CN107120913A - A kind of mao bamboon bar furnace drying method - Google Patents
A kind of mao bamboon bar furnace drying method Download PDFInfo
- Publication number
- CN107120913A CN107120913A CN201710347178.7A CN201710347178A CN107120913A CN 107120913 A CN107120913 A CN 107120913A CN 201710347178 A CN201710347178 A CN 201710347178A CN 107120913 A CN107120913 A CN 107120913A
- Authority
- CN
- China
- Prior art keywords
- mao bamboon
- drying
- bar
- bamboon bar
- mao
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of mao bamboon bar furnace drying method, belongs to mao bamboon processing technique field, and this method is to comprise the steps of：(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；(2) mao bamboon bar is put into clear water, washes away chip impurity；(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried；(4) hardening agent is uniformly coated with each mao bamboon bar surface, is then blown with fan against mao bamboon bar；(5) mao bamboon bar is put into drying baker and dried again；(6) mao bamboon bar is subjected to high temperature drying；(7) mao bamboon bar is subjected to room temperature cooling, it is then standby.The present invention can make wet mao bamboon be dried, and extend the resting period of mao bamboon；The invention enables the not mouldy and no moth of mao bamboon, mao bamboon easily preserves；The present invention improves economic well-being of workers and staff.
Description
Technical field
The invention belongs to mao bamboon processing technique field, more particularly to a kind of mao bamboon bar furnace drying method.
Background technology
Mao bamboon is that Chinese cultivated is long, area most wide, economic value also most important bamboo kind.Its pole type is thick, preferably supplies to build
Use, such as beam column, frame, scaffold are built, the thin bamboo strip is excellent, apparatus and handicraft for weaving various thicknesses, branch makees broom, tender
Bamboo and pole sheaths of bamboo shoots make paper making raw material.When being deposited after wet mao bamboon processing, easily mouldy and raw moth causes excessive economic loss.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of mao bamboon bar furnace drying method.
To solve the above problems, a kind of mao bamboon bar furnace drying method of the present invention, this method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 60~75 DEG C, drying time
For 30~40 minutes；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, be then uniformly coated with by force on each mao bamboon bar surface
Agent, is then blown with fan against mao bamboon bar, and the time that fan blows is 15~20 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 85~95
DEG C, drying time is 10~15 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 100~115 DEG C, and drying time is 8
~12 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
The hardening agent is made up of the composition of following parts by weight：Calcium hydroxide 15~20, soybean oil 20~30, titanium dioxide
Silicon 22~26, boric acid 10~13 and water 16~19.
The preparation method of the hardening agent is：Calcium hydroxide 15~20 and soybean oil 20~30 are added to water 16~19
In, mixed liquor a is uniformly mixing to obtain, silica 22~26 and boric acid 10~13 are added in mixed liquor a, is added while stirring
Heat, heating-up temperature is 80~90 DEG C, and mixing time is 10~13 minutes, you can the hardening agent is made.
Compared with prior art, the present invention has advantages below：The present invention can make wet mao bamboon be dried, extension mao bamboon
Resting period；The invention enables the not mouldy and no moth of mao bamboon, mao bamboon easily preserves；The present invention improves economic well-being of workers and staff.
Embodiment
Embodiment 1
A kind of mao bamboon bar furnace drying method, this method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 60 DEG C, and drying time is 30
Minute；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, be then uniformly coated with by force on each mao bamboon bar surface
Agent, is then blown with fan against mao bamboon bar, and the time that fan blows is 15 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 85 DEG C, is dried
The dry time is 10 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 100 DEG C, and drying time is 8 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
Hardening agent is made up of the composition of following parts by weight：Calcium hydroxide 15, soybean oil 20, silica 22, boric acid 10
With water 16.
The preparation method of hardening agent is：Calcium hydroxide 15 and soybean oil 20 are added in water 16, are uniformly mixing to obtain mixed
Liquid a is closed, silica 22 and boric acid 10 are added in mixed liquor a, heated while stirring, heating-up temperature is 80 DEG C, during stirring
Between be 10 minutes, you can be made the hardening agent.
It is demonstrated experimentally that the mouldy rate of mao bamboon is low under this parameter, raw moth rate is low.
Embodiment 2
A kind of mao bamboon bar furnace drying method, this method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 68 DEG C, and drying time is 35
Minute；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, be then uniformly coated with by force on each mao bamboon bar surface
Agent, is then blown with fan against mao bamboon bar, and the time that fan blows is 18 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 90 DEG C, is dried
The dry time is 13 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 108 DEG C, and drying time is 10 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
Hardening agent is made up of the composition of following parts by weight：Calcium hydroxide 18, soybean oil 25, silica 24, boric acid 12
With water 18.
