CN107118524A - A kind of inner container of icebox sheet material and preparation method thereof - Google Patents
A kind of inner container of icebox sheet material and preparation method thereof Download PDFInfo
- Publication number
- CN107118524A CN107118524A CN201710419420.7A CN201710419420A CN107118524A CN 107118524 A CN107118524 A CN 107118524A CN 201710419420 A CN201710419420 A CN 201710419420A CN 107118524 A CN107118524 A CN 107118524A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- icebox
- inner container
- preparation
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of inner container of icebox sheet material and preparation method thereof.The inner container of icebox is made with sheet material by the component including following parts by weight:100 parts of polyester materials, 0.1~5 part of titanium dioxide, 0.05~2 part of lubricant, 0.05~2 part of antioxidant.Sheet material provided by the present invention has higher glossiness, excellent resistance to polynary foaming agent corrosive nature and higher foodsafety, simultaneously because the sheet material is polyester material, belong to polar material, its as between inner container of icebox and polyurethane foaming layer have good cementitiousness, corona technique can be exempted, producting process difficulty is reduced.
Description
Technical field
The present invention relates to a kind of inner container of icebox, more particularly to a kind of inner container of icebox sheet material and preparation method thereof.
Background technology
Current refrigerator using sheet material level HIPS or ABS, passes through plate squeezing, plastics sucking moulding inner container of icebox mostly.However, ABS because
Its cost is higher, can not meet the reasons such as food security, is gradually substituted by sheet material level HIPS.HIPS is in order to reach height for sheet material level
The characteristics of toughness, the rubber of big particle diameter is added in the course of the polymerization process, thus its surface is matte effect, outward appearance, which is difficult to meet, to be wanted
Ask.Generally there is the HIPS of bloom effect, but bloom using multi-layer co-extruded method in laminating one layer of dumb light layer surface at present
HIPS surface chemical resistance is poor, easily cracks.When inner container of icebox is contacted with polyurethane foamed thermal-insulating layer, gather
Foaming agent in urethane insulating foam layer can produce corrosiveness to HIPS materials inner bag, easily form crackle.Thus, existing process
In by multi-layer co-extruded mode, in the laminating one layer of PE/PS alloy-layer in surface contacted with polyurethane foamed thermal-insulating layer, to carry
High inner container of icebox inner surface corrosion resistance.
To sum up, current refrigerator inner bag needs to use to reach the effect of the anti-foaming agent corrosion of outer surface high glaze, inner surface
Bloom HIPS, dumb light HIPS (high tenacity HIPS) and PE/PS alloys it is three-layer co-extruded go out manufacture craft.But the technical process is multiple
Miscellaneous, each thickness degree is difficult to control to, and production cost is higher.Simultaneously as HIPS belongs to non-polar material, polyurethane foamed thermal-insulating layer
Belong to polar material, the cementitiousness of the two need to be ensured using surface corona technique at present, producting process difficulty is added again.
The content of the invention
In view of the above-mentioned technical problem that current refrigerator inner bag is present, the present invention provide a kind of new inner container of icebox sheet material and
Its preparation method.
A kind of inner container of icebox sheet material, is made by the component including following parts by weight:100 parts of polyester materials, 0.1~5 part
Titanium dioxide, 0.05~2 part of lubricant, 0.05~2 part of antioxidant.
The polyester material be PET (polyethylene terephthalate), PBT (polybutylene terephthalate (PBT)),
PETG (polyethylene terephthalate -1,4 cyclohexane dimethanol ester), PCTG (poly terephthalic acid -1,4- hexamethylenes two
Methanol ester) in one or more.
The titanium dioxide is rutile type titanium white.
The lubricant is selected from one in stearic acid or its esters, Tissuemat E or the double stearic amides (EBS) of vinyl
Plant or a variety of.
Described antioxidant is one or two kinds of mixtures of hindered phenol compound or bi-ester of phosphite kind;It is preferred that anti-
Oxygen agent 168.
As currently preferred and embodiment, the inner container of icebox sheet material is by including the component system of following parts by weight
:100 parts of polyester materials, 1~2 part of titanium dioxide, 0.1~0.2 part of lubricant, 0.1~0.2 part of antioxidant.
The present invention also provides the preparation method of above-mentioned inner container of icebox sheet material, comprises the following steps:
(a) raw material is mixed;
(b) melting extrusion;
(c) cooling and shaping;
(d) cut.
