CN107118400A - It is a kind of to improve filler and the method for rubber binding ability - Google Patents
It is a kind of to improve filler and the method for rubber binding ability Download PDFInfo
- Publication number
- CN107118400A CN107118400A CN201710234447.9A CN201710234447A CN107118400A CN 107118400 A CN107118400 A CN 107118400A CN 201710234447 A CN201710234447 A CN 201710234447A CN 107118400 A CN107118400 A CN 107118400A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- master batch
- white carbon
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Filler and the method for rubber binding ability are improved the present invention relates to a kind of, solution polymerized butadiene styrene rubber kneads into carbon black rubber master batch with carbon black；Butadiene rubber or butadiene rubber and solution polymerized butadiene styrene rubber simultaneously knead into white carbon rubber master batch with white carbon, coupling agent, when there is processing oil, are added when preparing white carbon rubber master batch；The carbon black rubber master batch, white carbon rubber master batch, age resistor, activating agent, accelerator, vulcanizing agent are prepared into finished composition by composition ratio mixing.The present invention, which is applied in tire tread, can reduce tire drag, reduction heat, improve wearability, improve Life of Tyre.
Description
The application is entitled " a kind of low-heat-generation high abrasion-resistance rubber composition and its manufacture method ", Application No.
" 201410033355.0 ", the applying date are the divisional application of the Chinese patent application in " on January 23rd, 2014 ".
Technical field
The present invention relates to rubber materials, more particularly to tire manufacturing art.
Background technology
Automobile use will consume mass energy simultaneously and discharge substantial amounts of carbon dioxide, and the dynamic lag of reduction sizing material loses
People are enjoyed to pay close attention to always so as to reduce rolling resistance, reduce fuel consumption, reduction carbon emission.The method relevant with reduction rolling resistance
Laws ＆ Regulations are also accordingly put into effect, such as the labeling acts in Europe, the SmartWay certifications in the U.S., require reduction tire drag, its
It is middle reduction tread rubber dynamic lag loss and heat be reduce tire drag be most directly also maximally effective means it
One.The effective means that the loss of reduction sizing material dynamic lag causes tire drag and heat to decline at present is largely to use hard charcoal
It is black come alternative carbon black, but by the scattered of white carbon and and bad the brought negative effect of combination of polymer be exactly wear-resisting
The reduction of property, thus there are many researchers to do a lot of work in this respect.
Dispersant is made by a kind of modified silicon oil such as patent (application number 97191118.5) proposition and improves white carbon dispersiveness,
Improve heat and anti-wear performance, reduction Mooney viscosity.But it on the one hand may cause part silicone oil first in this way and carbon black knot
Close, reduce the possibility that rubber is combined with carbon black, it is impossible to give full play to the anti-wear performance of carbon black, on the other hand in the patent both
Add modified silicon oil and used coupling agent again, cost can be caused to increase, and modified silicon oil is not readily available, traditional rubber
Processing enterprise's especially tire plant is not easy tissue production.For another example patent (application number 201010119205.3) proposes mixed by tradition
Refine equipment using two step compounding process improvement white carbon to disperse, add carbon black when wherein second step is kneaded also is mixed into rubber simultaneously
General auxiliary agent such as age resistor, activating agent etc., some lower-molecular substances can be adsorbed onto carbon blacksurface, reduce carbon black and rubber it
Between effect, can cause carbon black to wearability contribute reduce.
The present invention utilizes the general raw material of current rubber, on the basis of general mixing facilities, using new formula and new technology
Not only improved white carbon to be combined with rubber and scattered and improve carbon black and is combined with rubber, so that reaching reduces rolling resistance and raising is resistance to
The purpose of mill property.
The content of the invention
For problem of the prior art, it is an object of the invention to provide a kind of rubber composition and preparation technology, using this
Said composition prepared by technique can be used for Tire production particularly low rolling resistance tyre and manufacture, and reduce heat, and reduction is rolled
Resistance improves wearability simultaneously.
