CN107053802A - A kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction and preparation method thereof - Google Patents
A kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction and preparation method thereof Download PDFInfo
- Publication number
- CN107053802A CN107053802A CN201710325887.5A CN201710325887A CN107053802A CN 107053802 A CN107053802 A CN 107053802A CN 201710325887 A CN201710325887 A CN 201710325887A CN 107053802 A CN107053802 A CN 107053802A
- Authority
- CN
- China
- Prior art keywords
- film
- cpe
- layers
- head
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a kind of composite sheet hose construction, and more particularly to a kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction and preparation method thereof.Including pet layer, the surface of described pet layer is provided with CPE middle levels, the surface in described CPE middle levels is provided with PE layers, the surface of described PE layers is provided with CPE top layers, the surface on described CPE top layers is provided with silk-screen table ink layer, the back side of described pet layer is provided with inner-printing ink layer, the back side of described inner-printing ink layer is provided with VMPET layers, the back side of described VMPET layers be provided with CPE bottoms, between described pet layer and CPE middle levels, inner-printing ink layer and VMPET interlayers, VMPET layers AD layers are respectively equipped between CPE bottoms.A kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction and preparation method thereof compact conformation, and using effect substantially, saves the energy.
Description
Technical field
The present invention is a kind of composite sheet hose construction, and more particularly to a kind of highlighted high-barrier cosmetics are aluminized composite sheet
Hose construction and preparation method thereof.
Background technology
The either domestic or external product of cosmetics in the market, packaging is multifarious, wherein directly wrapping
The plastic material of dress cosmetics has plastic bottle, plastic casing, polybag, coextruded plastic flexible pipe etc., because coextruded plastic flexible pipe is used
Raw material is few, cost is relatively low, by the development of more than ten years, has already taken up the main flow of Cosmetic Market, has been mainly used in face cleaning
Product, skin care item and cosmetology product etc..Although coextruded plastic flexible pipe is at present Cosmetic Market main flow, there is production effect
Rate is low, barrier and antioxidant difference shortcoming.
Chinese patent 201110308680.X, discloses a kind of colored translucent BOPET aluminizers, it is characterised in that it is wrapped
The former film layer of aluminium coated, colour-wash primary coat coating, BOPET is included, the thickness of BOPET original film layers is 12 microns, colour-wash bottom
Coating layer is located at the centre of aluminium coated and the former film layers of BOPET；The colored translucent BOPET aluminizers are by following manufacturer's legal systems
：The first step：BOPET original film selections：Select the former films of BOPET that thickness is 12 microns；Second step：At gilt coating
Reason：The red toner of 0.05% ratio and the yellow toner of 0.4% ratio are added into coating, be sufficiently mixed it is uniform after
On coating machine, the coating that solid content is 0.7~1.0 gram/m is carried out to former film corona surface using the anilox roll of 200 mesh, is applied
1 ± 0.2 micron of the thickness of coating after the completion of cloth；The red toner and yellow toner are the limited public affairs of the color skill metallic pigments in Zhongshan city
The serial toner of department, the coating machine is the model THG2100 of the vast Machinery Co., Ltd. in Wenzhou coating machine；3rd step：
The former films of the BOPET for gilt carrying out are inserted into vacuum aluminum-plating equipment, you can evaporation boat is opened and is preheated to equipment setting value
Between 70%~85%, aluminium wire transmission is then turned on, transfer rate is controlled between 180~450mm/min, starts equipment winding
To speed >=3.5m/s, open equipment baffle plate and start evaporation, aluminium steam, which is condensed to, cools down the BOPET that winding is not stopped on main hub surface
On the coated face of former film；Aluminum layer thickness according to measured by the device of on-line determination micro-coating thickness change of aluminizing thin film
Winding speed is adjusted, winding speed is controlled between 10.5~14.0m/s, the thickness control of aluminium coated is in the Ethylmercurichlorendimide of 75 Ethylmercurichlorendimides~85
Between, until the former film entire volume productions of BOPET are finished, shut down, cool down evaporation boat, vacuum pumping, open a position and unload film, detect thickness of aluminizing
Degree, product evaporation terminates.
