CN107083004A - A kind of composite surface material for charging pile - Google Patents
A kind of composite surface material for charging pile Download PDFInfo
- Publication number
- CN107083004A CN107083004A CN201710283748.0A CN201710283748A CN107083004A CN 107083004 A CN107083004 A CN 107083004A CN 201710283748 A CN201710283748 A CN 201710283748A CN 107083004 A CN107083004 A CN 107083004A
- Authority
- CN
- China
- Prior art keywords
- surface material
- composite surface
- temperature
- fibre
- charging pile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite surface material for charging pile, the composite surface material is made up of the following raw material:Resin 10% 20%, rubber 4% 6%, ceramics 1% 3%, graphite 4% 6%, carbon 4% 6%, glass fibre 8% 10%, carbon fiber 9% 15%, boron fibre 10% 20%, aramid fiber 2% 4%, silicon carbide fibre 1% 3%, asbestos fibre 4% 6%, whisker 5% 7%, wire 1% 3%, hard particulates 1% 3%, remaining is water, the present invention has high resilience and relatively low compression set performance, with excellent corrosion resistance, high-tensile and elongation percentage, and with higher resistivity, the preparation of the present invention can be completed within a short period of time simultaneously, and feed stock conversion is high, side reaction is few, product purity is higher.
Description
Technical field
The present invention relates to composite surface material technical field, and in particular to a kind of composite surface material for charging pile.
Background technology
It is functionally similar to fuel charger inside gas station to charging pile, can be fixed on ground or wall, be installed on public
Build in (public building, market, Public Parking etc.) and residential area parking lot or charging station, can be according to different voltage
Grade is the charging electric vehicle of various models.The input of charging pile is directly connected to AC network, and output end is equipped with filling
Plug is used to be charging electric vehicle.Charging pile generally provides two kinds of charging modes of normal charge and quick charge, Ren Menke
Used with being swiped the card using specific recharged card on the man-machine interactive interface that charging pile is provided, carry out corresponding charging side
The operations such as formula, charging interval, cost data printing, charging pile display screen can show the data such as charge volume, expense, charging interval,
And the composite on charging pile, be by two or more material of different nature, by method physically or chemically,
Material of the composition with new capability on macroscopical (microcosmic).Various materials make up for each other's deficiencies and learn from each other in performance, produce cooperative effect, make
The combination property of composite is better than former composition material and meets a variety of requirements, but existing composite its resilience
Property and higher compression set performance, the corrosion resistance not having, tensile strength and elongation percentage hand over low, and resistivity is not
Height, while the time prepared is longer, the concentration of product is relatively low.
The content of the invention
For problem above, the invention provides a kind of composite surface material for charging pile, with high resilience
With relatively low compression set performance, with excellent corrosion resistance, high-tensile and elongation percentage, and there is higher electricity
Resistance rate, while the preparation of the present invention can be completed within a short period of time, and feed stock conversion is high, side reaction is few, product purity
It is higher, the problem of effectively can solving in background technology.
To achieve these goals, the technical solution adopted by the present invention is as follows:A kind of surface recombination material for charging pile
Material, the composite surface material is to prepare composite surface material using multigroup raw material, and composite surface material raw material composition is:Resin
10%-20%, rubber 4%-6%, ceramics 1%-3%, graphite 4%-6%, carbon 4%-6%, glass fibre 8%-10%, carbon are fine
Tie up 9%-15%, boron fibre 10%-20%, aramid fiber 2%-4%, silicon carbide fibre 1%-3%, asbestos fibre 4%-6%,
Whisker 5%-7%, wire 1%-3%, hard particulates 1%-3%, remaining be water.
According to above-mentioned technical proposal, the wire is the wire of cupro-nickel 19, is by the 18-20% according to percentage by weight
Ni, 0.01-0.6% Mn, 0.1-1% Fe, 0.1-1% Al, 0.01-0.5% Si, 0.01-1% Sn, 0.01-
0.5% B, 0.001-0.1% Re and copper, carry out mixed smelting, then by obtained ingot casting peeling, forge;Finally will forging
Blank drawing after beating, repeats Drawing-anneal at least 2 times, until the wire of cupro-nickel 19 of specification needed for obtaining.
