CN107056047A - A kind of glass composition and its preparation method and application - Google Patents
A kind of glass composition and its preparation method and application Download PDFInfo
- Publication number
- CN107056047A CN107056047A CN201710428177.5A CN201710428177A CN107056047A CN 107056047 A CN107056047 A CN 107056047A CN 201710428177 A CN201710428177 A CN 201710428177A CN 107056047 A CN107056047 A CN 107056047A
- Authority
- CN
- China
- Prior art keywords
- weight
- glass composition
- glass
- sio
- zno
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present disclosure discloses a kind of glass composition, counted using the gross weight of the glass composition as 100%, the glass composition includes 55 65 weight % SiO2, 16 25 weight % Al2O3, 0.01 10 weight % B2O3, 9 18 weight % Na2O and 0.01 5 weight % ZnO;The glass composition is suitable for various working processes, chemical enhanced rear with higher shock resistance and bending strength.The disclosure additionally provides the preparation method of above-mentioned glass composition and its application in touch-screen is prepared, when being used to prepare the cover-plate glass of touch-screen after chemical enhanced using glass composition made from above-mentioned preparation method, touch panel device glass surface impact grinding can be effectively prevented.
Description
Technical field
This disclosure relates to strengthened glass technical field, in particular it relates to a kind of glass composition and preparation method thereof and should
With.
Background technology
Glass is always material indispensable during Display Technique develops, with the development of Display Technique, by chemical strong
The intensity of glass can be improved by changing the composition of change glass surface, and glass is more applied in the protection of display device.At present
Tablet personal computer, LCD TV, mobile phone, digital camera etc. are all equipped with touch-screen, and in use, touch-screen cover plate glass
Glass is prone to contact and rubbed, and adds casual delineation, touches, it is thick that resulting cut directly contributes touch screen surface
Rough, finish declines, and influences using effect, is more likely to result in screen rupture.
According to the demand in market, direction of the touch-screen cover-plate glass just gradually towards more high-quality is developed.The main body of its high-quality
Present surface stress is big, suitable, heat-resisting stress layer depth, heat shock resistance, it is frivolous it is suitable it is in large size in terms of.At present, carrying
Progress in terms of high toughness, reduction fragility is still barely satisfactory, does not there is breakthrough, the damage of touch-screen cover-plate glass
It is bad also to be caused more by damage-resistant energy deficiency.
Therefore good mechanical property after a kind of glass composition, reinforcing is needed badly, collapse resistance is anti-drop, can be prepared as high property
The touch-screen cover-plate glass of energy.
The content of the invention
The purpose of the disclosure is to provide a kind of glass combination composition formula, and the glass that the glass combination composition formula is prepared is fitted
Together in chemical enhanced, good mechanical property after reinforcing, collapse resistance, fall.
To achieve these goals, the disclosure provides a kind of glass composition, using the gross weight of the glass composition as
100% meter, the glass composition includes 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight %
B2O3, 9-18 weight % Na2O and 0.01-5 weight % ZnO.
In the glass composition that the disclosure is provided, SiO2It is the composition for constituting glass skeleton, SiO2Content is higher, resistance to
It can chemically increase with mechanical strength, the high temperature viscosity increase of glass, if SiO2Excessively, just it is difficult to the glass for obtaining material property length
Glass.SiO2Content is relatively low, is difficult to form glass, and strain point declines, coefficient of expansion increase, and acid resistance and alkali resistance can decline.
In view of the performances such as fusion temperature, crystallization ceiling temperature, glass expansion coefficient, mechanical strength, frit, the SiO of the disclosure2
Content is 55-65 weight %.
Al is introduced in the glass composition that the disclosure is provided2O3, non-bridging oxygen and Al form aluminum-oxygen tetrahedron, the volume
It is bigger than silicon-oxy tetrahedron, bigger gap is produced in glass structure, is conducive to ion exchange, finally causes chemical enhanced effect
Fruit is more preferably.But Al2O3Too high levels, it is difficult to found.On the contrary, Al2O3Content is too low, and the easy crystallization of glass, mechanical strength is relatively low
It is unfavorable for shaping, therefore the suitable Al of the disclosure2O3Content be 16-25 weight %.
Na is introduced in the glass composition that the disclosure is provided2O, Na are the main matters of ion exchange, pass through glass
In sodium ion and fused salt in potassium ion swap, the sodium ion allowed in radius larger potassium ion and glass is exchanged with each other
Position, so just generates squeezing action in glass surface, so as to reach the effect for improving strength of glass.Na2O belongs to outside network
Body, with fluxing action so that glass melting temperature is reduced, therefore the suitable Na of the disclosure2O content is 9-18 weight %.