The content of the invention
The present invention mainly solves the deficiencies in the prior art, and compact conformation, performance is outstanding, further protection
A kind of highlighted high-barrier cosmetics of environment are aluminized composite sheet hose construction and preparation method thereof.
The above-mentioned technical problem of the present invention is mainly what is be addressed by following technical proposals：
A kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction, including pet layer, the surface of described pet layer
Provided with CPE middle levels, the surface in described CPE middle levels is provided with PE layers, and the surface of described PE layers is provided with CPE top layers, described CPE
The surface on top layer is provided with silk-screen table ink layer, and the back side of described pet layer is provided with inner-printing ink layer, described inner-printing ink layer
The back side be provided with VMPET layer, the back side of described VMPET layers is provided with CPE bottoms, between described pet layer and CPE middle levels, inner print
Ink layer and VMPET interlayers, VMPET layers are respectively equipped with AD layers between CPE bottoms；
The material of described pet layer is to be poly- to stupid naphthalate；
The material on described CPE top layers, CPE middle levels and CPE bottoms is respectively haloflex；
The material of described VMPET layers is aluminized mylar；
The material adhesive layer of described AD layers.
A kind of highlighted high-barrier cosmetics are aluminized the preparation method of composite sheet hose construction, are carried out according to the following steps：
(1) step：Polyethylene raw material, inflation film are provided；
(2) step：Polyester film is provided, it is vacuum aluminum-coated；
(3) step：Polyester film, printing are provided；
(4) step：Adhesive is provided, dry type is combined；
(5) step：Compound half product enters drying room curing reaction；
(6) step：Polyethylene raw material is provided, extrusion is compound；
(7) step：Cut by specification；
(8) step：Sheet surface film glazing；
(9) step：Silk-screen printing；
(10) step：Tubulation and Pipe Cutting；
(11) step：Head adds mouth；
(12) step：Screw capping；
Wherein, the polyethylene pellet described in (1) step is transparent, is made and a variety of requires many money transparent membranes；(2) institute
The polyester film stated is transparent, simultaneously by sided corona treatment, passes through chemically treated in corona surface, and in chemical treatment face
Carry out vacuum aluminum-coated；Aluminized mylar is made：Described in (3) step is printed in the corona surface of transparent polyester film
Brush；Described in (4) step is wherein a polyethylene film (1) step, the using adhesive by way of compound
(2) the polyester printing film of step, the aluminized mylar three-layer thin-film of (3) step are bonded together；Described in (5) step is handle
The finished product of (4) step enters drying room curing reaction and is completely formed semi-finished product；Described in (6) step be described in (1) step wherein
Carry out extruding to be combined between a film and the semi-finished product of (5) that sheet material is made；The sheet material (5) step described in (7) step
Cut into the specification of various width；Described in (8) step glazing is carried out in sheet surface.Described in (9) step in sheet surface
Gloss oil surface screen-printed；Described in (10) step is the longitudinal garden degree positioning of sheet material (9) step, and side heat-sealing shaping is made soft
Pipe, while cutting into the small flexible pipe of various length；Described in (11) step is that small flexible pipe one end is carried out head；(12) step institute
The screw capping on head stated.
Preferably, the polyethylene film described in (1) step, top layer requires high saturating, middle level requires high-stiffness, internal layer requirement
Low-temperature heat-sealing；
The corona surface of polyester film described in (2) step is, by chemically treated, Vacuum Deposition to be carried out in chemical treatment face
Aluminium；
Described in (3) step is printed on polyester film, is printed on polyethylene film, is solved the shallow net of printing and is lost
The problem of point；
Compound semi-finished product described in (4) (5) step, film and film interlaminar strength >=4N/15mm；
Compound semi-finished product described in (4) (5) step, employ aluminized mylar, resistance oxygen rate≤10cm3/ (m2
24h.0.1MPa)；
Described in (6) step is to use high temperature extruding technology, makes film and film interlaminar strength >=6N/15mm；
Being sheet surface glazing and carrying out silk-screen printing described in (8) step (9) step；
Tubulation apparatus former described in (10) step uses copper rod, and it is soft that edge sealing carries out cutting using high-frequency heat sealing simultaneously
Pipe；
Done described in (11) step mouth use high temperature head method, head temperature control at 160-180 DEG C, make sheet material with
Peel strength >=10N/15mm between head, high-adhesive-strength.
