CN107034412A - It is a kind of for nonmagnetic substance of power connection fitting and preparation method thereof - Google Patents
It is a kind of for nonmagnetic substance of power connection fitting and preparation method thereof Download PDFInfo
- Publication number
- CN107034412A CN107034412A CN201710240195.0A CN201710240195A CN107034412A CN 107034412 A CN107034412 A CN 107034412A CN 201710240195 A CN201710240195 A CN 201710240195A CN 107034412 A CN107034412 A CN 107034412A
- Authority
- CN
- China
- Prior art keywords
- nonmagnetic substance
- rare earth
- iron
- power connection
- connection fitting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of for nonmagnetic substance of power connection fitting and preparation method thereof, and nonmagnetic substance is made including following percentage composition component:Carbon 2.85 3.2%, silicon 1.68 1.80%, manganese 15 19%, copper 5.4 5.8%, chromium 10 16%, nitrogen 0.5 0.8%, rare earth 0.8 1.4%, sulphur≤0.04, phosphorus≤0.02, surplus is iron, the steps such as the present invention is bred by melting, skimming, spheroidization and inoculation, cast, Ageing Treatment are made, obtained nonmagnetic substance has excellent electricity, mechanical property, and processability is good, austenite content is up to more than 80%, magnetic conductivity is less than 1.15, tensile strength is more than 904MPa, and yield strength is more than 723MPa.
Description
Technical field
The present invention relates to electric armour clamp technical field, and in particular to a kind of nonmagnetic substance for power connection fitting and
Its preparation method.
Background technology
With the development of China's power industry, conveying capacitance is significantly increased, to suspension clamp, strain clamp, damper
Gradually cause the concern of people the problem of consumed energy in electricity transmission process Deng wire gold utensil.Due to above gold utensil malleable cast iron
Just come to be made with steel ferromagnetism.When, by alternating current, the magnetic that a closure is just formed on electric armour clamp is returned in wire
Road, ferromagnetic material remagnetization under action of alternating magnetic field, the change of its magnetic induction intensity always lags behind the change of magnetic field intensity
Change (hysteresis).During remagnetization, due to the steering repeatedly of magnetic domain, the molecular friction inside ferromagnetic material generates heat
And energy loss is caused, the electric armour clamp of this composition closed-loop path is led during remagnetization because magnetic domain is turned to repeatedly
The power attenuation of cause, is exactly so-called magnetic hystersis loss.According to the law of electromagnetic induction, this alternating magnetic field can also be produced inside gold utensil
Raw induced electromotive force and induced-current, due to the presence of ferrous materials resistance, necessarily lead to power loss, i.e. eddy-current loss.
According to Lenz's law and Faraday's electromagnetic induction law, the induced electromotive force and the size of current of transmission line of electricity produced in gold utensil
It is directly proportional.Traditional malleable cast iron, the relative permeability of steel electric armour clamp material are big, there is magnetic hysteresis vortex phenomenon, in transmission of electricity
Larger magnetic hysteresis and eddy-current loss is produced on circuit.Accordingly, it would be desirable to develop the electric power that a kind of magnetic conductivity is relatively low, mechanical property is strong
Gold utensil material.
The content of the invention
For above-mentioned problem, the present invention proposes a kind of nonmagnetic substance and its system for power connection fitting
Preparation Method, is bred, spheroidization and inoculation, cast, the step such as Ageing Treatment are made, obtained nonmagnetic substance tool by melting, skimming
There are excellent electricity, mechanical property, and processability is good, austenite content is up to more than 80%, and magnetic conductivity is less than 1.15, tensile strength
More than 904MPa, yield strength is more than 723MPa.
In order to realize above-mentioned purpose, the present invention uses following technical scheme:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 2.85-
3.2%th, silicon 1.68-1.80%, manganese 15-19%, copper 5.4-5.8%, chromium 10-16%, nitrogen 0.5-0.8%, rare earth 0.8-
1.4%th, sulphur≤0.04, phosphorus≤0.02, surplus is iron.