The present invention is implemented based on following possible principle：
It is well known that can substantially reduce sizing material dynamic lag by application white carbon and silane coupler loses i.e. tan δ
Value, generally use 50-80 DEG C of sizing material, and the tan δ values under the conditions of 1-100Hz characterize tire drag, tire rolling when tan δ are low
Resistance is small, but widely applies white carbon to decline tire wear performance, Life of Tyre is influenceed, especially in truck tyre
In, thus it is general in truck tyre sizing material to use carbon black simultaneously using white carbon, to ensure wear hardness.Carbon black and rubber
With reference to better reinforcing property it is better, the present invention in addition to making larger improvement on formula, calendering process also makees larger improvement.Pass
Carbon black, age resistor, activating agent are all added together in system calendering process, and carbon blacksurface can adsorb these lower-molecular substances, reduce charcoal
Black and rubber combination, reduces reinforcing effect, thus reduces wearability.And the formula and preparation technology of the present invention are used, rubber
Glue can knead with carbon black, white carbon/coupling agent respectively in advance and form rubber master batch, add the low-molecular materials such as age resistor, activating agent
During matter, wearability can be improved, and heat can decline.White carbon and carbon black rubber master batch mixing when, it is microcosmic on make the spacing of carbon black particle
Increased from a distance between hard charcoal black track producing particle, reduce aggregation, make the reduction of tan δ values, so as to reduce tire drag and wheel viviparity
Heat.
The invention further relates to mode is implemented as follows：
A kind of low-heat-generation high abrasion-resistance rubber composition, by
(A) 100 parts by weight of rubber；
(B) 5-120 parts by weight of carbon black per；It is preferred that 10-100 parts by weight of carbon black per；More preferably 15-80 parts by weight of carbon black per；
(C) 0-100 parts by weight white carbon；It is preferred that 10-90 parts by weight white carbons；More preferably 15-80 parts by weight white carbon；
(D) 0-20 parts by weight coupling agent；
0-20 parts by weight processing oil；Parts by weight of activated dose of 0.5-8；0.5-8 parts by weight age resistor；Common 0.5-8 parts by weight
Accelerator and vulcanizing agent composition；
The rubber composition manufacture method, comprises the following steps：
The first step, kneads carbon black rubber master batch and white carbon rubber master batch respectively：
Rubber kneads into carbon black rubber master batch with carbon black；
Rubber kneads into white carbon rubber master batch with white carbon, coupling agent and (when there is processing oil, added when preparing white carbon rubber master batch
Enter)；
Second step, composition is pressed by the carbon black rubber master batch, white carbon rubber master batch, age resistor, activating agent, accelerator, vulcanizing agent
Ratio mixing is prepared into finished composition.
According to above-mentioned rubber composition, wherein rubber (A) is smoke sheet rubber, standard rubber, the synthesis rubber containing diene units
The one or more of glue.
According to above-mentioned rubber composition, wherein carbon black (B) specific surface area is 50-160m2/ g, preferably 70-140m2/ g, more
It is preferred that 80-130m2/g；Oil factor is 45-162ml/100g, preferably 85-142ml/100g, more preferably 95-132ml/100g.
According to above-mentioned rubber composition, the wherein specific surface area of white carbon (C) is 50-300m2/ g, preferably 100-
250m2/ g, more preferably 150-200m2/g。
According to above-mentioned rubber composition, wherein the coupling agent being mixed together with white carbon is white carbon consumption
0.5wt%-20wt%, preferably 1wt% -15wt%.
According to above-mentioned rubber composition, wherein coupling agent (D) is organo silane coupling agent, titanate coupling agent, zirconic acid
Fat coupling agent, nitro coupling agent, alcohol compound or combinations thereof, preferably organo silane coupling agent.
According to above-mentioned rubber composition, wherein the processing oil is petroleum processing oil, preferred aromatic hydrocarbons oil or naphthenic oil.
According to above-mentioned rubber composition, wherein accelerator includes but is not limited to sulfenamide type accelerators, thiazoles rush
Enter agent, thuriam acceserator, guanidines or combinations thereof, vulcanizing agent include but is not limited to Sulfur, insoluble sulfuy,
Oil-filled Sulfur, sulphur-donor or combinations thereof.
Root rubber composition mentioned above, wherein the preparation process first step, white carbon milling maternal rubber technique：Mixing time
2-10 minutes, melting temperature was kept for 0.5-5 minutes when reaching 110-180 DEG C (preferably 130-160 DEG C), preferably 1-3 minutes, works as group
Have in compound and added during processing oil in white carbon milling maternal rubber；Carbon black rubber master batch calendering process：Mixing time 0.5-10 minutes, it is excellent
Select 2-5 minutes.
According to above-mentioned rubber composition, it is one section of mixing or multistage mixing that wherein second step, which prepares finished composition method,.
