CN107020120A - The preparation method of ozone Heterogeneous oxidation solid catalyst - Google Patents
The preparation method of ozone Heterogeneous oxidation solid catalyst Download PDFInfo
- Publication number
- CN107020120A CN107020120A CN201710274895.1A CN201710274895A CN107020120A CN 107020120 A CN107020120 A CN 107020120A CN 201710274895 A CN201710274895 A CN 201710274895A CN 107020120 A CN107020120 A CN 107020120A
- Authority
- CN
- China
- Prior art keywords
- weight
- component
- iii
- solid catalyst
- ozone heterogeneous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and technical field of chemical engineering catalysts.With activated carbon, carnallite, kaolin, red metal and stone, cubric niter and dolomite make carrier after lithium hypochlorite and double (acetylacetone,2,4-pentanedione) beryllium reamings, add surfactant β hydroxyethyl dimethyls ammonium lauryl sulfate and activation process is carried out under ul-trasonic irradiation, then carrier in hydrothermal reaction kettle with composite mineralizer borax and potassium sulfate, the cyclopentadiene promethium of catalytic activity auxiliary agent predecessor three, it is hydrated three acetic acid terbiums, three (6, 6, 7, 7, 8, 8, 8 seven fluorine 2, 2 dimethyl 3, 5 octene diketone) dysprosium (III), trifluoromethayl sulfonic acid thulium (III), catalytic active center predecessor cobalt edetate, zinc lactate, ethylenediamine pyrocatechol tungsten complex and the golden potassium of tetrachloro, hydro-thermal reaction is carried out under the effect of emulsifying agent palmitic acid trimethylamine groups ethanol ester ammonium iodide, drying is removed after moisture, calcination obtains ozone Heterogeneous oxidation solid catalyst in Muffle furnace.
Description
Technical field
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and chemical catalyst skill
Art field.
Background technology
Ozonation technology using ozone oxidation ability it is strong the characteristics of, can be by many organic pollution oxidation Decompositions, extensively
For wastewater treatment.Catalytic ozonation technology is divided into ozone homogeneous catalytic oxidation and ozone heterogeneous catalytic oxidation, and ozone is equal
Phase catalysis oxidation has that the more difficult separation and recovery of catalyst is reused, ozone utilization rate is low causes water process operating cost higher,
Organic pollutant removal rate is relatively low simultaneously and easily causing secondary pollution of water is limited to its application;Ozone heterogeneous catalysis oxygen
There is change technology catalyst to be easily isolated and recycled and reusable, ozone utilization rate is high, organic pollutant removal rate is higher, drop
Low water process operating cost and receive significant attention its application the advantages of do not result in secondary pollution.Ozone heterogeneous catalysis
It is to reach local organic matter enrichment by catalyst surface absorption organic matter that oxidation of organic compounds, which is decomposed, while ozone molecule absorption exists
The hydroxyl radical free radical that catalyst surface produces high activity under catalyst action decomposes organic matter.Ozone heterogeneous catalytic oxidation
Handle in waste water technology, core technology is the preparation of ozone Heterogeneous oxidation solid catalyst.
Ozone Heterogeneous oxidation solid catalyst is generally made up of carrier, activated centre and auxiliary agent.Due to being polluted in waste water
Species are various, complex chemical composition feature, can produce harmful effect to performance such as absorption, the mithridatism of catalyst.
Prepare that the carrier structure that ozone Heterogeneous oxidation solid catalyst uses is more single at present, adsorptivity is relatively low;Activated centre is universal
Using normal transition metal salt, mithridatism is poor;Preparation method mainly has infusion process, the precipitation method, mixing method and collosol and gel etc.