According to above-mentioned technical proposal, the resin is terpene resin, is to sequentially add australene, water entrainer and catalyst
In cavitation machine, adjust successively to the first temperature, second temperature, the 3rd temperature, the 4th temperature and carry out polymerisation, washing removes band
Aqua, what Filtration of catalyst was made;Wherein, the water entrainer is toluene, and the catalyst is manganese dioxide.
According to above-mentioned technical proposal, the rubber is silicon rubber, is by methyl vinyl silicone rubber, calcium stearate, hard charcoal
Black, dimethyldiethoxysilane is added in kneader, to obtain molding materials;Molding materials are heated into 150~160 to take the photograph
Family name's degree, is vacuumized, and is incubated 2~3 hours;Molding materials temperature is reduced to 80 degrees Celsius;Into kneader add calcium carbonate,
Cerium oxide, isooctyl acid iron organic solution, Vinyl MQ silicon resin and silica flour, to obtain silicone rubber compounds;And by silicon rubber
Glue sizing material and 2,5- dimethyl -2,5- bishexane are added after opening rubber mixing machine mixing uniformly, are put in vulcanizing press in temperature
Silicon rubber is obtained after vulcanizing 5~15 minutes for 170 degrees Celsius.
A kind of preparation technology of composite surface material for charging pile, comprises the following steps:
(1) dispensing:By resin, rubber, ceramics, graphite, carbon, glass fibre, carbon fiber, boron fibre, aramid fiber, carbonization
Silica fibre, asbestos fibre, whisker, wire, hard particulates, weigh according to aforementioned proportion, standby;
(2) grind:By the resin after proportionally being weighed in step (1), rubber, ceramics, graphite, carbon, whisker, wire
And hard particulates, pass sequentially through lapping device and be ground, obtain fine powder, it is standby;
(3) mix:By the glass fibre after proportionally being weighed in step (1), carbon fiber, boron fibre, aramid fiber, carbon
SiClx fiber and asbestos fibre, are pre-mixed, and obtain mixture one, and being ground in step (2) is then obtained fine powder, plus
Enter into mixture one, raw mixture is obtained after screening;
(4) stir:The raw mixture obtained in step (3) is added into water entrainer and catalyst, entered by agitating device
Row is sufficiently stirred for, and remembers composite;
(5) tinning:By the composite after being sufficiently stirred in step (4), tinning is carried out.
According to above-mentioned technical proposal, the regulation during stirring is divided into four sections, constant velocity stage, accelerates boost phase, at the uniform velocity
Temperature rise period and deceleration buck stage, the speed of the constant velocity stage are maintained at 30 revs/min, accelerate average rate be 8 turns/
Minute;The speed of the at the uniform velocity temperature rise period is maintained at 300 revs/min of constant, 5 DEG C/min of temperature-averaging acceleration;It is described to slow down
The temperature of buck stage is first down to 200 revs/min, then keeps 20min, and temperature is down to 30 DEG C from 200 DEG C, and cooling Mean Speed is
4℃/min。
According to above-mentioned technical proposal, the screening net of the screening in the step (3), is a kind of screening net of 50-80 mesh.
According to above-mentioned technical proposal, the device of the tinning is automatic can filler.
Beneficial effects of the present invention:
The present invention has high resilience and relatively low compression set performance, anti-with excellent corrosion resistance, height
Tensile strength and elongation percentage, and with higher resistivity, while the preparation of the present invention can be completed within a short period of time, and it is former
Expect that high conversion rate, side reaction be few, product purity is higher.
Brief description of the drawings
Fig. 1 is preparation flow figure of the present invention.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1:
Referring to Fig. 1, the present invention provides a kind of composite surface material for charging pile, the composite surface material is to adopt
Composite surface material is prepared with multigroup raw material, composite surface material raw material composition is:Resin 10%, rubber 4%, ceramics 1%, stone
Ink 4%, carbon 4%, glass fibre 8%, carbon fiber 9%, boron fibre 10%, aramid fiber 2%, silicon carbide fibre 1%, asbestos are fine
Dimension 4%, whisker 5%, wire 1%, hard particulates 1%, remaining be water.
