CN107099648A - The structure property homogenization heat treatment method of the steel of laser deposition molding A 100 - Google Patents
The structure property homogenization heat treatment method of the steel of laser deposition molding A 100 Download PDFInfo
- Publication number
- CN107099648A CN107099648A CN201710499180.6A CN201710499180A CN107099648A CN 107099648 A CN107099648 A CN 107099648A CN 201710499180 A CN201710499180 A CN 201710499180A CN 107099648 A CN107099648 A CN 107099648A
- Authority
- CN
- China
- Prior art keywords
- steel
- heat treatment
- treatment method
- laser deposition
- deposition molding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to aero-manufacturing technology field, specifically provide a kind of structure property homogenization heat treatment method of the steel of laser deposition molding A 100, the high temperature anneal is carried out to it after the shaping of the steel of laser deposition molding A 100 first, it is heated in the range of 1100 DEG C~1300 DEG C and continues 2h~4h, room temperature is furnace-cooled to afterwards;Then after the completion of high annealing, 3 circulation normalized treatments are carried out to the steel of A 100, the normalized treatment includes the steel is heated into 900 DEG C ± 15 DEG C and continues 1h, and room temperature is air-cooled to afterwards;This method can eliminate the component segregation that laser direct deposition shapes the Steel materials of A 100, control tissue performance uniformity, it is ensured that the laser direct deposition shaping steel of A 100 can obtain good combination property.
Description
Technical field
The present invention relates to aero-manufacturing technology field, the structure property of more particularly to laser deposition molding A-100 steel is uniform
Change heat treatment method.
Background technology
Laser direct deposition shapes the one kind for belonging to increases material manufacturing technology, and A-100 steels are shaped using laser direct deposition
Make undercarriage pioneering for the world.A-100 steel is High-alloy Ultra-high Strength Steel, and alloying level is high, causes in laser direct deposition
Segregation phenomena easily occurs for material structure in shaping process of setting, is unfavorable for the uniformity of material structure performance, influences the comprehensive of material
Performance is closed, therefore how to control laser direct deposition to shape A-100 structure of steel performance uniformities, the component segregation of material is eliminated,
It is to ensure that laser direct deposition shaping A-100 steel can obtain good combination property and realize the key of application.
It is domestic at present still effectively to control laser direct deposition to shape A-100 structure of steel performance uniformities without a kind of
Method.
The content of the invention
To overcome at least one defect that above-mentioned prior art is present, the invention provides a kind of laser deposition molding A-
The structure property homogenization heat treatment method of 100 steel, comprises the following steps:
Step one, the high temperature anneal is carried out to it after the shaping of laser deposition molding A-100 steel, is heated to 1100
DEG C~1300 DEG C in the range of and continue 2h~4h, room temperature is furnace-cooled to afterwards;
After the completion of step 2, high annealing, 3 circulation normalized treatments, the normalized treatment bag are carried out to the A-100 steel
Include and the steel is heated to 900 DEG C ± 15 DEG C and continues 1h, room temperature is air-cooled to afterwards.
It is preferred that, the heating-up temperature of step one high temperature annealing is 1200 DEG C.
It is preferred that, the heat time of step one high temperature annealing is 2.5h.
It is preferred that, the heating-up temperature of normalized treatment is 900 DEG C in step 2.
The structure property homogenization heat treatment method for the laser deposition molding A-100 steel that the present invention is provided, can be eliminated sharp
Light Direct precipitation shapes the component segregation of A-100 Steel materials, controls tissue performance uniformity, it is ensured that laser direct deposition shapes
A-100 steel can obtain good combination property.
Brief description of the drawings
Fig. 1 is the flow chart of the structure property homogenization heat treatment method of laser deposition molding A-100 steel.
Embodiment
To make the purpose, technical scheme and advantage of the invention implemented clearer, below in conjunction with the embodiment of the present invention
Accompanying drawing, the technical scheme in the embodiment of the present invention is further described in more detail.
It should be noted that:The embodiments described below with reference to the accompanying drawings are exemplary, it is intended to for explaining this hair
It is bright, and be not considered as limiting the invention.In the accompanying drawings, same or similar label represents same or like from beginning to end
Element or element with same or like function.Described embodiment is a part of embodiment of the invention, rather than entirely
The embodiment in portion, in the case where not conflicting, the feature in embodiment and embodiment in the application can be mutually combined.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
The invention provides a kind of structure property homogenization heat treatment method of laser deposition molding A-100 steel, exist first
The high temperature anneal is carried out to it after the shaping of laser deposition molding A-100 steel, its system of heat treatment process is:By laser deposition into
Shape A-100 steel is heated in the range of 1100 DEG C to 1300 DEG C and continues 2 hours to 4 hours, is preferably to be heated in the present embodiment
1200 DEG C and continue 2.5 hours, room temperature is furnace-cooled to afterwards;Then after the completion of high annealing, the A-100 steel is carried out
3 circulation normalized treatments, normalized treatment technology establishment is:The steel is heated to 900 DEG C ± 15 DEG C and continues 1h, the present embodiment
In be preferably be heated to 900 DEG C, room temperature is air-cooled to afterwards.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
Those familiar with the art the invention discloses technical scope in, the change or replacement that can be readily occurred in, all should
It is included within the scope of the present invention.Therefore, protection scope of the present invention should using the scope of the claims as
It is accurate.
Claims (4)
1. a kind of structure property homogenization heat treatment method of laser deposition molding A-100 steel, it is characterised in that:Including following step
Suddenly:
Step one, laser deposition molding A-100 steel shaping after the high temperature anneal is carried out to it, be heated to 1100 DEG C~
In the range of 1300 DEG C and continue 2h~4h, room temperature is furnace-cooled to afterwards;
After the completion of step 2, high annealing, 3 circulation normalized treatments are carried out to the A-100 steel, the normalized treatment includes will
The steel is heated to 900 DEG C ± 15 DEG C and continues 1h, and room temperature is air-cooled to afterwards.
2. heat treatment method according to claim 1, it is characterised in that the heating-up temperature of step one high temperature annealing
For 1200 DEG C.
3. heat treatment method according to claim 1, it is characterised in that the heat time of step one high temperature annealing
For 2.5h.
4. heat treatment method according to claim 1, it is characterised in that the heating-up temperature of normalized treatment is in step 2
900℃。