CN107025968A - A kind of magnetic nanometer composite material - Google Patents
A kind of magnetic nanometer composite material Download PDFInfo
- Publication number
- CN107025968A CN107025968A CN201611271372.3A CN201611271372A CN107025968A CN 107025968 A CN107025968 A CN 107025968A CN 201611271372 A CN201611271372 A CN 201611271372A CN 107025968 A CN107025968 A CN 107025968A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnetic
- nano
- composite material
- nanometer composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of magnetic nanometer composite material, belong to pharmaceutical technology field, including by the raw material of following weight parts:60~70 parts of Co/C magnetic Nano materials, Fe3O460~70 parts of AC magnetic Nano materials, Fe3O4/TiO260~70 parts of magnetic Nano material, nano-calcium carbonate Ca45~60 part, 20~35 parts of nano-ceramic powder, 2~4 parts of photochemical catalyst, 1~3 part of adhesive, 1~3 part of reinforcing agent, Fe crystallite dimensions 20 40nm, TiO2The 45nm of crystallite dimension 25.The close contiguity between each composition can be strengthened by adding adhesive and reinforcing agent in the magnetic nanometer composite material of the present invention, prevent film from peeling off, and have stronger absorption characteristic to electromagnetic wave, be adapted to popularization and application.
Description
Technical field
The invention belongs to field of material technology, it is related to a kind of magnetic nanometer composite material, the materials application is in electromagnetic protection
With field of electromagnetic compatibility.
Background technology
With the progress of science and technology, with three kinds of electromagnetic conductive, electromagnetic induction and electromagnetic radiation between various electronic equipments
Mode is associated with each other and influences each other, and the equipment of operation and personnel can be interfered, influenceed and endangered under certain conditions.
Electromagnetic field transmits energy in the form of an electromagnetic wave, electromagnetism wave energy is converted into heat energy or other forms using electromagnetic wave absorbent material
Energy, be remove electromagnetic pollution effective means.Other electromagnetic wave absorbent material is in military technology, such as ECM and hidden
Body technical elements also have extensive purposes.Therefore, research and development electromagnet protective materials is very necessary.
Exploitation absorption band is wide, thickness of thin, absorbability are strong, the electromagnetic absorber of light weight has caused countries in the world
Concern.Nano material, particularly magnetic Nano metal material, due to physics characteristics such as unique light, electricity, magnetic, into
For the research emphasis of Material Field.But, on the one hand, magnetic Nano metal is easily drawn due to intrinsic magnetic and bigger serface
Rise and reunite, so as to be difficult to its abundant reciprocation with electromagnetic wave, can not embody good absorbing property;On the other hand,
Single magnetic metal material environmental stability is poor, and limited to the dissipation capabilities of electromagnetic wave, it is difficult to meet high-performance electric magnetic wave
The requirement of absorbing material.These all greatly limit magnetic Nano metal material and are inhaling the application study in the fields such as ripple.
The content of the invention
It is an object of the invention to the defect for overcoming above-mentioned technology presence, there is provided a kind of magnetic nanometer composite material, the material
Material has stronger absorption characteristic to electromagnetic wave.
Its concrete technical scheme is:
A kind of magnetic nanometer composite material, including by the raw material of following weight parts:60~70 parts of Co/C magnetic Nano materials,
Fe3O460~70 parts of-AC magnetic Nano materials, Fe3O4/TiO260~70 parts of magnetic Nano material, nano-calcium carbonate Ca45~60 part,
20~35 parts of nano-ceramic powder, 2~4 parts of photochemical catalyst, 1~3 part of adhesive, 1~3 part of reinforcing agent, Fe crystallite dimensions 20-
40nm, TiO2Crystallite dimension 25-45nm.
Further, including by the raw material of following weight parts:65 parts of Co/C magnetic Nano materials, Fe3O4- AC magnetic Nano materials
Expect 65 parts, Fe3O4/TiO2It is 65 parts of magnetic Nano material, 50 parts of nano-calcium carbonate, 30 parts of nano-ceramic powder, 3 parts of photochemical catalyst, viscous
2 parts of mixture, 2 parts of reinforcing agent.
Compared with prior art, beneficial effects of the present invention are:
Adhesive is added in the magnetic nanometer composite material of the present invention and reinforcing agent can strengthen tight between each composition
Close contiguity, prevents film from peeling off, and has stronger absorption characteristic to electromagnetic wave, is adapted to popularization and application.
Embodiment
Technical scheme is described in more detail with reference to specific embodiment.
