CN107081868A - A kind of low-temperature setting technique of drum-type brake pad - Google Patents
A kind of low-temperature setting technique of drum-type brake pad Download PDFInfo
- Publication number
- CN107081868A CN107081868A CN201710400773.2A CN201710400773A CN107081868A CN 107081868 A CN107081868 A CN 107081868A CN 201710400773 A CN201710400773 A CN 201710400773A CN 107081868 A CN107081868 A CN 107081868A
- Authority
- CN
- China
- Prior art keywords
- drum
- brake pad
- low
- temperature setting
- type brake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low-temperature setting technique of drum-type brake pad, comprise the following steps:A) mix, it is b) die-filling, c) once heat, d) reheating, e) cool down.The present invention coordinates Electromagnetic Heating by the way that auxiliary material is added in formula so that auxiliary material can improve temperature lifting speed, so as to save the time to a certain extent in heat production under electromagnetic action during Electromagnetic Heating;Addition novolac epoxy resin can effectively reduce solidification temperature, and curing rate is fast, greatlys save the energy, solidify the spent time while reducing, improve production efficiency.
Description
【Technical field】
The present invention relates to the technical field of the technical field of brake block, particularly brake block low-temperature setting.
【Background technology】
Brake is that the brake on automobile on an important part, automobile is broadly divided into drum-type and disc type.In drum brakes
Drum-type brake pad can be installed.Existing drum-type brake pad has a LOTES process in process of production.Existing low temperature
Of a relatively high, the energy for not only needing consumption more of the temperature of heating is needed in solidification process, at the same it is time-consuming also relatively long,
It is unfavorable for the raising of production efficiency.
【The content of the invention】
The purpose of the present invention is exactly to solve the problems of the prior art, proposes a kind of low-temperature solid chemical industry of drum-type brake pad
Skill, can reduce solidification temperature, while the time also can be saved.
To achieve the above object, the present invention proposes a kind of low-temperature setting technique of drum-type brake pad, comprises the following steps:
A) mix:Mixing is stirred by being added in agitating device for producing the basic components of brake block, in stirring
During addition auxiliary material and curing agent, auxiliary material is at least one of steel fibre and iron powder, and curing agent is epoxy novolac tree
Fat;
B) it is die-filling:Mixed liquor is poured into the mould with Electromagnetic Heating function;
C) once heat:Mixed liquor is heated to 55-65 DEG C using electromagnetic heating apparatus, continues 4-10 minutes;
D) reheating:Start after the completion of once heating and the content in mould is carried out with mould supporting pressurized equipment
Pressurization, while temperature is maintained into 90-100 DEG C, the heat-insulation pressure keeping time is 15-25 minutes;
E) cool down:Heat-insulation pressure keeping pulls out product after terminating from mould, by product cooling to normal temperature under normal temperature environment.
Preferably, the basic components for being used to produce brake block in the step a) mixing are Frication powder, barium sulfate, sulfuric acid
Calcium pyroborate, glass fibre, calcium hydroxide, calcium oxide, magnesia, liquid resin.
Preferably, the Electromagnetic Heating is provided with hermatic door, hermatic door is in air-tight state in internal heating space after closing.
Preferably, the novolac epoxy resin is bisphenol f type epoxy resin.
Preferably, the novolac epoxy resin and the mass ratio of basic components are 1:9-3:10.
Preferably, the auxiliary material and the mass ratio of basic components are 2:7-3:8.
Preferably, the auxiliary material is the mixture of steel fibre and iron powder, the mass ratio of steel fibre and iron powder is 1.5:
1-1:1。
Beneficial effects of the present invention:The present invention coordinates Electromagnetic Heating so that electromagnetism by the way that auxiliary material is added in formula
Auxiliary material can improve temperature lifting speed, so as to save the time to a certain extent in heat production under electromagnetic action during heating;
Addition novolac epoxy resin can effectively reduce solidification temperature, and curing rate is fast, greatlys save the energy, reduces simultaneously
Solidification the spent time, improve production efficiency.
The feature and advantage of the present invention will be described in detail by embodiment.
