CN107020381A - A kind of manufacture method of dental high-speed cell phone head - Google Patents
A kind of manufacture method of dental high-speed cell phone head Download PDFInfo
- Publication number
- CN107020381A CN107020381A CN201710123633.5A CN201710123633A CN107020381A CN 107020381 A CN107020381 A CN 107020381A CN 201710123633 A CN201710123633 A CN 201710123633A CN 107020381 A CN107020381 A CN 107020381A
- Authority
- CN
- China
- Prior art keywords
- cell phone
- head
- blank
- speed cell
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of manufacture method of dental high-speed cell phone head, particle mean size is used for 10 ~ 12 microns of the subsphaeroidal high-tap density powder of air water combined atomizing low-carbon 316L stainless steels, by being mixed and made into the feeding with mobility with multicomponent organic binder bond, required shape is injected into by advanced injector, product blank is made by degreasing and high temperature sintering, dental high-speed cell phone head is made by mechanical Vehicle Processing screw thread, polishing, sandblasting.The present invention replaces traditional brass to process welding, polishing, sandblasting, the technique of electro-plating method manufacture dental high-speed cell phone head with stainless steel.The present invention is adapted to produce in enormous quantities, reduces machining, reduces waste of material and saved copper resource, while stainless steel head it also avoid the precipitation of the lead during brass use, both economically and environmentally beneficial, service life also improves 5 times.
Description
Technical field
The present invention relates to field of medical device, and in particular to a kind of manufacture method of dental high-speed cell phone head.
Background technology
Dental high-speed cell phone is the professional tool that Hospitals at Present dental clinic is used, and dental high-speed cell phone is dental high-speed whirlpool
The abbreviation of mobile phone is taken turns, current application field is more and more extensive, except the department of stomatology, also internal medicine, orthopaedics, beauty and shaping industry
Use.Dental handpiece can be divided into major part according to the size of head(High pulling torque), it is standard header, mini first three kinds.In Clinical practice
Selection it is also different, major part dental high-speed cell phone is applied in the more of standby tooth;The general doctors of standard header are selected as treatment
Instrument;It is mini it is first as be useful in children or women patient.Dental high-speed cell phone is using in high pressure air drives handset machine head
Miniature turbine rotation, secondary speed is up to the r/min of 30-50 ten thousand, and the cutting linear velocity of car pin is up to 15m/s.
Requirement to dental high-speed cell phone mainly includes:Because the turbine of 1, generation rotation is just mounted in head, thus it is right
The required precision of the head is strict;2nd, the anti-resorption design of head, whether be resistant to professional thermal cleaning, whether be resistant to 135 DEG C and go out
Bacterium;3rd, the surface treatment of mobile phone must have coating, be subjected to high-temperature sterilization and non-corrosive, be difficult to be infected with dirt, easily cleaning disappears
Poison.
Complex-shaped due to head, current dental high-speed cell phone head is all to be split into two parts, is passed through with brass
It is machined, then Combination Welding, last polished polishing, plating crome metal are made.The processing method is necessarily caused:1st, process
Cost is high;2nd, raw material are wasted;3rd, plating pollution environment;4th, precision is reduced after welding, and is also easy to produce noise;5th, brass uses process
In have the precipitation of lead;6th, electrodeposited coating is easy to fall off.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of manufacture method of dental high-speed cell phone head, can overcome existing
There is brass to be machined the technical deficiency of dental high-speed cell phone head, manufactured using metal injection molded method, the shape of product
Shape will be completed once, it is only necessary to which endoporus is simply machined, then the corresponding screw thread of turning, be a kind of economical
Environmentally friendly practical dental high-speed cell phone head processing method.
The technical problems to be solved by the invention are achieved by the following technical programs:
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)It is mixed and is fed with multicomponent organic binder bond using 10-12 microns of low-carbon 316L powder of stainless steel of particle mean size
Material;
(2)The powder of stainless steel that previous step is treated is mixed and made into feeding with multicomponent organic binder bond;
(3)According to the design size of dental high-speed cell phone head, mould is made by certain shrinkage factor;
(4)The feeding is injected into the mould, satisfactory head injection blank is obtained;
(5)The head is injected into blank degreasing;
(6)Head after degreasing is injected into blank sintering blank is made through high temperature sintering;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and surface treated.
Further, the low-carbon 316L powder of stainless steel of 10-12 microns of described particle mean size, to combine mist by air water
The form that change processing is obtained is spherical or subsphaeroidal high-tap density powder.
