CN107119235A - A kind of auto parts and components alloy material - Google Patents
A kind of auto parts and components alloy material Download PDFInfo
- Publication number
- CN107119235A CN107119235A CN201710389164.1A CN201710389164A CN107119235A CN 107119235 A CN107119235 A CN 107119235A CN 201710389164 A CN201710389164 A CN 201710389164A CN 107119235 A CN107119235 A CN 107119235A
- Authority
- CN
- China
- Prior art keywords
- parts
- alloy material
- strontium
- titanium
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of auto parts and components alloy material, include the component of following parts by weight:80 85 parts of iron;0.2 0.35 parts of strontium;0.45 0.6 parts of cobalt;0.1 0.3 parts of magnesium;0.12 0.55 parts of titanium.The beneficial effects of the invention are as follows:The setting of titanium and strontium, makes all to greatly improve in resistance to abrasion, abrasive wear and the erosive resistance of sliding of surface of automobile part, while composition and ratio and order of addition by adjusting and controlling each element in alloy material, it is ensured that stability.
Description
Technical field
The present invention relates to a kind of metal material, more particularly to a kind of auto parts and components alloy material.
Background technology
With the continuous improvement of science and technology, hardware industry also constantly emerges, and iron-based handware is due to price at this stage
Cheap therefore most widely used, while iron-based handware, which also possesses, preferable use value, then iron-based handware makes
There is more defect during, such as:Easily it is oxidized, is easily corroded, while in automobile industry, preceding manufacturer's legal system
Standby metal material generally existing quality is general, and easy-to-rust, adaptive capacity to environment is poor, and service life is short;Non- desulfurization process causes
Fragility is big, and easy fracture has potential safety hazard.
Therefore, to solve the above problems, special provide a kind of new technical scheme.
The content of the invention
The present invention provides a kind of auto parts and components alloy material.
The technical solution adopted by the present invention is:
A kind of auto parts and components alloy material, includes the component of following parts by weight:80-85 parts of iron;0.2-0.35 parts of strontium;
0.45-0.6 parts of cobalt;0.1-0.3 parts of magnesium;0.12-0.55 parts of titanium.
Further, the parts by weight of the titanium are 0.25 part.
Further, the parts by weight of the iron are 82 parts.
Further, the parts by weight of the strontium are 0.25-0.3 parts.
Further, the parts by weight of the magnesium are 0.25 part.
The beneficial effects of the invention are as follows:The setting of titanium and strontium, makes in the resistance to slip abrasion of surface of automobile part, abrasive wear
All greatly improved with erosive resistance, while by adjusting and controlling the composition and ratio of each element and addition in alloy material
Sequentially, it is ensured that stability.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not constitute the restriction to protection scope of the present invention.
Embodiment 1
A kind of auto parts and components alloy material, includes the component of following parts by weight:80 parts of iron;0.2 part of strontium;0.45 part
Cobalt;0.1 part of magnesium;0.12 part of titanium.
The beneficial effects of the invention are as follows:The setting of titanium and strontium, makes in the resistance to slip abrasion of surface of automobile part, abrasive wear
All greatly improved with erosive resistance, while by adjusting and controlling the composition and ratio of each element and addition in alloy material
Sequentially, it is ensured that stability.
Embodiment 2
A kind of auto parts and components alloy material, includes the component of following parts by weight:82 parts of iron;0.28 part of strontium;0.5 part
Cobalt;0.2 part of magnesium;0.35 part of titanium.
The beneficial effects of the invention are as follows:The setting of titanium and strontium, makes in the resistance to slip abrasion of surface of automobile part, abrasive wear
All greatly improved with erosive resistance, while by adjusting and controlling the composition and ratio of each element and addition in alloy material
Sequentially, it is ensured that stability.
Embodiment 3
A kind of auto parts and components alloy material, includes the component of following parts by weight:85 parts of iron;0.35 part of strontium;0.6 part
Cobalt;0.3 part of magnesium;0.55 part of titanium.
The beneficial effects of the invention are as follows:The setting of titanium and strontium, makes in the resistance to slip abrasion of surface of automobile part, abrasive wear
All greatly improved with erosive resistance, while by adjusting and controlling the composition and ratio of each element and addition in alloy material
Sequentially, it is ensured that stability.
The above described is only a preferred embodiment of the present invention, being not the limit for making any other form to the present invention
System, and any modification made according to technical spirit of the invention or equivalent variations, still fall within model claimed of the invention
Enclose.
Claims (5)
1. a kind of auto parts and components alloy material, it is characterised in that:Include the component of following parts by weight:80-85 parts of iron;
0.2-0.35 parts of strontium;0.45-0.6 parts of cobalt;0.1-0.3 parts of magnesium;0.12-0.55 parts of titanium.
2. a kind of auto parts and components alloy material according to claim 1, it is characterised in that:The parts by weight of the titanium
For 0.25 part.
3. a kind of auto parts and components alloy material according to claim 1, it is characterised in that:The parts by weight of the iron
For 82 parts.
4. a kind of auto parts and components alloy material according to claim 1, it is characterised in that:The parts by weight of the strontium
For 0.25-0.3 parts.
5. a kind of auto parts and components alloy material according to claim 1, it is characterised in that:The parts by weight of the magnesium
For 0.25 part.