CN107056002A - A kind of composite enhanced septic tank - Google Patents
A kind of composite enhanced septic tank Download PDFInfo
- Publication number
- CN107056002A CN107056002A CN201710330807.5A CN201710330807A CN107056002A CN 107056002 A CN107056002 A CN 107056002A CN 201710330807 A CN201710330807 A CN 201710330807A CN 107056002 A CN107056002 A CN 107056002A
- Authority
- CN
- China
- Prior art keywords
- parts
- septic tank
- concrete
- layer
- composite enhanced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of composite enhanced septic tank, is related to environment sanitation facility technical field, the composite enhanced septic tank is made up of, the nexine is made up of plastics, the plastics are by including following material nexine, intermediate layer and outer layer successively：Polytetrafluoroethylene (PTFE), ABS resin, fibre reinforced composites, paraffin, maleic anhydride, coupling agent, age resistor, the intermediate layer are steel bar layer；The outer layer is concrete layer, and the concrete is by following material composition：Cement, sand, kaolinite, epoxy resin, reinforcing agent, the composite strengthening septic tank of the present invention, both the problem of simple plastic material structural strength is low had been solved, concrete is solved again divides the problem of pond easily produces leakage, it is convenient with management, exempt from maintenance, cost performance height, the advantage of good economy performance, be adapted to wide popularization and application.
Description
Technical field
The present invention relates to environment sanitation facility technical field, and in particular to a kind of composite enhanced septic tank.
Background technology
With the enhancing of people's environmental consciousness, increasing urban and rural residents have taken leave of health lavatory not up to standard and used
The lavatory of hygienic practice.Septic tank is the important component of sanitary privy, is the equipment for handling excrement and being filtered precipitation.
Its principle is that solidfied material is decomposed in bottom of pond, and the aquation object on upper strata flows away, it is therefore prevented that line clogging into pipeline, to solidfied material
Body (rubbish such as excrement) has the time hydrolysis of abundance.
Existing septic tank is made up of the pond body capping plate being constructed with bricks or concretes, and is embedded in ground
Under.
But it was verified that existing brick or concreting septic tank be embedded in underground by slowly drained soil and steam,
Moisture immersion, soda acid salt corrosion easily corrosion spalling, easily infiltration, poor durability, and intensity decreases, it is fragile；Due to heat expansion
Shrinkage natural phenomena has been directed at septic tank and seepage, the continuous polluted underground water of liquid dung of seepage to some extent has occurred, gives people
Health care belt greatly endangers.
To avoid the seepage of septic tank, in the prior art, useful polypropylene as septic tank main material, but poly- third
Alkene easy aging in low temperature, so as to influence the service life of septic tank.
The content of the invention
(1) technical problem solved
In view of the shortcomings of the prior art, the invention provides a kind of composite enhanced septic tank so that with high intensity and
Excellent resistance to ag(e)ing, and with good resistance to acids and bases, buy in service life behind underground and extend.
(2) technical scheme
To realize object above, the present invention is achieved by the following technical programs：
A kind of composite enhanced septic tank, is made up of nexine, intermediate layer and outer layer successively, and the nexine is made up of plastics,
The plastics are by including following material：Polytetrafluoroethylene (PTFE), ABS resin, fibre reinforced composites, paraffin, maleic anhydride, coupling
Agent, age resistor.
The intermediate layer is steel bar layer；
The outer layer is concrete layer, and the concrete is by following material composition：Cement, sand, kaolinite, epoxy resin,
Reinforcing agent.
It is preferred that, the plastics are by including the material of following parts by weight：50~80 parts of polytetrafluoroethylene (PTFE), ABS resin 60~
100 parts, it is 15~25 parts of fibre reinforced composites, 10~15 parts of paraffin, 5~10 parts of maleic anhydride, 1~3 part of coupling agent, anti-old
2~5 parts of agent.
It is preferred that, the fibre reinforced materials is glass fibre, carbon fiber, silicon carbide whisker, calcium sulfate crystal whiskers, six metatitanic acids
Potassium whisker, ZnOw, poly- (butyl acrylate-styrene) whisker, one kind in poly- (4-HBA ester) whisker or
Numerous compositions.
It is preferred that, the age resistor is N- phenyl-alpha-naphthylamines, N- phenyl-beta-naphthylamines, N-N '-diphenyl-para-phenylene diamine, N- benzene
One kind in base-N '-cyclohexyl p-phenylenediamine, BHT, styrene phenol.
