CN107022129A - A kind of sewing masked film - Google Patents

A kind of sewing masked film Download PDF

Info

Publication number
CN107022129A
CN107022129A CN201610062617.5A CN201610062617A CN107022129A CN 107022129 A CN107022129 A CN 107022129A CN 201610062617 A CN201610062617 A CN 201610062617A CN 107022129 A CN107022129 A CN 107022129A
Authority
CN
China
Prior art keywords
parts
sewing
film
masked film
masked
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610062617.5A
Other languages
Chinese (zh)
Inventor
栾泰虎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Charm Cosmetics Co Ltd
Original Assignee
Shanghai Charm Cosmetics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Charm Cosmetics Co Ltd filed Critical Shanghai Charm Cosmetics Co Ltd
Priority to CN201610062617.5A priority Critical patent/CN107022129A/en
Publication of CN107022129A publication Critical patent/CN107022129A/en
Pending legal-status Critical Current

Abstract

The component and the parts by weight of correspondence component included the invention discloses a kind of sewing with masked film is as follows：PE100 parts；45-65 parts of calcium carbonate；1-3 parts of cerium oxide；1-5 parts of nano zine oxide；0.05-0.2 parts of antioxidant；0.3-0.7 parts of calcium stearate；2.5-4.5 parts of coupling agent；0.5-2.5 parts of barium stearate；1-10 parts of stearic acid；Zinc stearate is 1-3 parts, 5-10 parts of laurene, 2-3 parts of dichloroethenyl salicylamide, 1-1.5 parts of thiazole, 2-3 parts of silver-loaded zirconium phosphate, 3-5 parts of potassium titanate crystal whisker.The sewing masked film can reach medical PE ranks film, with antibacterial effect, anesthetic can be made quickly to penetrate into by the skin of sewing person.