The invention further relates to a kind of rubber, it uses and prepared according to above-mentioned rubber composition.
The rubber that the present invention is used can be any rubber in this area, including but not limited to 1# smoke sheet rubbers, 2# smoked sheets
One or more in glue, 3# smoke sheet rubbers, 5# standard rubbers, 10# standard rubbers, 20# standard rubbers, rubber containing diene units.Rubber
Consumption be 100 parts by weight.
The carbon black specific surface that the present invention is used is 50-160m2/ g, preferably 70-140m2/ g, more preferably 80-130m2/g；
Oil factor is 45-162ml/100g, preferably 85-142ml/100g, more preferably 95-132ml/100g.The carbon black kind typically used
Class includes but is not limited to N134, N115, N110, N121, N234, N220, N375, N330, N339, and the consumption of carbon black is 5-120
Parts by weight, preferably 10-100 parts by weight, more preferably 15-80 parts by weight.
The white carbon specific surface area value that the present invention is used is 50-300m2/ g, preferably 100-250m2/ g, more preferably 150-
200m2/g.The consumption of white carbon is 0-100 parts by weight；It is preferred that 10-90 parts by weight；More preferably 15-80 parts by weight；
The coupling agent that the present invention is used is organo silane coupling agent, titanate coupling agent, zirconic acid fat coupling agent, nitro coupling
Agent, alcohol compound or combinations thereof, preferably organo silane coupling agent.Organo silane coupling agent below general formula table
Show：
(Rn-(RO)3-nSi-(Alk)m-(Ar)p)q(A) (I)
Rn’(RO)3-nSi-(Alk) (II)
Or Rn’(RO)3-nSi-(Alkenyl) (III)
In formula, as q=1, A is-SCN ,-SH ,-Cl ,-NH2；
As q=2, A is-Sx-；
R and R ' is branched or straight chain alkyl or phenolic group of the carbon atom from 1 to 4, and R and R ' can be with identical, can also be different；
N is 0,1 or 2；
Alk is the straight or branched alkyl containing 1 to 6 carbon atom；
AlkenyL is the straight or branched alkenyl containing 1 to 6 carbon atom；
M is 0 or 1；
Ar is the aryl containing 6 to 12 carbon atoms；
P is 0 or 1, p and n can not be 0 simultaneously；
X is 2 to 8；
Most common of which is double (triethoxy propyl silane) tetrasulfides and disulphide.Consumption is 0-20 weight
Part.With the 0.5wt%-20wt%, preferably 1wt%-15wt% that the coupling agent that white carbon is mixed together is white carbon consumption.
The activating agent that the present invention is used is zinc oxide, stearic acid；The processing oil used is petroleum processing oil preferred aromatic hydrocarbons
Oil or naphthenic oil, age resistor are p phenylenediamine type antioxidant, quinoline type antioxidant and physical protection agent microwax, general age resistor
Including but not limited to age resistor 6PPD, anti-aging agent RD, crystallite protection wax；Accelerator is sulfenamide type accelerators, thiazoles rush
Enter agent, thuriam acceserator, guanidines or combinations thereof, including but not limited to accelerator NS, accelerant CZ, promotion
Agent DPG；Vulcanizing agent be Sulfur, sulphur-donor or combinations thereof, including but not limited to common Cosan, insoluble sulfuy,
Oil-filled Sulfur.
Embodiment
The present invention is further described with embodiment below, but the scope of the present invention is not restricted by the embodiments.
