CN107130469A - A kind of full paper drum paper of half loosening pressure and preparation method thereof - Google Patents
A kind of full paper drum paper of half loosening pressure and preparation method thereof Download PDFInfo
- Publication number
- CN107130469A CN107130469A CN201710479373.5A CN201710479373A CN107130469A CN 107130469 A CN107130469 A CN 107130469A CN 201710479373 A CN201710479373 A CN 201710479373A CN 107130469 A CN107130469 A CN 107130469A
- Authority
- CN
- China
- Prior art keywords
- paper
- drum
- slurry
- full
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The full paper drum paper of half loosening pressure that the present invention is provided is through size degradation, mashing, bleaching, carry out with slurry obtaining rousing pulp material with filler and chemical assistant, drum pulp material is carried out dragging for slurry, drag for after starching by saturated steam processing, then extrusion dehydration is carried out, improve the surface quality of paper, improve the tightness and intensity of paper；In hot press forming technology, using the technique of low temperature loosening pressure, in this process because temperature is low, pressure is small, the reason for not pressing paper, and paper pulp fiber is not destroyed greatly, the intensity and pliability of drum paper effectively improve, intermediate frequency people's acoustic perspective is improved simultaneously, and sound is moist true, also improves the stereovision of low frequency, make the sound issued abundant, it is not noisy, it is not ear-piercing, it is sound clarity, natural, penetrating.
Description
Technical field
The invention belongs to the field of papermaking of loudspeaker drum paper, and in particular to a kind of full paper drum paper of half loosening pressure and preparation method thereof.
Background technology
Drum paper is divided into full paper according to unlike material and rouses paper, compound drum paper, wheat drawing drum paper etc..Common drum paper is compound drum paper,
It is typically to stick the resistance to vibrations side shattered of comparison at vibrations, such as rubber edge, sponge side, the material such as selvedge.Full paper drum paper is commonly called as
Loudspeaker cone, is the strength member that loudspeaker send sound.It is all hot-forming by paper pulp that total, which includes vibrations ring, is referred to as complete
Paper rouses paper.Full paper drum paper feature is exactly light, and sensitivity is high.
Full paper drum paper is widely used in moving active loundspeakerses, because power supply is 12-24 volt storage battery finite energies, so sharp
The characteristics of rousing paper with full paper is with less power with regard to loudspeaker can be promoted to have comparatively ideal acoustic pressure.Due to full paper drum in the market
Fiber is shorter in paper, and the toughness of drum paper is poor, causes loudspeaker a bit deficient in terms of tonequality that paper is roused using full paper.
The content of the invention
In order to solve problem above, the present invention provides one kind and improves people's acoustic perspective in intermediate frequency, and low frequency level
Sense, and the high full paper drum paper of toughness.
It is an object of the invention to provide a kind of full paper drum paper of half loosening pressure.
It is a further object of the present invention to provide the preparation method that a kind of full paper of half loosening pressure rouses paper.
According to the full paper drum paper of half loosening pressure of the embodiment of the present invention, prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, wood pulp is obtained, by weight ratio, to 80-120 parts
10-15 parts of fillers are added in wood pulp and 4-8 parts of chemical assistants progress are with slurry, bulging pulp material is uniformly mixing to obtain；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, and extrusion dehydration obtains being dehydrated paper
；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.75-0.85mm, hot-pressing drying 55-65s is carried out at 175-185 DEG C, paper is obtained；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
According to the full paper drum paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (1), the filler is
One or more in kaolin, titanium dioxide, gypsum, diatomite and calcium carbonate.
According to the full paper drum paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (1), the chemistry is helped
Agent includes 2-3 parts of cationic compounds, 1-2 parts of anion polysaccharides, 0.5-1.5 parts of dispersing agent for fibres and 0.5- by weight ratio
1.5 parts of drying strengthening agents.
According to the full paper drum paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (4), half obtained pine
The thickness for pressing full paper drum paper is 0.79-0.81mm.