It is preferred that, the concrete by following parts by weight material composition：40~50 parts of cement, husky 50~60 parts, kaolinite
100~120 parts of stone, 20~30 parts of epoxy resin, 0.5~2 part of reinforcing agent.
It is preferred that, the reinforcing agent by following parts by weight material composition：80~88 parts of polyacrylamide copolymer solution,
5~15 parts of hydroxypropyl methyl cellulose, 5~10 parts of triethanolamine, 3~8 parts of methyl silicon sodium alcoholate, 3~8 parts of waterproofing agent.
It is preferred that, the solid content of the reinforcing agent is 23~28%, pH value 8.5~10.
(3) beneficial effect
Compared with prior art, the present invention has the following effects that：
(1) nexine uses the plastic layer that polytetrafluoroethylene (PTFE) and ABS composite material are made, and can effectively prevent the seepage of sewage,
And fibrous material is also added in plastic layer, the mechanical strength of plastics is enhanced, while plastic material has good resistance to acids and bases,
Being embedded to behind underground has lasting service life；
(2) steel bar layer has very high compression strength in the middle of, make the resistance to compression of septic tank and, intensity and impact resistance ability all
It is obviously improved；
(3) outer layer is made by concrete, the characteristics of it has cheap.
To sum up, composite strengthening septic tank of the invention, had both solved the problem of simple plastic material structural strength is low, again
Solve concrete and divide pond the problem of easily produce leakage, it is convenient with management, exempt from maintenance, cost performance high, good economy performance
Advantage, is adapted to wide popularization and application.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
There is the accompanying drawing used required in technology description to be briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, on the premise of not paying creative work, can be with
Other accompanying drawings are obtained according to these accompanying drawings.
Fig. 1：The sectional drawing of the composite enhanced septic tank of the present invention；
1st, plastics nexine, 2, middle steel bar layer, 3, concrete outer layer.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not making
The every other embodiment obtained under the premise of creative work, belongs to the scope of protection of the invention.
Embodiment 1：
A kind of composite enhanced septic tank, is made up of nexine, intermediate layer and outer layer successively, and the nexine is made up of plastics,
The plastics are by including following material：80 parts of polytetrafluoroethylene (PTFE), 100 parts of ABS resin, 8 parts of ZnOw, poly- (4- hydroxy benzenes
Formic acid esters) 10 parts of whisker, 10 parts of paraffin, 6 parts of maleic anhydride, 1 part of coupling agent, 5 parts of N- phenyl-alpha-naphthylamines；
The intermediate layer is steel bar layer；
The outer layer is concrete layer, and the concrete is by following material composition：50 parts of cement, husky 55 parts, kaolinite 120
Part, 22 parts of epoxy resin, 2 parts of reinforcing agent.
The reinforcing agent by following parts by weight material composition：80 parts of polyacrylamide copolymer solution, hydroxypropyl methyl
15 parts of cellulose, 5 parts of triethanolamine, 6 parts of methyl silicon sodium alcoholate, 8 parts of waterproofing agent.
The solid content of the reinforcing agent is 23~25%, pH value 8.5~9.5.
Embodiment 2：
A kind of composite enhanced septic tank, is made up of nexine, intermediate layer and outer layer successively, and the nexine is made up of plastics,
The plastics are by including following material：80 parts of polytetrafluoroethylene (PTFE), 80 parts of ABS resin, 5 parts of glass fibre, 10 parts of calcium sulfate crystal whiskers,
15 parts of paraffin, 10 parts of maleic anhydride, 3 parts of coupling agent, 2 parts of 2,6- di-t-butyl -4- cresols；
The intermediate layer is steel bar layer；
The outer layer is concrete layer, and the concrete is by following material composition：45 parts of cement, husky 50 parts, kaolinite 105
Part, 20 parts of epoxy resin, 0.5 part of reinforcing agent.
The reinforcing agent by following parts by weight material composition：88 parts of polyacrylamide copolymer solution, hydroxypropyl methyl
10 parts of cellulose, 8 parts of triethanolamine, 3 parts of methyl silicon sodium alcoholate, 8 parts of waterproofing agent.
The solid content of the reinforcing agent is 25~28%, pH value 9.5~10.