(1) embodiment and comparative example are determined using following instrument and equipment and assay method：
Instrument and equipment prepared by the rubber sample of table 1
| Sequence number | Device name | Specifications and models | Manufacturer |
| 1 | Banbury | XSM-1/10-120 | Shanghai Kechuang rubber and plastics machine equipment Co., Ltd |
| 2 | Mill | 152.5*320 | Zhanjiang Machine Factory, Guangdong Prov. |
| 3 | Vulcanizing press | XLB-D600*600 | Zhejiang Huzhou east Machinery Co., Ltd. |
The method of testing and instrument of the vulcanizating glue physical performance of table 2
(2) embodiment and comparative example raw material：
Natural gum：STR20, Thailand's production standard rubber；
Cis-butadiene cement：BR9000, Yanshan Petrochemical；
Oil-filled Butadiene-Styrene Rubber：5025-2, Lanxess Corporation；
Non- oil-filled Butadiene-Styrene Rubber：VSL 4526-OHM, Lanxess Corporation；
Organo silane coupling agent：50%TESPT (double (triethoxy propyl silane) tetrasulfides) active ingredient, Nanjing daybreak
Photochemical factory；
N234 carbon blacks：Cabot (China) Co., Ltd；
White carbon：Newsil 1165MP are really into chemistry of silicones Co., Ltd；
Aromatic naphtha：TDAE, the German Chinese is contained；
Zinc oxide：Dalian zinc oxide factory, zinc oxide content >=99.7%；
Stearic acid：Boxing Huarun Grease Chemical Co., Ltd；
Anti-aging agent RD (2,2,4- trimethyl -1,2- dihyaroquinolines polymer)：Tianjin Ke Mai auxiliary agents Co., Ltd；
Antioxidant 4020 (N-(1,3- dimethylbutyl)-N ＇-diphenyl-para-phenylene diamine)：The holy scientific and technological limited public affairs of chemistry difficult to understand in Jiangsu
Department；
Protection wax：Hundred U.S. auspicious speciality chemical (Suzhou) Co., Ltds；
Accelerator NS (N tert butyl benzothiazole 2 sulfenamide)：Shandong Sunsine Chemical Co., Ltd.；
Accelerant CZ (N cyclohexyl 2 benzothiazole sulfenamide)：Shandong Sunsine Chemical Co., Ltd.；
Diphenylguanidine PG (diphenylguanidine)：Shandong Sunsine Chemical Co., Ltd.；
Sulfur：Qingdao gold and jade rib Industrial Co., Ltd.；
Number is parts by weight described in following examples and comparative example.
Comparative example 1
Basic recipe：STR20 100；N234 carbon blacks 40；White carbon Newsil 1165MP 10；Organo silane coupling agent
(50%TESPT) 2；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Accelerant CZ
1.3；Sulfur 1.2.
Preparation technology：Using traditional calendering process, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, one section of glue calendering process：100 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 40 parts of N234 charcoals
Black, 10 parts of white carbons, 2 parts of organo silane coupling agents (50%TESPT), 3.5 parts of zinc oxide, 2 parts of stearic acid, 1.5 parts of age resistor
RD, 2 parts of antioxidant 4020s, 1 part of protection wax input banbury pressurize 60 seconds, carry floating weight, clean, pressurize 120 seconds, then put on top
Bolt repressurization 60 seconds, it is standby that dumping prepares one section of rubber master batch.
2nd, finished composition calendering process：60rpm, 162 parts of one section of rubber master batch, 1.3 parts of accelerant CZs, 1.2 parts of Sulfur inputs are close
Mill, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
Embodiment 1
Basic recipe：STR20 100；N234 carbon blacks 40；White carbon Newsil 1165MP 10；Organo silane coupling agent
(50%TESPT) 2；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Accelerant CZ
1.3；Sulfur 1.2.
Preparation technology：Using banburying process of the present invention, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, carbon black rubber master batch calendering process：80 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 40 parts of N234 charcoals
Black input banbury pressurizes 60 seconds, carries floating weight, cleans, repressurization 60 seconds carries floating weight, and 60 seconds dumpings of repressurization prepare charcoal
Black rubber master batch is standby；
2nd, white carbon milling maternal rubber technique：20 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 10 parts of hard charcoals
Black Newsil 1165MP, 2 parts of organo silane coupling agent (50%TESPT) input banburies are pressurized to temperature and put on top for 150 DEG C
Bolt is kept for 90 seconds, and 60 seconds dumpings of repressurization prepare white carbon rubber master batch standby；
3rd, one section of milling maternal rubber technique：140 parts of carbon black rubber master batch, 32 parts of white carbon rubber master batch are put into banbury by 90rpm, plus
3.5 parts of zinc oxide, 2 parts of stearic acid, 1.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax are put into banburying by pressure 30 seconds
Machine, pressurizes 60 seconds, carries floating weight, and repressurization 60 seconds, dumping two sections of rubber master batch of preparation are standby；
4th, finished composition calendering process：60rpm, 162 parts of two sections of rubber master batch, 1.3 parts of accelerant CZs, 1.2 parts of Sulfur inputs are close
Mill, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature.
Comparative example 2
Basic recipe：STR20 100；N234 carbon blacks 15；White carbon Newsil 1165MP 35；Organo silane coupling agent
(50%TESPT) 8.4；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Accelerant CZ
2.0；Sulfur 1.6.