In the step (a), the raw material is disposably mixed to uniform rear stand-by.
In the step (b), the process conditions of the melting extrusion are:180~260 DEG C of temperature, vacuum 0.05~-
0.1MPa;It is preferred to use single screw extrusion machine in the present invention, its screw slenderness ratio is 20~38:1;Lamina is used in the present invention
Material extrusion way.
As the preferred embodiment of the present invention, each area's temperature of melting extrusion is as follows:
Region | 1st area | 2nd area | 3rd area | 4th area | 5th area | 6th area | 7th area | 8th area |
Temperature | 180 | 195 | 210 | 240 | 245 | 230 | 230 | 245 |
In the step (c), the chilling temperature of the cooling and shaping is 30~70 DEG C, is preferred to use oblique three roller in the present invention
Carry out cooling and shaping.
As the preferred embodiment of the present invention, three roll temperatures of oblique three roller be respectively 70 DEG C of upper roller, 30 DEG C of central roll,
30 DEG C of lower roll.
In the step (d), the cutting is that sawing or knife are cut, and is cut according to certain size, you can obtain being used for refrigerator
The sheet material of inner bag plastics sucking moulding.
As the preferred embodiment of the present invention, the preparation method of the inner container of icebox sheet material comprises the following steps:
(a) raw material is disposably mixed to uniform rear stand-by;
(b) by mixed material melting extrusion obtained by step (a), melt is obtained;The process conditions of the melting extrusion are:Temperature
180~260 DEG C of degree, 0.05~-0.1MPa of vacuum;
(c) above-mentioned melt is obtained into section bar in 30~70 DEG C of cooling and shapings;
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.
The present invention is had the advantages that:
The present invention is equipped with specific titanium dioxide, lubricant and antioxidant, passes through each component using polyester material as primary raw material
Synergy, gained sheet material have higher glossiness, excellent resistance to polynary foaming agent corrosive nature and yellowing-resistant ability, in addition
Also there is the multiple premium properties such as higher foodsafety;Particularly, based on tool between polar material and polyurethane foaming layer
There is good cementitiousness, the preparation technology of sheet material of the present invention can exempt corona step, substantially reduce production technology difficult
Degree.
Embodiment
Following examples are used to illustrate the present invention, but are not limited to the scope of the present invention.
A kind of inner container of icebox sheet material of embodiment 1
A kind of inner container of icebox sheet material, is formulated as follows:
100 parts of polyethylene terephthalates (PET), 1 part of titanium dioxide, the double stearic amides of 0.1 part of vinyl
(EBS), 0.1 part of irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters).
A kind of inner container of icebox sheet material of embodiment 2
A kind of inner container of icebox sheet material, is formulated as follows:
100 parts of polyethylene terephthalate -1,4 cyclohexane dimethanol esters (PETG), 2 parts of titanium dioxides, 0.1 part of second
Alkenyl double stearic amide (EBS), 0.1 part of irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters).
A kind of inner container of icebox sheet material of embodiment 3
A kind of inner container of icebox sheet material, is formulated as follows:
80 parts of polyethylene terephthalate -1,4 cyclohexane dimethanol esters (PETG), 20 parts of poly terephthalic acid -1,
4- cyclohexanedimethanoester esters (PCTG), 2 parts of titanium dioxides, 0.1 part of vinyl double stearic amide (EBS), 0.1 part of irgasfos 168
(three [2,4- di-tert-butyl-phenyls] phosphite esters).
A kind of inner container of icebox sheet material of comparative example 1
A kind of inner container of icebox sheet material, is formulated as follows:(it is that main material is different from the difference of embodiment 2, other auxiliary material consumptions are equal
It is identical)
100 parts of high impact polystyrenes (HIPS), 2 parts of titanium dioxides, 0.1 part of vinyl double stearic amide (EBS), 0.1
Part irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters).
Embodiment 4
The present embodiment provides the preparation method of refrigerator inner liner plates described in embodiment 1, comprises the following steps:
(a) by 100 parts of polyethylene terephthalates (PET), 1 part of titanium dioxide, the double stearic amides of 0.1 part of vinyl
(EBS), 0.1 part of irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters) is disposable well mixed rear stand-by in proportion.