The preparation method of paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention, methods described includes following step
Suddenly：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, wood pulp is obtained, by weight ratio, to 80-120 parts
10-15 parts of fillers are added in wood pulp and 4-8 parts of chemical assistants progress are with slurry, bulging pulp material is uniformly mixing to obtain；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, and extrusion dehydration obtains being dehydrated paper
；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.75-0.85mm, hot-pressing drying 55-65s is carried out at 175-185 DEG C, paper is obtained；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The preparation method of paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (1),
The beating degree of the mashing is 30-35 ° of SR.
The preparation method of paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (1),
The concentration of the wood pulp is 3.5-6.8%.
The preparation method of paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (1),
The time of the mashing is that the length of fiber in 60-90min, obtained slurry is 15-45mm.
In order to remove the moisture dragged in slurry as far as possible, paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention
Preparation method, it is preferable that in step (2), before extrusion dehydration, heating 10- is carried out using saturated steam to dragging for slurry
20min.The dehydration of paper is mainly by the way that caused by capillarity and vertical direction barometric gradient, paper is through supersaturation water
During steam, saturated steam can condense rapidly the water temperature achieved in quick heating, paper in paper and will raise, water
Viscosity and surface tension reduction, while combined surface area between the fiber softening in paper, reinforcing fiber, enhancing is whole dehydrated
The barometric gradient of journey capillarity and vertical direction, can make the moisture in paper be easier to be extruded out.
The preparation method of paper is roused according to the full paper of half loosening pressure of the embodiment of the present invention, it is preferable that in step (2),
The humidity of the dehydration paper is 36-48%.
Beneficial effects of the present invention are：
1. the full paper drum paper of half loosening pressure that the present invention is provided is carried out with slurry through size degradation, mashing, bleaching with filler and chemical assistant
Obtain rousing pulp material, drum pulp material carried out dragging for slurry, drag for after starching by saturated steam processing, then carry out extrusion dehydration,
Improve the surface quality of paper, improve the tightness and intensity of paper；In hot press forming technology, using the technique of low temperature loosening pressure,
In this process because temperature is low, pressure is small, and the reason for not pressing paper, paper pulp fiber is not destroyed greatly, drum paper
Intensity and pliability effectively improve, while improve people's acoustic perspective in intermediate frequency, sound is moist true, also improves
The stereovision of low frequency, makes the sound issued abundant, not noisy, not ear-piercing, sound clarity, natural, penetrating.
2. the preparation method that the full paper of half loosening pressure that the present invention is provided rouses paper, uses 175-185 DEG C during hot-forming
Middle low temperature, hot pressing die gap is to carry out hot-pressing drying 55-65s, the full paper drum of half loosening pressure that finally gives under 0.75-0.85mm
Paper intensity and toughness are significantly improved, and technique is simple, efficiency high.
Embodiment
To make the object, technical solutions and advantages of the present invention clearer, technical scheme will be carried out below
Detailed description.Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Base
Embodiment in the present invention, those of ordinary skill in the art are resulting on the premise of creative work is not made to be owned
Other embodiment, belongs to the scope that the present invention is protected.
Embodiment 1
The full paper drum paper of half loosening pressure, is prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, wood pulp is obtained, by weight ratio, to 80 parts of wood pulps
10 parts of calcium carbonate of middle addition, 2 parts of cationic compounds, 1 part of anion polysaccharide, 0.5 part of dispersing agent for fibre and 0.5 part of drying strengthening agent enter
Row is with slurry, is uniformly mixing to obtain bulging pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, and extrusion dehydration obtains being dehydrated paper
；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.75mm, carries out hot-pressing drying 55s in the case where temperature is 175 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The thickness of the full paper drum paper of half loosening pressure is 0.79mm.
Embodiment 2
The full paper drum paper of half loosening pressure, is prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, beating degree is 30 ° of SR, obtains wood pulp, by weight
Proportioning, added into 120 parts of wood pulps 5 parts of titanium dioxide, 10 parts of calcium carbonate, 3 parts of cationic compounds, 2 parts of anion polysaccharides,
1.5 parts of dispersing agent for fibres and 1.5 parts of drying strengthening agents progress are with slurry, are uniformly mixing to obtain bulging pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, and extrusion dehydration obtains being dehydrated paper
；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.85mm, carries out hot-pressing drying 65s in the case where temperature is 185 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The thickness of the full paper drum paper of half loosening pressure is 0.81mm.
