CN107142074A - A kind of preparation method of de-oxime type one component room temperature fluid sealant - Google Patents
A kind of preparation method of de-oxime type one component room temperature fluid sealant Download PDFInfo
- Publication number
- CN107142074A CN107142074A CN201710319315.6A CN201710319315A CN107142074A CN 107142074 A CN107142074 A CN 107142074A CN 201710319315 A CN201710319315 A CN 201710319315A CN 107142074 A CN107142074 A CN 107142074A
- Authority
- CN
- China
- Prior art keywords
- fluid sealant
- parts
- room temperature
- temperature fluid
- oxime type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fluid sealant technology of preparing, more particularly to a kind of preparation method of de-oxime type one component room temperature fluid sealant.Its dispensing component and number are as follows:107 25~60 parts of glue;3~15 parts of crosslinking agent;20~55 parts of filler;3~15 parts of auxiliary agent;1~10 part of coupling agent;Organotin catalysts 0.01%~0.15%.After above-mentioned formula and method, not only there is stronger physical property, and possess rapid curing nature, and due to the addition of the loose structure filler and hygroscopic polymer of rational formula, the filler and hydrophilic macromolecule of its cellular structure can in fluid sealant steam in absorption air, so as to improve the fixed line speed of fluid sealant, obtained fluid sealant intensity>2.5MPa, stretch rate>300%th, shear>2.0MPa, 4h curing depth reach as high as 1.9mm.
Description
Technical field
The present invention relates to a kind of fluid sealant technology of preparing, more particularly to a kind of system of de-oxime type one component room temperature fluid sealant
Preparation Method.
Background technology
Single-component room-temperature-vulsilicone silicone rubber can for a long time be used in super-wide temperature range (- 60 ~ 200 DEG C) environment, with excellent
Good electrical insulation properties and chemical stability, weatherability have good cementability to multiple material, are widely used in
All trades and professions;But existing single-component room-temperature-vulsilicone silicone rubber is not conformed to due to its unreasonable and preparation method of formula collocation
Reason so that the solidification rate of single-component room-temperature-vulsilicone silicone rubber is low, low production efficiency, wastes the time cost of enterprise.
The content of the invention
Improve close while performance and storge quality is ensured the technical problem to be solved in the present invention is to provide one kind
The fixed line speed of sealing, improves the preparation method of the de-oxime type one component room temperature fluid sealant of production efficiency.
In order to solve the above-mentioned technical problem, de-oxime type one component room temperature fluid sealant of the invention, its dispensing component and number
It is as follows:
107 25~60 parts of glue
3~15 parts of crosslinking agent
20~55 parts of filler
3~15 parts of auxiliary agent
1~10 part of coupling agent
Organotin catalysts 0.01%~0.15%.
Further, the dispensing component and number of the filler are as follows:
Nano-calcium carbonate 10 ~ 40
Sepiolite 2 ~ 20
Bentonite 2 ~ 20
Coarse whiting 5 ~ 40.
Further, the nano-calcium carbonate surface is by being modified, and modifying agent is that surfactant-based, coupling agent class or both is multiple
Close and be modified.
Further, the bentonite is organic modified bentonite, and modifying agent is organic amine.
Further, 107 glue is 20,000 viscosity, 50,000 viscosity, the one or more of 80,000 viscosity.
Further, the crosslinking agent be methyl tributanoximo silane and vinyl tributyl ketoximyl silane, both
Ratio is 0.1~5:5~0.1.
Further, the coupling agent is the one or more of KH550, KH560, KH602, KH792 silane coupler.
Further, the component of the auxiliary agent is one kind in polyethylene glycol, polypropylene glycol or is used in combination, the polyethylene glycol
Molecular weight is that 200,400,600,800 one or more are used in combination, and the polypropylene glycols amount is 400,1000 one kind or is used in combination.
A kind of preparation method of above-mentioned de-oxime type one component room temperature fluid sealant, comprises the following steps:
A, 25~60 parts of 107 glue, 3~15 parts of crosslinking agent, 3~15 parts of auxiliary agent are placed in planetary stirrer, vacuum is stirred
10~40min is mixed to be well mixed;
B, 20~55 parts of filler added in planetary stirrer in batches, be stirred under vacuum 15~75min and be well mixed;
C, will 1~10 part of coupling agent, 0.01%~0.15% organotin catalysts add planetary stirrer in, be stirred under vacuum 10~
40min is to obtain product.
