CN107033843A - Leak-stoppage agent for radiator - Google Patents
Leak-stoppage agent for radiator Download PDFInfo
- Publication number
- CN107033843A CN107033843A CN201710268776.5A CN201710268776A CN107033843A CN 107033843 A CN107033843 A CN 107033843A CN 201710268776 A CN201710268776 A CN 201710268776A CN 107033843 A CN107033843 A CN 107033843A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- leak
- radiator
- stoppage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Leak-stoppage agent for radiator, formula：20 35 parts of bath of glass, 15 20 parts of guar hydroxypropyltrimonium ammonium chloride, 24 parts of sodium tetraborate, 13 15 parts of lignocellulosic, 24 parts of pH value conditioning agent, 0.5 1.5 parts of anticorrosion and bactericidal agent, 0.8 1.7 parts of defoamer；Under stirring, bath of glass, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anticorrosion and bactericidal agent and defoamer are added, suspension is formed；It is 68 that pH value conditioning agent regulation pH value is added into suspension, filtering；Sodium tetraborate is added, is stirred 5 10 minutes, suspension is transformed into gel, produce Leak-stoppage agent.Guar hydroxypropyltrimonium ammonium chloride is added in raw material of the present invention, when pH value is 68, viscosity is maximum, is cross-linked into the characteristic of some larger material, so as to fast leak-stopping, and mending-leakage effect stability；Sodium tetraborate is added, gel is made, volume diminishes, and is convenient for carrying.
Description
Technical field
Field is maintained the present invention relates to auto repair, and in particular to a kind of Leak-stoppage agent for radiator.
Background technology
Coolant seepage inevitably occurs during automobile engine use.The common practice is by seepage part
Disintegration is changed, the carry out soldering that condition possesses.However, in the prior art, during cooling system seepage, vehicle is generally being used
During, during disintegration handling, laborious, expensive；Do not handle, can be probably due to radiating deficiency causes engine scuffing etc. serious
Accident.
The content of the invention
The purpose of the present invention be overcome in place of above-mentioned the deficiencies in the prior art there is provided a kind of mending-leakage effect it is good be used for automobile
The Leak-stoppage agent of water tank.
To reach above-mentioned purpose, the present invention is adopted the following technical scheme that：A kind of Leak-stoppage agent for radiator, by weight
Part includes following each component：20-35 parts of bath of glass, 15-20 parts of guar hydroxypropyltrimonium ammonium chloride, 2-4 parts of sodium tetraborate,
13-15 parts of lignocellulosic, 2-4 parts of pH value conditioning agent, 0.5-1.5 parts of anticorrosion and bactericidal agent, 0.8-1.7 parts of defoamer.
The preparation method of the Leak-stoppage agent is：
Step 1：Under stirring, bath of glass is added, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anti-
Rotten bactericide and defoamer, form suspension；
Step 2：PH value conditioning agent is added into suspension again, the pH value of regulation suspension is 6-8, filtering；
Step 3：Sodium tetraborate is eventually adding, is stirred 5-10 minutes, suspension is transformed into gel, produce Leak-stoppage agent.
Further, each component of the Leak-stoppage agent for radiator is calculated by weight is：20 parts of bath of glass, melon
18 parts of that glue hydroxypropyl-trimethyl ammonium chloride, 3 parts of sodium tetraborate, 13 parts of lignocellulosic, 4 parts of pH value conditioning agent, antisepsis and sterilization
0.8 part of agent, 0.8 part of defoamer.
Further, each component of the Leak-stoppage agent for radiator is calculated by weight is：28 parts of bath of glass, melon
15 parts of that glue hydroxypropyl-trimethyl ammonium chloride, 2 parts of sodium tetraborate, 14 parts of lignocellulosic, 2 parts of pH value conditioning agent, antisepsis and sterilization
0.5 part of agent, 1 part of defoamer.
Further, each component of the Leak-stoppage agent for radiator is calculated by weight is：35 parts of bath of glass, melon
20 parts of that glue hydroxypropyl-trimethyl ammonium chloride, 2 parts of sodium tetraborate, 15 parts of lignocellulosic, 3 parts of pH value conditioning agent, antisepsis and sterilization
1.5 parts of agent, 1.7 parts of defoamer.
Beneficial effects of the present invention：The present invention adds guar hydroxypropyltrimonium ammonium chloride in the feed, and pH value is 6-8
When, viscosity is maximum, is cross-linked into the characteristic of some larger material, so as to fast leak-stopping, and mending-leakage effect stability；Add tetraboric acid
Sodium, is made gel, and volume diminishes, and is convenient for carrying.
Further advantage, target and the feature of the present invention embodies part by following explanation, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Embodiment
With reference to the following example, the present invention is described in further detail, to make those skilled in the art with reference to specification
Word can be implemented according to this.
Embodiment 1
The present invention is calculated by weight for each component of the Leak-stoppage agent of radiator：20 parts of bath of glass, guar gum hydroxyl
18 parts of hydroxypropyltrimonium chloride, 3 parts of sodium tetraborate, 13 parts of lignocellulosic, 4 parts of pH value conditioning agent, anticorrosion and bactericidal agent 0.8
Part, 0.8 part of defoamer.
