, polyethyleneimine 2-4, ethylene bis stearamide 1, polybenzimidazoles 5, tetrahydrofurfuryl carbinol
1st, stabilizer 2.
Further, inorganic matter and nano ceramics the plating solution mixed liquor is made up of the raw material of following weight parts：Asphalt mixtures modified by epoxy resin
Fat 15-25, auxiliary agent 15-25, filler 50-65 and curing agent 5-20.
It is preferred that, inorganic matter and nano ceramics the plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin
20th, auxiliary agent methyl iso-butyl ketone (MIBK), methyl ethyl ketone peroxide and the tertiary fourth fat of peracetic acid totally 25, nano aluminium oxide 65 and curing agent two
Monoethanolamine 18.
It is preferred that, the auxiliary agent is one kind in methyl iso-butyl ketone (MIBK), methyl ethyl ketone peroxide and the tertiary fourth fat of peracetic acid
Or any several mixture.
It is preferred that, the filler is nano silicon and the mixture of nano aluminium oxide either or both of which.
It is preferred that, the mass ratio of nano silicon and nano aluminium oxide is 1 in the filler：1.
It is preferred that, the curing agent is diethanol amine.
Compared with prior art, the invention has the advantages that：
The hard plastic that the present invention is provided, can replace the strengthened glass of heavy fragility, make tablet personal computer display screen lighter stronger
It is tough.And hard plastic hardness is up to 9H (Hardness), than the 4H of general plastic cement, it is higher by as many as twice.In general, reinforcing glass
Although glass is heavy frangible, because of hard scratch resistance, into the protective glass of wisdom device；It is special that the present invention is plated on plastic cement top layer
Organic and inorganic the admixture plates the film, can solve the problem of general plastic cement hardness is not enough.Inorganic ceramic is hard heat-resisting, organic polymer material
Soft soft, the admixture plates the film combines both specialities, and after being processed on plastic cement top layer, hard plastic will possess the hard of strengthened glass
Degree, weight only has glass half less than the resistance to degree of falling is even more glass twice.In addition, hard plastic is easily cut, it can make various
Shape and size.
Embodiment
The present invention is further described with reference to embodiment.
Embodiment 1
A kind of hard plastics display screen of tablet personal computer, including hard plastic matrix, the hard plastic matrix lower surface
Adhere to one layer of rupture pressure disc, the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, the inorganic mixing
Plated film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made；
The hard plastic matrix is made up of the raw material of following weight parts：Polyvinyl chloride 10, resin 20, polypropylene 150, aluminosilicate
Salt powder 12, sodium carbonate 2, ammonium dihydrogen phosphate 0.5, lauryl sodium sulfate 0.6, isocyanuric acid three-glycidyl ester 0.6, four hydroxyls
Methylmethane 3, polyethyleneimine 4, ethylene bis stearamide 1, polybenzimidazoles 6, tetrahydrofurfuryl carbinol 1, stabilizer 3；
Inorganic matter and nano ceramics the plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin 15, methyl tert-butyl
Base ketone 25, filler nanometer silica 50 and curing agent diethanol amine 20.
Embodiment 2
A kind of hard plastics display screen of tablet personal computer, including hard plastic matrix, the hard plastic matrix lower surface
Adhere to one layer of rupture pressure disc, the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, the inorganic mixing
Plated film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made；
The hard plastic matrix is made up of the raw material of following weight parts：Polyvinyl chloride 15, resin 15, polypropylene 160, aluminosilicate
Salt powder 11, sodium carbonate 2, ammonium dihydrogen phosphate 0.4, lauryl sodium sulfate 0.7, isocyanuric acid three-glycidyl ester 0.6, four hydroxyls
Methylmethane 4, polyethyleneimine 2-4, ethylene bis stearamide 1, polybenzimidazoles 5, tetrahydrofurfuryl carbinol 1, stabilizer 2；
Inorganic matter and nano ceramics the plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin 20, auxiliary agent methyl
Isobutyl ketone, methyl ethyl ketone peroxide and the tertiary fourth fat of peracetic acid totally 25, nano aluminium oxide 65 and curing agent diethanol amine 18.
Embodiment 3
A kind of hard plastics display screen of tablet personal computer, including hard plastic matrix, the hard plastic matrix lower surface
Adhere to one layer of rupture pressure disc, the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, the inorganic mixing
Plated film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made；
The hard plastic matrix is made up of the raw material of following weight parts：Polyvinyl chloride 20, resin 10, polypropylene 170, aluminosilicate
Salt powder 10, sodium carbonate 3, ammonium dihydrogen phosphate 0.3, lauryl sodium sulfate 0.7, isocyanuric acid three-glycidyl ester 0.5, four hydroxyls
Methylmethane 4, polyethyleneimine 2, ethylene bis stearamide 2, polybenzimidazoles 4, tetrahydrofurfuryl carbinol 2, stabilizer 1；
Inorganic matter and nano ceramics the plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin 25, auxiliary agent peroxide
Change the tertiary fourth fat 15 of acetic acid, filler nanometer silica and nano aluminium oxide each 30 and curing agent diethanol amine 5.