It is preferred that, it is made for the nonmagnetic substance of power connection fitting, including following percentage composition component:Carbon 3-
3.2%th, silicon 1.75-1.80%, manganese 18-19%, copper 5.6-5.8%, chromium 15-16%, nitrogen 0.6-0.8%, sulphur≤0.04, phosphorus≤
0.02, surplus is iron.
It is preferred that, in addition to aluminium 0-4%, aluminium is added in the form of being electrolysed aluminium sheet.
It is preferred that, the rare earth is mass ratio 1:4 cerium, erbium composition, the rare earth are added in the form of the oxide.
It is preferred that, for the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1620-1630 DEG C under nitrogen atmosphere, then by quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks
It is added thereto, sampling analysis, adjustment;
2) skim and breed:1440-1460 DEG C is cooled to, deslagging agent is sprayed to molten iron surface, 1-3min is stirred, deoxidation is taken off
Slag, then adds rare earth-stabilizedization inovulant inoculation thereto, is incubated 8-10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, nodularization is sequentially placed from lower to upper at bag bottom
Agent and rare earth inovulant, then molten iron is poured into nodularization bag, silicon titanate innoculant is added with stream during pouring into, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 900-1000 DEG C of quenching and preserving heat 1-2h, then in 500-700 DEG C of tempering insulation
1-2h, repeats above-mentioned quenching, is tempered once, air cooling of coming out of the stove.
It is preferred that, step 1) in before and after ferromanganese the ratio between addition be 2:1.
It is preferred that, step 2) deslagging agent consumption be molten steel quality 0.4-0.6%, rare earth-stabilizedization inovulant consumption be iron
The 0.6-1% of water quality.
It is preferred that, step 3) nodulizer be rare earth magnesium copper and iron nodulizer, consumption be molten steel quality 0.7-0.8%.
It is preferred that, step 3) middle rare earth inovulant and silicon titanate innoculant addition ratio be 1:1, it is the 0.3- of molten steel quality
0.5%.
Due to using above-mentioned technical scheme, the beneficial effects of the invention are as follows:The present invention is bred by melting, skimming, ball
The steps such as change is bred, poured into a mould, Ageing Treatment are made, using rational formula composition and process modification, obtained nonmagnetic substance
Good with excellent electricity, mechanical property, and processability, austenite content is up to more than 80%, and magnetic conductivity is less than 1.15, and tension is strong
Degree is more than 904MPa, and yield strength is more than 723MPa.
Nitrogenous content and high manganses and chromium content cast iron materials are made in the present invention, and wherein copper, manganese, chromium is conducive to expanding austenitic area, stable difficult to understand
Family name's body, Gao Meng, the solubility for being advantageously selected for improving nitrogen of chromium, not only increases obdurability by nitriding, strengthens impact resistance,
And high nitrogen is conducive to improving the stability of austenite, suppresses ferritic and formed, it is ensured that low magnetic property, improve the power of cast iron materials
Learn performance and corrosion stability.Carbon is graphite element, and silicon, copper can effectively weaken to promote graphite element or reduce Gao Meng and bring
Chilling tendency, and silicon, copper can reduce the formation of carbide, promote the stability of austenite structure.Coordinated using Multi inoculation
Nodularization, improves the homogenization of metallographic structure, is conducive to the reasonably combined of each component, and crystal grain thinning strengthens structure property, significantly
Improve the combination property of nonmagnetic substance.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the present invention is clearly and completely described.Based on embodiments of the invention, the common skill in this area
The every other embodiment that art personnel are obtained under the premise of creative work is not made, belongs to the model that the present invention is protected
Enclose.
Embodiment 1:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 3%, silicon
1.68%th, manganese 18%, copper 5.5%, chromium 14%, nitrogen 0.6%, rare earth 1.2%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.Also
Including aluminium 4%.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1620 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1450 DEG C are cooled to, the deslagging agent of molten steel quality 0.4% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.8% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.7% and the rare earth inovulant of molten steel quality 0.4%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.4% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 950 DEG C of quenching and preserving heat 1.5h, then in 600 DEG C of tempering insulation 1.5h, repeat
Above-mentioned quenching, be tempered once, air cooling of coming out of the stove.
