CN107141828A - The manufacture craft of Neto is packed using the composite environment-friendly type fine work of ultralight clay material - Google Patents
The manufacture craft of Neto is packed using the composite environment-friendly type fine work of ultralight clay material Download PDFInfo
- Publication number
- CN107141828A CN107141828A CN201710254287.4A CN201710254287A CN107141828A CN 107141828 A CN107141828 A CN 107141828A CN 201710254287 A CN201710254287 A CN 201710254287A CN 107141828 A CN107141828 A CN 107141828A
- Authority
- CN
- China
- Prior art keywords
- parts
- neto
- clay material
- ultralight clay
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses the manufacture craft that a kind of composite environment-friendly type fine work using ultralight clay material packs Neto, includes following steps：（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：50 60 parts of paper pulp, 30 40 parts of PPG, 20 30 parts of PEPA, 5 10 parts of poly (vinyl alcohol) binder, 23 parts of kaolin, 2 parts of silica 1,10 12 parts of bamboo charcoal powder, 12 parts of food coloring, 12 parts of crosslinking agent, 34 parts of polyglycolic acid resin, 23 parts of glycerine；Above-mentioned each raw material is sequentially poured into stirring in container and obtains ultralight clay material within 35 hours；（2）Neto mould is chosen, and ultralight clay material is injected in mould.This product can reach the environmental requirement of food-grade, it is possible to achieve accurately freely match colors, it is possible to achieve broken colour coordinates, it might even be possible to make different picture on surface, and light weight, easy-formation, moulding is fine, can preserve for a long time.
Description
Technical field
The present invention relates to packaging field technology, a kind of composite environment-friendly type fine work bag using ultralight clay material is referred in particular to
Fill the manufacture craft of Neto.
Background technology
Neto/liner is generally used for being placed on package interior, plays a part of support packaging product, traditionally consumer
The material that electronic packaging liner/Neto is used is generally plastic uptake, paper pulp support, EVA etc., and these mode generally existings, which, to be unable to reach
Environmental requirement, selling at exorbitant prices, need die sinking the problems such as.Therefore, it is necessary to be improved to current Neto/liner.
The content of the invention
In view of this, in view of the existing deficiencies of the prior art, its main purpose is to provide a kind of using ultralight viscous the present invention
The composite environment-friendly type fine work of soil material packs the manufacture craft of Neto, and it is played most for industries such as electronic product and luxury goods
The purposes such as good protectiveness, low cost, Environmental Safety.
To achieve the above object, the present invention is using following technical scheme：
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：50-60 parts of paper pulp, polyethers are more
First alcohol 30-40 parts, 5-10 parts of poly (vinyl alcohol) binder of 20-30 parts of PEPA, 2-3 parts of kaolin, silica 1-
2 parts, 10-12 parts of bamboo charcoal powder, 1-2 parts of food coloring, 1-2 parts of crosslinking agent, 3-4 parts of polyglycolic acid resin, 2-3 parts of glycerine；
Above-mentioned each raw material is sequentially poured into stirring in container and obtains ultralight clay material within 3-5 hours；
（2）Neto mould is chosen, and ultralight clay material is injected in mould；
（3）Heat drying is carried out to Neto mould, temperature control is between 100-120 DEG C, and warm-up time is 5-10 minutes；
（4）Neto simultaneously natural air drying 10-12 hours are taken out in die sinking.
As a kind of preferred scheme, the Neto mould is disposable gypsum or aluminum alloy mould.
As a kind of preferred scheme, further comprise there is step（5）UV glazings are carried out to Neto.
The present invention has clear advantage and beneficial effect compared with prior art, specifically, by above-mentioned technical proposal
Understand：
Present invention employs the ultralight clay material of special formulation, specific hardness and drying time are made up to, expection is reached
The color and surface effect of design, after particular procedure is carried out, applied to industries such as consumer electronics product, cosmetics, gifts
Packaging Neto, this product can reach the environmental requirement of food-grade, it is possible to achieve accurately freely match colors, it is possible to achieve colorful
Color coordinates, it might even be possible to make different picture on surface, and light weight, easy-formation, moulding is fine, can preserve for a long time.