Embodiment 3
The full paper drum paper of half loosening pressure, is prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, beating degree is 35 ° of SR, obtains wood pulp, the wood pulp
Concentration be 3.8%, added by weight ratio into 100 parts of wood pulps 3 parts of titanium dioxide, 3 parts of kaolin, 2 parts of gypsum, 2 parts
Diatomite, 5 parts of calcium carbonate, 1.5 parts of cationic compounds, 1.5 parts of anion polysaccharides, 1.5 parts of dispersing agent for fibres and 1.5 parts are dry strong
Agent progress is with slurry, is uniformly mixing to obtain bulging pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, then utilizes saturated steam pair
Drag for slurry and carry out heating 10min, extrusion dehydration obtains being dehydrated paper, the humidity of the dehydration paper is 36%；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.85mm, carries out hot-pressing drying 65s in the case where temperature is 185 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The thickness of the full paper drum paper of half loosening pressure is 0.8mm.
Embodiment 4
The full paper drum paper of half loosening pressure, is prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, the time of the mashing is fibre in 90min, obtained slurry
The length of dimension is 15mm, and bleaching, beating degree is 32.5 ° of SR, obtains wood pulp, the concentration of the wood pulp is 3.7%, is matched somebody with somebody by weight
Than adding 3 parts of titanium dioxide, 3 parts of kaolin, 2 parts of gypsum, 2 parts of diatomite, 5 parts of calcium carbonate, 1.5 parts of sun into 100 parts of wood pulps
Ionic compound, 1.5 parts of anion polysaccharides, 1.5 parts of dispersing agent for fibres and 1.5 parts of drying strengthening agents progress are with slurry, are uniformly mixing to obtain
Drum pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, then utilizes saturated steam pair
Drag for slurry and carry out heating 20min, extrusion dehydration obtains being dehydrated paper, the humidity of the dehydration paper is 48%；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.8mm, carries out hot-pressing drying 60s in the case where temperature is 180 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The thickness of the full paper drum paper of half loosening pressure is 0.8mm.
Embodiment 5
The full paper drum paper of half loosening pressure, is prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, the time of the mashing is fibre in 60min, obtained slurry
The length of dimension is 45mm, and bleaching, beating degree is 32.5 ° of SR, obtains wood pulp, the concentration of the wood pulp is 3.7%, is matched somebody with somebody by weight
Than adding 3 parts of titanium dioxide, 3 parts of kaolin, 2 parts of gypsum, 2 parts of diatomite, 5 parts of calcium carbonate, 1.5 parts of sun into 100 parts of wood pulps
Ionic compound, 1.5 parts of anion polysaccharides, 1.5 parts of dispersing agent for fibres and 1.5 parts of drying strengthening agents progress are with slurry, are uniformly mixing to obtain
Drum pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, then utilizes saturated steam pair
Drag for slurry and carry out heating 20min, extrusion dehydration obtains being dehydrated paper, the humidity of the dehydration paper is 48%；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is
0.8mm, carries out hot-pressing drying 60s in the case where temperature is 180 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
The thickness of the full paper drum paper of half loosening pressure is 0.8mm.
Experimental example
The full paper of half loosening pressure that testing example 1-5 is obtained rouses the mechanical property of paper, the results are shown in Table 1.Wherein control group is selected
Full paper drum paper purchased in market.
The full paper of the loosening pressure of table 1 half rouses the mechanical property of paper
| Experimental group | Tensile strength kN/m | Fracture toughness J.m/kg |
| Control group | 2.381 | 13.72 |
| Embodiment 1 | 2.532 | 19.34 |
| Embodiment 2 | 2.324 | 18.36 |
| Embodiment 3 | 2.635 | 20.31 |
| Embodiment 4 | 2.613 | 19.54 |
| Embodiment 5 | 2.635 | 20.65 |
From table 1 it follows that the tensile strength and fracture toughness of the full paper drum paper of half loosening pressure that the present invention is provided are with compareing
Group illustrates that the full paper drum paper of half loosening pressure that the present invention is provided has high toughness and intensity compared to being significantly improved.