Preparation technology：Using traditional calendering process, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, one section of glue calendering process：100 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 15 parts of N234 charcoals
Black, 35 parts of white carbons, 8.4 parts of organo silane coupling agents (50%TESPT), 3.5 parts of zinc oxide, 2 parts of stearic acid, 1.5 parts it is anti-old
Agent RD, 2 parts of antioxidant 4020s, 1 part of protection wax input banbury pressurize 60 seconds, carry floating weight, clean, repressurization 120 seconds, then carry
Floating weight repressurization 60 seconds, it is standby that dumping prepares one section of rubber master batch.
2nd, finished composition calendering process：60rpm, 168.4 parts of one section of rubber master batch, 1.3 parts of accelerant CZs, 1.2 parts of Sulfurs are put into
Banbury, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
Embodiment 2
Basic recipe：STR20 100；N234 carbon blacks 15；White carbon Newsil 1165MP 35；Organo silane coupling agent
(50%TESPT) 8.4；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Accelerant CZ
2.0；Sulfur 1.6.
Preparation technology：Using banburying process of the present invention, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, carbon black rubber master batch calendering process：30 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 15 parts of N234 charcoals
Black input banbury pressurizes 60 seconds, carries floating weight, cleans, pressurizes 60 seconds, carry floating weight, 60 seconds dumpings of repressurization prepare carbon black
Rubber master batch is standby.
2nd, white carbon milling maternal rubber technique：70 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 35 parts of hard charcoals
Black Newsil 1165MP, 8.4 parts of organo silane coupling agent (50%TESPT) input banburies are pressurized to temperature and put on for 150 DEG C
Push up bolt to be kept for 90 seconds, 60 seconds dumpings of repressurization prepare white carbon rubber master batch standby.
3rd, one section of milling maternal rubber technique：45 parts of carbon black rubber master batch, 113.4 parts of white carbon rubber master batch are put into banbury by 90rpm,
Pressurization 30 seconds, 3.5 parts of zinc oxide, 2 parts of stearic acid, 1.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax input are close
Mill, pressurizes 60 seconds, carries floating weight, and repressurization 60 seconds, dumping two sections of rubber master batch of preparation are standby；
4th, finished composition calendering process：60rpm, 168.4 parts of two sections of rubber master batch, 2.0 parts of accelerant CZs, 1.6 parts of Sulfurs are put into
Banbury, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature.
Comparative example 3
Basic recipe：STR20 80；BR9000 20；N234 carbon blacks 10；White carbon Newsil 1165MP 40；Organosilicon
Alkane coupling agent (50%TESPT) 9.6；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Promote
Enter agent CZ 2.0；Sulfur 1.6.
Preparation technology：Using traditional calendering process, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, one section of glue calendering process：80 parts of STR20,20 parts of BR9000 are put into banbury, pressurizeed 30 seconds, by 10 by 90rpm
Part N234 carbon black, 40 parts of white carbons, 9.6 parts of organo silane coupling agents (50%TESPT), 3.5 parts of zinc oxide, 2 parts of stearic acid,
1.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection waxes input banbury pressurize 60 seconds, carry floating weight, repressurization 120 seconds,
Floating weight repressurization is put forward again 60 seconds, dumping prepares one section of rubber master batch standby
2nd, finished composition calendering process：60rpm, 164.1 parts of one section of rubber master batch, 2.0 parts of accelerant CZs, 1.6 parts of Sulfurs are put into
Banbury, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
Embodiment 3
Basic recipe：STR20 80；BR9000 20；N234 carbon blacks 10；White carbon Newsil 1165MP 40；Organosilicon
Alkane coupling agent (50%TESPT) 9.6；Zinc oxide 3.5；Stearic acid 2；Protection wax 1；Anti-aging agent RD 1.5；Antioxidant 4020 2；Promote
Enter agent CZ 2.0；Sulfur 1.6.