Method attachment activity center and adjuvant component are easily liquated out in carrier surface, activated centre and adjuvant component, cause catalyst
Easily lose catalytic activity.For exist in current ozone Heterogeneous oxidation solid catalyst preparation method Catalyst Adsorption compared with
Low, mithridatism is poor and easily loses catalytic activity problem, and exploitation is strengthened using multicomponent porous carrier through reaming, surface active
The adsorptivity of catalyst, catalytic activity auxiliary agent predecessor, normal transition Organometallic are made using Rare-earth chemicals
Compound and precious metal chemical complex are made catalytic active center predecessor and prepared with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering
Ozone Heterogeneous oxidation solid catalyst containing multi-element metal has to improve the preparation method of catalyst mithridatism and catalytic activity
There are larger environmental benefit and higher practical value.
The content of the invention
For existing in current ozone Heterogeneous oxidation solid catalyst preparation method, Catalyst Adsorption is relatively low, mithridatism
Poor to lose catalytic activity problem with easy, exploitation strengthens catalyst using multicomponent porous carrier through reaming, surface active
Adsorptivity, catalytic activity auxiliary agent predecessor, normal transition metallo-organic compound and expensive are made using Rare-earth chemicals
Metallic compound is made catalytic active center predecessor and prepared with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering containing polynary gold
The ozone Heterogeneous oxidation solid catalyst of category to improve the preparation method of catalyst mithridatism and catalytic activity, it is characterized in that
Component A can be added in closed reactor and deionized water stirring prepares the aqueous solution, the weight concentration for control component A is 2%~6%,
After the completion of prepared by solution, B component is added under agitation, 35 DEG C~50 DEG C are warming up to, continues stirring reaction 3h~6h, is filtered, instead
Product is answered to obtain reaming modified support after 102 DEG C~106 DEG C dry constant weights;Reaming modified support puts into ultrasound reactor,
The aqueous solution prepared by component C and deionized water is added, the weight concentration of component C is 3%~8%, is uniformly mixed, and control is super
Sound power density is 0.3~0.8W/m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasound
Surface active carrier mixed liquor;Ultrasonic surface activated carrier mixed liquor is transferred in hydrothermal reaction kettle, add D components and go from
The aqueous solution that sub- water is prepared, the weight concentration of D components is 40%~55%, by weight, D component deionized water solutions:Ultrasonic table
Weight ratio=1 of face activated carrier mixed liquor:(1.5~2), control 120 DEG C~180 DEG C of temperature, the hydro-thermal reaction time be 8h~
16h, then dries to obtain fine particle;Fine particle is in Muffle furnace, 600 DEG C~950 DEG C, and calcination 3h~8h obtains ozone non-
Homogeneous oxidizing solid catalyst.The component A is made up of lithium hypochlorite, double (acetylacetone,2,4-pentanedione) berylliums, by weight, lithium hypochlorite:
Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:(1~1.6), B component is by activated carbon, carnallite, kaolin, red metal and stone, saliter
Stone, dolomite composition, by weight, activated carbon:Carnallite:Kaolin:Red metal and stone:Cubric niter:Dolomitic weight ratio=
(5~15):(7~17):(9~19):(11~21):(13~23):(15~25), by weight, component A:The weight of B component
The ratio between=1:(10~20), component C is beta-hydroxyethyl dimethyl dodecyl base ammonium sulfate, by weight, component C:Reaming, which is modified, to be carried
Weight ratio=1 of body:(5~10), D components are by composite mineralizer borax, potassium sulfate, the ring penta of catalytic activity auxiliary agent predecessor three
Diene promethium, three acetic acid terbiums of hydration, three (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosiums (III), three
Fluoromethane sulfonic acid thulium (III) Rare-earth chemicals, catalytic active center predecessor normal transition metallo-organic compound
The golden potassium of cobalt edetate, zinc lactate, ethylenediamine pyrocatechol tungsten complex and precious metal chemical complex tetrachloro, emulsifying agent palmitic acid three