Embodiment 3：
A kind of composite enhanced septic tank, is made up of nexine, intermediate layer and outer layer successively, and the nexine is made up of plastics,
The plastics are by including following material：60 parts of polytetrafluoroethylene (PTFE), 60 parts of ABS resin, poly- (butyl acrylate-styrene) whisker 10
Part, 12 parts of glass fibre, 3 parts of silicon carbide whisker, 12 parts of paraffin, 5 parts of maleic anhydride, 1 part of coupling agent, N-N '-diphenyl are to benzene
3 parts of diamines.
The intermediate layer is steel bar layer；
The outer layer is concrete layer, and the concrete is by following material composition：50 parts of cement, husky 60 parts, kaolinite 100
Part, 30 parts of epoxy resin, 1 part of reinforcing agent.
The reinforcing agent by following parts by weight material composition：85 parts of polyacrylamide copolymer solution, hydroxypropyl methyl
15 parts of cellulose, 10 parts of triethanolamine, 8 parts of methyl silicon sodium alcoholate, 5 parts of waterproofing agent.
The solid content of the reinforcing agent is 25~27%, pH value 8.5~9.
To sum up, the embodiment of the present invention has the advantages that：The composite strengthening septic tank of the present invention, both solves list
The problem of pure plastic material structural strength is low, solves concrete and divides the problem of pond easily produces leakage, with manager again
Just, exempt from maintenance, cost performance height, the advantage of good economy performance, be adapted to wide popularization and application.
It should be noted that herein, such as first and second or the like relational terms are used merely to a reality
Body or operation make a distinction with another entity or operation, and not necessarily require or imply these entities or deposited between operating
In any this actual relation or order.Moreover, term " comprising ", "comprising" or its any other variant are intended to
Nonexcludability is included, so that process, method, article or equipment including a series of key elements not only will including those
Element, but also other key elements including being not expressly set out, or also include being this process, method, article or equipment
Intrinsic key element.In the absence of more restrictions, the key element limited by sentence "including a ...", it is not excluded that
Also there is other identical element in process, method, article or equipment including the key element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic；And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (7)
1. a kind of composite enhanced septic tank, it is characterised in that be made up of successively nexine, intermediate layer and outer layer；
The nexine is made up of plastics, and the plastics are by including following material：Polytetrafluoroethylene (PTFE), ABS resin, fiber-reinforced composite
Material, paraffin, maleic anhydride, coupling agent, age resistor；
The intermediate layer is steel bar layer；
The outer layer is concrete layer, and the concrete is by following material composition：Cement, sand, kaolinite, epoxy resin, enhancing
Agent.
2. composite enhanced septic tank as claimed in claim 1, it is characterised in that the plastics are by including following parts by weight
Material：50~80 parts of polytetrafluoroethylene (PTFE), 60~100 parts of ABS resin, 15~25 parts of fibre reinforced composites, paraffin 10~15
Part, 5~10 parts of maleic anhydride, 1~3 part of coupling agent, 2~5 parts of age resistor.
3. composite enhanced septic tank as claimed in claim 2, it is characterised in that the fibre reinforced materials is glass fibers
Dimension, carbon fiber, silicon carbide whisker, calcium sulfate crystal whiskers, crystal whisker of hexa potassium titanate, ZnOw, poly- (butyl acrylate-styrene)
One or more compositions in whisker, poly- (4-HBA ester) whisker.
4. composite enhanced septic tank as claimed in claim 3, it is characterised in that the age resistor be N- phenyl-alpha-naphthylamines,
N- phenyl-beta-naphthylamines, N-N '-diphenyl-para-phenylene diamine, N- phenyl-N '-cyclohexyl p-phenylenediamine, 2,6- di-t-butyl -4- first
One kind in phenol, styrene phenol.
5. composite enhanced septic tank as claimed in claim 4, it is characterised in that the concrete by following parts by weight thing
Matter is constituted：40~50 parts of cement, husky 50~60 parts, 100~120 parts of kaolinite, 20~30 parts of epoxy resin, reinforcing agent 0.5~2
Part.
6. composite enhanced septic tank as claimed in claim 5, it is characterised in that the reinforcing agent by following parts by weight thing
Matter is constituted：80~88 parts of polyacrylamide copolymer solution, 5~15 parts of hydroxypropyl methyl cellulose, 5~10 parts of triethanolamine,
3~8 parts of methyl silicon sodium alcoholate, 3~8 parts of waterproofing agent.
7. composite enhanced septic tank as claimed in claim 6, it is characterised in that the solid content of the reinforcing agent is 23~
28%, pH value 8.5~10.