Description

A kind of sewing masked film
Technical field
The present invention relates to medical cosmetic technical field, more particularly to a kind of sewing masked film.
Background technology
Polyethylene English name:Poly (ethylene) Chinese nickname:Polyethylene from high pressure process;LDPE;Polyethylene from high pressure process is molded Material;Type low density polyethylene resin;Hi-fax;LLDPE;Low pressure low density polyethylene (LDPE);PE;Polyvinyl resin;Poly- second Alkene wax;Low molecular weight polyethylene;PE waxes;Low density polyethylene (LDPE);For making agricultural, food and industrial packaging film, electric wire Cable is coated and coating, composed paper etc.;Keep storage sealing, be stored in place that is shady and cool, drying, it is ensured that workplace has good Good ventilation or exhaust apparatus.Polyethylene（Polyethylene, abbreviation PE）It is a kind of aggregated obtained thermoplastic resin of ethene Fat.Industrially, the also copolymer including ethene Yu a small amount of alpha-olefin.Polyethylene odorless, nontoxic, feel ceraceous, with excellent Resistance to low temperature（Minimum reachable -100 ~ -70 °C of temperature in use）, chemical stability is good, is resistant to the erosion of most of soda acids（No The resistance to acid with oxidizing property）.Common solvent is not dissolved under normal temperature, water imbibition is small, and electrical insulating property is excellent.The performance of polyethylene takes Certainly in its polymerization methodses.Ziegler-Natta is carried out under middle pressure (15-30 atmospheric pressure) organic compound catalytic condition That be polymerized is high density polyethylene (HDPE) (HDPE).The polyethylene molecule polymerizeing under the conditions of this is linear, and strand is very Long, molecular weight is up to hundreds of thousands.If in high pressure (100-300MPa), high temperature (190-210C), peroxide catalyzed bar Radical polymerization under part, that produce is then low density polyethylene (LDPE) (LDPE), and it is side chain chemical combination structure.Polyethylene is typical Thermoplastic is odorless, tasteless, nontoxic flammable white powder.The PE resins of processing and forming are extruded granulations Wax-like particulate material, outward appearance is creamy white.Its molecular weight is in the range of 10,000 one loa ten thousand.Molecular weight more than 100,000 is then superelevation point Sub- weight northylen fUHMWPE3.Molecular weight is higher, and its physical and mechanical property is better, closer to the requirement level of engineering material.But Molecular weight is higher, and its difficulty processed also increases therewith.Its resistance to low temperature is excellent for 10-130C for polyethylene fusing point.- 60 Good mechanical property can be still kept at DEG C, but temperature in use is at 80 ~ 110 DEG C.Polyethylene chemical stability preferably, at room temperature may be used Resistance to dust technology, the hydrochloric acid of dilute sulfuric acid and any concentration, hydrofluoric acid, phosphoric acid, formic acid, acetic acid, ammoniacal liquor, amine, hydrogen peroxide, hydrogen-oxygen Change the solution such as sodium, potassium hydroxide.But the not mixed liquor of the corrosion of powerful oxidation corrosion resistance, such as oleum concentrated nitric acid, chromic acid and sulfuric acid. Above-mentioned solvent can produce slow corrosion function to polyethylene at room temperature, and at 90-100 DEG C, the concentrated sulfuric acid and concentrated nitric acid meeting Polyethylene is rapidly corroded, it is destroyed or is decomposed.Polyethylene is in the presence of air, sunlight and oxygen, it may occur that aging, becomes Color, it is cracked, becomes fragile or efflorescence, loses its mechanical property.At a temperature of processing and forming, also it can kill its melt because of oxidation Degree declines, and occurs discoloration, striped occurs, so in processing and forming and attention is should give during using process or selection.Just because of poly- Ethene possesses as above speciality, is easily worked shaping, therefore the regeneration of polyethylene is reclaimed with very far-reaching value.
Sewing is a kind of Micro trauma pigmenting of skin.It is that pigment is implanted into skin histology to form stable color lump, by It is very thin in epidermis, into translucent, so the pigment of implantation shows implantation color and luster by epidermis, with reach cover flaw, Maximize favourable factors and minimize unfavourable ones, modify the effect beautified.Because the pigment for being pierced into skin is that fine granularity, diameter are both less than 1 micron, after implantation It will soon be surrounded by collagen, it is impossible to swallowed by phagocyte, so as to form semipermanent mark in skin surface.Referred to as " sewing " also " text embroider ".
Loving beauty is part of human nature.Increasing people likes upper sewing, but because has micro- to skin during sewing Wound, it is therefore desirable to local to use anesthetic.Generally required in operating process to being coated anaesthetic at sewing, then applied with an epiphragma In surgical field, the time for accelerating anaesthetic to come into force, while making to be releived by people's mood of sewing, calm.
At present, what market was accustomed to using is the winding film or domestic food level preservative film of packing, and it has following lack Point：
1st, material is dangerous or even poisonous
2nd, material is very thick, it is impossible to docile human body surface
3rd, material can not cut to 32 millimeters and 40 mm wides
4th, needed during materials'use and cutter coordinates.
The content of the invention
In order to solve the problems of the prior art, it can speed up anesthetic it is an object of the invention to provide one kind and go deep into skin Skin, make the sewing masked film that is comfortable on by sewing people.The sewing masked film can reach medical PE ranks film, with anti- Bacterium effect, can be such that anesthetic quickly penetrates into by the skin of sewing person.
To achieve the above object, the present invention uses following technical scheme：Component that a kind of sewing is included with masked film and right Answer the parts by weight of component as follows：
PE100 parts；45-65 parts of calcium carbonate；1-3 parts of cerium oxide；1-5 parts of nano zine oxide；0.05-0.2 parts of antioxidant；Stearic acid 0.3-0.7 parts of calcium；2.5-4.5 parts of coupling agent；0.5-2.5 parts of barium stearate；1-10 parts of stearic acid；Zinc stearate is 1-3 parts, the moon Alkene 5-10 parts of osmanthus, 2-3 parts of dichloroethenyl salicylamide, 1-1.5 parts of thiazole, 2-3 parts of silver-loaded zirconium phosphate, potassium titanate crystal whisker 3-5 Part.
Further preferred technical scheme, the sewing leaves a fracture with masked film every a segment distance.
Technical scheme still more preferably, the sewing is wrapped on company's spool of medical grade material with masked film.Institute State sewing and cover film thickness less than 0.01 millimeter.Ultrathin design is easy to operation and comfortable, ventilative.
Another object of the present invention is to provide a kind of purposes of medical grade PE films, and the medical grade PE films are above-mentioned sewing With masked film, when sewing, the film is used to be covered in the skin surface for coating anesthetic.
Primary efficacy of the present invention has：Using above-mentioned formula, antibacterial effect can be realized, and reached the other PE of medical grade Membrane material, it is quite safe to human body；The film is ultra-thin, flexible, using breakpoint formula, leaves a fracture every a segment distance, thus It is easy to use without cutter.
In addition, it has further the advantage that：
It is of the invention thoroughly to solve people to jeopardizing the worry of the poor material of inherently safe, allow each user to have good Usage experience, adds the safety coefficient of semipermanent cosmetic and sewing industry.
Embodiment
To make the object, technical solutions and advantages of the present invention of greater clarity, with reference to instantiation, to the present invention It is further described.It should be understood that these descriptions are merely illustrative, and it is not intended to limit the scope of the present invention.In addition, In illustrating below, the description to known features and technology is eliminated, to avoid unnecessarily obscuring idea of the invention.
A kind of embodiment 1, sewing includes the component of following parts by weight with masked film：
PE100 grams；45 grams of calcium carbonate；1 gram of cerium oxide；1 gram of nano zine oxide；0.05 gram of antioxidant；0.3 gram of calcium stearate；It is even Join 2.5 grams of agent；0.5 gram of barium stearate；1 gram of stearic acid；Zinc stearate is 1 gram, 5 grams of laurene, dichloroethenyl salicylamide 2 Gram, 1 gram of thiazole, 2 grams of silver-loaded zirconium phosphate, 3 grams of potassium titanate crystal whisker.
Above-mentioned material is commercially available.
The sewing leaves a fracture with masked film every a segment distance.The sewing is wrapped in medical grade material with masked film On company's spool of material.
A kind of purposes of medical grade PE films, the medical grade PE films are above-mentioned sewing masked film, when sewing, the film The skin surface of anesthetic is coated for being covered in.
A kind of embodiment 2, sewing includes the component of following parts by weight with masked film：
PE100 grams；65 grams of calcium carbonate；3 grams of cerium oxide；5 grams of nano zine oxide；0.2 gram of antioxidant；0.7 gram of calcium stearate；Coupling 4.5 grams of agent；2.5 grams of barium stearate；10 grams of stearic acid；Zinc stearate is 3 grams, 10 grams of laurene, dichloroethenyl salicylamide 3 Gram, 1.5 grams of thiazole, 3 grams of silver-loaded zirconium phosphate, 5 grams of potassium titanate crystal whisker.
Above-mentioned material is commercially available, and the sewing is less than 0.01 millimeter with film thickness is covered.
A kind of embodiment 3, sewing includes the component of following parts by weight with masked film：
PE100 grams；60 grams of calcium carbonate；2 grams of cerium oxide；3 grams of nano zine oxide；0.1 gram of antioxidant；0.5 gram of calcium stearate；Coupling 4 grams of agent；2 grams of barium stearate；8 grams of stearic acid；Zinc stearate is 2 grams, 7 grams of laurene, 2 grams of dichloroethenyl salicylamide, thiophene 1 gram of azoles, 2 grams of silver-loaded zirconium phosphate, 4 grams of potassium titanate crystal whisker.
Above-mentioned material is commercially available, and obtained sewing is less than 0.01 millimeter with film thickness is covered.
Primary efficacy of the present invention has：Using above-mentioned formula, antibacterial effect can be realized, and reached the other PE of medical grade Membrane material, it is quite safe to human body；The film is ultra-thin, flexible, using breakpoint formula, leaves a fracture every a segment distance, thus It is easy to use without cutter.
In addition, it has further the advantage that：
It is of the invention thoroughly to solve people to jeopardizing the worry of the poor material of inherently safe, allow each user to have good Usage experience, adds the safety coefficient of semipermanent cosmetic and sewing industry.
The foregoing is merely illustrative of the preferred embodiments of the present invention, the protection domain being not intended to limit the invention, it is all Within the spirit and principles in the present invention, any modification for being made, equivalent substitution, it is all contained within protection scope of the present invention.