Methyl aminoethanol ester ammonium iodide is constituted, by weight, borax:Potassium sulfate:Three cyclopentadiene promethiums:It is hydrated three acetic acid terbiums:Three (6,
The fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,7,7,8,8,8- seven) dysprosium (III):Trifluoromethayl sulfonic acid thulium (III):Glucose
Sour cobalt:Zinc lactate:Ethylenediamine pyrocatechol tungsten complex:Tetrachloro gold potassium:The weight of palmitic acid trimethylamine groups ethanol ester ammonium iodide
The ratio between=(4~8):(6~10):(3~6):(4~7):(5~8):(6~9):(10~15):(12~18):(4~7):(6~
9):(6~20).Activated carbon, carnallite, kaolin, red metal and stone, cubric niter, the dolomite of the B component are crushed respectively,
Deionized water washing, which is dried, to be removed after moisture, and -200 mesh ,+400 mesh sieves point are carried out through standard screen, control particle diameter be 0.0370mm~
0.0750 mm。
What the technical method of the present invention was realized in:Lithium hypochlorite LiClO, double (second can be being added in closed reactor
Acyl acetone) beryllium C10H14BeO4The aqueous solution is prepared with deionized water stirring, it is 0.0370mm~0.0750mm to add particle diameter after screening
Activated carbon, carnallite, kaolin, red metal and stone, cubric niter and dolomite porous material carrier, in certain temperature and stirring condition
Under, the small Be of aqueous solution Ionic Radius2+(0.31Å)、Li+(0.60Å)Displace part ion radius in porous material big
Ca2+(0.99Å)、K+(1.33Å)、Ba2+(1.35Å)Plasma, the aperture of porous material carrier becomes big, surface roughness increase,
Filtering, dries the reaming modified support input ultrasound reactor after constant weight, adds beta-hydroxyethyl dimethyl dodecyl base sulphur
Sour ammonium [C12H25N(CH3)2CH2CH2OH]+CH3SO4 -The aqueous solution, control ultrasonic power density, ultrasonic frequency, temperature and ultrasound
Duration of oscillation, under ultrasonic cavitation effect, beta-hydroxyethyl dimethyl dodecyl base ammonium sulfate [C12H25N(CH3)2CH2CH2OH]+
CH3SO4 -It is easy to escape into reaming modified support duct from the aqueous solution or is attached to reaming modified support surface, is beneficial to carrier
Being interconnected and carrier surface activation for duct, enhances adsorptivity;After the completion of ultrasonic activation, the mixing of ultrasonic surface activated carrier
Liquid is transferred in hydrothermal reaction kettle, with borax Na2B4O7·10H2O, potassium sulfate K2SO4Before composite mineralizer, catalytic activity auxiliary agent
Drive the cyclopentadiene promethium Pm (C of thing three5H5)3, hydration three acetic acid terbium C6H11O7Tb, three (the fluoro- 2,2- diformazans of 6,6,7,7,8,8,8- seven
Base -3,5- octenes diketone) dysprosium (III) C30H30DyF21O6, trifluoromethayl sulfonic acid thulium (III) C18H54ErN3Si6Rare earth metal has
Machine compound, catalytic active center component predecessor normal transition metallo-organic compound cobalt edetate C12H22O14Co, lactic acid
Zinc C6H10O6Zn, ethylenediamine pyrocatechol tungsten complex (NH2CH2CH2NH3)2[W(VI)O2(OC6H4O)2] and the golden potassium of tetrachloro
KAuCl4Precious metal chemical complex, in emulsifying agent palmitic acid trimethylamine groups ethanol ester ammonium iodide C16H33COOCH2CH2N(CH3)3Under I is used
Hydro-thermal reaction is carried out, mineralizer accelerates diffusion, activates reactant lattice, promotes the progress of solid phase reaction, ultrasonic table
Face activated carrier and Rare-earth chemicals, normal transition metallo-organic compound, precious metal chemical complex Uniform Doped, breast
Agent palmitic acid trimethylamine groups ethanol ester ammonium iodide make reaction solution formed quasi-stationary emulsion prevent separation of solid and liquid, sedimentation, together
When to the further surface active of porous carrier, by the way that in certain temperature, the hydro-thermal reaction of time, drying obtains the thin of Uniform Doped
Powder material;The fine silt thing of Uniform Doped is in Muffle furnace, through high temperature sintering, and organic matter carbonization therein is further strengthened
The microcellular structure of porous carrier, obtains porous carrier supported rare earth metal oxide, transition metal oxide and noble metal shape
Into catalytic active center ozone Heterogeneous oxidation solid catalyst, improve the mithridatism and catalytic activity of catalyst.