After above-mentioned formula and method, not only with stronger physical property, and possess rapid curing nature, and
Due to the addition of the loose structure filler and hygroscopic polymer of rational formula, the filler and hydrophily high score of its cellular structure
Son can in fluid sealant steam in absorption air, so as to improve the fixed line speed of fluid sealant, obtained fluid sealant intensity>
2.5MPa, stretch rate>300%th, shear>2.0MPa, 4h curing depth reach as high as 1.9mm.
Embodiment
The de-oxime type one component room temperature fluid sealant of the present invention, its dispensing component and number are as follows:
107 25~60 parts of glue
3~15 parts of crosslinking agent
20~55 parts of filler
3~15 parts of auxiliary agent
1~10 part of coupling agent
Organotin catalysts 0.01%~0.15%.
Wherein, the dispensing component and number of filler are as follows:
Nano-calcium carbonate 10 ~ 40
Sepiolite 2 ~ 20
Bentonite 2 ~ 20
Coarse whiting 5 ~ 40.
Nano-calcium carbonate surface is by being modified, and modifying agent is that surfactant-based, coupling agent class or both is composite modified, particularly
Using fatty acid modified nano-calcium carbonate to be excellent;Described bentonite is organic modified bentonite, and modifying agent is organic amine.
Further, 107 described glue be 20,000 viscosity, 50,000 viscosity, 80,000 viscosity one or more be used in combination, particularly,
With 20,000 with 50,000 and using, 20,000 with 80,000 and using, 50,000 with 80,000 and with to be excellent;Crosslinking agent is methyl tributanoximo silane and ethene
Base tributanoximo silane is used in combination, and both ratios are 0.1~5:5~0.1, particularly using ratio as 1~3:3~1 be excellent;It is even
Connection agent is that the silane coupler such as KH550, KH560, KH602, KH792 is alone or be used in combination, particularly with KH550 and KH560 and use,
KH550 and KH602 and use, KH560 and KH792 and with to be excellent;The component of auxiliary agent be polyethylene glycol, polypropylene glycol in one kind or
It is used in combination, particularly using polyethylene glycol and polypropylene glycol and use and ratio as 1~3:3~1 be excellent;The molecular weight polyethylene glycol is
200th, 400,600,800 one or more are used in combination, particularly using molecular weight as 200 with 400 polyethylene glycol and with to be excellent;It is described
Polypropylene glycols amount is 400,1000 a kind of or be used in combination, particularly with and with being urged for excellent, described catalyst for organic tin
Agent is excellent with 0.08%~0.12%.
A kind of preparation method of above-mentioned de-oxime type one component room temperature fluid sealant, comprises the following steps:
A, 25~60 parts of 107 glue, 3~15 parts of crosslinking agent, 3~15 parts of auxiliary agent are placed in planetary stirrer, vacuum is stirred
10~40min is mixed to be well mixed;
B, 20~55 parts of filler added in planetary stirrer in batches, be stirred under vacuum 15~75min and be well mixed;
C, will 1~10 part of coupling agent, 0.01%~0.15% organotin catalysts add planetary stirrer in, be stirred under vacuum 10~
40min is to obtain product.
Below by instantiation to the preparation method of the de-oxime type one component room temperature fluid sealant of the present invention to illustrating:
Embodiment 1
107 glue, 100g auxiliary agents (polyethylene glycol, the mass ratio 1 of molecular weight 200 and 600 by 450g viscosity for 50,000:1 is used in combination), 50g
(methyl tributanoximo silane, vinyl tributyl ketoximyl silane mass ratio are 1 to crosslinking agent:1) it is placed in planetary stirrer, very
Sky stirring 10 minutes, then divide 2 addition 200g nano-calcium carbonates, 50g sepiolites, 50g bentonites, 80g coarse whitings, it is stirred under vacuum 60
Minute, 20g coupling agents (KH550), 0.8g organotin catalysts are eventually adding, are stirred under vacuum 20 minutes, you can plastic emitting.This glue system
Piece intensity 2.62MPa, stretch rate 310%, shearing 2.1MPa, 4h curing depth up to 1.8mm.
