CN107141997A - Aqueous radiation proof acrylic polyurethane finish paint - Google Patents
Aqueous radiation proof acrylic polyurethane finish paint Download PDFInfo
- Publication number
- CN107141997A CN107141997A CN201710452905.6A CN201710452905A CN107141997A CN 107141997 A CN107141997 A CN 107141997A CN 201710452905 A CN201710452905 A CN 201710452905A CN 107141997 A CN107141997 A CN 107141997A
- Authority
- CN
- China
- Prior art keywords
- parts
- radiation proof
- finish paint
- acrylic polyurethane
- proof acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of aqueous radiation proof acrylic polyurethane finish paint, is made up of the component of following parts by weight：Waterborne epoxy modified 150 200 parts of polyurethane resin, 200 300 parts of deionized water, 13 parts of propylene glycol monomethyl ether, 50 180 parts of filler, 1 10 parts of pigment, prevent 0.5 0.8 parts of reducing agent, 0.5 1 parts of ethylenediamine tetra-acetic acid, 25 parts of mosanom, 35 parts of auxiliary agent.The finish paint of the present invention has very strong adhesive force to various base materials, and the hardness of coating is high, and wearability is good, the effects such as specific radiation proof, release anion, is environment friendly and pollution-free paint.
Description
Technical field
The present invention relates to paint technology field, and in particular to a kind of aqueous radiation proof acrylic polyurethane finish paint.
Background technology
With the continuous progress of society, various countries are improved constantly to the consciousness of environmental protection.And now widely used solvent-borne type is applied
Contain substantial amounts of volatilizable organic compound (VOC) in material, organic compound (VOC) is poisonous, inflammable, pollutes the atmosphere, to ring
Border and human body all cause harm.Therefore, in order to reduce pollution of these organic solvents to environment, water paint is included in by China
The developing direction of industrial coating from now on.But China applies the water on floor paint, metallic anti-rust paint and marine paint at present
Property industrial coating its water resistance, chemical resistance, anti-radiation, wearability and weatherability are undesirable.
The content of the invention
The technical problems to be solved by the invention are that improving a kind of method is easily achieved, and are capable of the aqueous anti-spoke of industrialization
Penetrate acrylic polyurethane finish paint.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of aqueous radiation proof acrylic polyurethane finish paint, is made up of the component of following parts by weight：It is waterborne epoxy modified
150-200 parts of polyurethane resin, 200-300 parts of deionized water, 1-3 parts of propylene glycol monomethyl ether, 50-180 parts of filler, pigment 1-10
Part, prevent 0.5-0.8 parts of reducing agent, 0.5-1 parts of ethylenediamine tetra-acetic acid, 2-5 parts of mosanom, 3-5 parts of auxiliary agent.
The auxiliary agent is one kind or 2 kinds and its above in levelling agent, catalyst, defoamer, stabilizer, lubricant etc.
Combination.
The filler is the mixture of organic germanium and carbide, and the ratio both it is 1：99, it is hot in itself using carbide
Conduction function, produces heat energy and links, germanium is a kind of semiconductor element, without toxicity.More than 32 DEG C of temperature will one of them
More than electronics de-orbit, send anion and far infrared, reach sterilization and the effect of fresh air；There is radiation proof simultaneously
Function.
A kind of preparation method of aqueous radiation proof acrylic polyurethane finish paint, step is as follows：
(1) waterborne epoxy modified polyurethane resin (PUD) is pumped into batching kettle stirring, temperature in the kettle rises to 55-60 DEG C,
Stirring is lower to be kept for 5 minutes；
(2) pure water tank and propylene glycol monomethyl ether head tank valve, the deionized water of addition half amount and the third of whole amount are opened
Glycol methyl ether and mosanom, the steam temperature in kettle stop heating when reaching 65-70 DEG C, while starting agitating function, make thing
Material is heated evenly, and is stirred 20-35 minutes；
(3) filler, pigment and ethylenediamine tetrem are stirring evenly and then adding into, high-speed stirred 20 minutes is then pumped into sand mill
Closed grinding, until fineness is qualified, pump is to adding the deionized water of surplus with paint kettle, preventing reducing agent and auxiliary agent, and stirring is equal
Even detection is qualified, and through filtering, pail pack packaging and storage is pumped into using measuring pump.