Relative to art methods, outstanding feature of the present invention is that activated carbon, carnallite, kaolinite are used in technology of preparing
Native, red metal and stone, cubric niter, dolomite porous material make carrier, due to lithium hypochlorite LiClO and double (acetylacetone,2,4-pentanedione) berylliums
C10H14BeO4Reaming effect, beta-hydroxyethyl dimethyl dodecyl base ammonium sulfate [C12H25N(CH3)2CH2CH2OH]+CH3SO4 -, palm fibre
Palmitic acid acid trimethylamine groups ethanol ester ammonium iodide C16H33COOCH2CH2N(CH3)3I is interconnected and surface activation to duct;It is logical
Cross hydro-thermal reaction and reach Rare-earth chemicals, normal transition metallo-organic compound and precious metal chemical complex and uniformly mix
Miscellaneous and be attached in carrier surface and duct, high temperature sintering makes organic matter carbonization strengthen and form multi-level micropore knot
In structure, the multi-element metal catalytic activity of porous carrier supported rare earth metal oxide, transition metal oxide and noble metal formation
The heart is combined more firm with porous carrier, and the ozone Heterogeneous oxidation solid catalyst of preparation has stronger adsorptivity, polynary
The cooperative effect of metal, the noble metal of particularly doping have stability and high activity, can suppress metal catalytic activity component
Liquate out, the mithridatism and catalytic activity of catalyst are improved, with good environmental benefit and economic benefit.
Embodiment
Embodiment 1:1.35g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 1.65g, 140ml deionized waters, being added to volume is
500ml's can be uniformly mixed in closed reactor, and the weight concentration of the aqueous solution is 2.1%, lithium hypochlorite:Double (levulinics
Ketone) beryllium weight ratio=1:1.2;Add deionized water wash to it is neutral, 103 DEG C dry remove -200 mesh of sieving after moisture~+
The 2.75g activated carbons of 400 mesh standard sieves, 3.75g carnallites, 4.75g kaolin, the red metals and stones of 5.75g, 6.75g cubric niters,
The weight of 7.75g dolomites, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums(3g):The weight of porous material(31.5g)=1:10.5,
36 DEG C are warming up to, reaming modified support 31g is obtained after continuing stirring reaction 3.2h, filtering, 103 DEG C of dry constant weights;It is super in 500ml
In sound wave reactor, reaming modified support 31g is put into, 3.25g beta-hydroxyethyl dimethyl dodecyl base ammonium sulfate is added and is dissolved in
The aqueous solution of 100ml deionized waters, the weight concentration of the aqueous solution is 3.1%, is uniformly mixed, beta-hydroxyethyl dimethyl ten
Dialkyl group ammonium sulfate(3.25g):Reaming modified support(31g )=1:9.5;It is 0.4 W/m to control ultrasonic power density3, ultrasound
41 DEG C of wave frequency rate 21kHz, temperature, sonic oscillation 2.2h;After the completion of ultrasonic activation, the ultrasonic surface in ultrasound reactor is lived
Change carrier mixed liquor to be transferred in 500ml hydrothermal reaction kettles, add by 2.1g boraxs, 3.05g potassium sulfates, the rings penta 2 of 1.6g tri-
Alkene promethium, 2.05g are hydrated three acetic acid terbiums, 2.6g tri- (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosium
(III), 3.05g trifluoromethayl sulfonic acids thulium (III), 5.05g cobalt edetates, 6.1g zinc lactates, 2.05g catechols second two
The water that the golden potassium of amine tungsten complex, 3.1g tetrachloros, 3.05g palmitic acid trimethylamine groups ethanol ester ammonium iodides and 50ml deionized waters are prepared
Solution, the weight concentration of the aqueous solution is 40.3%, the weight of the aqueous solution:The weight of ultrasonic surface activated carrier mixed liquor=
83.8g:134.25g =1:1.6,125 DEG C of temperature is controlled, the hydro-thermal reaction time is 8.3h, then dries to obtain fine silt for 105 DEG C
Thing;Fine silt thing is in Muffle furnace, 620 DEG C, calcination 3.2h, and after cooling down, the ozone that can obtain fine particle shape is heterogeneous
Oxidized solid catalyst.