【Embodiment】
A kind of low-temperature setting technique of drum-type brake pad of the present invention, comprises the following steps:
A) mix:Mixing is stirred by being added in agitating device for producing the basic components of brake block, in stirring
During addition auxiliary material and curing agent, auxiliary material is at least one of steel fibre and iron powder, and curing agent is epoxy novolac tree
Fat;
B) it is die-filling:Mixed liquor is poured into the mould with Electromagnetic Heating function;
C) once heat:Mixed liquor is heated to 55-65 DEG C using electromagnetic heating apparatus, continues 4-10 minutes;
D) reheating:Start after the completion of once heating and the content in mould is carried out with mould supporting pressurized equipment
Pressurization, while temperature is maintained into 90-100 DEG C, the heat-insulation pressure keeping time is 15-25 minutes;
E) cool down:Heat-insulation pressure keeping pulls out product after terminating from mould, by product cooling to normal temperature under normal temperature environment.
The basic components for being used to produce brake block in the step a) mixing are Frication powder, barium sulfate, calcium sulfate crystal whiskers, glass
Glass fiber, calcium hydroxide, calcium oxide, magnesia, liquid resin, the Electromagnetic Heating are provided with hermatic door, and hermatic door is interior after closing
Portion heating space is in air-tight state, and the novolac epoxy resin is bisphenol f type epoxy resin, the novolac epoxy resin and base
The mass ratio of plinth component is 1:9-3:10, the mass ratio of the auxiliary material and basic components is 2:7-3:8, the auxiliary material is steel
The mass ratio of the mixture of fiber and iron powder, steel fibre and iron powder is 1.5:1-1:1.
The course of work of the present invention:
In the course of the work, auxiliary material is added in formula a kind of low-temperature setting technique of drum-type brake pad of the present invention, matches somebody with somebody
Close Electromagnetic Heating so that auxiliary material can improve temperature lifting speed, so that one in heat production under electromagnetic action during Electromagnetic Heating
Determine to have saved the time in degree;Addition novolac epoxy resin can effectively reduce solidification temperature, and curing rate is fast, saves significantly
About the energy, solidifies the spent time while reducing, improves production efficiency.
Above-described embodiment is the description of the invention, is not limitation of the invention, it is any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (7)
1. a kind of low-temperature setting technique of drum-type brake pad, it is characterised in that:Comprise the following steps:
A) mix:Mixing is stirred by being added in agitating device for producing the basic components of brake block, in whipping process
Middle addition auxiliary material and curing agent, auxiliary material is at least one of steel fibre and iron powder, and curing agent is novolac epoxy resin;
B) it is die-filling:Mixed liquor is poured into the mould with Electromagnetic Heating function;
C) once heat:Mixed liquor is heated to 55-65 DEG C using electromagnetic heating apparatus, continues 4-10 minutes;
D) reheating:Start after the completion of once heating and the content in mould is added with mould supporting pressurized equipment
Pressure, while temperature is maintained into 90-100 DEG C, the heat-insulation pressure keeping time is 15-25 minutes;
E) cool down:Heat-insulation pressure keeping pulls out product after terminating from mould, by product cooling to normal temperature under normal temperature environment.
2. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:Step a) the mixing
In be used for produce brake block basic components be Frication powder, barium sulfate, calcium sulfate crystal whiskers, glass fibre, calcium hydroxide, oxidation
Calcium, magnesia, liquid resin.
3. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:The Electromagnetic Heating is set
There are hermatic door, hermatic door to be in air-tight state in internal heating space after closing.
4. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:The epoxy novolac tree
Fat is bisphenol f type epoxy resin.
5. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:The epoxy novolac tree
Fat and the mass ratio of basic components are 1:9-3:10.
6. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:The auxiliary material and base
The mass ratio of plinth component is 2:7-3:8.
7. a kind of low-temperature setting technique of drum-type brake pad as claimed in claim 1, it is characterised in that:The auxiliary material is steel
The mass ratio of the mixture of fiber and iron powder, steel fibre and iron powder is 1.5:1-1:1.