CN107089822A - A kind of pierced carving technique of Nixing pottery - Google Patents
A kind of pierced carving technique of Nixing pottery Download PDFInfo
- Publication number
- CN107089822A CN107089822A CN201710242351.7A CN201710242351A CN107089822A CN 107089822 A CN107089822 A CN 107089822A CN 201710242351 A CN201710242351 A CN 201710242351A CN 107089822 A CN107089822 A CN 107089822A
- Authority
- CN
- China
- Prior art keywords
- mud
- color
- base substrate
- weathered
- pattern
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the pierced carving technique of a kind of preparation method of Nixing pottery, more particularly to a kind of Nixing pottery；Comprise the following steps：(1) select mud (2) dispensing (3) to prepare pierced carving pug (4) and prepare pattern segments (5) making base substrate (6) dry (7) firing；The present invention is by making combination forming by hand, change traditional drawing embryo and make forming method, base substrate is constituted by orderly, regular pattern or the combination of unordered, irregular pattern slice, pattern is consistent inside and outside base substrate, by the middle weathering color mud and the dispensing of severely-weathered color mud of different component, it can realize that color mud pattern is mutually sucked, in sintering procedure, difficult for drop-off and cracking, burns till rate high.
Description
Technical field
The present invention relates to the pierced carving technique of a kind of preparation method of Nixing pottery, more particularly to a kind of Nixing pottery.
Background technology
Nixing pottery originates from Guangxi Qinzhou, existing more than 1300 years history, with Jiangsu's purple sand ceramics, Yunnan Jian Shui potteries, Sichuan
Rongchang County's pottery is listed as the big name pottery of China four.The emerging technique pottery of Qiezhou mud, with a long history, make a name China and foreign countries, and Qiezhou Nixing pottery has distinctness
Regional characteristic, with its unique raw material, technological process, modelling feature, product category, the sculptured ornament gimmick shown unique characteristics and
Coastal characteristic of folk customs of one's native land of Beibu Bay, guangxi being had etc. is taken the course of its own in the World Ceramic realm of art and literature, it is necessary to paid attention to Nixing pottery
Excavation, protection and the succession of culture, promote traditional handicraft progress, are allowed to develop.
Pierced carving technique is by making combination forming by hand, changing traditional drawing embryo forming method, pass through orderly, rule
Pattern or the combination of unordered, irregular pattern slice constitute base substrate, and base substrate forms inside and outside pattern unanimously, referred to as pierced carving, tradition
Nixing pottery is to draw embryo forming technique, is bold in innovation on the basis of the succession technique of Nixing pottery, breaks through succession and draws embryo forming technique,
Make more to take the course of its own on Nixing pottery representation style, plasticity more preferably, is brought business opportunity to Tao Ye sustainable developments, can be fabricated to
Various pottery pierced carving product, decorative effect is extremely strong, is that traditional Nixing pottery is developed.
The content of the invention
The present invention is in order to solve the above technical problems, there is provided a kind of pierced carving technique of Nixing pottery.
Realized particular by following technical scheme：
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Weathered mudstone during selection is natural, ground, press filtration obtains middle weathering color mud；Selection is natural severely-weathered each
Color mud stone is planted, ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 5~1: 1~5 mass ratio, it is ground, dehydration, true
It is empty pugging, old, prepare color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 3~6h, and mud bar is cut into required figure with knife
Case piece, puts moisturizing in foamed gypsum case into, obtains pattern segments；
(5) base substrate is made, by the pattern segments made, superposition, combination are stripped into by mould molding after standing 3~4h
Type, stands after 10~13h, carries out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, by dried base substrate kiln-firing.
Described middle weathering a variety of colors mud stone, is collected in Qinzhou City region, is a kind of clay of maroon.
Described severely-weathered a variety of colors mud stone, is collected in Qinzhou City region, is a kind of clay with multiple color.
The pierced carving technique of described Nixing pottery, middle weathering color mud, the mixing ratio of severely-weathered color mud are 3: 2.
The pierced carving technique of described Nixing pottery, color mud of the step (2) after dispensing, water content is 25~35%.
Described pattern segments, its thickness is 6~10mm, and the pattern segments water content of preparation is 20~30%.
Described kiln-firing, is that dried base substrate is put into firing kiln, first with 18~22 DEG C/h speed by temperature
Degree is risen to after 100 DEG C, then is risen to temperature after 400 DEG C with 28~32 DEG C/h speed, then with 38~42 DEG C/h speed by temperature
Degree is risen to after 550 DEG C, then temperature is risen to temperature after 1050 DEG C to 48~52 DEG C/h speed, and 2h is incubated at this temperature
Afterwards, cooling is taken out.
