CN107142430A - The manufacture craft of insulation aluminium based on door and window - Google Patents
The manufacture craft of insulation aluminium based on door and window Download PDFInfo
- Publication number
- CN107142430A CN107142430A CN201710366141.9A CN201710366141A CN107142430A CN 107142430 A CN107142430 A CN 107142430A CN 201710366141 A CN201710366141 A CN 201710366141A CN 107142430 A CN107142430 A CN 107142430A
- Authority
- CN
- China
- Prior art keywords
- briquet
- door
- window
- manufacture craft
- insulation aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the manufacture craft of the insulation aluminium based on door and window, each component is uniformly mixed in proportion, briquet is pressed into after being well mixed；The briquet suppressed is positioned in vacuum furnace chamber, 1250 DEG C are warming up to 35 50 DEG C/min programming rate, 5 6h are incubated；It is 500 550 DEG C to control in-furnace temperature, and briquet is placed under 700 750 DEG C of environment and carries out heat treatment 79 hours；Briquet is subjected to Quenching Treatment, hardening heat is 500 550 DEG C, and temperature control is at 250 300 DEG C after quenching；After air cooling, hot rolling is carried out after reheating；Tension straingtening, amount of tension is controlled 1~2%；Ageing Treatment, aging temp is 200~220 DEG C, and soaking time is 11 12h.
Description
Technical field
The present invention relates to a kind of aluminium, and in particular to the manufacture craft of the insulation aluminium based on door and window.
Background technology
With the development of science and technology, alloy material is more and more used on the section bar of door and window, titanium alloy, aluminium alloy etc. are
Can as door and window section bar, especially aluminum alloy materials, because aluminium alloy has the advantages that lightweight, with processing, door and window is closed with aluminium
Gold is more and more.
But current aluminium alloy soundproof effect is poor, easily deforms, toughness declines under cryogenic, it is easy to be broken,
And without the effect being preferably incubated.
The content of the invention
The technical problems to be solved by the invention are the poor mutabilities of existing aluminium soundproof effect and made without insulation
With, and preparation technology is complicated, it is therefore intended that provide the manufacture craft of the insulation aluminium based on door and window, solve existing aluminium every
The audio poor mutability of fruit and without insulation effect, and preparation technology it is complicated the problem of.
The present invention is achieved through the following technical solutions：
The manufacture craft of insulation aluminium based on door and window, comprises the following steps：
(1) each component is uniformly mixed in proportion, briquet is pressed into after being well mixed；
(2) briquet suppressed is positioned in vacuum furnace chamber, 1250 is warming up to 35-50 DEG C/min programming rate
DEG C, it is incubated 5-6h；
(3) it is 500-550 DEG C to control in-furnace temperature, and it is small that briquet is placed on into progress heat treatment 7-9 under 700-750 DEG C of environment
When；
(4) briquet is subjected to Quenching Treatment, hardening heat is 500-550 DEG C, and temperature control is at 250-300 DEG C after quenching；
(5) after air cooling, hot rolling is carried out after reheating；
(6) tension straingtening, amount of tension is controlled 1~2%；
(7) Ageing Treatment, aging temp is 200~220 DEG C, and soaking time is 11-12h.
The component includes the component of following parts by weight：22 parts of copper, 38 parts of silicon, 29 parts of nickel, 14 parts of chromium, 10 parts of magnesium, zinc 7
Part, 7 parts of manganese, 11 parts of iron, 4 parts of titanium, 20 parts of cerium, 26 parts of micron order alumina powder, 39 parts of carbon dust, 22 parts of tin-doped indium oxide, fluorine doped
15 parts of tin oxide.
In-furnace temperature is controlled to be 525 DEG C in the manufacture craft of insulation aluminium based on door and window, the step (3).
Briquet is placed under 745 DEG C of environment in the manufacture craft of insulation aluminium based on door and window, the step (3) and carried out
It is heat-treated 7.5 hours
Briquet is carried out Quenching Treatment by the manufacture craft of the insulation aluminium based on door and window, the step (4), and hardening heat is
540 DEG C, temperature control is at 280 DEG C after quenching.
Aging temp is 215 DEG C in the manufacture craft of insulation aluminium based on door and window, the step (7), and soaking time is
11.5h。
The present invention compared with prior art, has the following advantages and advantages：
1st, the manufacture craft of insulation aluminium of the present invention based on door and window, component of the invention complements each other, prepared aluminium
Material has preferable soundproof effect, is unlikely to deform fracture, and with preferable insulation effect；
2nd, the manufacture craft of insulation aluminium of the present invention based on door and window, preparation technology of the invention is simple, is easy to production, raw
Preferably, intensity is more preferable, and heat insulating ability is also preferable for the soundproof effect of the aluminium of production.