B is introduced in the glass composition that the disclosure is provided2O3It can reduce glass viscosity, improve that glass is brittle and light
Through worry.Boron is made boron exist in the form of trihedral by zinc compressing in the present invention, boron epoxide our unit and silica base unit
The combination complex anion group more increasingly complex than boron oxygen group can be coupled to, boron atom can exist with planar design, non-bridging oxygen
Quantity increase.Glass is after chemical enhanced, when by foreign impacts, and boron oxygen trihedral produces sliding in glass, can be abundant
External force is laid down, glass shock resistance, the suitable B of the disclosure is improved2O3Content is 0.01-10 weight %.
ZnO is introduced in the glass composition that the disclosure is provided, Zn-ef ficiency is in the middle of cyberspace, to silica around
Tetrahedron plays accumulation, improves the Young's modulus of glass, improves stability, glass, increase ion-exchange speed and depth, this
Suitable ZnO content is disclosed for 0.01-5 weight %.
The disclosure additionally provides a kind of preparation method of glass composition, and this method is included in a heated condition, by glass
Melted, be homogenized after composition material mixing, moulding by casting and annealed, using the gross weight of the glass composition as 100%
Meter, the glass composition includes 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3、
9-18 weight % Na2O and 0.01-5 weight % ZnO.
The disclosure additionally provides the glass composition that preparation method as described above is prepared.
The disclosure additionally provides application of the glass composition as described above in touch-screen is prepared.
The disclosure additionally provides a kind of touch panel device using glass composition as described above.
By above-mentioned technical proposal, boron atom is oppressed by zinc atom in the glass composition that the disclosure is provided, and boron is former
Son exists with three-fold coordination, and the fragility for reducing glass is not susceptible to devitrification and is easy to vitrifying.The glass composition have compared with
The low coefficient of expansion and higher light transmittance, are suitable for various working processes;There is excellent impact resistance after chemical enhanced
Can and bending strength, compression stress is that the shock resistance of 52g steel balls highly is 1400-1750mm in 907-995MPa, falling ball impact test, curved
Qu Qiangdu is 2021-2689N, can effectively prevent from showing the impact of product glass surface, is relatively applied to make touch-screen cover plate
Glass.
Other feature and advantage of the disclosure will be described in detail in subsequent embodiment part.
Embodiment
Embodiment of this disclosure is described in detail below.It should be appreciated that described herein specific
Embodiment is merely to illustrate and explained the disclosure, is not limited to the disclosure.
In the disclosure, in the case where not making opposite explanation, the density of the glass composition is according to GB/
T7962.15-2010《The part of colouless optical glass method of testing the 20th:Density》Determined using Archimedes method.
In the disclosure, in the case where not making opposite explanation, the thermal coefficient of expansion of the glass composition is according to ASTM
E228-1985《The test method of solid material linear thermal expansion is determined with suprasil dilatometer》Measure is obtained.
In the disclosure, in the case where not making opposite explanation, the Young's modulus of the glass composition is according to GB/
T7962.15-2010《The part of colouless optical glass method of testing the 6th:Young's modulus, modulus of shearing and Poisson's ratio》Use resonance
Method is determined and obtained.
In the disclosure, in the case where not making opposite explanation, the acid resistance of the glass composition is according to GB/
T7962.15-2010《The part of colouless optical glass method of testing the 14th:Acid-resistant stability》Measure is obtained.
In the disclosure, in the case where not making opposite explanation, compression stress and the reinforcing depth of the glass composition
GB/T 18144-2008《Glass strain assay method》Measure is obtained.
In the disclosure, in the case where not making opposite explanation, the fracture toughness of the glass composition is according to GB4161-
2007《Metal material Plane Strain Fracture Toughness KICTest method》Measure is obtained.
In the disclosure, in the case where not making opposite explanation, the impact strength of the glass composition uses 52g's
Steel ball is determined and obtained.
In the disclosure, in the case where not making opposite explanation, the bending strength of the glass composition is according to JC-T
676-1997《Glass material bending strength test method》Measure is obtained.
In the disclosure, in the case where not making opposite explanation, the transmitance of the glass composition is according to GB/T5433-
1985《Domestic glass transmitance assay method》Measure is obtained.
Disclosure first aspect provides a kind of glass composition, is counted using the gross weight of the glass composition as 100%,
The glass composition includes 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3、9-18
Weight % Na2O and 0.01-5 weight % ZnO.
Boron atom is oppressed by zinc atom in the glass composition that the disclosure is provided, and boron atom exists with three-fold coordination, drop
The fragility of low glass is not susceptible to devitrification and is easy to vitrifying.The glass composition has the relatively low coefficient of expansion and higher
Light transmittance, be suitable for various working processes;There is excellent impact resistance and bending strength after chemical enhanced, compression should
Power is that the shock resistance of 52g steel balls is highly 1400-1750mm in 907-995MPa, falling ball impact test, and bending strength is 2021-2689N,
It can effectively prevent from showing the impact of product glass surface, relatively be applied to make touch-screen cover-plate glass.