Claims (5)

1. a kind of sewing masked film, it is characterised in that：Component and the weight of correspondence component that the sewing is included with masked film Part is as follows：PE100 parts；45-65 parts of calcium carbonate；1-3 parts of cerium oxide；1-5 parts of nano zine oxide；0.05-0.2 parts of antioxidant；Firmly 0.3-0.7 parts of resin acid calcium；2.5-4.5 parts of coupling agent；0.5-2.5 parts of barium stearate；1-10 parts of stearic acid；Zinc stearate is 1-3 Part, 5-10 parts of laurene, 2-3 parts of dichloroethenyl salicylamide, 1-1.5 parts of thiazole, 2-3 parts of silver-loaded zirconium phosphate, potassium titanate is brilliant Must be 3-5 parts.
2. a kind of sewing masked film as claimed in claim 1, it is characterised in that：The sewing masked film every one section away from From leaving a fracture.
3. a kind of sewing masked film as claimed in claim 2, it is characterised in that：The sewing is wrapped in medical with masked film On company's spool of level material.
4. a kind of sewing masked film as claimed in claim 1, it is characterised in that：The sewing is less than with covering film thickness 0.01 millimeter.
5. a kind of purposes of medical grade PE films, it is characterised in that：The medical grade PE films are that the sewing described in claim 1 hides Epiphragma, when sewing, the film is used to be covered in the skin surface for coating anesthetic.
CN201610062617.5A 2016-01-29 2016-01-29 A kind of sewing masked film Pending CN107022129A (en)