Preparation technology：Using banburying process of the present invention, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, cis-butadiene cement/white carbon milling maternal rubber technique：20 parts of BR9000 are put into banbury by 90rpm, are pressurizeed 30 seconds, will
10 parts of white carbon Newsil 1165MP, 2.4 parts of organo silane coupling agent (50%TESPT) input banburies are pressurized to temperature and are
150 DEG C carry floating weight and are kept for 90 seconds, and 60 seconds dumpings of repressurization prepare cis-butadiene cement/white carbon rubber master batch standby；
2nd, natural gum/white carbon milling maternal rubber technique：60 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 30
Part white carbon Newsil 1165MPa, 7.2 parts of organo silane coupling agents (50%TESPT) input banburies are pressurized to temperature and are
150 DEG C carry floating weight and are kept for 90 seconds, and 60 seconds dumpings of repressurization prepare natural gum/white carbon rubber master batch standby；
3rd, natural gum/carbon black rubber master batch calendering process：20 parts of STR20 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 10 parts
N234 carbon blacks input banbury pressurizes 60 seconds, carries floating weight, cleans, pressurizes 60 seconds, puies forward floating weight, 60 seconds dumpings of repressurization, system
Standby natural gum/carbon black rubber master batch is standby；
4th, prepared by one section of rubber master batch：Banbury rotating speed 90rpm, by 32.4 parts of cis-butadiene cements/white carbon rubber master batch, 97.2 parts it is natural
Glue/white carbon rubber master batch, 30 parts of natural gum/carbon black rubber master batch input banburies pressurize 30 seconds, by 3.5 parts of zinc oxide, 2 parts of stearic acid, 1
Part protection wax, 1.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s input banburies, pressurize 60 seconds, carry floating weight, repressurization 60 seconds,
It is standby that dumping prepares one section of rubber master batch；
5th, finished composition calendering process：60rpm, 169.6 parts of one section of rubber master batch, 2.0 parts of accelerant CZs, 1.6 parts of Sulfurs are put into
Banbury, pressurizes 60 seconds, carries floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
The comparative example 1-3 of table 3 and embodiment 1-3 service check results
* embodiment is the relative indices using corresponding comparative example as 100 respectively, and higher expression is worn away.
From table 3 it is observed that embodiment 1 and comparative example 1 be formulated it is identical but using the calendering process of the present invention, heat and
Abrasion are all better than comparative example 1；Embodiment 2 is compared, heat substantially drops using new formula and the calendering process of the present invention with comparative example 2
Low, the tan δ values for characterizing rolling resistance are significantly lower than comparative example 2；Comparative example 3 and embodiment 3, formula are identical, and rubber is natural gum
It is used in combination with cis-butadiene cement, embodiment 3 is using the calendering process of the present invention, and heat and wear hardness are all better than comparative example 3；Data above
Illustrate the formula and calendering process using the present invention, tire heat, reduction rolling resistance can be reduced while improving wearability.
Comparative example 4
Basic recipe：SBR5025-2 96.25；BR9000 30；N234 carbon blacks 50；White carbon Newsil 1165MP25；
Organo silane coupling agent (50%TESPT) 4；Zinc oxide 3；Stearic acid 2；Protection wax 1；Anti-aging agent RD 2.5；Antioxidant 4020 2；
Accelerant CZ 1.1；Diphenylguanidine PG 0.5；Sulfur 1.8.
Preparation technology：Using traditional calendering process, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, one section of glue calendering process：96.25 parts of SBR5025-2 and 30 part of BR9000 are put into banbury, pressurization by 90rpm
30 seconds, by 50 parts of N234 carbon blacks, 25 parts of white carbons, 4 parts of organo silane coupling agents (50%TESPT), 3 parts of zinc oxide, 2 parts of tristearin
Acid, 2.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax input banbury pressurize 60 seconds, carry floating weight, clean, then add
Pressure 120 seconds, then put forward floating weight repressurization 60 seconds, it is standby that dumping prepares one section of rubber master batch.
2nd, finished composition calendering process：60rpm, by 215.75 parts of one section of rubber master batch, 1.1 parts of accelerant CZs, 0.5 part of accelerator
DPG, 1.8 parts of Sulfur input banburies, pressurize 60 seconds, carry floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
Embodiment 4
Basic recipe：SBR5025-2 96.25；BR9000 30；N234 carbon blacks 50；White carbon Newsil 1165MP25；
Organo silane coupling agent (50%TESPT) 4；Zinc oxide 3；Stearic acid 2；Protection wax 1；Anti-aging agent RD 2.5；Antioxidant 4020 2；
Accelerant CZ 1.1；Diphenylguanidine PG 0.5；Sulfur 1.8.