Further, described treated powder of stainless steel and described multicomponent organic binder bond are with 0.70 ~ 0.61:
0.30 ~ 0.39 volume ratio mixing.Wherein, step(3)Described certain shrinkage factor, refers to that the blank produced by feeding passes through
Sintering obtains the shrinkage factor of the simple metal part of densification, and the selection by powder is different, binding agent content is different, also differs.
After the species composition determination of metal dust and binding agent and the volume ratio of metal dust and binding agent are determined, it may be determined that the receipts
Shrinkage.
Further, described multicomponent organic binder bond is LDPE(Low density polyethylene (LDPE)), paraffin wax, DBP(Adjacent benzene
Dibutyl carboxylic acid), injection stage PP(Available for injection molding polypropylene)、EVA(Ethylene-vinyl acetate copolymer)、
PMMA613 powder(Polymethyl methacrylate), at least six kinds of mixture in stearic acid, each component mixes with arbitrary proportion.
Further, the temperature of described high temperature sintering is 1380-1393 DEG C, and sintering time is 150-180min.Wherein,
By the sintering blank obtained by method of the present invention density up to stainless steel solid density 97-99%.
Further, described treated powder of stainless steel and multicomponent organic adhesive are mixed using efficient kneader
Agent.
Further, the feeding is injected into the mould using high speed electric syringe.Wherein, it is described to meet
It is required that, refer to injecting the outward appearance flawless of blank, pore-free bubble, lack the open defects such as material, current mark, density meets design will
Ask.
Further, described degreasing is using trichloro ethylene and head described in hexamethylene mixed liquid dipping injects blank,
The weight change of blank is injected according to head, 40-60% binding agent is removed.
Further, described trichloro ethylene and hexamethylene mixed liquor, the volume percent content of wherein trichloro ethylene is
50-100%。
Further, the surface treatment includes being polished and blasting treatment the sintering blank.
The present invention has the advantages that:
Copper product is substituted using stainless steel, material cost is saved, and stainless steel mechanical performance is higher than brass and not leaded, using gas
The organic binder bond formation feeding of the preferred special proportioning of powder of stainless steel collocation of water combined atomizing, and coordinate series of process
The head density of production up to stainless steel solid density 97-99%, therefore lifting product service life;Head one-shot forming,
Omit the processes such as machining, laser welding, reduction processing cost and equipment investment;10-12 microns of preferred average particle size it is low
Carbon 316L powder of stainless steel, it is ensured that it has good decay resistance, it is ball that obtained form is handled by air water combined atomizing
Shape or subsphaeroidal high-tap density powder, optimal metal dust and binding agent volume ratio are determined through many experiments, it is ensured that production
The shrinkage factor of product is minimum, i.e., deflection is minimum when product is sintered, and improves Product Precision;Electroplating work procedure is saved, can be directly to production
Product polishing sandblasting will not bring the problems such as electrodeposited coating comes off, it is environmentally friendly, production process it is unleaded separate out, meet Rosh requirement with
And the development trend of current green economy.
Brief description of the drawings
Fig. 1 is dental high-speed cell phone handpiece structure schematic plan view.
Fig. 2 dental high-speed cell phone handpiece structure schematic isometrics.
Embodiment
With reference to embodiment, the present invention will be described in detail, and embodiment is only the preferred embodiment of the present invention,
It is not limitation of the invention.