According to the disclosure in a first aspect, mechanical performance in order to further lift glass composition, between parameters
Obtain under balance, preferable case, the glass composition includes 59-63 weight % SiO2, 18-22 weight % Al2O3、3-8
Weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO.
According to the first aspect of the disclosure, it is preferable that counted using the gross weight of the glass composition as 100%, the glass
Glass composition by 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight %
Na2O and 0.01-5 weight % ZnO compositions;Preferably, the glass composition by 59-63 weight % SiO2, 18-22 weight
Measure % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO compositions.
According to the disclosure in a first aspect, above-mentioned glass composition uses KNO in 420 DEG C3Strengthen depth after liquation reinforcing 4h
For 30-52 μm, compression stress is that the shock resistance of 52g steel balls is highly 1400-1750mm, bending in 907-995MPa, falling ball impact test
Intensity is 2021-2689N.
Disclosure second aspect provides a kind of preparation method of glass composition, and this method is included in a heated condition,
Will glass combination raw material mix after melted, be homogenized, moulding by casting and annealed, using the gross weight of the glass composition as
100% meter, is counted using the gross weight of the glass composition as 100%, and the glass composition includes 55-65 weight %'s
SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight % Na2O and 0.01-5 weight %'s
ZnO。
According to disclosure second aspect, in order to further lift the mechanical performance of glass composition, between parameters
Balance is obtained, the glass composition includes 59-63 weight % SiO2, 18-22 weight % Al2O3, 3-8 weight %
B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO.
According to disclosure second aspect, it is preferable that counted using the gross weight of the glass composition as 100%, the glass
Composition by 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight %
Na2O and 0.01-5 weight % ZnO compositions;Preferably, the glass composition by 59-63 weight % SiO2, 18-22 weight
Measure % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO compositions.
According to disclosure second aspect, the condition of the melting includes:Temperature is 1550-1670 DEG C, and the time is 4-10h;
Those skilled in the art can determine specific melting temperature and melting time according to actual conditions.
According to disclosure second aspect, the condition of the annealing includes:Temperature is 600-800 DEG C, and the time is 3-6h;Ability
Field technique personnel can determine specific annealing temperature and annealing time according to actual conditions.
The homogenizing and moulding by casting can use various methods commonly used in the art;Stirring can for example be passed through
Make that the bubble in the glass composition of melting is overflowed, each component is uniformly distributed, can in stainless steel mould moulding by casting, it is described
Step is step and parameter commonly used in the art with parameter, and the disclosure has no particular limits to this.
The disclosure third aspect provides the glass composition that preparation method as described above is prepared;The glass group
Compound is suitable for working process, and the disclosure has no particular limits for the method for working process, can routinely make for this area
Various working process modes, such as section, polishing and chemical tempering.
Disclosure fourth aspect provides application of the glass composition as described above in touch-screen is prepared.
According to disclosure fourth aspect, the glass composition is applied to that when preparing touch-screen chemical enhanced raising need to be carried out
Mechanical performance.The chemical enhanced method can be the conventional use of various chemical enhanced methods of those skilled in the art, this
It is open that this is had no particular limits;Preferably, the chemical enhanced condition includes:By the glass composition in forced fluid
Middle reinforcing 3-6h, temperature is 410-450 DEG C;It is highly preferred that the forced fluid is KNO3Liquation, without adding accelerator, protection
The assisted and strengthened composition such as agent.
The aspect of the disclosure the 5th provides at least one glassy layer in a kind of touch panel device, the touch panel device and used
Glass composition as described above.
The present invention is further described below by embodiment.
Table 1 lists the glass composition and its physical property (density, transmitance manufactured by press over system described in the disclosure
And the coefficient of expansion) and reinforcing after mechanical performance (compression stress, reinforcing depth, impact strength and bending strength).It is described
The step of preparation, includes:Glass composition is proportionally mixed, mixture is put into 1600-1670 DEG C of heating in platinum-rhodium crucible
7h, glass compositions melt body is obtained using platinum rod stirring homogenizing;The glass compositions melt body is poured into room in mould
The lower moulding by casting of temperature, is cooled to the glass composition workpiece after being poured into a mould after room temperature;By the glass composition workpiece in
600-670 DEG C of insulation 4h is made annealing treatment, and obtains annealed glass composition workpiece;By the annealed glass composition workpiece in
420 DEG C of KNO3The glass composition workpiece after 4h is strengthened is handled in liquation;Using the glass composition workpiece after reinforcing as
Sample determines mechanical strength.
