CN107116735A - A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally - Google Patents

A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally Download PDF

Info

Publication number
CN107116735A
CN107116735A CN201710338222.8A CN201710338222A CN107116735A CN 107116735 A CN107116735 A CN 107116735A CN 201710338222 A CN201710338222 A CN 201710338222A CN 107116735 A CN107116735 A CN 107116735A
Authority
CN
China
Prior art keywords
color lump
model
plane materiel
aluminium hydrate
colorant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710338222.8A
Other languages
Chinese (zh)
Inventor
马海滨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhengzhou Austrian Technology Co Ltd
Original Assignee
Zhengzhou Austrian Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhengzhou Austrian Technology Co Ltd filed Critical Zhengzhou Austrian Technology Co Ltd
Priority to CN201710338222.8A priority Critical patent/CN107116735A/en
Publication of CN107116735A publication Critical patent/CN107116735A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally, comprise the following steps that：Make embedded color lump pattern model：Embedded color lump pattern makes shaping by computer three-dimensional Software for Design, then by numerically controlled automatic bender；Making artificial jade entity plane materiel embeds color lump pattern specific implementation step：Embedded color lump pattern model is placed in safety glass template, is pressed on model；Casting premix colorant inside the unitary space being spaced apart toward model, model inside and outside by the allotment of required pattern color opened by different interval region；Safety glass template is vacuumized；When premix colorant starts to react and be not fully cured, tranquil placement, curing molding sanding and polishing are carried out according still further to conventional method.The preparation method for the artificial jade's entity plane materiel for embedding color lump naturally that the present invention is provided, because it directly reduces board material splice cost of labor and takes new technology to process, production efficiency is greatly improved.

Description

A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally
Technical field
The invention belongs to building decoration product technical field, and in particular to a kind of artificial jade's solid face for embedding color lump naturally The preparation method of material.
Background technology
Artificial jade's entity plane materiel needs to obtain nature colourful pattern effect, and conventional method is to use seamless spliced mode handle Artificial jade's entity plane materiel of different colours cuts the blocking splicing of block-by-block again integrally on request, and this is that artificial jade's workpiece will Seek an important special process indispensable during the post-production of colourful pattern.Especially in tea table facestock, tabletop The seamless colorful splicing effect that the family workplaces such as material, flat tea tray and work top are shown requires more smooth complete It is beautiful.But traditional manufacturing technology be the prefabricated component handled well on request according still further to splicing pattern requirement cut into polylith, It then will be carved one by one with trimmer smoothly right and wrong each piece of the every a line to be spliced and be related to is stupefied again, it It is bonded one by one with special splicing resin glue again afterwards, sanding and polishing is also wanted after the completion of this step.This joining method is to simple lines And operation of also embarking on journey reluctantly is processed in a small number of block workpiece splicings of geometry, but almost can not be complete for slightly more complex art designing's pattern Into, and it is time-consuming, the warping resistance performance of spliced sheet material is also influenceed to a certain extent.
The content of the invention
The purpose of the present invention is that provides a kind of artificial jade for embedding color lump naturally to solve the deficiencies in the prior art The preparation method of stone entity plane materiel, the preparation method manufacture craft is simple, practical operation is convenient, low manufacture cost, colourful pattern enrich And each unit adhesive surface cohesive force is strong, warping resistance is functional, effect is attractive in appearance, with good wide market prospects.
The purpose of the present invention is realized in the following manner：
A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally, is comprised the following steps that：
（1）Make embedded color lump pattern model：Color lump pattern is embedded by computer three-dimensional Software for Design, then by numerically controlled automatic bending Mechanism is molded, and keeps a cross section of model regular concordant；Embedded color lump pattern model is prepared from by stainless strip；
（2）Making artificial jade entity plane materiel embeds color lump pattern specific implementation step：
A. above-mentioned embedded color lump pattern model is placed in the safety glass template for wiping across releasing agent, color lump pattern mold is embedded Type it is smooth it is cross-section contact safety glass template downwards, this model is just whole safety glass form spacing into different zones Separate unit space；
B. pressed on model, or shift to an earlier date preset magnetic material Adsorption Model to protect below safety glass template Model of a syndrome cross section and safety glass template contacts are tight, leave no gaps in order to avoid gummosis alters material；
C. casting premix colorant inside the unitary space being spaced apart toward model, inside and outside required pattern is pressed in different interval region to model Mixing color is opened, and is cast simultaneously respectively, and casting thickness will be consistent；
D. cast after premix colorant, safety glass template feeding artificial stone Special vacuum equipment is evacuated to -0.09 ~ - 0.1MP, is kept for 3-5 minutes；
（3）Solidification process：When premix colorant starts to react and be not fully cured, i.e., before the complete gel of premix in 5 minutes Embedded color lump pattern model is taken out, tranquil placement, curing molding sanding and polishing are carried out according still further to conventional method.