Embodiment
Present invention is disclosed the manufacture craft that a kind of composite environment-friendly type fine work using ultralight clay material packs Neto, bag
Following steps are included：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：50-60 parts of paper pulp, polyethers are more
First alcohol 30-40 parts, 5-10 parts of poly (vinyl alcohol) binder of 20-30 parts of PEPA, 2-3 parts of kaolin, silica 1-
2 parts, 10-12 parts of bamboo charcoal powder, 1-2 parts of food coloring, 1-2 parts of crosslinking agent, 3-4 parts of polyglycolic acid resin, 2-3 parts of glycerine；
Above-mentioned each raw material is sequentially poured into stirring in container and obtains ultralight clay material within 3-5 hours.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is between 100-120 DEG C, and warm-up time is 5-10 minutes；
The Neto mould is disposable gypsum or aluminum alloy mould.
（4）Neto simultaneously natural air drying 10-12 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Invention is described further with multiple embodiments below：
Embodiment 1
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：50 parts of paper pulp, PPG
38 parts, 25 parts of PEPA, 10 parts of poly (vinyl alcohol) binder, 2 parts of kaolin .5 parts of silica 1, bamboo charcoal powder 12
Part, 1.6 parts of food coloring, 1 part of crosslinking agent, 4 parts of polyglycolic acid resin, 2.4 parts of glycerine；Above-mentioned each raw material is sequentially poured into
Stirring obtains ultralight clay material in 3 hours in container.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is at 110 DEG C, and warm-up time is 6 minutes；The Neto mould
Have for disposable gypsum or aluminum alloy mould.
（4）Neto simultaneously natural air drying 12 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Embodiment 2
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：55 parts of paper pulp, PPG
32 parts, 22 parts of PEPA, 9 parts of poly (vinyl alcohol) binder, 2.8 parts of kaolin, silica 1 part, 10 parts of bamboo charcoal powder,
1.5 parts of food coloring, 2 parts of crosslinking agent, 3 parts of polyglycolic acid resin, 2 parts of glycerine；Above-mentioned each raw material is sequentially poured into container
Middle stirring obtains ultralight clay material in 5 hours.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is between 100 DEG C, and warm-up time is 7 minutes；In described
It is disposable gypsum or aluminum alloy mould to hold in the palm mould.
（4）Neto simultaneously natural air drying 11 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Embodiment 3
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：60 parts of paper pulp, PPG
37 parts, 20 parts of PEPA, 8 parts of poly (vinyl alcohol) binder, 2.6 parts of kaolin, 2 parts of silica, 11 parts of bamboo charcoal powder,
1 part of food coloring, 1.5 parts of crosslinking agent, 3.5 parts of polyglycolic acid resin, 3 parts of glycerine；Above-mentioned each raw material is sequentially poured into appearance
Stirring obtains ultralight clay material in 3.5 hours in device.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is at 120 DEG C, and warm-up time is 8 minutes；The Neto mould
Have for disposable gypsum or aluminum alloy mould.
（4）Neto simultaneously natural air drying 10 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Embodiment 4
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：58 parts of paper pulp, PPG
35 parts, 30 parts of PEPA, 5 parts of poly (vinyl alcohol) binder, 2.3 parts of kaolin .4 parts of silica 1, bamboo charcoal powder
10.5 parts, 1.3 parts of food coloring, 1.4 parts of crosslinking agent, 3.7 parts of polyglycolic acid resin, 2.5 parts of glycerine；By above-mentioned each raw material
Sequentially pour into stirring in container and obtain ultralight clay material in 4.5 hours.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is between 115 DEG C, and warm-up time is 9 minutes；In described
It is disposable gypsum or aluminum alloy mould to hold in the palm mould.