Embodiment 2:0.24g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 0.36g, 10ml deionized waters, being added to volume is
100ml's can be uniformly mixed in closed reactor, and the weight concentration of the aqueous solution is 5.7%, lithium hypochlorite:Double (levulinics
Ketone) beryllium weight ratio=1:1.5;Add deionized water wash to it is neutral, 103 DEG C dry remove -200 mesh of sieving after moisture~+
The 1.45g activated carbons of 400 mesh standard sieves, 1.65g carnallites, 1.85g kaolin, the red metals and stones of 2.05g, 2.25g cubric niters,
The weight of 2.45g dolomites, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums(0.6g):The weight of porous material(11.7g)=1:
19.5,48 DEG C are warming up to, reaming modified support 11.5g is obtained after continuing stirring reaction 5.8h, filtering, 105 DEG C of dry constant weights;
In 100ml ultrasound reactors, reaming modified support 11.5g is put into, 2.2g beta-hydroxyethyl dimethyl dodecyl base sulphur is added
Sour ammonium is dissolved in the aqueous solution of 26ml deionized waters, and the weight concentration of the aqueous solution is 7.8%, is uniformly mixed, beta-hydroxyethyl two
Methyl ammonium lauryl sulfate(2.2g):Reaming modified support(11.5g )=1:5.2;It is 0.7 W/ to control ultrasonic power density
m3, ultrasonic frequency 29kHz, 54 DEG C of temperature, sonic oscillation 4.7h;After the completion of ultrasonic activation, super in ultrasound reactor
Sound surface active carrier mixed liquor is transferred in 100ml hydrothermal reaction kettles, add by 0.78g boraxs, 0.97g potassium sulfates,
The cyclopentadiene promethiums of 0.58g tri-, 0.67g be hydrated three acetic acid terbiums, 0.78g tri- (fluoro- 2,2- dimethyl -3 of 6,6,7,7,8,8,8- seven,
5- octenes diketone) dysprosium (III), 0.87g trifluoromethayl sulfonic acids thulium (III), 1.48g cobalt edetates, 1.77g zinc lactates,
The golden potassium of 0.68g ethylenediamine pyrocatechols tungsten complex, 0.87g tetrachloros, 1.98g palmitic acid trimethylamine groups ethanol ester ammonium iodides and
The aqueous solution that 10ml deionized waters are prepared, the weight concentration of the aqueous solution is 53.3%, the weight of the aqueous solution:Ultrasonic surface is lived
Change weight=21.43g of carrier mixed liquor:39.7g =1:1.9,175 DEG C of temperature is controlled, the hydro-thermal reaction time is 15.5h, then
105 DEG C dry to obtain fine silt thing;Fine silt thing is in Muffle furnace, 930 DEG C, calcination 7.5h, after cooling down, can obtain fine powder
Granular ozone Heterogeneous oxidation solid catalyst.
Comparative example 1:Preparation process is not added with lithium hypochlorite, double (acetylacetone,2,4-pentanedione) berylliums, Β-hydroxyethyl dimethyl dodecyl
Outside ammonium sulfate, palmitic acid trimethylamine groups ethanol ester ammonium iodide, borax and potassium sulfate, whole preparation process, preparation condition and implementation
Example 1 is identical.
The parameter of ozone Heterogeneous oxidation solid catalyst prepared by embodiment 1, embodiment 2 and comparative example 1 is included in table 1.