In summary, the beneficial effects of the present invention are：The present invention is bold on the basis of the succession technique of Nixing pottery
Innovation, breaks through succession and draws embryo forming technique, make more to take the course of its own on Nixing pottery representation style, plasticity is more preferable, to Tao Yeke
Sustainable development brings business opportunity, can be fabricated to various pottery pierced carving product, promotes traditional Nixing pottery technique progress, pierced carving
Technique is by making combination forming by hand, changing traditional drawing embryo and make forming method, pass through orderly, regular pattern or nothing
Sequence, the slice combination of irregular pattern constitute pattern inside and outside base substrate, the base substrate of making and unanimously, pass through the middle weathering color of different component
The dispensing of mud and severely-weathered color mud, can realize that color mud pattern is mutually sucked, in sintering procedure, difficult for drop-off and cracking, burn till
Rate is high, makes Nixing pottery decorative effect stronger, each making molding pattern is all different, without comparativity, is the biography of Nixing pottery
Hold and develop and made creative contribution.
Embodiment
The embodiment to the present invention is described in further detail below, but the invention is not limited in these realities
Mode is applied, any improvement or replacement on the present embodiment essence spirit still falls within the claims in the present invention claimed
Scope.
Embodiment 1
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Natural middle weathered mudstone is collected in Qinzhou City region, ground, press filtration obtains middle weathering color mud；Admiring
Natural severely-weathered a variety of colors mud stone is collected in state city region, and ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 5: 1 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, water content is prepared into for 25% color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 3h, and it is 6mm that mud bar is cut into thickness with knife
Pattern segments, put moisturizing in foamed gypsum case into, obtain water content be 20% pattern segments；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 3h by mould molding,
Stand after 10h, carry out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, dried base substrate kiln-firing is first risen to temperature after 100 DEG C with 18 DEG C/h speed, then with
28 DEG C/h speed rises to temperature after 400 DEG C, then is risen to temperature after 550 DEG C with 38 DEG C/h speed, then with 48 DEG C/h's
Speed rises to temperature temperature after 1050 DEG C, is incubated at this temperature after 2h, takes out cooling.
Embodiment 2
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Natural middle weathered mudstone is collected in Qinzhou City region, ground, press filtration obtains middle weathering color mud；Admiring
Natural severely-weathered a variety of colors mud stone is collected in state city region, and ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 1: 5 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, water content is prepared into for 35% color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 6h, and mud bar is cut into thickness with knife is
10mm pattern segments, put moisturizing in foamed gypsum case into, obtain the pattern segments that water content is 30%；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 4h by mould molding,
Stand after 13h, carry out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, dried base substrate kiln-firing is first risen to temperature after 100 DEG C with 22 DEG C/h speed, then with
32 DEG C/h speed rises to temperature after 400 DEG C, then is risen to temperature after 550 DEG C with 42 DEG C/h speed, then with 52 DEG C/h's
Speed rises to temperature temperature after 1050 DEG C, is incubated at this temperature after 2h, takes out cooling.
Embodiment 3
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Natural middle weathered mudstone is collected in Qinzhou City region, ground, press filtration obtains middle weathering color mud；Admiring
Natural severely-weathered a variety of colors mud stone is collected in state city region, and ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 3: 2 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, water content is prepared into for 30% color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 5h, and it is 8mm that mud bar is cut into thickness with knife
Pattern segments, put moisturizing in foamed gypsum case into, obtain water content be 25% pattern segments；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 4h by mould molding,
Stand after 11h, carry out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, dried base substrate kiln-firing is first risen to temperature after 100 DEG C with 20 DEG C/h speed, then with
30 DEG C/h speed rises to temperature after 400 DEG C, then is risen to temperature after 550 DEG C with 40 DEG C/h speed, then with 50 DEG C/h's
Speed rises to temperature temperature after 1050 DEG C, is incubated at this temperature after 2h, takes out cooling.
Embodiment 4
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Natural middle weathered mudstone is collected in Qinzhou City region, ground, press filtration obtains middle weathering color mud；Admiring
Natural severely-weathered a variety of colors mud stone is collected in state city region, and ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 5: 2 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, water content is prepared into for 35% color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 6h, and it is 8mm that mud bar is cut into thickness with knife
Pattern segments, put moisturizing in foamed gypsum case into, obtain water content be 25% pattern segments；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 4h by mould molding,
Stand after 13h, carry out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, dried base substrate kiln-firing is first risen to temperature after 100 DEG C with 18 DEG C/h speed, then with
28 DEG C/h speed rises to temperature after 400 DEG C, then is risen to temperature after 550 DEG C with 40 DEG C/h speed, then with 52 DEG C/h's
Speed rises to temperature temperature after 1050 DEG C, is incubated at this temperature after 2h, takes out cooling.