（4）Neto simultaneously natural air drying 10.5 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Embodiment 5
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：54 parts of paper pulp, PPG
30 parts, 28 parts of PEPA, 6 parts of poly (vinyl alcohol) binder, 2.5 parts of kaolin .8 parts of silica 1, bamboo charcoal powder
11.5 parts, 2 parts of food coloring, 1.6 parts of crosslinking agent, 3.2 parts of polyglycolic acid resin, 2.8 parts of glycerine；By above-mentioned each raw material according to
Sequence pours into stirring in container and obtains ultralight clay material in 4.2 hours.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is at 105 DEG C, and warm-up time is 10 minutes；The Neto mould
Have for disposable gypsum or aluminum alloy mould.
（4）Neto simultaneously natural air drying 11.5 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Embodiment 6
A kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, includes following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：52 parts of paper pulp, PPG
40 parts, 26 parts of PEPA, 7 parts of poly (vinyl alcohol) binder, 3 parts of kaolin .7 parts of silica 1, bamboo charcoal powder 10.8
Part, 1.8 parts of food coloring, 1.8 parts of crosslinking agent, 3.9 parts of polyglycolic acid resin, 2.7 parts of glycerine；By above-mentioned each raw material sequentially
Pour into stirring in container and obtain ultralight clay material in 4 hours.
（2）Neto mould is chosen, and ultralight clay material is injected in mould.
（3）Heat drying is carried out to Neto mould, temperature control is between 118 DEG C, and warm-up time is 5 minutes；In described
It is disposable gypsum or aluminum alloy mould to hold in the palm mould.
（4）Neto simultaneously natural air drying 11.8 hours are taken out in die sinking.
（5）UV glazings are carried out to Neto.
Drop test, burn-in test, friction testing, classical test and powder are carried out to Neto made from each above-mentioned embodiment
Dirt is tested, and above-mentioned test all passes through, and is fully met the protectiveness requirement of consumer electronics product and is opened box body and test etc. and disappears
The vivid demand of Fei Duan product brand.
The design focal point of the present invention is：Present invention employs the ultralight clay material of special formulation, make up to specific
Hardness and drying time, reach the color and surface effect of desired design, carry out particular procedure after, applied to consumer electricity
The packaging Neto of the industries such as sub- product, cosmetics, gift, this product can reach the environmental requirement of food-grade, it is possible to achieve essence
Accurate freely matches colors, it is possible to achieve broken colour coordinates, it might even be possible to make different picture on surface, light weight, easy-formation, moulding
Finely, it can preserve for a long time.
The above described is only a preferred embodiment of the present invention, be not intended to limit the scope of the present invention,
Therefore any subtle modifications, equivalent variations and modifications that every technical spirit according to the present invention is made to above example, still
Belong in the range of technical solution of the present invention.
Claims (3)
1. a kind of composite environment-friendly type fine work using ultralight clay material packs the manufacture craft of Neto, it is characterised in that：Including
There are following steps：
（1）Allocate ultralight clay material：Ultralight clay material includes following raw material：50-60 parts of paper pulp, polyethers are more
First alcohol 30-40 parts, 5-10 parts of poly (vinyl alcohol) binder of 20-30 parts of PEPA, 2-3 parts of kaolin, silica
1-2 parts, 10-12 parts of bamboo charcoal powder, 1-2 parts of food coloring, 1-2 parts of crosslinking agent, 3-4 parts of polyglycolic acid resin, glycerine 2-3
Part；Above-mentioned each raw material is sequentially poured into stirring in container and obtains ultralight clay material within 3-5 hours；
（2）Neto mould is chosen, and ultralight clay material is injected in mould；
（3）Heat drying is carried out to Neto mould, temperature control is between 100-120 DEG C, and warm-up time is 5-10 minutes；
（4）Neto simultaneously natural air drying 10-12 hours are taken out in die sinking.
2. the composite environment-friendly type fine work according to claim 1 using ultralight clay material packs the manufacture craft of Neto,
It is characterized in that：The Neto mould is disposable gypsum or aluminum alloy mould.
3. the composite environment-friendly type fine work according to claim 1 using ultralight clay material packs the manufacture craft of Neto,
It is characterized in that：Further comprise there is step（5）UV glazings are carried out to Neto.