The embodiment of table 1 and comparative example prepare ozone Heterogeneous oxidation solid catalysis agent parameter
Project | Average pore size (nm) | Pore volume (cm3/g) | BET is than surface (m2/g) |
Embodiment 1 | 4.618 | 0.6123 | 778.53 |
Embodiment 2 | 4.134 | 0.5645 | 669.28 |
Comparative example 1 | 2.256 | 0.3280 | 474.52 |
Claims (2)
1. a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, it is characterized in that A groups can added in closed reactor
Divide and deionized water stirring prepares the aqueous solution, the weight concentration for controlling component A is 2%~6%, after the completion of prepared by solution, in stirring
Lower addition B component, is warming up to 35 DEG C~50 DEG C, continues stirring reaction 3h~6h, and filtering, reaction product is dry at 102 DEG C~106 DEG C
Reaming modified support is obtained after dry constant weight, reaming modified support input ultrasound reactor, addition is matched somebody with somebody by component C and deionized water
The aqueous solution of system, the weight concentration of component C is 3%~8%, is uniformly mixed, and it is 0.3~0.8W/ to control ultrasonic power density
m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasonic surface activated carrier mixed liquor, transfer
Into hydrothermal reaction kettle, the aqueous solution that D components and deionized water are prepared is added, the weight concentration of D components is 40%~55%, is pressed
Weight meter, D component deionized water solutions:Weight ratio=1 of ultrasonic surface activated carrier mixed liquor:(1.5~2), control temperature
120 DEG C~180 DEG C, the hydro-thermal reaction time is 8h~16h, then dries to obtain fine silt thing, fine silt thing is in Muffle furnace, 600
DEG C~950 DEG C, calcination 3h~8h obtains ozone Heterogeneous oxidation solid catalyst;The component A by expanding agent lithium hypochlorite,
Double (acetylacetone,2,4-pentanedione) beryllium compositions, by weight, lithium hypochlorite:Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:(1~1.6), B groups
Divide and be made up of activated carbon, carnallite, kaolin, red metal and stone, cubric niter, dolomite, by weight, activated carbon:Carnallite:Kaolinite
Soil:Red metal and stone:Cubric niter:Dolomitic weight ratio=(5~15):(7~17):(9~19):(11~21):(13~23):
(15~25), by weight, component A:Weight ratio=1 of B component:(10~20), component C is beta-hydroxyethyl dimethyl 12
Alkylsurfuric acid ammonium, by weight, component C:Weight ratio=1 of reaming modified support:(5~10), D components are by composite mineralizer
Borax, potassium sulfate, the cyclopentadiene promethium of catalytic activity auxiliary agent predecessor three, three acetic acid terbiums of hydration, three (6,6,7,7,8,8,8- seven
Fluoro- 2,2- dimethyl -3,5- octene diketone) dysprosium (III), trifluoromethayl sulfonic acid thulium (III) Rare-earth chemicals, urge
Change activated centre predecessor normal transition metallo-organic compound cobalt edetate, zinc lactate, ethylenediamine pyrocatechol tungsten to coordinate
Thing and the golden potassium of precious metal chemical complex tetrachloro, emulsifying agent palmitic acid trimethylamine groups ethanol ester ammonium iodide composition, by weight, borax:
Potassium sulfate:Three cyclopentadiene promethiums:It is hydrated three acetic acid terbiums:Three (the fluoro- 2,2- dimethyl -3,5- octenes two of 6,6,7,7,8,8,8- seven
Ketone) dysprosium (III):Trifluoromethayl sulfonic acid thulium (III):Cobalt edetate:Zinc lactate:Ethylenediamine pyrocatechol tungsten complex:Tetrachloro
Golden potassium:The weight ratio of palmitic acid trimethylamine groups ethanol ester ammonium iodide=(4~8):(6~10):(3~6):(4~7):(5~
8):(6~9):(10~15):(12~18):(4~7):(6~9):(6~20).
2. B component is made up of activated carbon, carnallite, kaolin, red metal and stone, cubric niter, dolomite according to claim 1,
Activated carbon, carnallite, kaolin, red metal and stone, cubric niter, dolomite are crushed respectively, and deionized water washing, which is dried, removes water
After point, sieved through standard screen, it is 0.0370mm~0.0750mm to control particle diameter.