Preparation technology：Using banburying process of the present invention, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, carbon black rubber master batch calendering process：82.5 parts of SBR5025-2 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 34 parts
N234 carbon blacks input banbury is pressurizeed 60 seconds, and 16 parts of carbon blacks are put into banbury pressurizes 60 seconds, carries floating weight, and repressurization is arranged for 60 seconds
Glue, prepares carbon black rubber master batch standby.
2nd, white carbon milling maternal rubber technique：30 parts of BR9000 and 13.75 part of SBR5025-2 are put into banbury by 90rpm,
Pressurization 30 seconds, by 25 parts of white carbon Newsil 1165MP, 4 parts of organo silane coupling agent (50%TESPT) input banbury pressurizations
It is 150 DEG C to temperature and proposes floating weight holding 90 seconds, 60 seconds dumpings of repressurization prepares white carbon rubber master batch standby.
3rd, one section of milling maternal rubber technique：132.5 parts of carbon black rubber master batch, 72.75 parts of white carbon rubber master batch are put into banburying by 90rpm
Machine, pressurizes 30 seconds, and 3 parts of zinc oxide, 2 parts of stearic acid, 2.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax input are close
Mill, pressurizes 60 seconds, carries floating weight, and repressurization 60 seconds, dumping two sections of rubber master batch of preparation are standby；
4th, finished composition calendering process：60rpm, by 215.75 parts of two sections of rubber master batch, 1.1 parts of accelerant CZs, 0.5 part of accelerator
DPG, 1.8 parts of Sulfur input banburies, pressurize 60 seconds, carry floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature.
Comparative example 5
Basic recipe：VSL 4526-OHM 70；BR9000 30；N234 carbon blacks 50；White carbon Newsil 1165MP25；
Organo silane coupling agent (50%TESPT) 4；Aromatic naphtha 17；Zinc oxide 3；Stearic acid 2；Protection wax 1；Anti-aging agent RD 2.5；It is anti-old
Agent 4,020 2；Accelerant CZ 1.1；Diphenylguanidine PG 0.5；Sulfur 1.8.
Preparation technology：Using traditional calendering process, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, one section of glue calendering process：70 parts of VSL 4526-OHM and 30 parts of BR9000 are put into banbury, pressurization by 90rpm
30 seconds, by 50 parts of N234 carbon blacks, 25 parts of white carbons, 4 parts of organo silane coupling agents (50%TESPT), 17 parts of aromatic naphtha, 3 parts of oxygen
Change zinc, 2 parts of stearic acid, 2.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax input banbury to pressurize 60 seconds, put on top
Bolt, is cleaned, repressurization 120 seconds, then puies forward floating weight repressurization 60 seconds, and it is standby that dumping prepares one section of rubber master batch.
2nd, finished composition calendering process：60rpm, by 206.5 parts of one section of rubber master batch, 1.1 parts of accelerant CZs, 0.5 part of accelerator
DPG, 1.8 parts of Sulfur input banburies, pressurize 60 seconds, carry floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature
Embodiment 5
Basic recipe：VSL4526-OHM 70；BR9000 30；N234 carbon blacks 50；White carbon Newsil 1165MP25；Have
Machine silane coupling agent (50%TESPT) 4；Aromatic naphtha 17；Zinc oxide 3；Stearic acid 2；Protection wax 1；Anti-aging agent RD 2.5；Age resistor
4020 2；Accelerant CZ 1.1；Diphenylguanidine PG 0.5；Sulfur 1.8.
Preparation technology：Using banburying process of the present invention, banbury is XSM-1/10-120, and capacity is 1 liter, ram piston pressure
2MPa。
1st, carbon black rubber master batch calendering process：70 parts of VSL 4526-OHM are put into banbury by 90rpm, are pressurizeed 30 seconds, by 30 parts
N234 carbon blacks input banbury is pressurizeed 60 seconds, and 20 parts of carbon blacks are put into banbury pressurizes 60 seconds, carries floating weight, and repressurization is arranged for 60 seconds
Glue, prepares carbon black rubber master batch standby.
2nd, white carbon milling maternal rubber technique：30 parts of BR9000 are put into banbury by 90rpm, are pressurizeed 30 seconds, by 25 parts of hard charcoals
Black Newsil 1165MP, 4 parts of organo silane coupling agents (50%TESPT), 17 parts of aromatic naphtha input banburies are pressurized to temperature and are
150 DEG C carry floating weight and are kept for 90 seconds, and 60 seconds dumpings of repressurization prepare white carbon rubber master batch standby.