The preparation method of the Leak-stoppage agent is：
Step 1：Under stirring, bath of glass is added, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anti-
Rotten bactericide and defoamer, stirring form suspension after 2 hours；
Step 2：PH value conditioning agent is added into suspension again, the pH value of regulation suspension is 6, filtering；
Step 3：Sodium tetraborate is eventually adding, is stirred 5 minutes, suspension is transformed into gel, produce Leak-stoppage agent.
Embodiment 2
The present invention is calculated by weight for each component of the Leak-stoppage agent of radiator：28 parts of bath of glass, guar gum hydroxyl
15 parts of hydroxypropyltrimonium chloride, 2 parts of sodium tetraborate, 14 parts of lignocellulosic, 2 parts of pH value conditioning agent, anticorrosion and bactericidal agent 0.5
Part, 1 part of defoamer.
The preparation method of the Leak-stoppage agent is：
Step 1：Under stirring, bath of glass is added, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anti-
Rotten bactericide and defoamer, stirring form suspension after 1.5 hours；
Step 2：PH value conditioning agent is added into suspension again, the pH value of regulation suspension is 7, filtering；
Step 3：Sodium tetraborate is eventually adding, is stirred 8 minutes, suspension is transformed into gel, produce Leak-stoppage agent.
Embodiment 3
The present invention is calculated by weight for each component of the Leak-stoppage agent of radiator：35 parts of bath of glass, guar gum hydroxyl
20 parts of hydroxypropyltrimonium chloride, 2 parts of sodium tetraborate, 15 parts of lignocellulosic, 3 parts of pH value conditioning agent, anticorrosion and bactericidal agent 1.5
Part, 1.7 parts of defoamer.
The preparation method of the Leak-stoppage agent is：
Step 1：Under stirring, bath of glass is added, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anti-
Rotten bactericide and defoamer, stirring form suspension after 1 hour；
Step 2：PH value conditioning agent is added into suspension again, the pH value of regulation suspension is 8, filtering；
Step 3：Sodium tetraborate is eventually adding, is stirred 10 minutes, suspension is transformed into gel, produce Leak-stoppage agent.
Leak-stopping examination is carried out to the water tank of the aperture with diameter 0.8-1mm using the Leak-stoppage agent of the gained of the embodiment of the present invention 2
Test, result of the test is as follows：
Although embodiment of the present invention is disclosed as above, it is not restricted in specification and embodiment listed
With it can be applied to various suitable the field of the invention completely, can be easily for those skilled in the art
Other modification is realized, therefore under the universal limited without departing substantially from claim and equivalency range, the present invention is not limited
In specific details and shown here as the embodiment with description.
Claims (4)
1. a kind of Leak-stoppage agent for radiator, it is characterised in that by weight including following each component：Bath of glass 20-35
Part, 15-20 parts of guar hydroxypropyltrimonium ammonium chloride, 2-4 parts of sodium tetraborate, 13-15 parts of lignocellulosic, pH value conditioning agent
2-4 parts, 0.5-1.5 parts of anticorrosion and bactericidal agent, 0.8-1.7 parts of defoamer；
The preparation method of the Leak-stoppage agent is：
Step 1：Under stirring, add bath of glass, guar hydroxypropyltrimonium ammonium chloride, lignocellulosic, anti-corrosion and kill
Microbial inoculum and defoamer, form suspension；
Step 2：PH value conditioning agent is added into suspension again, the pH value of regulation suspension is 6-8, filtering；
Step 3：Sodium tetraborate is eventually adding, is stirred 5-10 minutes, suspension is transformed into gel, produce Leak-stoppage agent.
2. the Leak-stoppage agent according to claim 1 for radiator, it is characterised in that：The stopping for radiator
The each component of leakage agent is calculated by weight is：20 parts of bath of glass, 18 parts of guar hydroxypropyltrimonium ammonium chloride, sodium tetraborate 3
Part, 13 parts of lignocellulosic, 4 parts of pH value conditioning agent, 0.8 part of anticorrosion and bactericidal agent, 0.8 part of defoamer.
3. the Leak-stoppage agent according to claim 1 for radiator, it is characterised in that：The stopping for radiator
The each component of leakage agent is calculated by weight is：28 parts of bath of glass, 15 parts of guar hydroxypropyltrimonium ammonium chloride, sodium tetraborate 2
Part, 14 parts of lignocellulosic, 2 parts of pH value conditioning agent, 0.5 part of anticorrosion and bactericidal agent, 1 part of defoamer.
4. the Leak-stoppage agent according to claim 1 for radiator, it is characterised in that：The stopping for radiator
The each component of leakage agent is calculated by weight is：35 parts of bath of glass, 20 parts of guar hydroxypropyltrimonium ammonium chloride, sodium tetraborate 2
Part, 15 parts of lignocellulosic, 3 parts of pH value conditioning agent, 1.5 parts of anticorrosion and bactericidal agent, 1.7 parts of defoamer.