Preferably, the transparent polyethylene pellet described in (1) step, using more than three layers coextrusion film blowing equipment, blown film temperature
Three kinds of CPE top layers, CPE middle levels, the transparent membrane of CPE bottoms is made between 185-195 DEG C in degree control；It is saturating described in (2)
Bright polyester film, the face by sided corona treatment is chemically treated by cable roll and drying unit, and is entered in chemical treatment face
Row is vacuum aluminum-coated；Aluminized mylar (VMPET) is made：Described in (3) step is entered in the corona surface of transparent polyester film
Row printing, ink setting temperature control is at 60-90 DEG C；Described in (4) step is to utilize adhesive by way of dry type is compound,
50-80 DEG C of drying adhesive temperature control, wherein two polyethylene film of (1) step, the polyester printing film of (2) step,
The aluminized mylar four-level membrane of (3) step is bonded together；Described in (5) step is that the finished product of (4) step is entered drying room
Curing reaction is completely formed semi-finished product, and drying room temperature control is at 60 DEG C；Described in (6) step is its described in (1) step
In carry out that extrusion is compound to be made sheet material, the temperature difference in 6 areas of screw rod of extruder between a film and the semi-finished product of (5)
For 160 DEG C, 200 DEG C, 240 DEG C, 280 DEG C, 320 DEG C, 320 DEG C, the temperature of T-shaped mould head is set as 320 DEG C；Described in (7) step
The sheet material of (5) step is cut into the specification of various width；Described in (8) step (9) step sheet surface carry out glazing and
Silk-screen printing, using being UV ink, ultraviolet drying technology；Described in (10) step is the longitudinal garden degree of sheet material (9) step
Flexible pipe is made in positioning, the tuber of the dither mode of use, scrap (bridge) heat-sealing shaping, while cutting into various length by size
Small flexible pipe；Described in (11) step is that small flexible pipe one end is carried out head, and head temperature is set in 160-180 DEG C, makes head
Expect melt and dissolved situation, sheet material of fitting；The screw capping on head described in (12) step.
Advantage：A. production efficiency is high；B. production cost is low；C. good barrier property：D. antioxidant is good；C. have golden sense, it is attractive in appearance.
Therefore, a kind of highlighted high-barrier cosmetics for providing of the present invention are aluminized composite sheet hose construction and its preparation side
Method, compact conformation, using effect substantially, saves the energy.
Brief description of the drawings
Fig. 1 is the material Rotating fields schematic diagram of the present invention；
Fig. 2 is the preparation technology flow chart of the present invention.
Embodiment
Below by embodiment, and with reference to accompanying drawing, technical scheme is described in further detail.
Embodiment 1：As depicted in figs. 1 and 2, a kind of highlighted high-barrier cosmetics are aluminized composite sheet hose construction, including
Pet layer 1, the surface of described pet layer 1 is provided with CPE middle levels 2, and the surface in described CPE middle levels 2 is provided with PE layers 3, described PE
The surface of layer 3 is provided with CPE top layers 4, and the surface on described CPE top layers 4 is provided with silk-screen table ink layer 5, described pet layer 1
The back side is provided with inner-printing ink layer 6, and the back side of described inner-printing ink layer 6 is provided with VMPET layers 7, the back side of described VMPET layers 7
Provided with CPE bottoms 8, between described pet layer 1 and CPE middle levels 2, between inner-printing ink layer 6 and VMPET layers 7, VMPET layers 7 and CPE bottoms
AD layers 9 are respectively equipped between layer 8；
The material of described pet layer 1 is to be poly- to stupid naphthalate；
The material on described CPE top layers 4, CPE middle levels 2 and CPE bottoms 8 is respectively haloflex；
The material of described VMPET layers 7 is aluminized mylar；
The material adhesive layer of described AD layers 9.
