CN107059206A - A kind of antipilling fabric containing mineral powder and preparation method thereof - Google Patents
A kind of antipilling fabric containing mineral powder and preparation method thereof Download PDFInfo
- Publication number
- CN107059206A CN107059206A CN201710228685.9A CN201710228685A CN107059206A CN 107059206 A CN107059206 A CN 107059206A CN 201710228685 A CN201710228685 A CN 201710228685A CN 107059206 A CN107059206 A CN 107059206A
- Authority
- CN
- China
- Prior art keywords
- parts
- mineral powder
- fibre
- fabric containing
- containing mineral
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antipilling fabric containing mineral powder and preparation method thereof.It is made up of the component of following parts by weight：90 100 parts of string, 40 60 parts of chemical fibre, 13 parts of mineral powder.The antipilling fabric of the present invention is made of string and chemical fibre blending, the smooth exquisiteness in surface, it is not easy to pollute pathogenic bacteria, and anti-pilling property is good, and service life is long, continuously using a few year not balling-ups.The mineral powder material source that the present invention is added is wide, and performance is good, and preparation method is simple, is adapted to large-scale industrial production.
Description
Technical field
The invention belongs to textile technology field, and in particular to a kind of antipilling fabric containing mineral powder and preparation method thereof.
Background technology
With the development of technology, the fabric of clothes has developed diversified form, from traditional pure cotton to chemical fibre, then
To chemical fibre and pure cotton blending, then to cotton ramie blended spinning, the cloth textile of preparation is not only accomplished warming, also had concurrently softly, smooth, still
The smooth cloth textile in surface is during frequent threading, and easy balling-up causes garment surface rough after balling-up, wearing
It is uncomfortable.
Patent 201410801036.X discloses a kind of Weaving method of anti-fluffing and anti-pilling fabric, fabric prepared by this method
Although the not balling-up in short time useful life, in prolonged use time also can pilling, and the fabric hold
Easy breed bacteria, long with to healthy unfavorable.
Patent 201210220124.1 discloses a kind of antipilling fabric, and the antipilling fabric includes the superiors, centre
Layer and orlop composition, the superiors are that polyester fiber and string blending are formed, and the intermediate layer is that polyolefin is fine
Dimension, the orlop is synthetic fibers.The fabric preparation method is complicated, and there is also in a short time using phozy but long-term use
The problem of fluffing.
The content of the invention
Durable fabric and preparation method thereof is used it is an object of the invention to provide a kind of smooth anti pilling.
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：90-100 parts of string, changes
Learn 40-60 parts of fiber, 1-3 parts of mineral powder.
The string is selected from cotton fiber, and sisal fiber, abaca fibre, abutilon fibre, monkey grass, coconut palm palm fibre is fine
One or more in dimension, ramee.
The chemical fibre is acrylic fibers, and terylene, polyester fiber, polypropylene fibre, viscose rayon, polyvinyl formal is fine
One or more in dimension, CUP.
Described mineral powder is selected from the one or more in obsidian powder, Fly-ash, petrified wood powder, aspidelite powder.
A kind of preparation method of the antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Mineral powder is put into solvent, stirred, the solution that mass concentration is 1-5% is made；
（2）According to parts by weight, 90-100 parts of strings and 40-60 parts of chemical fibres are chosen as raw material of fabric, then use
250-350 DEG C of high temperature carries out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5-6 hours, obtain anti pilling material
Material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The solvent is water, 30% ethanol water, 15% glycerin solution, 2% sulfuric acid solution or 1% hydrochloric acid solution.
Beneficial effects of the present invention:The antipilling fabric of the present invention is made of string and chemical fibre blending, table
The smooth exquisiteness in face, it is not easy to pollute pathogenic bacteria, and anti-pilling property is good, service life is long, continuously using a few year not balling-ups.
The mineral powder material source that the present invention is added is wide, and performance is good, and preparation method is simple, is adapted to large-scale industrial production.
Embodiment
With reference to specific embodiment, the present invention will be further described.