According to above-mentioned technical proposal, the wire is the wire of cupro-nickel 19, is by the 18-20% according to percentage by weight
Ni, 0.01-0.6% Mn, 0.1-1% Fe, 0.1-1% Al, 0.01-0.5% Si, 0.01-1% Sn, 0.01-
0.5% B, 0.001-0.1% Re and copper, carry out mixed smelting, then by obtained ingot casting peeling, forge;Finally will forging
Blank drawing after beating, repeats Drawing-anneal at least 2 times, until the wire of cupro-nickel 19 of specification needed for obtaining;The resin is terpene
Olefine resin, is to sequentially add australene, water entrainer and catalyst in cavitation machine, adjust successively to the first temperature, second temperature,
3rd temperature, the 4th temperature carry out polymerisation, and washing removes water entrainer, what Filtration of catalyst was made;Wherein, the band
Aqua is toluene, and the catalyst is manganese dioxide;The rubber is silicon rubber, is by methyl vinyl silicone rubber, stearic acid
Calcium, white carbon, dimethyldiethoxysilane are added in kneader, to obtain molding materials;Molding materials are heated to 150
~160 degrees Celsius, vacuumize, and be incubated 2~3 hours;Molding materials temperature is reduced to 80 degrees Celsius;Added into kneader
Calcium carbonate, cerium oxide, isooctyl acid iron organic solution, Vinyl MQ silicon resin and silica flour, to obtain silicone rubber compounds;And
By silicone rubber compounds and 2,5- dimethyl -2,5- bishexane is added after opening rubber mixing machine mixing uniformly, is put in vulcanizing press
Silicon rubber is obtained after temperature vulcanizes 5~15 minutes for 170 degrees Celsius.
A kind of preparation technology of composite surface material for charging pile, comprises the following steps:
(1) dispensing:By resin, rubber, ceramics, graphite, carbon, glass fibre, carbon fiber, boron fibre, aramid fiber, carbonization
Silica fibre, asbestos fibre, whisker, wire, hard particulates, weigh according to aforementioned proportion, standby;
(2) grind:By the resin after proportionally being weighed in step (1), rubber, ceramics, graphite, carbon, whisker, wire
And hard particulates, pass sequentially through lapping device and be ground, obtain fine powder, it is standby;
(3) mix:By the glass fibre after proportionally being weighed in step (1), carbon fiber, boron fibre, aramid fiber, carbon
SiClx fiber and asbestos fibre, are pre-mixed, and obtain mixture one, and being ground in step (2) is then obtained fine powder, plus
Enter into mixture one, raw mixture is obtained after screening;
(4) stir:The raw mixture obtained in step (3) is added into water entrainer and catalyst, entered by agitating device
Row is sufficiently stirred for, and remembers composite;
(5) tinning:By the composite after being sufficiently stirred in step (4), tinning is carried out.
According to above-mentioned technical proposal, the regulation during stirring is divided into four sections, constant velocity stage, accelerates boost phase, at the uniform velocity
Temperature rise period and deceleration buck stage, the speed of the constant velocity stage are maintained at 30 revs/min, accelerate average rate be 8 turns/
Minute;The speed of the at the uniform velocity temperature rise period is maintained at 300 revs/min of constant, 5 DEG C/min of temperature-averaging acceleration;It is described to slow down
The temperature of buck stage is first down to 200 revs/min, then keeps 20min, and temperature is down to 30 DEG C from 200 DEG C, and cooling Mean Speed is
4℃/min;The screening net of screening in the step (3), is a kind of screening net of 50-80 mesh;The device of the tinning
For automatic can filler.
Embodiment 2:
Referring to Fig. 1, the present invention provides a kind of composite surface material for charging pile, the composite surface material is to adopt
Composite surface material is prepared with multigroup raw material, composite surface material raw material composition is:Resin 15%, rubber 5%, ceramics 2%, stone
Ink 5%, carbon 5%, glass fibre 9%, carbon fiber 12%, boron fibre 15%, aramid fiber 3%, silicon carbide fibre 2%, asbestos
Fiber 5%, whisker 6%, wire 2%, hard particulates 2%, remaining be water.