Under a kind of hard plastics display screen of tablet personal computer, including hard plastic matrix, the hard plastic matrix
One layer of rupture pressure disc of surface attachment, the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film, described inorganic
The admixture plates the film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made.Wherein：It is special that the present invention is plated on plastic cement top layer
Organic and inorganic the admixture plates the film, the problem of general plastic cement hardness is not enough can be solved.Inorganic ceramic is hard heat-resisting, organic polymer
Light weight is soft, and the admixture plates the film combines both specialities, and after being processed on plastic cement top layer, hard plastic will possess strengthened glass
Hardness, weight only has glass half less than the resistance to degree of falling is even more glass twice.
The hard plastic that the present invention is provided, can replace the strengthened glass of heavy fragility, make Intelligent flat computer screen lighter
It is more tough.And hard plastic hardness is up to 9H (Hardness), than the 4H of general plastic cement, it is higher by as many as twice.In general, strong
Although it is heavy frangible to change glass, because of hard scratch resistance, into the protective glass of wisdom device；The present invention plates spy on plastic cement top layer
Different organic and inorganic the admixture plates the film, can solve the problem of general plastic cement hardness is not enough.Inorganic ceramic is hard heat-resisting, organic polymer
Material is softly soft, and the admixture plates the film combines both specialities, and after being processed on plastic cement top layer, hard plastic will possess strengthened glass
Hardness, weight only has glass half less than the resistance to degree of falling is even more glass twice.In addition, hard plastic is easily cut, it can make
Variously-shaped and size.
Described above is only the preferred embodiment of the present invention, it should be pointed out that：For the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (9)
1. a kind of hard plastics display screen of tablet personal computer, it is characterised in that：Including hard plastic matrix, the hard modeling
Matrix body lower surface adheres to one layer of rupture pressure disc, and the hard plastic body upper surface adheres to one layer of organic and inorganic the admixture plates the film,
The inorganic the admixture plates the film is the plated film that inorganic matter and nano ceramics plating solution mixed liquor are made.
2. the hard plastics display screen of tablet personal computer according to claim 1, it is characterised in that：The hard plastic
Matrix is made up of the raw material of following weight parts：Polyvinyl chloride 10-20, resin 10-20, polypropylene 150-170, aluminosilicate powder
10-12, sodium carbonate 2-3, ammonium dihydrogen phosphate 0.3-0.5, lauryl sodium sulfate 0.6-0.7, isocyanuric acid three-glycidyl ester
0.5-0.6, tetramethylol methane 3-4, polyethyleneimine 2-4, ethylene bis stearamide 1-2, polybenzimidazoles 4-6, tetrahydrochysene furan
Mutter methanol 1-2, stabilizer 1-3.
3. the hard plastics display screen of tablet personal computer according to claim 2, it is characterised in that：The hard plastic
Matrix is made up of the raw material of following weight parts：Polyvinyl chloride 15, resin 15, polypropylene 160, aluminosilicate powder 11, sodium carbonate
2nd, ammonium dihydrogen phosphate 0.4, lauryl sodium sulfate 0.7, isocyanuric acid three-glycidyl ester 0.6, tetramethylol methane 4, poly- second
Alkene imines 2-4, ethylene bis stearamide 1, polybenzimidazoles 5, tetrahydrofurfuryl carbinol 1, stabilizer 2.
4. the hard plastics display screen of tablet personal computer according to claim 1, it is characterised in that：The inorganic matter and
Nano ceramics plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin 15-25, auxiliary agent 15-25, filler 50-65 and
Curing agent 5-20.
5. the hard plastics display screen of tablet personal computer according to claim 4, it is characterised in that：The inorganic matter and
Nano ceramics plating solution mixed liquor is made up of the raw material of following weight parts：Epoxy resin 20, auxiliary agent methyl iso-butyl ketone (MIBK), peroxidating first
Ethyl ketone and the tertiary fourth fat of peracetic acid totally 25, nano aluminium oxide 65 and curing agent diethanol amine 18.
6. the hard plastics display screen of tablet personal computer according to claim 4, it is characterised in that：The auxiliary agent is first
Base isobutyl ketone, methyl ethyl ketone peroxide and one kind or any several mixture in the tertiary fourth fat of peracetic acid.
7. the hard plastics display screen of tablet personal computer according to claim 4, it is characterised in that：The filler is to receive
The mixture of rice silica and nano aluminium oxide either or both of which.
8. the hard plastics display screen of tablet personal computer according to claim 7, it is characterised in that：Received in the filler
The mass ratio of rice silica and nano aluminium oxide is 1：1.
9. the hard plastics display screen of tablet personal computer according to claim 4, it is characterised in that：The curing agent is
Diethanol amine.