CN107057328A - A kind of medical refrigerator insulation material of low power consuming and preparation method - Google Patents
A kind of medical refrigerator insulation material of low power consuming and preparation method Download PDFInfo
- Publication number
- CN107057328A CN107057328A CN201710425203.9A CN201710425203A CN107057328A CN 107057328 A CN107057328 A CN 107057328A CN 201710425203 A CN201710425203 A CN 201710425203A CN 107057328 A CN107057328 A CN 107057328A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation material
- low power
- power consuming
- medical refrigerator
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to insulation material manufacturing technology field there is provided a kind of medical refrigerator insulation material of low power consuming and preparation method, the medical refrigerator insulation material of low power consuming includes the component of following parts by weight:50 75 parts of choysotile, 15 23 parts of sepiolite, 29 parts of expanded perlite, 11 15 parts of PPG, 11 15 parts of foaming agent, 11 15 parts of foaming stabiliser, 15 23 parts of polyurethane resin.It is an object of the invention to provide a kind of medical refrigerator insulation material of low power consuming and preparation method, the insulation material effectively reduces the thermal conductivity factor and refrigerator energy consumption of polyurethane foam, thermal conductivity factor can be in 16.0 17.5mW/mK, and with excellent low temperature resistant dimensional stability and higher compressive strength, it is environment-friendly, it can meet and use under the conditions of prolonged cold.
Description
Technical field
The invention belongs to insulation material manufacturing technology field, in particular it relates to a kind of medical refrigerator insulation material of low power consuming
And preparation method.
Background technology
In recent years, with the increasingly rise of life science and biological gene technology, the demand of the medical freezer product of low temperature
In ascendant trend year by year, the medical refrigerator demand of especially -86 DEG C of low temperature is maximum, the quilt in medical treatment, scientific research, biotechnology field
The preparation of low temperature environment and the low-temperature storage of material are widely used in, because the medical refrigerator cabinet internal-external temperature difference of low temperature is larger, therefore cabinet
Interior Temperature Distribution is generally uneven to have a strong impact on the quality and safety for preserving thing, simultaneously because polyurethane foam be chronically at compared with
Under low temperature conditions, there is higher requirement to Low-Temperature Size stability, compressive strength and the thermal conductivity factor of polyurethane foam, and
Common cyclopentane type combined polyether emphasis considers foaming agent security, while the foam density prepared is higher and size of foam is steady
Qualitative and heat insulating ability is poor, and work contraction distortion amount relatively large cause froth bed of the foam with the time under the conditions of prolonged cold
Thickness will be gradually reduced, and the performance such as thermal conductivity factor and compression strength of foam will all decrease, and polyurethane foam insulation is heat-insulated
Performance reduction is obvious, largely effects on heat insulation effect and adds energy consumption, causes the wasting of resources.
The content of the invention
For defect of the prior art, it is an object of the invention to provide a kind of medical refrigerator insulation material of low power consuming and system
Preparation Method, the insulation material effectively reduces the thermal conductivity factor and refrigerator energy consumption of polyurethane foam, and thermal conductivity factor can be in 16.0-
17.5mW/mK, and with excellent low temperature resistant dimensional stability and higher compressive strength, it is environment-friendly, it can meet long-term
Used under cryogenic conditions;Present invention simultaneously provides its preparation method.
There is provided a kind of low power consuming medical refrigerator insulation material according to an aspect of the present invention, the medical refrigerator insulation of low power consuming
Material includes the component of following parts by weight:
50-75 parts of choysotile,
15-23 parts of sepiolite,
2-9 parts of expanded perlite,
11-15 parts of PPG,
11-15 parts of foaming agent,
11-15 parts of foaming stabiliser,
15-23 parts of polyurethane resin.
Preferably, the medical refrigerator insulation material of the low power consuming includes the component of following parts by weight:
60-75 parts of choysotile,
15-21 parts of sepiolite,
5-9 parts of expanded perlite,
11-14 parts of PPG,
11-13 parts of foaming agent,
11-12 parts of foaming stabiliser,
15-22 parts of polyurethane resin.
Preferably, the medical refrigerator insulation material of the low power consuming includes the component of following parts by weight:
65 parts of choysotile,
17 parts of sepiolite,
6 parts of expanded perlite,
12 parts of PPG,
12 parts of foaming agent,
11 parts of foaming stabiliser,
17 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 90-100:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
Compared with prior art, the present invention has following beneficial effect:
(1)The medical refrigerator insulation material of low power consuming prepared by the present invention, the thermal conductivity factor of insulation material is in 16.0-17.5mW/m
K, monthly the low 5-8% of the more general insulation material of energy consumption, has saved the energy, while foam density is compared with pure cyclopentane systems, resists
Compressive Strength is higher, low temperature resistant dimensional stability is more preferable, it is possible to decrease foam global density 10-12%, the foam that the present invention is generated in addition
System itself has higher strength and toughness, and the adhesion strength with refrigerator box body is higher, is not in shelling lamination problem, bubble
The dimensional stability and good fluidity of foam, can meet the use requirement under the conditions of prolonged cold, and preparation method of the present invention is easy easily
Operation, production process three-waste free pollution, safety and environmental protection;
(2)The foaming agent added in insulation material of the present invention, compared with sodium acid carbonate, on the premise of equal consumption, Ke Yiyou
The coefficient of foaming of effect increase froth pulp and the shrinkage factor of product, the quality of the froth pulp of raising.Selected because molecular sieve has
Type suction-operated, can only binding molecule diameter be less than molecular sieve bore diameter material, and exclude can not enter duct material.Simultaneously
Molecular sieve can also determine the order of Preferential adsorption according to the polarity of different material molecule, and polarity molecule that is strong and easily polarizing is excellent
First it is adsorbed, and has adsorbed after the big molecule of polarity, the suction-operated of the molecule small to polarity weakens significantly, is not inhaled even
It is attached.The polarity of water is more much bigger than carbon dioxide, therefore molecular sieve Preferential adsorption moisture, even if molecular sieve adsorption carbon dioxide,
But after moisture is encountered, wherein the carbon dioxide adsorbed can also be replaced by water and be desorbed out.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.