Embodiment 2:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 2.95%, silicon
1.72%th, manganese 16%, copper 5.6%, chromium 15%, nitrogen 0.8%, rare earth 1%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.Also wrap
Include aluminium 2%.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1630 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1450 DEG C are cooled to, the deslagging agent of molten steel quality 0.6% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.6% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.7% and the rare earth inovulant of molten steel quality 0.3%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.3% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 900 DEG C of quenching and preserving heat 2h, then in 500 DEG C of tempering insulation 2h, repeat above-mentioned
Quench, be tempered once, air cooling of coming out of the stove.
Embodiment 3:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 2.85%, silicon
1.8%th, manganese 17%, copper 5.7%, chromium 10%, nitrogen 0.7%, rare earth 0.8%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.Also wrap
Include aluminium 3%.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1620 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1440 DEG C are cooled to, the deslagging agent of molten steel quality 0.5% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.8% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.8% and the rare earth inovulant of molten steel quality 0.5%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.5% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 1000 DEG C of quenching and preserving heat 1h, then in 550 DEG C of tempering insulation 1.5h, repeat
Above-mentioned quenching, be tempered once, air cooling of coming out of the stove.
Embodiment 4:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 3.1%, silicon
1.75%th, manganese 18%, copper 5.7%, chromium 12%, nitrogen 0.65%, rare earth 1.2%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1620 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1460 DEG C are cooled to, the deslagging agent of molten steel quality 0.5% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.7% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.8% and the rare earth inovulant of molten steel quality 0.4%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.4% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 1000 DEG C of quenching and preserving heat 1.5h, then in 700 DEG C of tempering insulation 1.5h, weight
Answer above-mentioned quenching, be tempered once, air cooling of coming out of the stove.
Embodiment 5:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 3.2%, silicon
1.75%th, manganese 19%, copper 5.6%, chromium 14%, nitrogen 0.5%, rare earth 1.1%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.Also
Including aluminium 1%.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1620 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1450 DEG C are cooled to, the deslagging agent of molten steel quality 0.4% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.7% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.8% and the rare earth inovulant of molten steel quality 0.3%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.3% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 950 DEG C of quenching and preserving heat 2h, then on 500 DEG C of tempering insulation 1.5h, repetition
State quenching, be tempered once, air cooling of coming out of the stove.
Embodiment 6:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 3.15%, silicon
1.7%th, manganese 15%, copper 5.8%, chromium 16%, nitrogen 0.75%, rare earth 1.4%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.Also
Including aluminium 2%.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1630 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1440 DEG C are cooled to, the deslagging agent of molten steel quality 0.4% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 1% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.8% and the rare earth inovulant of molten steel quality 0.3%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.3% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 950 DEG C of quenching and preserving heat 1h, then in 600 DEG C of tempering insulation 1h, repeat above-mentioned
Quench, be tempered once, air cooling of coming out of the stove.
Embodiment 7:
A kind of nonmagnetic substance for power connection fitting, including following percentage composition component are made:Carbon 3.05%, silicon
1.78%th, manganese 15%, copper 5.6%, chromium 15%, nitrogen 0.7%, rare earth 0.9%, sulphur≤0.04, phosphorus≤0.02, surplus is iron.