(b) mixture obtained by step (a) is heated into melting extrusion by single screw rod plate squeezing machine and obtains melt, extruder it is each
Area's temperature is as shown in the table, vacuum -0.1MPa.
Region | 1st area | 2nd area | 3rd area | 4th area | 5th area | 6th area | 7th area | 8th area |
Temperature | 180 | 195 | 210 | 240 | 245 | 230 | 230 | 245 |
(c) melt obtained by step (b) is subjected to cooling and shaping by oblique three roller, obtains section bar, on three roll temperatures are respectively
70 DEG C of roller, 30 DEG C of central roll, 30 DEG C of lower roll.
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.
Testing result:
(1) its surface gloss is tested under 60 ° of angle conditions using vancometer by the sheet material prepared by this programme
For 110~120;
(2) sheet material is after plastics sucking moulding inner bag, and surface gloss is up to 100~110;
(3) sheet material is cut into 100mm*20mm strip and is placed in polynary foaming agent and soak 24h, dissolving is not as a result produced
And Swelling;
(4) using the refrigerator made by the case courage of the plate forming, in its inner bag oil surface, by 10 cycle height
(- 40 DEG C~60 DEG C) experiments of temperature circulation, inner bag surface does not produce corrosion line and cracking phenomena.
Embodiment 5
The present embodiment provides the preparation method of refrigerator inner liner plates described in embodiment 2, comprises the following steps:
(a) by 100 parts of polyethylene terephthalates -1,4 cyclohexane dimethanol ester (PETG), 2 parts of titanium dioxides, 0.1
Part vinyl double stearic amide (EBS), 0.1 part of irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters) are in proportion
It is disposable well mixed rear stand-by.
(b) mixture obtained by step (a) is heated into melting extrusion by single screw rod plate squeezing machine and obtains melt, extruder it is each
The step (b) of area's temperature be the same as Example 5, vacuum -0.1MPa.
(c) melt obtained by step (b) is subjected to cooling and shaping by oblique three roller, obtains section bar, three roll temperature be the same as Examples 5
Step (c).
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.
Testing result:
(1) its surface gloss is tested under 60 ° of angle conditions using vancometer by the sheet material prepared by this programme
For 110~120;
(2) sheet material is after plastics sucking moulding inner bag, and surface gloss is up to 100~110;
(3) sheet material is cut into 100mm × 20mm strip and is placed in polynary foaming agent and soak 24h, as a result do not produced molten
Solution and Swelling;
(4) using the refrigerator made by the case courage of the plate forming, in its inner bag oil surface, by 10 cycle height
(- 40 DEG C~60 DEG C) experiments of temperature circulation, inner bag surface does not produce corrosion line and cracking phenomena.
Embodiment 6
The present embodiment provides the preparation method of refrigerator inner liner plates described in embodiment 3, comprises the following steps:
(a) by 80 parts of polyethylene terephthalates -1,4 cyclohexane dimethanol ester (PETG), 20 parts of poly- terephthaldehydes
Acid -1,4 cyclohexane dimethanol ester (PCTG), 2 parts of titanium dioxides, 0.1 part of vinyl double stearic amide (EBS), 0.1 part of antioxygen
Agent 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters) is disposable well mixed rear stand-by in proportion.
(b) mixture obtained by step (a) is heated into melting extrusion by single screw rod plate squeezing machine and obtains melt, extruder it is each
The step (b) of area's temperature be the same as Example 5, vacuum -0.1MPa.
(c) melt obtained by step (b) is subjected to cooling and shaping by oblique three roller, obtains section bar, three roll temperatures are with implementation
The step (c) of example 5.
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.
Testing result:
(1) its surface gloss is tested under 60 ° of angle conditions using vancometer by the sheet material prepared by this programme
For 110~120;
(2) sheet material is after plastics sucking moulding inner bag, and surface gloss is up to 100~110;
(3) sheet material is cut into 100mm*20mm strip and is placed in polynary foaming agent and soak 24h, dissolving is not as a result produced
And Swelling;
(4) using the refrigerator made by the case courage of the plate forming, in its inner bag oil surface, by 10 cycle height
(- 40 DEG C~60 DEG C) experiments of temperature circulation, inner bag surface does not produce corrosion line and cracking phenomena.