Embodiment 1
A kind of magnetic nanometer composite material, including by the raw material of following weight parts:60 parts of Co/C magnetic Nano materials,
Fe3O460 parts of-AC magnetic Nano materials, Fe3O4/TiO260 parts of magnetic Nano material, nano-calcium carbonate Ca45 part, nano-ceramic powder 20
Part, 2 parts of photochemical catalyst, 1 part of adhesive, 1 part of reinforcing agent.
The preparation method of magnetic nanometer composite material of the present invention, 60 parts of Co/C magnetic Nano materials, Fe3O4- AC magnetic
60 parts of nano material, Fe3O4/TiO260 parts of magnetic Nano material, nano-calcium carbonate Ca45 part, 20 parts of nano-ceramic powder, photochemical catalyst
2 parts, 1 part of adhesive, grind 1-3 hours in 1 part of addition ball mill of reinforcing agent, obtain composite granule, then add catalyst 2
~4 parts, 1~3 part of adhesive, 1~3 part of reinforcing agent, be sufficiently mixed, get product.
Embodiment 2
A kind of magnetic nanometer composite material, including by the raw material of following weight parts:65 parts of Co/C magnetic Nano materials,
Fe3O465 parts of-AC magnetic Nano materials, Fe3O4/TiO265 parts of magnetic Nano material, 50 parts of nano-calcium carbonate, nano-ceramic powder 30
Part, 3 parts of photochemical catalyst, 2 parts of adhesive, 2 parts of reinforcing agent.
The preparation method of magnetic nanometer composite material of the present invention, by 65 parts of Co/C magnetic Nano materials, Fe3O4- AC magnetic
65 parts of nano material of property, Fe3O4/TiO265 parts of magnetic Nano material, 50 parts of nano-calcium carbonate, 30 parts of nano-ceramic powder, photocatalysis
Ground 1-3 hours in 3 parts of agent, 2 parts of adhesive, 2 parts of addition ball mills of reinforcing agent, obtain composite granule, then add catalysis
2~4 parts of agent, 1~3 part of adhesive, 1~3 part of reinforcing agent, are sufficiently mixed, get product.
Embodiment 3
A kind of magnetic nanometer composite material, including by the raw material of following weight parts:70 parts of Co/C magnetic Nano materials,
Fe3O470 parts of-AC magnetic Nano materials, Fe3O4/TiO270 parts of magnetic Nano material, 60 parts of nano-calcium carbonate, nano-ceramic powder 35
Part, 4 parts of photochemical catalyst, 3 parts of adhesive, 3 parts of reinforcing agent.
The preparation method of magnetic nanometer composite material of the present invention, by 70 parts of Co/C magnetic Nano materials, Fe3O4- AC magnetic
70 parts of nano material of property, Fe3O4/TiO270 parts of magnetic Nano material, 60 parts of nano-calcium carbonate, 35 parts of nano-ceramic powder, photocatalysis
Ground 1-3 hours in 4 parts of agent, 3 parts of adhesive, 3 parts of addition ball mills of reinforcing agent, obtain composite granule, then add catalysis
2~4 parts of agent, 1~3 part of adhesive, 1~3 part of reinforcing agent, are sufficiently mixed, get product.
The foregoing is only a preferred embodiment of the present invention, protection scope of the present invention not limited to this, any ripe
Those skilled in the art are known in the technical scope of present disclosure, the letter for the technical scheme that can be become apparent to
Altered or equivalence replacement are each fallen within protection scope of the present invention.
Claims (2)
1. a kind of magnetic nanometer composite material, it is characterised in that including the raw material by following weight parts:Co/C magnetic Nano materials
60~70 parts, Fe3O460~70 parts of-AC magnetic Nano materials, Fe3O4/TiO260~70 parts of magnetic Nano material, nano-calcium carbonate
45~60 parts, 20~35 parts of nano-ceramic powder, 2~4 parts of photochemical catalyst, 1~3 part of adhesive, 1~3 part of reinforcing agent, Fe crystal grain chis
Very little 20-40nm, TiO2Crystallite dimension 25-45nm.
2. magnetic nanometer composite material according to claim 1, it is characterised in that including the raw material by following weight parts:
65 parts of Co/C magnetic Nano materials, Fe3O465 parts of-AC magnetic Nano materials, Fe3O4/TiO265 parts of magnetic Nano material, nano-sized carbon
Sour 50 parts of calcium, 30 parts of nano-ceramic powder, 3 parts of photochemical catalyst, 2 parts of adhesive, 2 parts of reinforcing agent.