3rd, one section of milling maternal rubber technique：120 parts of carbon black rubber master batch, 76 parts of white carbon rubber master batch are put into banbury by 90rpm, plus
3 parts of zinc oxide, 2 parts of stearic acid, 2.5 parts of anti-aging agent RDs, 2 parts of antioxidant 4020s, 1 part of protection wax are put into banbury by pressure 30 seconds,
Pressurization 60 seconds, carries floating weight, and repressurization 60 seconds, dumping two sections of rubber master batch of preparation are standby；
4th, finished composition calendering process：60rpm, by 206.5 parts of two sections of rubber master batch, 1.1 parts of accelerant CZs, 0.5 part of accelerator
DPG, 1.8 parts of Sulfur input banburies, pressurize 60 seconds, carry floating weight, repressurization 120 seconds, dumping, 105-110 DEG C of temperature.
The comparative example 4-5 of table 4 and embodiment 4-5 service check results
* embodiment is the relative indices using corresponding comparative example as 100 respectively, and higher expression is worn away.
As can be seen from Table 4, in SBR and BR and with the calendering process in formula using the present invention, heat and abrasivity
Comparative example can be superior to, resilience increase, heat reduction, anti-wear performance are improved.Data above illustrate using the present invention formula and
Calendering process, can reduce tire heat, reduction rolling resistance while improving wearability.
Claims (12)
1. a kind of improve filler and the method for rubber binding ability, it is characterised in that：Solution polymerized butadiene styrene rubber kneads into charcoal with carbon black
Black rubber master batch；Butadiene rubber or butadiene rubber and solution polymerized butadiene styrene rubber simultaneously knead into white carbon rubber master batch with white carbon, coupling agent, when
When having processing oil, added when preparing white carbon rubber master batch；By the carbon black rubber master batch, white carbon rubber master batch, age resistor, activating agent, rush
Enter agent, vulcanizing agent and be prepared into finished composition by composition ratio mixing.
2. a kind of as claimed in claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Rubber is with 100 weights
Measure part meter：Carbon black is -120 parts by weight, preferably 10-100 parts by weight, more preferably 15-80 parts by weight；White carbon 0-100 parts by weight,
It is preferred that 10-90 parts by weight, more preferably 15-80 parts by weight；Coupling agent 0-20 parts by weight；Processing oil 0-20 parts by weight；Activating agent
0.5-8 parts by weight；Age resistor 0.5-8 parts by weight；Accelerator and the common 0.5-8 parts by weight of vulcanizing agent.
3. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein carbon black ratio
Surface area is 50-160m2/ g, preferably 70-140m2/ g, more preferably 80-130m2/g；Oil factor is 45-162ml/100g, preferably
85-142ml/100g, more preferably 95-132ml/100g.
4. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein white carbon
Specific surface area is 50-300m2/ g, preferably 100-250m2/ g, more preferably 150-200m2/g。
5. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein with hard charcoal
The black coupling agent being mixed together is the 0.5wt%-20wt%, preferably 1wt% -15wt% of white carbon consumption.
6. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein coupling agent
For organo silane coupling agent, titanate coupling agent, zirconic acid fat coupling agent, nitro coupling agent, alcohol compound or combinations thereof,
It is preferred that organo silane coupling agent.
7. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：It is wherein described to add
Work oil is petroleum processing oil, preferred aromatic hydrocarbons oil or naphthenic oil.
8. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein accelerator
Including but not limited to sulfenamide type accelerators, thiazole accelerator, thuriam acceserator, guanidines or their group
Close, vulcanizing agent includes but is not limited to Sulfur, insoluble sulfuy, oil-filled Sulfur, sulphur-donor or combinations thereof.
9. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：White carbon rubber master batch
Mixing time 2-10 minutes, melting temperature is kept for 0.5-5 minutes when reaching 110-180 DEG C (preferably 130-160 DEG C), preferably 1-3
Minute, added when there is processing oil in composition in white carbon milling maternal rubber；Carbon black rubber master batch mixing time 0.5-10 minutes, it is excellent
Select 2-5 minutes.
10. a kind of according to claim 1 improve filler and the method for rubber binding ability, it is characterised in that：Wherein refining eventually
Gluing method is one section of mixing or multistage mixing.
11. a kind of rubber composition, it uses and prepared according to claim 1-10 methods describeds.
12. a kind of rubber, it is prepared using rubber composition according to claim 11.