Comparative example 2
The present embodiment provides the preparation method of refrigerator inner liner plates described in comparative example 1, comprises the following steps:
(a) by 100 parts of high impact polystyrenes (HIPS), 2 parts of titanium dioxides, the double stearic amides of 0.1 part of vinyl
(EBS), 0.1 part of irgasfos 168 (three [2,4- di-tert-butyl-phenyls] phosphite esters) is disposable well mixed rear stand-by in proportion.
(b) mixture obtained by step (a) is heated into melting extrusion by single screw rod plate squeezing machine and obtains melt, extruder it is each
Area's temperature is as shown in the table, vacuum -0.1MPa.
Region | 1st area | 2nd area | 3rd area | 4th area | 5th area | 6th area | 7th area | 8th area |
Temperature | 160 | 175 | 190 | 210 | 210 | 205 | 200 | 205 |
(c) melt obtained by step (b) is subjected to cooling and shaping by oblique three roller, obtains section bar, three roll temperatures are upper roller 90
DEG C, 50 DEG C of central roll, 50 DEG C of lower roll.
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.
Testing result:
(1) its surface gloss is tested under 60 ° of angle conditions using vancometer by the sheet material prepared by this programme
For 30~40;
(2) sheet material is after plastics sucking moulding inner bag, and surface gloss is up to 5~20;
(3) sheet material is cut into 100mm*20mm strip and is placed in polynary foaming agent and soak 24h, as a result batten occurs molten
Solve phenomenon;
(4) using the refrigerator made by the case courage of the plate forming, in its inner bag oil surface, by 10 cycle height
(- 40 DEG C~60 DEG C) experiments of temperature circulation, inner bag surface produces corrosion line and cracking phenomena.
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.
Claims (11)
1. a kind of inner container of icebox sheet material, it is characterised in that include the component of following parts by weight:100 parts of polyester materials, 0.1~5
Part titanium dioxide, 0.05~2 part of lubricant, 0.05~2 part of antioxidant.
2. inner container of icebox sheet material according to claim 1, it is characterised in that the polyester material is poly terephthalic acid
It is glycol ester, polybutylene terephthalate (PBT), polyethylene terephthalate -1,4 cyclohexane dimethanol ester, poly- to benzene
One or more in dioctyl phthalate -1,4 cyclohexane dimethanol ester.
3. inner container of icebox sheet material according to claim 1, it is characterised in that the titanium dioxide is rutile titanium dioxide
Powder.
4. inner container of icebox sheet material according to claim 1, it is characterised in that the lubricant is selected from stearic acid or its salt
One or more in the double stearic amides (EBS) of class, Tissuemat E or vinyl.
5. inner container of icebox sheet material according to claim 1, it is characterised in that described antioxidant is hindered phenol compound
Or one or two kinds of mixtures of bi-ester of phosphite kind;It is preferred that irgasfos 168.
6. a kind of preparation method of any inner container of icebox sheet materials of claim 1-5, it is characterised in that including (a) raw material
Mixing;(b) melting extrusion;(c) cooling and shaping;(d) four steps is cut.
7. preparation method according to claim 6, it is characterised in that in the step (a), the raw material is disposably complete
Portion is mixed to uniform rear stand-by.
8. preparation method according to claim 6, it is characterised in that in the step (b), the work of the melting extrusion
Skill condition is:180~260 DEG C of temperature, 0.05~-0.1MPa of vacuum;It is preferred to use single screw extrusion machine, its screw slenderness ratio
For 20~38:1.
9. preparation method according to claim 6, it is characterised in that in the step (c), the cooling of the cooling and shaping
Temperature is 30~70 DEG C, it is preferred to use oblique three roller carries out cooling and shaping.
10. preparation method according to claim 6, it is characterised in that in the step (d), the cutting for sawing or
Knife is cut.
11. preparation method according to claim 6, it is characterised in that comprise the following steps:
(a) raw material is disposably mixed to uniform rear stand-by;
(b) by mixed material melting extrusion obtained by step (a), melt is obtained;The process conditions of the melting extrusion are:Temperature
180~260 DEG C, 0.05~-0.1MPa of vacuum;
(c) above-mentioned melt is obtained into section bar in 30~70 DEG C of cooling and shapings;
(d) above-mentioned gained section bar is cut according to certain size, that is, obtains the sheet material for inner container of icebox plastics sucking moulding.