According to above-mentioned technical proposal, the wire is the wire of cupro-nickel 19, is by the 18-20% according to percentage by weight
Ni, 0.01-0.6% Mn, 0.1-1% Fe, 0.1-1% Al, 0.01-0.5% Si, 0.01-1% Sn, 0.01-
0.5% B, 0.001-0.1% Re and copper, carry out mixed smelting, then by obtained ingot casting peeling, forge;Finally will forging
Blank drawing after beating, repeats Drawing-anneal at least 2 times, until the wire of cupro-nickel 19 of specification needed for obtaining;The resin is terpene
Olefine resin, is to sequentially add australene, water entrainer and catalyst in cavitation machine, adjust successively to the first temperature, second temperature,
3rd temperature, the 4th temperature carry out polymerisation, and washing removes water entrainer, what Filtration of catalyst was made;Wherein, the band
Aqua is toluene, and the catalyst is manganese dioxide;The rubber is silicon rubber, is by methyl vinyl silicone rubber, stearic acid
Calcium, white carbon, dimethyldiethoxysilane are added in kneader, to obtain molding materials;Molding materials are heated to 150
~160 degrees Celsius, vacuumize, and be incubated 2~3 hours;Molding materials temperature is reduced to 80 degrees Celsius;Added into kneader
Calcium carbonate, cerium oxide, isooctyl acid iron organic solution, Vinyl MQ silicon resin and silica flour, to obtain silicone rubber compounds;And
By silicone rubber compounds and 2,5- dimethyl -2,5- bishexane is added after opening rubber mixing machine mixing uniformly, is put in vulcanizing press
Silicon rubber is obtained after temperature vulcanizes 5~15 minutes for 170 degrees Celsius.
A kind of preparation technology of composite surface material for charging pile, comprises the following steps:
(1) dispensing:By resin, rubber, ceramics, graphite, carbon, glass fibre, carbon fiber, boron fibre, aramid fiber, carbonization
Silica fibre, asbestos fibre, whisker, wire, hard particulates, weigh according to aforementioned proportion, standby;
(2) grind:By the resin after proportionally being weighed in step (1), rubber, ceramics, graphite, carbon, whisker, wire
And hard particulates, pass sequentially through lapping device and be ground, obtain fine powder, it is standby;
(3) mix:By the glass fibre after proportionally being weighed in step (1), carbon fiber, boron fibre, aramid fiber, carbon
SiClx fiber and asbestos fibre, are pre-mixed, and obtain mixture one, and being ground in step (2) is then obtained fine powder, plus
Enter into mixture one, raw mixture is obtained after screening;
(4) stir:The raw mixture obtained in step (3) is added into water entrainer and catalyst, entered by agitating device
Row is sufficiently stirred for, and remembers composite;
(5) tinning:By the composite after being sufficiently stirred in step (4), tinning is carried out.
According to above-mentioned technical proposal, the regulation during stirring is divided into four sections, constant velocity stage, accelerates boost phase, at the uniform velocity
Temperature rise period and deceleration buck stage, the speed of the constant velocity stage are maintained at 30 revs/min, accelerate average rate be 8 turns/
Minute;The speed of the at the uniform velocity temperature rise period is maintained at 300 revs/min of constant, 5 DEG C/min of temperature-averaging acceleration;It is described to slow down
The temperature of buck stage is first down to 200 revs/min, then keeps 20min, and temperature is down to 30 DEG C from 200 DEG C, and cooling Mean Speed is
4℃/min;The screening net of screening in the step (3), is a kind of screening net of 50-80 mesh;The device of the tinning
For automatic can filler.
Embodiment 3:
Referring to Fig. 1, the present invention provides a kind of composite surface material for charging pile, the composite surface material is to adopt
Composite surface material is prepared with multigroup raw material, composite surface material raw material composition is:Resin 20%, rubber 6%, ceramics 3%, stone
Ink 6%, carbon 6%, glass fibre 10%, carbon fiber 15%, boron fibre 20%, aramid fiber 4%, silicon carbide fibre 3%, asbestos
Fiber 6%, whisker 7%, wire 3%, hard particulates 3%, remaining be water.