Embodiment 5
A kind of pierced carving technique of Nixing pottery, comprises the following steps：
(1) mud is selected：Natural middle weathered mudstone is collected in Qinzhou City region, ground, press filtration obtains middle weathering color mud；Admiring
Natural severely-weathered a variety of colors mud stone is collected in state city region, and ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 4: 3 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, water content is prepared into for 30% color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is entered
Row superposition, is rubbed, and is mixed, and is fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 3h, and mud bar is cut into thickness with knife is
10mm pattern segments, put moisturizing in foamed gypsum case into, obtain the pattern segments that water content is 25%；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 3h by mould molding,
Stand after 13h, carry out repaired biscuit with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, dried base substrate kiln-firing is first risen to temperature after 100 DEG C with 20 DEG C/h speed, then with
28 DEG C/h speed rises to temperature after 400 DEG C, then is risen to temperature after 550 DEG C with 40 DEG C/h speed, then with 52 DEG C/h's
Speed rises to temperature temperature after 1050 DEG C, is incubated at this temperature after 2h, takes out cooling.
Experimental example
1st, proportioning test：The present invention makes full use of the effect mutually sucked between middle weathering mud and reinforcing wind mud, meanwhile,
By reasonably matching, the blending between two kinds of color mud colors is realized, the proportioning test between two kinds of color mud is now carried out, to prove
The middle weathering mud of the present invention and the ratio range that the mass ratio of severely-weathered mud is 5~1: 1~5, it is specific as shown in table 1：
Table 1
| The shared number of middle weathering mud and severely-weathered mud difference | Fire spoilage % |
| 6: 1~5 | 8 |
| 0：1~5 | 12 |
| 5~1: 0 | 10 |
| 5~1: 6 | 8 |
| 6∶6 | 9 |
| 5∶1 | 3 |
| 1∶5 | 6 |
| 3∶2 | 2 |
| 5∶2 | 4 |
| 4∶3 | 3 |
Explanation：As known to upper table, middle weathering mud of the invention and severely-weathered mud are drawn by the experiment of inventor repeatedly
Optimum ratio, weathering mud and severely-weathered mud are mutually sucked in could realizing, using single middle weathering color mud or single
Severely-weathered color mud so that the firing spoilage of product is greatly improved.
Claims (7)
1. the pierced carving technique of a kind of Nixing pottery, it is characterised in that comprise the following steps：
(1) mud is selected：Weathered mudstone during selection is natural, ground, press filtration obtains middle weathering color mud；The natural severely-weathered various face of selection
Color mud stone, ground, press filtration obtains severely-weathered color mud；
(2) dispensing：Middle weathering color mud, severely-weathered color mud are mixed by 5~1: 1~5 mass ratio, ground, dehydration, vacuum are practiced
It is mud, old, prepare color mud；
(3) pierced carving pug is prepared, the color mud that selecting step (2) is prepared is squeezed into slice, different color slice is folded
Plus, rub, mix, be fabricated to the pattern mud bar that blending twists pureed state；
(4) pattern segments are prepared, pierced carving pug prepared by step (3) is stood after 3~6h, and mud bar is cut into required pattern with knife
Piece, puts moisturizing in foamed gypsum case into, obtains pattern segments；
(5) base substrate is made, by the pattern segments made, superposition, combination stand stripping forming after 3~4h by mould molding, quiet
Put after 10~13h, repaired biscuit is carried out with trimming machine, then polish to obtain base substrate；
(6) dry, the base substrate that step (5) is made dries in the shade naturally；
(7) fire, by dried base substrate kiln-firing.
2. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that described middle weathering a variety of colors mud stone,
Qinzhou City region is collected in, is a kind of clay of maroon.
3. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that described severely-weathered a variety of colors mud stone,
Qinzhou City region is collected in, is a kind of clay with multiple color.
4. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that middle weathering color mud, severely-weathered color mud it is mixed
Composition and division in a proportion is 3: 2.
5. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that color mud of the step (2) after dispensing, aqueous
Measure as 25~35%.
6. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that described pattern segments, its thickness is 6~
10mm, the pattern segments water content of preparation is 20~30%.
7. the pierced carving technique of Nixing pottery as claimed in claim 1, it is characterised in that described kiln-firing, being will be dried
Base substrate be put into firing kiln, first temperature is risen to after 100 DEG C with 18~22 DEG C/h speed, then with 28~32 DEG C/h speed
Temperature is risen to after 400 DEG C, then risen to temperature after 550 DEG C with 38~42 DEG C/h speed, then with 48~52 DEG C/h speed
Temperature is risen to after 1050 DEG C by temperature, is incubated at this temperature after 2h, cooling is taken out.