A kind of highlighted high-barrier cosmetics are aluminized the preparation method of composite sheet hose construction, are carried out according to the following steps：
(1) step：Polyethylene raw material, inflation film are provided；
(2) step：Polyester film is provided, it is vacuum aluminum-coated；
(3) step：Polyester film, printing are provided；
(4) step：Adhesive is provided, dry type is combined；
(5) step：Compound half product enters drying room curing reaction；
(6) step：Polyethylene raw material is provided, extrusion is compound；
(7) step：Cut by specification；
(8) step：Sheet surface film glazing；
(9) step：Silk-screen printing；
(10) step：Tubulation and Pipe Cutting；
(11) step：Head adds mouth；
(12) step：Screw capping；
Wherein, the polyethylene pellet described in (1) step is transparent, is made and a variety of requires many money transparent membranes；(2) institute
The polyester film stated is transparent, simultaneously by sided corona treatment, passes through chemically treated in corona surface, and in chemical treatment face
Carry out vacuum aluminum-coated；Aluminized mylar is made：Described in (3) step is printed in the corona surface of transparent polyester film
Brush；Described in (4) step is wherein a polyethylene film (1) step, the using adhesive by way of compound
(2) the polyester printing film of step, the aluminized mylar three-layer thin-film of (3) step are bonded together；Described in (5) step is handle
The finished product of (4) step enters drying room curing reaction and is completely formed semi-finished product；Described in (6) step be described in (1) step wherein
Carry out extruding to be combined between a film and the semi-finished product of (5) that sheet material is made；The sheet material (5) step described in (7) step
Cut into the specification of various width；Described in (8) step glazing is carried out in sheet surface.Described in (9) step in sheet surface
Gloss oil surface screen-printed；Described in (10) step is the longitudinal garden degree positioning of sheet material (9) step, and side heat-sealing shaping is made soft
Pipe, while cutting into the small flexible pipe of various length；Described in (11) step is that small flexible pipe one end is carried out head；(12) step institute
The screw capping on head stated.
Polyethylene film described in (1) step, top layer requires high saturating, and middle level requires high-stiffness, and internal layer requires low-temperature heat-sealing；
The corona surface of polyester film described in (2) step is, by chemically treated, Vacuum Deposition to be carried out in chemical treatment face
Aluminium；
Described in (3) step is printed on polyester film, is printed on polyethylene film, is solved the shallow net of printing and is lost
The problem of point；
Compound semi-finished product described in (4) (5) step, film and film interlaminar strength >=4N/15mm；
Compound semi-finished product described in (4) (5) step, employ aluminized mylar, resistance oxygen rate≤10cm3/ (m2
24h.0.1MPa)；
Described in (6) step is to use high temperature extruding technology, makes film and film interlaminar strength >=6N/15mm；
Being sheet surface glazing and carrying out silk-screen printing described in (8) step (9) step；
Tubulation apparatus former described in (10) step uses copper rod, and it is soft that edge sealing carries out cutting using high-frequency heat sealing simultaneously
Pipe；
Done described in (11) step mouth use high temperature head method, head temperature control at 160-180 DEG C, make sheet material with
Peel strength >=10N/15mm between head, high-adhesive-strength.