For the preparation method of the nonmagnetic substance of power connection fitting, step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part manganese is then added thereto
Iron, is warming up to 1630 DEG C, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added into it under nitrogen atmosphere
In, sampling analysis, adjustment;
2) skim and breed:1450 DEG C are cooled to, the deslagging agent of molten steel quality 0.6% is sprayed to molten iron surface, 1- is stirred
3min, deoxidation is skimmed, and the rare earth-stabilizedization inovulant inoculation of molten steel quality 0.8% is then added thereto, is incubated 8-
10min, obtains primary molten iron;
3) spheroidization and inoculation:Spheroidization and inoculation processing is carried out using method is poured in bag, molten iron is sequentially placed from lower to upper at bag bottom
The rare earth magnesium copper and iron nodulizer of quality 0.7% and the rare earth inovulant of molten steel quality 0.5%, then molten iron is poured into nodularization bag,
The silicon titanate innoculant of molten steel quality 0.5% is added during pouring into stream, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 900 DEG C of quenching and preserving heat 1.5h, then on 550 DEG C of tempering insulation 2h, repetition
State quenching, be tempered once, air cooling of coming out of the stove.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that:It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic;And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (9)
1. a kind of nonmagnetic substance for power connection fitting, it is characterised in that be made including following percentage composition component:Carbon
2.85-3.2%, silicon 1.68-1.80%, manganese 15-19%, copper 5.4-5.8%, chromium 10-16%, nitrogen 0.5-0.8%, rare earth 0.8-
1.4%th, sulphur≤0.04, phosphorus≤0.02, surplus is iron.
2. a kind of nonmagnetic substance for power connection fitting, it is characterised in that be made including following percentage composition component:Carbon
3-3.2%, silicon 1.75-1.80%, manganese 18-19%, copper 5.6-5.8%, chromium 15-16%, nitrogen 0.6-0.8%, sulphur≤0.04, phosphorus
≤ 0.02, surplus is iron.
3. the nonmagnetic substance according to claim 1 or 2 for power connection fitting, it is characterised in that:Also include aluminium
0-4%, aluminium is added in the form of being electrolysed aluminium sheet.
4. the nonmagnetic substance according to claim 1 or 2 for power connection fitting, it is characterised in that:The rare earth
For mass ratio 1:4 cerium, erbium composition, the rare earth are added in the form of the oxide.
5. the preparation method of the nonmagnetic substance according to claim 1 or 2 for power connection fitting, its feature exists
In step is as follows:
1) melt:The pig iron, steel scrap are added melting is heated in medium-frequency induction furnace, part ferromanganese is then added thereto,
1620-1630 DEG C is warming up under nitrogen atmosphere, then quartz sand, silicon nitride, ferrochrome, cathode copper and other surplus stocks are added it
In, sampling analysis, adjustment;
2) skim and breed:1440-1460 DEG C is cooled to, deslagging agent is sprayed to molten iron surface, 1-3min is stirred, deoxidation is skimmed, so
Add rare earth-stabilizedization inovulant inoculation thereto afterwards, be incubated 8-10min, obtain primary molten iron;
3) spheroidization and inoculation:Using bag in pour method carry out spheroidization and inoculation processing, bag bottom be sequentially placed from lower to upper nodulizer with
Rare earth inovulant, then molten iron is poured into nodularization bag, silicon titanate innoculant is added with stream during pouring into, two grades of molten iron are obtained;
4) pour into a mould:In the casting die of two grades of molten iron castings, first casting will be cooled down to obtain;
5) Ageing Treatment:By first casting first in 900-1000 DEG C of quenching and preserving heat 1-2h, then in 500-700 DEG C of tempering insulation 1-
2h, repeats above-mentioned quenching, is tempered once, air cooling of coming out of the stove.
6. the preparation method of the nonmagnetic substance according to claim 5 for power connection fitting, it is characterised in that:Step
It is rapid 1) in before and after ferromanganese the ratio between addition be 2:1.
7. the preparation method of the nonmagnetic substance according to claim 5 for power connection fitting, it is characterised in that:Step
Rapid 2) deslagging agent consumption is the 0.4-0.6% of molten steel quality, and rare earth-stabilizedization inovulant consumption is the 0.6-1% of molten steel quality.
8. the preparation method of the nonmagnetic substance according to claim 5 for power connection fitting, it is characterised in that:Step
Rapid 3) nodulizer is rare earth magnesium copper and iron nodulizer, and consumption is the 0.7-0.8% of molten steel quality.
9. the preparation method of the nonmagnetic substance according to claim 5 for power connection fitting, it is characterised in that:Step
Rapid 3) middle rare earth inovulant is 1 with silicon titanate innoculant addition ratio:1, it is the 0.3-0.5% of molten steel quality.