The drum paper obtained under conditions of 20 DEG C of relative humidity 60% to embodiment 5 carries out Fo tests, obtains its resonance frequency
Rate is 43.89Hz, pliable Cms:155 μm/N, sound pressure level SPL:95.5dB, the equivalent mass Mms of vibrational system：84.66g.
Test result illustrates that the drum paper that the present invention is provided not only improves people's acoustic perspective in intermediate frequency, also improves low frequency
Stereovision.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, change or replacement can be readily occurred in, should all be contained
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be based on the protection scope of the described claims.
Claims (10)
1. a kind of full paper drum paper of half loosening pressure, it is characterised in that prepared by the method comprised the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, wood pulp is obtained, by weight ratio, to 80-120 parts of wood pulps
Middle 10-15 parts of fillers of addition and 4-8 parts of chemical assistants progress are with slurry, are uniformly mixing to obtain bulging pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out half tone and drags for slurry, and extrusion dehydration obtains being dehydrated paper；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is 0.75-
0.85mm, carries out hot-pressing drying 55-65s at 175-185 DEG C, obtains paper；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
2. the full paper drum paper of half loosening pressure according to claim 1, it is characterised in that in step (1), the filler is kaolinite
One or more in soil, titanium dioxide, gypsum, diatomite and calcium carbonate.
3. the full paper drum paper of half loosening pressure according to claim 1, it is characterised in that in step (1), the chemical assistant is by weight
Amount part proportioning includes 2-3 parts of cationic compounds, 1-2 parts of anion polysaccharides, 0.5-1.5 parts of dispersing agent for fibres and 0.5-1.5 parts
Drying strengthening agent.
4. the full paper drum paper of half loosening pressure according to claim 1, it is characterised in that in step (4), the obtained full paper of half loosening pressure
The thickness of drum paper is 0.79-0.81mm.
5. a kind of full paper of half loosening pressure rouses the preparation method of paper, it is characterised in that the described method comprises the following steps：
(1) paper pulp is prepared：By wood raw material size degradation, mashing, bleaching, wood pulp is obtained, by weight ratio, to 80-120 parts of wood pulps
Middle 10-15 parts of fillers of addition and 4-8 parts of chemical assistants progress are with slurry, are uniformly mixing to obtain bulging pulp material；
(2) slurry shaping is dragged for：The drum pulp material that step (1) is obtained carries out dragging for slurry, and extrusion dehydration obtains being dehydrated paper；
(3) it is hot-forming：The dehydration paper that step (2) is obtained is placed in hot pressing die, and hot pressing die gap is 0.75-
0.85mm, hot-pressing drying 55-65s is carried out at 175-185 DEG C, paper is obtained；
(4) it is punched：Shaping is punched out to the paper that step (3) is obtained, that is, obtains the full paper drum paper of half loosening pressure.
6. the full paper of half loosening pressure according to claim 5 rouses the preparation method of paper, it is characterised in that described to beat in step (1)
The beating degree of slurry is 30-35 ° of SR.
7. the full paper of half loosening pressure according to claim 5 rouses the preparation method of paper, it is characterised in that in step (1), the wood
The concentration of slurry is 3.5-6.8%.
8. the full paper of half loosening pressure according to claim 5 rouses the preparation method of paper, it is characterised in that described to beat in step (1)
The time of slurry is that the length of fiber in 60-90min, obtained slurry is 15-45mm.
9. the full paper of half loosening pressure according to claim 5 rouses the preparation method of paper, it is characterised in that in step (2), in extruding
Before dehydration, heating 10-20min is carried out to dragging for slurry using saturated steam.
10. the full paper of half loosening pressure according to claim 5 rouses the preparation method of paper, it is characterised in that described in step (2)
The humidity for being dehydrated paper is 36-48%.