Embodiment
For the object, technical solutions and advantages of the present invention are more clearly understood, with reference to embodiment, to present invention work
Further to describe in detail, exemplary embodiment and its explanation of the invention is only used for explaining the present invention, is not intended as to this
The restriction of invention.
Embodiment
The manufacture craft of insulation aluminium of the present invention based on door and window, comprises the following steps：
(1) each component is uniformly mixed in proportion, briquet is pressed into after being well mixed；
(2) briquet suppressed is positioned in vacuum furnace chamber, 1250 is warming up to 35-50 DEG C/min programming rate
DEG C, it is incubated 5-6h；
(3) it is 500-550 DEG C to control in-furnace temperature, and it is small that briquet is placed on into progress heat treatment 7-9 under 700-750 DEG C of environment
When；
(4) briquet is subjected to Quenching Treatment, hardening heat is 500-550 DEG C, and temperature control is at 250-300 DEG C after quenching；
(5) after air cooling, hot rolling is carried out after reheating；
(6) tension straingtening, amount of tension is controlled 1~2%；
(7) Ageing Treatment, aging temp is 200~220 DEG C, and soaking time is 11-12h.
It is 525 DEG C that in-furnace temperature is controlled in the step (3).
Briquet is placed under 745 DEG C of environment in the step (3) and carries out 7.5 hours of heat treatment
Briquet is carried out Quenching Treatment by the step (4), and hardening heat is 540 DEG C, and temperature control is at 280 DEG C after quenching.
Aging temp is 215 DEG C in the step (7), and soaking time is 11.5h.
The component includes the component of following parts by weight：22 parts of copper, 38 parts of silicon, 29 parts of nickel, 14 parts of chromium, 10 parts of magnesium, zinc 7
Part, 7 parts of manganese, 11 parts of iron, 4 parts of titanium, 20 parts of cerium, 26 parts of micron order alumina powder, 39 parts of carbon dust, 22 parts of tin-doped indium oxide, fluorine doped
15 parts of tin oxide.
Above-described embodiment, has been carried out further to the purpose of the present invention, technical scheme and beneficial effect
Describe in detail, should be understood that the embodiment that the foregoing is only the present invention, be not intended to limit the present invention
Protection domain, within the spirit and principles of the invention, any modification, equivalent substitution and improvements done etc. all should be included
Within protection scope of the present invention.
Claims (5)
1. the manufacture craft of the insulation aluminium based on door and window, it is characterised in that comprise the following steps：
(1) each component is uniformly mixed in proportion, briquet is pressed into after being well mixed；
(2) briquet suppressed is positioned in vacuum furnace chamber, 1250 DEG C, guarantor is warming up to 35-50 DEG C/min programming rate
Warm 5-6h；
(3) it is 500-550 DEG C to control in-furnace temperature, and briquet is placed under 700-750 DEG C of environment and carries out heat treatment 7-9 hours；
(4) briquet is subjected to Quenching Treatment, hardening heat is 500-550 DEG C, and temperature control is at 250-300 DEG C after quenching；
(5) after air cooling, hot rolling is carried out after reheating；
(6) tension straingtening, amount of tension is controlled 1~2%；
(7) Ageing Treatment, aging temp is 200~220 DEG C, and soaking time is 11-12h.
2. the manufacture craft of the insulation aluminium according to claim 1 based on door and window, it is characterised in that the step (3)
It is middle to control in-furnace temperature to be 525 DEG C.
3. the manufacture craft of the insulation aluminium according to claim 1 based on door and window, it is characterised in that the step (3)
Middle briquet is placed under 745 DEG C of environment carries out heat treatment 7.5 hours.
4. the manufacture craft of the insulation aluminium according to claim 1 based on door and window, it is characterised in that the step (4)
Briquet is subjected to Quenching Treatment, hardening heat is 540 DEG C, and temperature control is at 280 DEG C after quenching.
5. the manufacture craft of the insulation aluminium according to claim 1 based on door and window, it is characterised in that the step (7)
Middle aging temp is 215 DEG C, and soaking time is 11.5h.