The step（1）The thickness of middle stainless strip is 0.2-0.5mm, and width is 35-45mm.
It is special that the premix colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and artificial stone Oil colour, the mass fraction of above-mentioned raw materials is respectively：100 parts of unsaturated polyester resin, 180-220 parts of filling aluminium hydrate, 0.5-1.5 parts of catalyst, 0.8-2 parts of curing agent, special oil colour 0.02-0.8 parts of artificial stone.
The filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A Aluminium hydrate powder is 100 parts, and H-WF-90 aluminium hydrate powders are 80-120 parts.
The premix colorant is according to unsaturated polyester resin, filling aluminium hydrate, catalyst, the special oil colour of artificial stone It is mixed and stirred for uniformly with the sequencing of curing agent, and curing agent must finally be individually added into and be stirred for uniformly.
The catalyst is cobalt naphthenate, and curing agent is methyl ethyl ketone peroxide.
The thickness of the premix colorant is 5-15mm.
The magnetic force that the pressure or magnetic material applied in the step b is produced is on per unit length on model cross section Power is 10-20N/m.
With the high speed development of electronics technology, the appearance of numerical control automatic electronic equipment, artificial jade involved in the present invention Stone is embedded color lump pattern unit gap model and made using aluminium alloy or stainless steel substrates band naturally, can be set by numerical control automatic electronic Standby to be rapidly completed, efficiency high, relative cost is low and can repeatedly use.
Relative to prior art, the preparation method for the artificial jade's entity plane materiel for embedding color lump naturally that the present invention is provided, Because it directly reduces board material splice cost of labor and takes new technology to process, production efficiency is greatly improved；And each unit Natural seamless, each color lump composed pattern complexity of the embedded natural adhesive effect of color lump is various.The present invention overcomes original to a greater extent The easy deformation cracking of product caused by having joining method, the inherent shortcoming of weatherability difference, and in terms of designs are spliced more It is rich and varied.The bonding plane warping resistance made using this method is consistent with whole plate facestock and has a style of one's own.So artificial Jade sheet material decorations field is more extensive using scope, especially develops in terms of artificial jade's furniture entity plane materiel and more wins one Raise.
Brief description of the drawings
Fig. 1 is one of embedded color lump pattern model of the present invention.
Fig. 2 is the artificial jade's entity plane materiel for embedding color lump naturally prepared using one of embedded color lump pattern model.
Fig. 3 is the two of the embedded color lump pattern model of the present invention.
Fig. 4 is the artificial jade's entity plane materiel for embedding color lump naturally prepared using the two of embedded color lump pattern model.
Fig. 5 is the three of the embedded color lump pattern model of the present invention.
Embodiment
Stainless strip in the present invention is 304 cold rolled stain less steels of composite elastic requirement, possesses 304 cold rolling stainless Steel common physical characteristic, it is necessary to meet following parameter characteristic：Elastic hardness is strong in 110-200HV, luminosity 8K to minute surface, tension Degree >=520MP, elongation percentage >=40%, yield strength >=205N/mm2, longitudinal modulus of elasticity（20 DEG C, KNmm2）：193.
The special oil colour of artificial stone is serial purchased from the pure Leather Color Paste LR of Luo Li companies of Britain.
In the solidification process after exhausting vacuum step, it is important to before the complete gel state moment will occur for resin Above-mentioned steel piece band model is taken out in 5 minutes.This time point is extremely important, and the other production technologies of facestock are entered according to conventional steps OK.Facestock gel state is a lasting chemical reaction process, in this gel process above-mentioned several material chemical moleculars it Between occur hinge reaction, outward appearance is mainly shown as the transition process that material is hardened from liquid pasty state to solid-state, so in access panel The presclerotic 5 minutes gel states of material mainly see the viscosity of reaction material to determine the firm time point of sheet material, it is ensured that satisfactorily take out Take the working experience of the operation skilled worker of steel band model extremely important.And curing rate of the sheet material from liquid to solid-state is main Depending on environment temperature（Production environment temperature is typically advisable at 5 DEG C -35 DEG C）Height and catalyst, the adding proportion of curing agent. Generally, hardening of resin probably needs 20-30 minutes, that is to say, that after the completion of vacuum step, is taken out after 15-25 minutes Steel piece band model, the specific time needs as the case may be to determine.