Table 1
Glass is reduced compared with the glass composition that can be seen that disclosure offer according to the numeric ratio of each embodiment of the disclosure
Fragility, be not susceptible to devitrification and be easy to vitrifying, with the relatively low coefficient of expansion, be suitable for chemical enhanced;The glass group
The short texture of compound, while reinforcing depth is 30-52 μm after reinforcing, compression stress is 52g in 907-995MPa, falling ball impact test
Steel ball shock resistance is highly 1400-1750mm, and bending strength is 2021-2689N, can effectively prevent from showing product glass surface
Impact grinding, be not susceptible to devitrification, relatively be applied to make touch-screen cover-plate glass.
In embodiment of the present disclosure 7-15, the glass composition includes 59-63 weight % SiO2, 18-22 weight %
Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2During O and 0.8-3 weight % ZnO, its coefficient of expansion is not higher than
86×10-7/℃;Reinforcing depth is not less than 36.1 μm;Compression stress is 947-977MPa, and average value reaches 961.3MPa;Falling sphere
The shock resistance of 52g steel balls is highly 1600-1700mm in experiment;Bending strength is 2038-2346N, and average bending strength reaches
2189N.The glass composition parameters opened in this work in preferred scope are in a preferable scope, parameters
Equilibrium makes the glass composition have more superior performance.
The preferred embodiment of the disclosure described in detail above, still, the disclosure are not limited in above-mentioned embodiment
Detail, in the range of the technology design of the disclosure, a variety of simple variants can be carried out with technical scheme of this disclosure, this
A little simple variants belong to the protection domain of the disclosure.
It is further to note that each particular technique feature described in above-mentioned embodiment, in not lance
In the case of shield, it can be combined by any suitable means.In order to avoid unnecessary repetition, the disclosure to it is various can
The combination of energy no longer separately illustrates.
In addition, can also be combined between a variety of embodiments of the disclosure, as long as it is without prejudice to originally
Disclosed thought, it should equally be considered as disclosure disclosure of that.
Claims (13)
1. a kind of glass composition, it is characterised in that counted using the gross weight of the glass composition as 100%, the glass group
Compound includes 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight %
Na2O and 0.01-5 weight % ZnO.
2. glass composition according to claim 1, wherein, the glass composition includes 59-63 weight % SiO2、
18-22 weight % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO.
3. glass composition according to claim 1, wherein, counted using the gross weight of the glass composition as 100%, institute
State SiO of the glass composition by 55-65 weight %2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight
Measure % Na2O and 0.01-5 weight % ZnO compositions;Preferably, the glass composition by 59-63 weight % SiO2、18-
22 weight % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO compositions.
4. the glass composition according to any one in claim 1-3, wherein, the compression stress of the glass composition
For 907-995MPa, reinforcing depth is 30-52 μm, and the shock resistance of falling ball impact test 52g steel balls is highly 1400-1750mm, and bending is strong
Spend for 2021-2689N.
5. a kind of preparation method of glass composition, this method is included in a heated condition, after glass combination raw material is mixed
Melted, be homogenized, moulding by casting and being annealed, it is characterised in that being counted using the gross weight of the glass composition as 100%, institute
Stating glass composition includes 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight
Measure % Na2O and 0.01-5 weight % ZnO.
6. preparation method according to claim 5, wherein, the glass composition includes 59-63 weight % SiO2、18-
22 weight % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO.
7. preparation method according to claim 5, wherein, counted using the gross weight of the glass composition as 100%, it is described
Glass composition by 55-65 weight % SiO2, 16-25 weight % Al2O3, 0.01-10 weight % B2O3, 9-18 weight %
Na2O and 0.01-5 weight % ZnO compositions;Preferably, the glass composition by 59-63 weight % SiO2, 18-22 weight
Measure % Al2O3, 3-8 weight % B2O3, 12-16 weight % Na2O and 0.8-3 weight % ZnO compositions.
8. the preparation method according to any one in claim 5-7, wherein, the condition of the melting includes:Temperature is
1550-1670 DEG C, the time is 4-10h.
9. the preparation method according to any one in claim 5-7, wherein, the condition of the annealing includes:Temperature is
600-800 DEG C, the time is 3-6h.
10. the glass composition that the preparation method in claim 5-9 described in any one is prepared.
11. application of the glass composition in claim 1-4 and claim 10 described in any one in touch-screen is prepared.
12. application according to claim 11, wherein, the glass composition is applied to be changed when preparing touch-screen
Learn reinforcing;Preferably, the chemical enhanced condition includes:The glass composition is strengthened into 3-6h, temperature in forced fluid
For 410-450 DEG C;It is highly preferred that the forced fluid is KNO3Liquation.
13. a kind of touch panel device, it is characterised in that at least one glassy layer usage right requires 1- in the touch panel device
4 and claim 10 in glass composition described in any one.