Embodiment 1
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：95 parts of cotton fiber, polyester fiber 45
Part, 2 parts of obsidian powder.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Obsidian powder is put into water, stirred, the solution that mass concentration is 3% is made；
（2）According to parts by weight, 95 parts of cotton fibers and 45 parts of polyester fibers are chosen as raw material of fabric, then using 300 DEG C
High temperature carries out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Embodiment 2
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：90 parts of abaca fibre, polypropylene fibre
40 parts, 1 part of Fly-ash.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Fly-ash is put into water, stirred, the solution that mass concentration is 1% is made；
（2）According to parts by weight, 90 parts of abaca fibres and 40 parts of polypropylene fibres are chosen as raw material of fabric, then using 250 DEG C
High temperature carry out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 6 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Embodiment 3
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：100 parts of sisal fiber, viscose rayon
60 parts, 3 parts of petrified wood powder.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Petrified wood powder is put into 30% ethanol water, stirred, the solution that mass concentration is 3% is made；
（2）According to parts by weight, 100 parts of sisal fibers and 60 parts of viscose rayons are chosen as raw material of fabric, then using 300 DEG C
High temperature carry out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Embodiment 4
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：96 parts of abutilon fibre, polyvinyl alcohol contracting
48 parts of formaldehyde fibers, 1 part of aspidelite powder.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Aspidelite powder is put into water, stirred, the solution that mass concentration is 3% is made；
（2）According to parts by weight, 96 parts of abutilon fibres and 48 parts of vinylons are chosen as raw material of fabric, then adopt
High temperature polymerization is carried out with 300 DEG C of high temperature, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Embodiment 5
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：96 parts of coconut fibre, CUP 48
Part, 1 part of vesuvian powder.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Vesuvian powder is put into water, stirred, the solution that mass concentration is 3% is made；
（2）According to parts by weight, 96 parts of coconut fibres and 48 parts of CUPs are chosen as raw material of fabric, then using 300 DEG C
High temperature carries out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Embodiment 6
A kind of antipilling fabric containing mineral powder, is made up of the component of following parts by weight：96 parts of coconut fibre, CUP 48
Part, 1 part of daylight stone flour.
The preparation method of the above-mentioned antipilling fabric containing mineral powder, is carried out in accordance with the following steps：
（1）Daylight stone flour is put into 15% glycerin solution, stirred, the solution that mass concentration is 3% is made；
（2）According to parts by weight, 96 parts of coconut fibres and 48 parts of CUPs are chosen as raw material of fabric, then using 300 DEG C
High temperature carries out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5 hours, obtain anti pilling material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
The web surface of above-mentioned preparation is smooth, and clothes is made, continuously wearing not balling-up in 5 years, nondiscolouring.
Claims (6)
1. a kind of antipilling fabric containing mineral powder, it is characterised in that be made up of the component of following parts by weight：String
90-100 parts, 40-60 parts of chemical fibre, 1-3 parts of mineral powder.
2. a kind of antipilling fabric containing mineral powder according to claim 1, it is characterised in that the string is selected from cotton
Flower fiber, sisal fiber, abaca fibre, abutilon fibre, monkey grass, coconut fibre, one kind in ramee or it is a kind of with
On.
3. a kind of antipilling fabric containing mineral powder according to claim 1, it is characterised in that the chemical fibre is nitrile
One kind in synthetic fibre, terylene, polyester fiber, polypropylene fibre, viscose rayon, vinylon, CUP or one
More than kind.
4. a kind of antipilling fabric containing mineral powder according to claim 1, it is characterised in that described mineral powder is selected from black
One or more in sunlight stone flour, Fly-ash, petrified wood powder, aspidelite powder.
5. a kind of preparation method of the antipilling fabric containing mineral powder, it is characterised in that carry out in accordance with the following steps：
（1）Mineral powder is put into solvent, stirred, the solution that mass concentration is 1-5% is made；
（2）According to parts by weight, 90-100 parts of strings and 40-60 parts of chemical fibres are chosen as raw material of fabric, then use
250-350 DEG C of high temperature carries out high temperature polymerization, then natural cooling obtains mixing material；
（3）By step（2）In obtained mixed cloth be immersed in step（1）In solution in 5-6 hours, obtain anti pilling material
Material；
（4）By step（3）In obtained anti pilling material be put into the spinneret of special-shaped spinneret orifice and carry out spinning, obtain resisting
Ball fiber；
（5）By step（4）In anti-pill fibre by the way of through knitting device textile process, obtain anti-fluffing and anti-pilling fabric.
6. the preparation method of the antipilling fabric containing mineral powder according to claim 5, it is characterised in that the solvent is
Water, 30% ethanol water, 15% glycerin solution, 2% sulfuric acid solution or 1% hydrochloric acid solution.