Transparent polyethylene pellet described in (1) step, using more than three layers coextrusion film blowing equipment, blown film temperature control exists
Between 185-195 DEG C, three kinds of CPE top layers, CPE middle levels, the transparent membrane of CPE bottoms is made；Transparent polyester described in (2) is thin
Film, the face by sided corona treatment is chemically treated by cable roll and drying unit, and carries out Vacuum Deposition in chemical treatment face
Aluminium；Aluminized mylar (VMPET) is made：Described in (3) step is printed in the corona surface of transparent polyester film, oil
Black drying temperature control is at 60-90 DEG C；Described in (4) step is the drying adhesive using adhesive by way of dry type is compound
50-80 DEG C of temperature control, wherein two polyethylene film, the polyester printing film of (2) step, (3) step of (1) step
Aluminized mylar four-level membrane is bonded together；Described in (5) step is that the finished product of (4) step is entered drying room curing reaction is complete
Semi-finished product are made entirely, and drying room temperature control is at 60 DEG C；Described in (6) step is the wherein a film described in (1) step
Carry out that extrusion is compound to be made sheet material between the semi-finished product of (5), the temperature in 6 areas of screw rod of extruder is respectively 160 DEG C,
200 DEG C, 240 DEG C, 280 DEG C, 320 DEG C, 320 DEG C, the temperature of T-shaped mould head is set as 320 DEG C；Described in (7) step (5) step
Sheet material cut into the specifications of various width；Glazing and silk-screen printing are carried out in sheet surface described in (8) step (9) step,
Using being UV ink, ultraviolet drying technology；Described in (10) step is the longitudinal garden degree positioning of sheet material (9) step, is used
Dither mode tuber, scrap (bridge) heat-sealing shaping flexible pipe is made, while cutting into the small flexible pipe of various length by size；
Described in (11) step is that small flexible pipe one end is carried out head, and head temperature is set in 160-180 DEG C, makes head material thawing shape
Condition, sheet material of fitting；The screw capping on head described in (12) step.
Claims (4)
- The composite sheet hose construction 1. a kind of highlighted high-barrier cosmetics are aluminized, it is characterised in that：It is described including pet layer (1) The surface of pet layer (1) is provided with CPE middle levels (2), and the surface in described CPE middle levels (2) is provided with PE layers (3), described PE layers (3) Surface be provided with CPE top layers (4), the surface on described CPE top layers (4) is provided with silk-screen table ink layer (5), described pet layer (1) the back side is provided with inner-printing ink layer (6), and the back side of described inner-printing ink layer (6) is provided with VMPET layers (7), described The back side of VMPET layers (7) be provided with CPE bottoms (8), between described pet layer (1) and CPE middle levels (2), inner-printing ink layer (6) and It is respectively equipped with AD layers (9) between VMPET layers (7), between VMPET layers (7) and CPE bottoms (8)；The material of described pet layer (1) is to be poly- to stupid naphthalate；The material on described CPE top layers (4), CPE middle levels (2) and CPE bottoms (8) is respectively haloflex；The material of described VMPET layers (7) is aluminized mylar；The material adhesive layer of described AD layers (9).
- The preparation method of composite sheet hose construction 2. the highlighted high-barrier cosmetics described in a kind of utilization claim 1 are aluminized, It is characterized in that carrying out according to the following steps：(1) step：Polyethylene raw material, inflation film are provided；(2) step：Polyester film is provided, it is vacuum aluminum-coated；(3) step：Polyester film, printing are provided；(4) step：Adhesive is provided, dry type is combined；(5) step：Compound half product enters drying room curing reaction；(6) step：Polyethylene raw material is provided, extrusion is compound；(7) step：Cut by specification；(8) step：Sheet surface film glazing；(9) step：Silk-screen printing；(10) step：Tubulation and Pipe Cutting；(11) step：Head adds mouth；(12) step：Screw capping；Wherein, the polyethylene pellet described in (1) step is transparent, is made and a variety of requires many money transparent membranes；Described in (2) Polyester film is transparent, simultaneously by sided corona treatment, passes through chemically treated in corona surface, and is carried out in chemical treatment face Vacuum aluminum-coated；Aluminized mylar is made：Described in (3) step is printed in the corona surface of transparent polyester film； Described in (4) step is wherein a polyethylene film, (2) step (1) step using adhesive by way of compound Polyester printing film, the aluminized mylar three-layer thin-film of (3) step is bonded together；Described in (5) step is (4) The finished product of step enters drying room curing reaction and is completely formed semi-finished product；Described in (6) step is wherein a thin described in (1) step Carry out extruding to be combined between film and the semi-finished product of (5) that sheet material is made；The sheet material (5) step described in (7) step is cut into The specification of various width；Described in (8) step glazing is carried out in sheet surface.Described in (9) step in sheet surface gloss oil table Face silk-screen printing；Described in (10) step is the longitudinal garden degree positioning of sheet material (9) step, and flexible pipe is made in side heat-sealing shaping, together When cut into the small flexible pipes of various length；Described in (11) step is that small flexible pipe one end is carried out head；Described in (12) step The screw capping on head.