The preparation method of hardening agent is：Calcium hydroxide 15 and soybean oil 25 are added in water 18, are uniformly mixing to obtain mixed
Liquid a is closed, silica 24 and boric acid 12 are added in mixed liquor a, heated while stirring, heating-up temperature is 85 DEG C, during stirring
Between be 12 minutes, you can be made the hardening agent.
It is demonstrated experimentally that the mouldy rate of mao bamboon is minimum under this parameter, raw moth rate is minimum.
Therefore, the present embodiment is preferred embodiment.
Embodiment 3
A kind of mao bamboon bar furnace drying method, this method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 75 DEG C, and drying time is 40
Minute；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, be then uniformly coated with by force on each mao bamboon bar surface
Agent, is then blown with fan against mao bamboon bar, and the time that fan blows is 20 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 95 DEG C, is dried
The dry time is 15 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 115 DEG C, and drying time is 12 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
Hardening agent is made up of the composition of following parts by weight：Calcium hydroxide 20, soybean oil 30, silica 26, boric acid 13
With water 19.
The preparation method of hardening agent is：Calcium hydroxide 20 and soybean oil 30 are added in water 19, are uniformly mixing to obtain mixed
Liquid a is closed, silica 26 and boric acid 13 are added in mixed liquor a, heated while stirring, heating-up temperature is 90 DEG C, during stirring
Between be 13 minutes, you can be made the hardening agent.
It is demonstrated experimentally that the mouldy rate of mao bamboon is low under this parameter, raw moth rate is minimum.
Claims (6)
1. a kind of mao bamboon bar furnace drying method, it is characterised in that:This method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 60~75 DEG C, and drying time is 30
~40 minutes；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, is then uniformly coated with hardening agent on each mao bamboon bar surface,
Then blown with fan against mao bamboon bar, the time that fan blows is 15~20 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 85~95 DEG C, is dried
The dry time is 10~15 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 100~115 DEG C, and drying time is 8~12
Minute；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
2. a kind of mao bamboon bar furnace drying method according to claim 1, it is characterised in that：The hardening agent is by following parts by weight
Composition be made：Calcium hydroxide 15~20, soybean oil 20~30, silica 22~26, boric acid 10~13 and water 16~19.
3. a kind of preparation method of hardening agent according to claim 2, it is characterised in that：The preparation method of the hardening agent
It is：Calcium hydroxide 15~20 and soybean oil 20~30 are added in water 16~19, mixed liquor a is uniformly mixing to obtain, by dioxy
SiClx 22~26 and boric acid 10~13 are added in mixed liquor a, are heated while stirring, and heating-up temperature is 80~90 DEG C, during stirring
Between be 10~13 minutes, you can be made the hardening agent.
4. a kind of mao bamboon bar furnace drying method according to claim 1, it is characterised in that：This method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 60 DEG C, drying time is 30 points
Clock；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, is then uniformly coated with hardening agent on each mao bamboon bar surface,
Then blown with fan against mao bamboon bar, the time that fan blows is 15 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 85 DEG C, during drying
Between be 10 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 100 DEG C, and drying time is 8 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
5. a kind of mao bamboon bar furnace drying method according to claim 1, it is characterised in that：This method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 68 DEG C, drying time is 35 points
Clock；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, is then uniformly coated with hardening agent on each mao bamboon bar surface,
Then blown with fan against mao bamboon bar, the time that fan blows is 18 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 90 DEG C, during drying
Between be 13 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 108 DEG C, and drying time is 10 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.
6. a kind of mao bamboon bar furnace drying method according to claim 1, it is characterised in that：This method is to comprise the steps of：
(1) whole mao bamboon is truncated into fixed length mao bamboon thick bamboo tube, then mao bamboon thick bamboo tube is splitted into and waits a point mao bamboon bar；
(2) mao bamboon bar is put into clear water, washes away chip impurity；
(3) the mao bamboon bar cleaned up is put into drying baker and tentatively dried, drying temperature is 75 DEG C, drying time is 40 points
Clock；
(4) the mao bamboon bar after preliminary drying is taken out out of drying baker, is then uniformly coated with hardening agent on each mao bamboon bar surface,
Then blown with fan against mao bamboon bar, the time that fan blows is 20 minutes；
(5) the mao bamboon bar after (4) step process is put into drying baker and dried again, drying temperature is 95 DEG C, during drying
Between be 15 minutes；
(6) the mao bamboon bar after drying again is subjected to high temperature drying, drying temperature is 115 DEG C, and drying time is 12 minutes；
(7) the mao bamboon bar after high temperature is dried carries out room temperature cooling, then standby.