Embodiment 1：
A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally, is comprised the following steps that：
（1）Make embedded color lump pattern model：Color lump pattern is embedded by computer three-dimensional Software for Design, then by numerically controlled automatic bending Mechanism is molded, and keeps a cross section of model regular concordant；Embedded color lump pattern model is prepared from by stainless strip；
（2）Making artificial jade entity plane materiel embeds color lump pattern specific implementation step：
A. above-mentioned embedded color lump pattern model is placed in the safety glass template for wiping across releasing agent, color lump pattern mold is embedded Type it is smooth it is cross-section contact safety glass template downwards, this model is just whole safety glass form spacing into different zones Separate unit space；
B. pressed on model, or shift to an earlier date preset magnetic material Adsorption Model to protect below safety glass template Model of a syndrome cross section and safety glass template contacts are tight, leave no gaps in order to avoid gummosis alters material；
C. casting premix colorant inside the unitary space being spaced apart toward model, inside and outside required pattern is pressed in different interval region to model Mixing color is opened, and is cast simultaneously respectively, and casting thickness will be consistent；
D. cast after premix colorant, safety glass template feeding artificial stone Special vacuum equipment is evacuated to -0.09 ~ - 0.1MP, is kept for 3-5 minutes；
（3）Solidification process：When premix colorant starts to react and be not fully cured, i.e., before the complete gel of premix in 5 minutes Embedded color lump pattern model is taken out, tranquil placement, curing molding sanding and polishing are carried out according still further to conventional method.
Step（1）The thickness of middle stainless strip is 0.2-0.5mm, and width is 35-45mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：100 parts of unsaturated polyester resin, 180-220 parts of filling aluminium hydrate, catalysis 0.5-1.5 parts of agent, 0.8-2 parts of curing agent, special oil colour 0.02-0.8 parts of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens It is 100 parts to change aluminium powder, and H-WF-90 aluminium hydrate powders are 80-120 parts.
Colorant is premixed according to unsaturated polyester resin, filling aluminium hydrate, catalyst, the special oil colour of artificial stone and is consolidated The sequencing of agent is mixed and stirred for uniformly, and curing agent must finally be individually added into and be stirred for uniformly.
Catalyst is cobalt naphthenate（C14H22CoO4）, curing agent is methyl ethyl ketone peroxide（C8H18O6）.
The thickness for premixing colorant is 5-15mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 10-20N/m。
Embodiment 2：
A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally, is comprised the following steps that：
（1）Make embedded color lump pattern model：Color lump pattern is embedded by computer three-dimensional Software for Design, then by numerically controlled automatic bending Mechanism is molded, as shown in figure 1, keep a cross section of model regular concordant, it is flat as contact safety glass template solidification The one side of platform；Embedded color lump pattern model is prepared from by stainless strip；
（2）Making artificial jade entity plane materiel embeds color lump pattern specific implementation step：
A. above-mentioned embedded color lump pattern model is placed in the safety glass template for wiping across releasing agent, color lump pattern mold is embedded Type it is smooth it is cross-section contact safety glass template downwards, this model is just whole safety glass form spacing into different zones Separate unit space；
B. pressed on model, or shift to an earlier date preset magnetic material Adsorption Model to protect below safety glass template Model of a syndrome cross section and safety glass template contacts are tight, leave no gaps in order to avoid gummosis alters material；
C. casting premix colorant inside the unitary space being spaced apart toward model, inside and outside required pattern is pressed in different interval region to model Mixing color is opened, and is cast simultaneously respectively, and casting thickness will be consistent；It is noted that in this model both sides unitary space during casting Will uniformly be cast premix simultaneously, to prevent from altering material between different colorants；
D. cast after premix colorant, safety glass template feeding artificial stone Special vacuum equipment be evacuated to -0.09MP, Kept for 3 minutes；
（3）Solidification process：When premix colorant starts to react and be not fully cured, i.e., before the complete gel of premix in 5 minutes Embedded color lump pattern model is taken out, tranquil placement is carried out according still further to conventional method, curing molding sanding and polishing is final to be made Artificial jade's entity plane materiel it is as shown in Figure 2.