According to above-mentioned technical proposal, the wire is the wire of cupro-nickel 19, is by the 18-20% according to percentage by weight
Ni, 0.01-0.6% Mn, 0.1-1% Fe, 0.1-1% Al, 0.01-0.5% Si, 0.01-1% Sn, 0.01-
0.5% B, 0.001-0.1% Re and copper, carry out mixed smelting, then by obtained ingot casting peeling, forge;Finally will forging
Blank drawing after beating, repeats Drawing-anneal at least 2 times, until the wire of cupro-nickel 19 of specification needed for obtaining;The resin is terpene
Olefine resin, is to sequentially add australene, water entrainer and catalyst in cavitation machine, adjust successively to the first temperature, second temperature,
3rd temperature, the 4th temperature carry out polymerisation, and washing removes water entrainer, what Filtration of catalyst was made;Wherein, the band
Aqua is toluene, and the catalyst is manganese dioxide;The rubber is silicon rubber, is by methyl vinyl silicone rubber, stearic acid
Calcium, white carbon, dimethyldiethoxysilane are added in kneader, to obtain molding materials;Molding materials are heated to 150
~160 degrees Celsius, vacuumize, and be incubated 2~3 hours;Molding materials temperature is reduced to 80 degrees Celsius;Added into kneader
Calcium carbonate, cerium oxide, isooctyl acid iron organic solution, Vinyl MQ silicon resin and silica flour, to obtain silicone rubber compounds;And
By silicone rubber compounds and 2,5- dimethyl -2,5- bishexane is added after opening rubber mixing machine mixing uniformly, is put in vulcanizing press
Silicon rubber is obtained after temperature vulcanizes 5~15 minutes for 170 degrees Celsius.
A kind of preparation technology of composite surface material for charging pile, comprises the following steps:
(1) dispensing:By resin, rubber, ceramics, graphite, carbon, glass fibre, carbon fiber, boron fibre, aramid fiber, carbonization
Silica fibre, asbestos fibre, whisker, wire, hard particulates, weigh according to aforementioned proportion, standby;
(2) grind:By the resin after proportionally being weighed in step (1), rubber, ceramics, graphite, carbon, whisker, wire
And hard particulates, pass sequentially through lapping device and be ground, obtain fine powder, it is standby;
(3) mix:By the glass fibre after proportionally being weighed in step (1), carbon fiber, boron fibre, aramid fiber, carbon
SiClx fiber and asbestos fibre, are pre-mixed, and obtain mixture one, and being ground in step (2) is then obtained fine powder, plus
Enter into mixture one, raw mixture is obtained after screening;
(4) stir:The raw mixture obtained in step (3) is added into water entrainer and catalyst, entered by agitating device
Row is sufficiently stirred for, and remembers composite;
(5) tinning:By the composite after being sufficiently stirred in step (4), tinning is carried out.
According to above-mentioned technical proposal, the regulation during stirring is divided into four sections, constant velocity stage, accelerates boost phase, at the uniform velocity
Temperature rise period and deceleration buck stage, the speed of the constant velocity stage are maintained at 30 revs/min, accelerate average rate be 8 turns/
Minute;The speed of the at the uniform velocity temperature rise period is maintained at 300 revs/min of constant, 5 DEG C/min of temperature-averaging acceleration;It is described to slow down
The temperature of buck stage is first down to 200 revs/min, then keeps 20min, and temperature is down to 30 DEG C from 200 DEG C, and cooling Mean Speed is
4℃/min;The screening net of screening in the step (3), is a kind of screening net of 50-80 mesh;The device of the tinning
For automatic can filler.
Based on above-mentioned, it is an advantage of the current invention that with high resilience and relatively low compression set performance, having
Excellent corrosion resistance, high-tensile and elongation percentage, and with higher resistivity, while the preparation of the present invention is when shorter
It is interior to complete, and feed stock conversion is high, side reaction is few, product purity is higher.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
Any modifications, equivalent substitutions and improvements made within refreshing and principle etc., should be included in the scope of the protection.
Claims (8)
1. a kind of composite surface material for charging pile, it is characterised in that:The composite surface material is to use multigroup raw material
Composite surface material is prepared, composite surface material raw material composition is:Resin 10%-20%, rubber 4%-6%, ceramics 1%-
3%th, graphite 4%-6%, carbon 4%-6%, glass fibre 8%-10%, carbon fiber 9%-15%, boron fibre 10%-20%, virtue
It is synthetic fibre fiber 2%-4%, silicon carbide fibre 1%-3%, asbestos fibre 4%-6%, whisker 5%-7%, wire 1%-3%, hard
Matter particulate 1%-3%, remaining be water.
