CN107128911A - A kind of method that utilization bagasse prepares activated carbon - Google Patents
A kind of method that utilization bagasse prepares activated carbon Download PDFInfo
- Publication number
- CN107128911A CN107128911A CN201710266775.7A CN201710266775A CN107128911A CN 107128911 A CN107128911 A CN 107128911A CN 201710266775 A CN201710266775 A CN 201710266775A CN 107128911 A CN107128911 A CN 107128911A
- Authority
- CN
- China
- Prior art keywords
- bagasse
- activated carbon
- sodium carbonate
- carbonate liquor
- utilization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of method that utilization bagasse prepares activated carbon, crushed after bagasse is dried, be then added in sodium carbonate liquor and soak 10 20h, the weight ratio of the bagasse and sodium carbonate liquor after drying is 1:3‑6;By the bagasse dehydration after immersion, it is subsequently placed in Muffle furnace and carries out charing process, obtain carbide;By carbide chlorohydric acid pickling, then neutrality is washed to, finally dries and sieve, produce.The recycling that this method solve bagasse, the waste for avoiding resource and environmental pollution provide effective way, sugar industry can be directly used for by its activated carbon prepared, added value of product is high, good social and economic benefit can be produced, and the activated carbon decolorizing ability of the present invention is strong, stability is good, and intensity is high, safety non-toxic.
Description
Technical field
The present invention relates to a kind of preparation method of activated carbon, the method that especially a kind of utilization bagasse prepares activated carbon,
Belong to technical field of fine.
Background technology
China is the big country of Sugar Production and consumption, and cane sugar manufacture is with a long history in China.Bagasse is sugar industry
Principal by product, the composition of bagasse is based on cellulose, hemicellulose and lignin, albumen, starch and soluble sugar content
It is less;Because the degree of lignification of bagasse is higher, there is the reasons such as silicified cell in stem epidermis, its be all difficult to for a long time by
Effective trans-utilization, often goes out of use without or being only simple as fuel, utilization rate is very low, not only causes resource
Waste, but also bring the pollution of environment.
In the last few years, there is scholar that bagasse is produced into activated carbon, and for the adsorption treatment of heavy metal waste water, achieved one
Fixed effect.But, bagasse active carbon has that absorption stability is bad, intensity is not high, absorption property one in use
As the problems such as, so as to constrain the use of bagasse active carbon.
The content of the invention
There is provided one kind for the deficiency existed present invention aim to address the activated carbon prepared in the prior art using bagasse
The method that activated carbon is prepared using bagasse, its decoloring ability is strong, and stability is good, and intensity is high, safety non-toxic.
Technical scheme
A kind of method that utilization bagasse prepares activated carbon, comprises the following steps:
(1) crushed after bagasse is dried, be then added in sodium carbonate liquor and soak 10-20h, the bagasse after drying
Weight ratio with sodium carbonate liquor is 1:3-6;
(2) bagasse after immersion is dehydrated, is subsequently placed in Muffle furnace and carries out charing process, obtain carbide;
(3) by carbide chlorohydric acid pickling, then neutrality is washed to, finally dries and sieve, produce.
Further, in step (1), the drying temperature is 105-110 DEG C.
Further, in step (1), the sodium carbonate liquor concentration is 1-3mol/L.
Further, in step (1), the weight ratio of bagasse and sodium carbonate liquor after drying is 1:4.
Further, in step (2), the charing process temperature is 450-550 DEG C, and the time is 2-4h.
Further, in step (3), the sieving was 100 mesh sieves.
Beneficial effects of the present invention:The present invention uses bagasse for raw material to prepare activated carbon, is not only solution bagasse
Recycling, avoid the waste and environmental pollution of resource from providing effective way, and bagasse is a kind of safety non-toxic in itself
Recyclable organism material, sugar industry can be directly used for by its activated carbon prepared, added value of product is high, can produce
Good social and economic benefit, and the activated carbon decolorizing ability of the present invention is strong, and stability is good, and intensity is high, safety non-toxic.
Embodiment
With reference to embodiment, the invention will be further described.
Embodiment 1
Crushed after bagasse is dried at 105 DEG C, be then added in 1mol/L sodium carbonate liquors and soak 12h, after drying
Bagasse and sodium carbonate liquor weight ratio be 1:4;By the bagasse centrifugal dehydration after immersion, it is subsequently placed in Muffle furnace
Row charing process, charing process temperature is 450 DEG C, and the time is 4h, obtains carbide;By intermediate product chlorohydric acid pickling, then water
Neutrality is washed till, finally dried at 110 DEG C, cross 100 mesh sieves, produced.
The activated carbon iodine number that experiment measures the present embodiment is 550mg/g, and yield is 39%, and intensity is 88%.
Embodiment 2
Crushed after bagasse is dried at 110 DEG C, be then added in 3mol/L liquor zinci chloridis and soak 10h, after drying
Bagasse and sodium carbonate liquor weight ratio be 1:4;By the bagasse centrifugal dehydration after immersion, it is subsequently placed in Muffle furnace
Row charing process, charing process temperature is 500 DEG C, and the time is 3h, obtains carbide;By intermediate product chlorohydric acid pickling, then water
Neutrality is washed till, finally in 108 DEG C of drying, is produced.
The activated carbon iodine number that experiment measures the present embodiment is 530mg/g, and yield is 37%, and intensity is 91%.
Claims (6)
1. a kind of method that utilization bagasse prepares activated carbon, it is characterised in that comprise the following steps:
(1) crushed after bagasse is dried, be then added in sodium carbonate liquor and soak 10-20h, bagasse and carbon after drying
The weight ratio of acid sodium solution is 1:3-6;
(2) bagasse after immersion is dehydrated, is subsequently placed in Muffle furnace and carries out charing process, obtain carbide;
(3) by carbide chlorohydric acid pickling, then neutrality is washed to, finally dries and sieve, produce.
2. the method for preparing activated carbon using bagasse as claimed in claim 1, it is characterised in that in step (1), described to dry
Dry temperature is 105-110 DEG C.
3. the method for preparing activated carbon using bagasse as claimed in claim 1, it is characterised in that in step (1), the carbon
Acid sodium solution concentration is 1-3mol/L.
4. the method for preparing activated carbon using bagasse as claimed in claim 1, it is characterised in that in step (1), after drying
Bagasse and sodium carbonate liquor weight ratio be 1:4.
5. the method for preparing activated carbon using bagasse as claimed in claim 1, it is characterised in that in step (2), the charcoal
It is 450-550 DEG C to change treatment temperature, and the time is 2-4h.
6. the method that the utilization bagasse as described in any one of claim 1 to 5 prepares activated carbon, it is characterised in that step (3)
In, the sieving was 100 mesh sieves.