Embodiment 1
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 2
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 11 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 3
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 12 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 4
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1380 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 5
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1393 DEG C of high temperature sintering 150min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 6
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 80%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
40% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 7
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.69:
0.31 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
30 parts of piece paraffin, DBP10 parts, PP10 parts of injection stage, EVA10 parts, 5 parts of PMMA613 powder, 30 parts of stearic acid, prepare organic viscous
Weighed after knot agent;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 100%, i.e., using pure
Trichloro ethylene soaks the head injection blank, injects blank weight change according to the weight of organic binder bond and head, removes
60% binding agent in the head injection blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 8
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.66:
0.34 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
50 parts of piece paraffin, DBP15 parts, EVA10 parts, 15 parts of PMMA613 powder, 60 parts of stearic acid, prepare and weighed after organic binder bond;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 9
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.61:
0.39 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE10 parts, cut
45 parts of piece paraffin, DBP20 parts, PP10 parts of injection stage, 15 parts of PMMA613 powder, 20 parts of stearic acid, prepare after organic binder bond claim
Weight;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Embodiment 10
A kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)The low-carbon 316L powder of stainless steel of 10 microns of particle mean size is chosen, the air water combined atomizing powder of stainless steel obtains shape
State is subsphaeroidal high-tap density powder;
(2)Use the powder of stainless steel that efficient kneader treats previous step with multicomponent organic binder bond with 0.70:
0.30 volume ratio is mixed and made into feeding, and described organic binder bond is made up of the component of following weight fraction:LDPE15 parts, cut
10 parts of piece paraffin, DBP25 parts, PP5 parts of injection stage, EVA15 parts, 5 parts of stearic acid, prepare and weighed after organic binder bond;
(3)According to the prior designed size of dental high-speed cell phone head, shrinkage factor is determined by the composition and volume ratio of feeding,
Make mould;
(4)The feeding is injected into by the mould using high speed electric syringe, head injection blank is obtained;
(5)Using trichloro ethylene and hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50%.Mix immersion
The head injection blank is steeped, blank weight change is injected according to the weight of organic binder bond and head, the head note is removed
50% binding agent penetrated in blank, i.e. degreasing;
(6)Head injection blank after degreasing is placed in vacuum degreasing sintering furnace, through 1385 DEG C of high temperature sintering 180min
Sintering blank is made;
(7)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and polished, sandblasting.
Each embodiment is detected, detection includes testing its linear shrinkage and density, and GB/T10125-
2012 NSS salt spray tests.Test result is shown in Table 1.
Table 1:Test result table
Linear shrinkage(%) | Salt spray test | Up to stainless steel solid density(%) | |
Embodiment 1 | 9 | 96h has no corrosion | 99 |
Embodiment 2 | 12 | 96h has no corrosion | 98 |
Embodiment 3 | 10 | 96h has no corrosion | 98 |
Embodiment 4 | 13 | 96h has no corrosion | 99 |
Embodiment 5 | 11 | 96h has no corrosion | 97 |
Embodiment 6 | 10 | 96h has no corrosion | 98 |
Embodiment 7 | 15 | 96h has no corrosion | 99 |
Embodiment 8 | 9 | 96h has no corrosion | 97 |
Embodiment 9 | 12 | 96h has no corrosion | 99 |
Embodiment 10 | 10 | 96h has no corrosion | 97 |
It can be seen that each embodiment possesses good precision and preferably corrosion resistance.
Above content is to combine specific preferred embodiment further description made for the present invention, it is impossible to assert
The specific implementation of the present invention is confined to these explanations.For the those of ordinary skill of technical field that the present invention belongs to, not
On the premise of departing from present inventive concept, some simple deduction or replace can also be made, the guarantor of the present invention should be all considered as belonging to
Protect scope.
Claims (8)
1. a kind of manufacture method of dental high-speed cell phone head, comprises the following steps:
(1)It is mixed and is fed with multicomponent organic binder bond using 10-12 microns of low-carbon 316L powder of stainless steel of particle mean size
Material;
(2)The feeding is injected into a mould made according to the design size of dental high-speed cell phone head, head note is obtained
Penetrate blank;
(3)The head is injected into blank degreasing;
(4)Head after degreasing is injected into blank sintering blank is made through high temperature sintering;
(5)On the sintering blank integral type finished product is obtained after predeterminated position processing screw thread and surface treated.
2. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that described particle mean size
10-12 microns of low-carbon 316L powder of stainless steel, is spherical or subsphaeroidal to handle obtained form by air water combined atomizing
High-tap density powder.
3. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that described is treated
Powder of stainless steel is with described multicomponent organic binder bond with 0.70 ~ 0.61:0.30 ~ 0.39 volume ratio mixing.
4. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that described multicomponent has
Machine binding agent is at least six kinds of mixing in LDPE, paraffin wax, DBP, injection stage PP, EVA, PMMA613 powder, stearic acid
Thing.
5. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that described high temperature sintering
Temperature be 1380-1393 DEG C, calcination time is 150-180min.
6. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that described degreasing is to adopt
With trichloro ethylene and hexamethylene mixed liquor, the head injection blank is soaked, 40-60% binding agent is removed.
7. the manufacture method of dental high-speed cell phone head according to claim 6, it is characterised in that described trichloro ethylene
With hexamethylene mixed liquor, the wherein volume percent content of trichloro ethylene is 50-100%.
8. the manufacture method of dental high-speed cell phone head according to claim 1, it is characterised in that the surface treatment bag
Include and the sintering blank is polished and blasting treatment.