Step（1）The thickness of middle stainless strip is 0.2mm, and width is 35mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 180, catalyst 0.5 G, the g of curing agent 0.8, the special g of oil colour 0.02 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 80 g.
Colorant is premixed according to unsaturated polyester resin, filling aluminium hydrate, catalyst, the special oil colour of artificial stone and is consolidated The sequencing of agent is mixed and stirred for uniformly, and curing agent must finally be individually added into and be stirred for uniformly.
Catalyst is cobalt naphthenate, and curing agent is methyl ethyl ketone peroxide.
The thickness for premixing colorant is 5mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 10N/m。
Embodiment 3：
- 0.091MP is evacuated in step d, is kept for 3 minutes；
Step（1）The thickness of middle stainless strip is 0.25mm, and width is 36mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 185, catalyst 0.6 G, the g of curing agent 1, the special g of oil colour 0.1 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 85 g.
The thickness for premixing colorant is 6mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 11N/m.Embedded pattern color lump model is as shown in figure 3, final obtained artificial jade's entity plane materiel is as shown in Figure 4.
Other be the same as Examples 2.
Embodiment 4：
- 0.092MP is evacuated in step d, is kept for 4 minutes；
Step（1）The thickness of middle stainless strip is 0.28mm, and width is 37mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 190, catalyst 0.7 G, the g of curing agent 1.2, the special g of oil colour 0.2 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 90 g.
The thickness for premixing colorant is 7mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 12N/m.Embedded pattern color lump model is as shown in Figure 5.
Other be the same as Examples 2.
Embodiment 5：
- 0.093MP is evacuated in step d, is kept for 4 minutes；
Step（1）The thickness of middle stainless strip is 0.30mm, and width is 38mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 195, catalyst 0.8 G, the g of curing agent 1.3, the special g of oil colour 0.3 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 95 g.
The thickness for premixing colorant is 8mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 13N/m。
Other be the same as Examples 2.
Embodiment 6：
- 0.094MP is evacuated in step d, is kept for 5 minutes；
Step（1）The thickness of middle stainless strip is 0.35mm, and width is 39mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 198, catalyst 0.9 G, the g of curing agent 1.4, the special g of oil colour 0.35 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 98 g.
The thickness for premixing colorant is 9mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 14N/m。
Other be the same as Examples 2.
Embodiment 7：
- 0.095MP is evacuated in step d, is kept for 5 minutes；
Step（1）The thickness of middle stainless strip is 0.38mm, and width is 40mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 200, catalyst 1.0 G, the g of curing agent 1.5, the special g of oil colour 0.4 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 100 g.
The thickness for premixing colorant is 10mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 15N/m。
Other be the same as Examples 2.
Embodiment 8：
- 0.096MP is evacuated in step d, is kept for 3 minutes；
Step（1）The thickness of middle stainless strip is 0.4mm, and width is 41mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 205, catalyst 1.1 G, the g of curing agent 1.6, the special g of oil colour 0.45 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 105 g.
The thickness for premixing colorant is 11mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 16N/m。
Other be the same as Examples 2.
Embodiment 9：
- 0.097MP is evacuated in step d, is kept for 3 minutes；
Step（1）The thickness of middle stainless strip is 0.42mm, and width is 42mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 210, catalyst 1.2 G, the g of curing agent 1.7, the special g of oil colour 0.5 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 110g.
The thickness for premixing colorant is 12mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 17N/m。
Other be the same as Examples 2.
Embodiment 10：
- 0.098MP is evacuated in step d, is kept for 4 minutes；
Step（1）The thickness of middle stainless strip is 0.45mm, and width is 43mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 215, catalyst 1.3g, the g of curing agent 1.8, the special g of oil colour 0.6 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 115g.
The thickness for premixing colorant is 13mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 18N/m。
Other be the same as Examples 2.
Embodiment 11：
- 0.099MP is evacuated in step d, is kept for 4 minutes；
Step（1）The thickness of middle stainless strip is 0.48mm, and width is 44mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 218, catalyst 1.4g, the g of curing agent 1.9, the special g of oil colour 0.7 of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 118g.
The thickness for premixing colorant is 14mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 19N/m。
Other be the same as Examples 2.
Embodiment 12：
- 0.1MP is evacuated in step d, is kept for 5 minutes；
Step（1）The thickness of middle stainless strip is 0.5mm, and width is 45mm.
Premixing colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness of artificial stone Pigment, the mass fraction of above-mentioned raw materials is respectively：Unsaturated polyester resin 100g, the g of filling aluminium hydrate 220, catalyst 1.5g, curing agent 2g, the special oil colour 0.8g of artificial stone.
Filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A hydrogen-oxygens Change aluminium powder is 100 g, and H-WF-90 aluminium hydrate powders are 120g.
The thickness for premixing colorant is 15mm.
The magnetic force that the pressure or magnetic material applied in step b is produced is that the power on model cross section on per unit length is 20N/m。
Other be the same as Examples 2.
Above-described is only the preferred embodiment of the present invention, it is noted that for those skilled in the art, Under the premise of general idea of the present invention is not departed from, some changes and improvements can also be made, these should also be considered as the present invention's Protection domain.

Claims (8)

1. a kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally, it is characterised in that：Comprise the following steps that：
（1）Make embedded color lump pattern model：Color lump pattern is embedded by computer three-dimensional Software for Design, then by numerically controlled automatic bending Mechanism is molded, and keeps a cross section of model regular concordant；Embedded color lump pattern model is prepared from by stainless strip；
（2）Making artificial jade entity plane materiel embeds color lump pattern specific implementation step：
A. above-mentioned embedded color lump pattern model is placed in the safety glass template for wiping across releasing agent, color lump pattern mold is embedded Type it is smooth it is cross-section contact safety glass template downwards, this model is just whole safety glass form spacing into different zones Separate unit space；
B. pressed on model, or shift to an earlier date preset magnetic material Adsorption Model to protect below safety glass template Model of a syndrome cross section and safety glass template contacts are tight, leave no gaps in order to avoid gummosis alters material；
C. casting premix colorant inside the unitary space being spaced apart toward model, inside and outside required pattern is pressed in different interval region to model Mixing color is opened, and is cast simultaneously respectively, and casting thickness will be consistent；
D. cast after premix colorant, safety glass template feeding artificial stone Special vacuum equipment is evacuated to -0.09 ~ - 0.1MP, is kept for 3-5 minutes；
（3）Solidification process：When premix colorant starts to react and be not fully cured, i.e., before the complete gel of premix in 5 minutes Embedded color lump pattern model is taken out, tranquil placement, curing molding sanding and polishing are carried out according still further to conventional method.
2. the preparation method of the artificial jade's entity plane materiel according to claim 1 for embedding color lump naturally, it is characterised in that： The step（1）The thickness of middle stainless strip is 0.2-0.5mm, and width is 35-45mm.
3. the preparation method of the artificial jade's entity plane materiel according to claim 1 for embedding color lump naturally, it is characterised in that： The premix colorant includes unsaturated polyester resin, filling aluminium hydrate, catalyst, curing agent and the special oiliness face of artificial stone Expect, the mass fraction of above-mentioned raw materials is respectively：100 parts of unsaturated polyester resin, 180-220 parts of filling aluminium hydrate, catalyst 0.5-1.5 parts, 0.8-2 parts of curing agent, special oil colour 0.02-0.8 parts of artificial stone.
4. the preparation method of the artificial jade's entity plane materiel according to claim 3 for embedding color lump naturally, it is characterised in that： The filling aluminium hydrate includes H-WF-15A aluminium hydrate powders and H-WF-90 aluminium hydrate powders, and H-WF-15A aluminium hydroxides Powder is 100 parts, and H-WF-90 aluminium hydrate powders are 80-120 parts.
5. the preparation method of the artificial jade's entity plane materiel according to claim 3 for embedding color lump naturally, it is characterised in that： The premix colorant is according to unsaturated polyester resin, filling aluminium hydrate, catalyst, the special oil colour of artificial stone and curing agent Sequencing be mixed and stirred for uniformly, and curing agent must finally be individually added into be stirred for it is uniform.
6. the preparation method of the artificial jade's entity plane materiel according to claim 3 for embedding color lump naturally, it is characterised in that： The catalyst is cobalt naphthenate, and curing agent is methyl ethyl ketone peroxide.
7. the preparation method of the artificial jade's entity plane materiel according to claim 1 for embedding color lump naturally, it is characterised in that： The thickness of the premix colorant is 5-15mm.
8. the preparation method of the artificial jade's entity plane materiel according to claim 1 for embedding color lump naturally, it is characterised in that： The magnetic force that the pressure or magnetic material applied in the step b is produced is that the power on model cross section on per unit length is 10- 20N/m。
CN201710338222.8A 2017-05-15 2017-05-15 A kind of preparation method for the artificial jade's entity plane materiel for embedding color lump naturally Pending CN107116735A (en)