- The preparation method of composite sheet hose construction 3. a kind of highlighted high-barrier cosmetics according to claim 2 are aluminized, It is characterized in that：Polyethylene film described in (1) step, top layer requires high saturating, and middle level requires high-stiffness, and internal layer requires Low Temperature Thermal Envelope；The corona surface of polyester film described in (2) step is, by chemically treated, to be carried out in chemical treatment face vacuum aluminum-coated；Described in (3) step is printed on polyester film, is printed on polyethylene film, is solved the shallow net of printing and is lost a little Problem；Compound semi-finished product described in (4) (5) step, film and film interlaminar strength >=4N/15mm；Compound semi-finished product described in (4) (5) step, employ aluminized mylar, resistance oxygen rate≤10cm3/ (m2 24h.0.1MPa)；Described in (6) step is to use high temperature extruding technology, makes film and film interlaminar strength >=6N/15mm；Being sheet surface glazing and carrying out silk-screen printing described in (8) step (9) step；Tubulation apparatus former described in (10) step uses copper rod, and edge sealing carries out cutting flexible pipe simultaneously using high-frequency heat sealing；The method that mouth uses high temperature head is done described in (11) step, head temperature control makes sheet material and head at 160-180 DEG C Between peel strength >=10N/15mm, high-adhesive-strength.
- The preparation method of composite sheet hose construction 4. a kind of highlighted high-barrier cosmetics according to claim 2 are aluminized, It is characterized in that：Transparent polyethylene pellet described in (1) step, using more than three layers coextrusion film blowing equipment, blown film temperature control Between 185-195 DEG C, three kinds of CPE top layers, CPE middle levels, the transparent membrane of CPE bottoms is made；Transparent polyester described in (2) Film, the face by sided corona treatment is chemically treated by cable roll and drying unit, and carries out vacuum in chemical treatment face Aluminize；Aluminized mylar (VMPET) is made：Described in (3) step is printed in the corona surface of transparent polyester film, Ink setting temperature control is at 60-90 DEG C；Described in (4) step is that using adhesive by way of dry type is compound, glue dries Dry 50-80 DEG C of temperature control, wherein two polyethylene film, the polyester printing film of (2) step, (3) step of (1) step Aluminized mylar four-level membrane be bonded together；Described in (5) step is that the finished product of (4) step is entered drying room curing reaction Semi-finished product are completely formed, and drying room temperature control is at 60 DEG C；Described in (6) step is wherein a thin described in (1) step Carry out that extrusion is compound to be made sheet material between film and the semi-finished product of (5), the temperature in 6 areas of screw rod of extruder is respectively 160 DEG C, 200 DEG C, 240 DEG C, 280 DEG C, 320 DEG C, 320 DEG C, the temperature of T-shaped mould head is set as 320 DEG C；Described in (7) step (5) step Sheet material cut into the specifications of various width；Glazing and silk-screen printing are carried out in sheet surface described in (8) step (9) step, Using being UV ink, ultraviolet drying technology；Described in (10) step is the longitudinal garden degree positioning of sheet material (9) step, is used Dither mode tuber, scrap (bridge) heat-sealing shaping flexible pipe is made, while cutting into the small flexible pipe of various length by size； Described in (11) step is that small flexible pipe one end is carried out head, and head temperature is set in 160-180 DEG C, makes head material thawing shape Condition, sheet material of fitting；The screw capping on head described in (12) step.