Embodiment 2
107 glue, 100g auxiliary agents (polyethylene glycol of molecular weight 400, the polypropylene glycol matter of molecular weight 400 by 400g viscosity for 80,000
Amount compares 1:1), (methyl tributanoximo silane, vinyl tributyl ketoximyl silane mass ratio are 5 to 50g crosslinking agents:3) it is placed in row
In star agitator, it is stirred under vacuum 20 minutes, then divides 2 addition 240g nano-calcium carbonates, 30g sepiolites, 50g bentonites, 100g
Coarse whiting, is stirred under vacuum 50 minutes, is eventually adding 30g coupling agents (KH560, KH602 mass ratio 1:1), 0.8g organotin catalysts,
It is stirred under vacuum 25 minutes, you can plastic emitting.This glue film-making intensity 2.58MPa, stretch rate 360%, shearing 2.2MPa, 4h curing depth can
Up to 1.9mm.
Embodiment 3
It is 1 by 450g mass ratioes:1 glue of 20,000 viscosity 107 and the glue of 50,000 viscosity 107,70g auxiliary agents (poly- the third the two of molecular weight 400
Alcohol), 40g crosslinking agents (methyl tributanoximo silane, vinyl tributyl ketoximyl silane mass ratio be 4:3) it is placed in planet stirring
In device, it is stirred under vacuum 30 minutes, then divides 2 addition 300g nano-calcium carbonates, 20g bentonites, 100g coarse whitings, is stirred under vacuum 70 points
Clock, is eventually adding 20g coupling agents (KH792), 0.8g organotin catalysts, is stirred under vacuum 30 minutes, you can plastic emitting.This glue film-making
Intensity 2.53MPa, stretch rate 310%, shearing 2.2MPa, 4h curing depth up to 1.85mm.
As can be seen here, the fluid sealant that prepared by the inventive method possesses rapid curing nature, and (4h curing depths are reached as high as
1.9mm), proof strength (>2.5MPa), stretch rate (>300%), shear (>It can meet quick solid while 2.0MPa) etc. requirement
Change demand, its effect is notable.
Claims (8)
1. a kind of de-oxime type one component room temperature fluid sealant, it is characterised in that:Its dispensing component and number are as follows:
107 25~60 parts of glue
3~15 parts of crosslinking agent
20~55 parts of filler
3~15 parts of auxiliary agent
1~10 part of coupling agent
Organotin catalysts 0.01%~0.15%.
2. according to the de-oxime type one component room temperature fluid sealant described in claim 1, it is characterised in that:The dispensing component of the filler
And number is as follows:
Nano-calcium carbonate 10 ~ 40
Sepiolite 2 ~ 20
Bentonite 2 ~ 20
Coarse whiting 5 ~ 40.
According to the de-oxime type one component room temperature fluid sealant described in claim 2, it is characterised in that:The nano-calcium carbonate surface warp
Cross modified, modifying agent is that surfactant-based, coupling agent class or both is composite modified.
3. according to the de-oxime type one component room temperature fluid sealant described in claim 2, it is characterised in that:The bentonite changes to be organic
Property bentonite, modifying agent is organic amine.
4. according to the de-oxime type one component room temperature fluid sealant described in claim 1, it is characterised in that:107 glue is 20,000 viscous
Degree, 50,000 viscosity, the one or more of 80,000 viscosity.
5. according to the de-oxime type one component room temperature fluid sealant described in claim 1, it is characterised in that:The crosslinking agent is methyl three
Butanone oximino silane and vinyl tributyl ketoximyl silane, both ratios are 0.1~5:5~0.1.
6. according to the de-oxime type one component room temperature fluid sealant described in claim 1, it is characterised in that:The coupling agent be KH550,
The one or more of KH560, KH602, KH792 silane coupler.
7. according to the de-oxime type one component room temperature fluid sealant described in claim 1, it is characterised in that:The component of the auxiliary agent is poly-
One kind in ethylene glycol, polypropylene glycol is used in combination, the molecular weight polyethylene glycol be 200,400,600,800 it is one or more of simultaneously
With the polypropylene glycols amount is 400,1000 one kind or is used in combination.
8. a kind of preparation method of de-oxime type one component room temperature fluid sealant as claimed in claim 1, comprises the following steps:
A, 25~60 parts of 107 glue, 3~15 parts of crosslinking agent, 3~15 parts of auxiliary agent are placed in planetary stirrer, vacuum is stirred
10~40min is mixed to be well mixed;
B, 20~55 parts of filler added in planetary stirrer in batches, be stirred under vacuum 15~75min and be well mixed;
C, will 1~10 part of coupling agent, 0.01%~0.15% organotin catalysts add planetary stirrer in, be stirred under vacuum 10~
40min is to obtain product.