2. a kind of composite surface material for charging pile according to claim 1, it is characterised in that:The wire is
The wire of cupro-nickel 19, is Mn, 0.1-1% of Ni, 0.01-0.6% by the 18-20% according to percentage by weight Fe, 0.1-
1% Al, 0.01-0.5% Si, 0.01-1% Sn, 0.01-0.5% B, 0.001-0.1% Re and copper, are mixed
Melting is closed, then by obtained ingot casting peeling, is forged;Rear blank drawing will be finally forged, Drawing-anneal is repeated at least 2 times, directly
The wire of cupro-nickel 19 of specification to needed for obtaining.
3. a kind of composite surface material for charging pile according to claim 1, it is characterised in that:The resin is terpene
Olefine resin, is to sequentially add australene, water entrainer and catalyst in cavitation machine, adjust successively to the first temperature, second temperature,
3rd temperature, the 4th temperature carry out polymerisation, and washing removes water entrainer, what Filtration of catalyst was made;Wherein, the band
Aqua is toluene, and the catalyst is manganese dioxide.
4. a kind of composite surface material for charging pile according to claim 1, it is characterised in that:The rubber is silicon
Rubber, is to add methyl vinyl silicone rubber, calcium stearate, white carbon, dimethyldiethoxysilane in kneader, so as to
Obtain molding materials;Molding materials are heated to 150~160 degrees Celsius, vacuumized, and are incubated 2~3 hours;By molding materials
Temperature is reduced to 80 degrees Celsius;Calcium carbonate, cerium oxide, isooctyl acid iron organic solution, vinyl MQ silicon tree are added into kneader
Fat and silica flour, to obtain silicone rubber compounds;And silicone rubber compounds and 2,5- dimethyl -2,5- bishexanes are added into opening
After the mixing of formula rubber mixing machine is uniform, puts in vulcanizing press and obtain silicon rubber after temperature vulcanizes 5~15 minutes for 170 degrees Celsius.
5. a kind of preparation technology of composite surface material for charging pile, it is characterised in that:Comprise the following steps:
(1) dispensing:Resin, rubber, ceramics, graphite, carbon, glass fibre, carbon fiber, boron fibre, aramid fiber, carborundum is fine
Dimension, asbestos fibre, whisker, wire, hard particulates, weigh according to aforementioned proportion, standby;
(2) grind:By the resin after proportionally being weighed in step (1), rubber, ceramics, graphite, carbon, whisker, wire and hard
Matter particulate, passes sequentially through lapping device and is ground, and obtains fine powder, standby;
(3) mix:By the glass fibre after proportionally being weighed in step (1), carbon fiber, boron fibre, aramid fiber, carborundum
Fiber and asbestos fibre, are pre-mixed, and obtain mixture one, and being ground in step (2) is then obtained fine powder, is added to
In mixture one, raw mixture is obtained after screening;
(4) stir:The raw mixture obtained in step (3) is added into water entrainer and catalyst, filled by agitating device
Divide stirring, remember composite;
(5) tinning:By the composite after being sufficiently stirred in step (4), tinning is carried out.
6. a kind of preparation technology of composite surface material for charging pile according to claim 5, it is characterised in that:Institute
Regulation when stating stirring is divided into four sections, and constant velocity stage, acceleration boost phase, at the uniform velocity temperature rise period and deceleration buck stage are described
The speed of constant velocity stage is maintained at 30 revs/min, and it is 8 revs/min to accelerate average rate;The speed of the at the uniform velocity temperature rise period
It is maintained at 300 revs/min of constant, 5 DEG C/min of temperature-averaging acceleration;The temperature of the deceleration buck stage is first down to 200 revs/min
Clock, then 20min is kept, temperature is down to 30 DEG C from 200 DEG C, and cooling Mean Speed is 4 DEG C/min.
7. a kind of preparation technology of composite surface material for charging pile according to claim 5, it is characterised in that:Institute
The screening net of the screening in step (3) is stated, is a kind of screening net of 50-80 mesh.
8. a kind of preparation technology of composite surface material for charging pile according to claim 5, it is characterised in that:Institute
The device for stating tinning is automatic can filler.