Following item is should be noted during the construction of the present invention：
Note dustless, oil-free of body surface etc. when the 1st, spraying or brush.
2nd, the paint prepared should be finished in 4 hours, in case gel is wasted.
3rd, product meets and stored under rated condition, effective storage life 1 year, such as more than 1 year through examining qualified may continue to
Use.
The beneficial effects of the invention are as follows：The finish paint of the present invention has very strong adhesive force to various base materials, and coating
Hardness is high, and wearability is good, the effects such as specific radiation proof, release anion, is environment friendly and pollution-free paint.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1-3, wherein filler are the mixture of organic germanium and carbide, and the part by weight both it is 1：99, it is single
Position is kg；
Embodiment 1-3 preparation method is as follows：
(1) waterborne epoxy modified polyurethane resin (PUD) is pumped into batching kettle stirring, temperature in the kettle rises to 55-60 DEG C,
Stirring is lower to be kept for 5 minutes；
(2) pure water tank and propylene glycol monomethyl ether head tank valve, the deionized water of addition half amount and the third of whole amount are opened
Glycol methyl ether and mosanom, the steam temperature in kettle stop heating when reaching 65-70 DEG C, while starting agitating function, make thing
Material is heated evenly, and is stirred 20-35 minutes；
(3) filler, pigment and ethylenediamine tetrem are stirring evenly and then adding into, high-speed stirred 20 minutes is then pumped into sand mill
Closed grinding, until fineness is qualified, pump is to adding the deionized water of surplus with paint kettle, preventing reducing agent and auxiliary agent, and stirring is equal
Even detection is qualified, and through filtering, pail pack packaging and storage is pumped into using measuring pump.
Further, in order to verify that scheme provided by the present invention can reach technique effect, to the institute of embodiment 1,2 and 3
The scheme of offer is tested, and specific experiment data are as shown in table 1：
Table 1
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (4)
1. a kind of aqueous radiation proof acrylic polyurethane finish paint, it is characterised in that be made up of the component of following parts by weight：It is aqueous
150-200 parts of epoxy modified polyurethane resin, 200-300 parts of deionized water, 1-3 parts of propylene glycol monomethyl ether, 50-180 parts of filler, face
Expect 1-10 parts, prevent 0.5-0.8 parts of reducing agent, 0.5-1 parts of ethylenediamine tetra-acetic acid, 2-5 parts of mosanom, 3-5 parts of auxiliary agent.
2. aqueous radiation proof acrylic polyurethane finish paint according to claim 1, it is characterised in that the auxiliary agent is levelling
The combination of one kind in agent, catalyst, defoamer, stabilizer, lubricant etc. or 2 kinds and its above.
3. aqueous radiation proof acrylic polyurethane finish paint according to claim 1, it is characterised in that the filler is organic
The mixture of germanium and carbide, the weight ratio both it is 1：99.
4. a kind of preparation method of any one of claim 1-3 aqueous radiation proof acrylic polyurethane finish paints, its feature exists
It is as follows in step：
(1) waterborne epoxy modified polyurethane resin is pumped into batching kettle stirring, temperature in the kettle rises to 55-60 DEG C, protected under agitation
Hold 5 minutes；
(2) pure water tank and propylene glycol monomethyl ether head tank valve are opened, the deionized water of half amount and the propane diols of whole amount is added
Methyl ether and mosanom, stop heating when the steam temperature in kettle reaches 65-70 DEG C, while start agitating function, make material by
It is hot uniform, stir 20-35 minutes；
(3) filler, pigment and ethylenediamine tetrem are stirring evenly and then adding into, high-speed stirred 20 minutes is then pumped into sand mill closed
Grinding, until fineness is qualified, pump is to adding the deionized water of surplus with paint kettle, preventing reducing agent and auxiliary agent, and stir inspection
It is qualified to survey, and through filtering, pail pack packaging and storage is pumped into using measuring pump.