Embodiment 1
A kind of medical refrigerator insulation material of low power consuming that the present embodiment is provided, the medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
75 parts of choysotile,
15 parts of sepiolite,
9 parts of expanded perlite,
11 parts of PPG,
15 parts of foaming agent,
11 parts of foaming stabiliser,
23 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 100:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
Embodiment 2
A kind of medical refrigerator insulation material of low power consuming that the present embodiment is provided, the medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
50 parts of choysotile,
23 parts of sepiolite,
2 parts of expanded perlite,
15 parts of PPG,
11 parts of foaming agent,
15 parts of foaming stabiliser,
15 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 90:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
Embodiment 3
A kind of medical refrigerator insulation material of low power consuming that the present embodiment is provided, the medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
75 parts of choysotile,
15 parts of sepiolite,
9 parts of expanded perlite,
11 parts of PPG,
13 parts of foaming agent,
11 parts of foaming stabiliser,
22 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 95:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
Embodiment 4
A kind of medical refrigerator insulation material of low power consuming that the present embodiment is provided, the medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
60 parts of choysotile,
21 parts of sepiolite,
5 parts of expanded perlite,
14 parts of PPG,
11 parts of foaming agent,
12 parts of foaming stabiliser,
15 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 95:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
Embodiment 5
A kind of medical refrigerator insulation material of low power consuming that the present embodiment is provided, the medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
65 parts of choysotile,
17 parts of sepiolite,
6 parts of expanded perlite,
12 parts of PPG,
12 parts of foaming agent,
11 parts of foaming stabiliser,
17 parts of polyurethane resin.
Preferably, the foaming agent is made up of bicarbonate and molecular sieve.
Preferably, the ratio between described bicarbonate and molecular sieve number is 90-100:1.
Preferably, the bicarbonate is sodium acid carbonate or saleratus.
Preferably, the foaming stabiliser is sulfonic surfactant.
Another aspect of the present invention provides a kind of preparation method of the medical refrigerator insulation material of low power consuming, the preparation side
Method comprises the following steps:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.
The specific embodiment of the present invention is described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (8)
1. a kind of medical refrigerator insulation material of low power consuming, it is characterised in that:The medical refrigerator insulation material of low power consuming is included such as
The component of lower parts by weight:
50-75 parts of choysotile,
15-23 parts of sepiolite,
2-9 parts of expanded perlite,
11-15 parts of PPG,
11-15 parts of foaming agent,
11-15 parts of foaming stabiliser,
15-23 parts of polyurethane resin.
2. the medical refrigerator insulation material of low power consuming according to claim 1, it is characterised in that:The medical refrigerator of low power consuming
Insulation material includes the component of following parts by weight:
60-75 parts of choysotile,
15-21 parts of sepiolite,
5-9 parts of expanded perlite,
11-14 parts of PPG,
11-13 parts of foaming agent,
11-12 parts of foaming stabiliser,
15-22 parts of polyurethane resin.
3. the medical refrigerator insulation material of low power consuming according to claim 2, it is characterised in that:The medical refrigerator of low power consuming
Insulation material includes the component of following parts by weight:
65 parts of choysotile,
17 parts of sepiolite,
6 parts of expanded perlite,
12 parts of PPG,
12 parts of foaming agent,
11 parts of foaming stabiliser,
17 parts of polyurethane resin.
4. the medical refrigerator insulation material of low power consuming according to claim 1, it is characterised in that:The foaming agent is by bicarbonate
Salt and molecular sieve composition.
5. the medical refrigerator insulation material of low power consuming according to claim 4, it is characterised in that:The bicarbonate and molecule
It is 90-100 to sieve the ratio between parts by weight:1.
6. the medical refrigerator insulation material of low power consuming according to claim 5, it is characterised in that:The bicarbonate is carbonic acid
Hydrogen sodium or saleratus.
7. the medical refrigerator insulation material of low power consuming according to claim 1, it is characterised in that:The foaming stabiliser is sulphur
The surfactant of acidic group.
8. the preparation method of the medical refrigerator insulation material of low power consuming as described in claim any one of 1-7, it is characterised in that:Institute
State method specific as follows:
PPG is weighed, choysotile, sepiolite, expanded perlite, foaming agent, foaming stabiliser are added thereto, is filled
Divide and stir into colloidal, stand 1-2h, you can.