CN107011796A - A kind of coating and preparation method thereof - Google Patents
A kind of coating and preparation method thereof Download PDFInfo
- Publication number
- CN107011796A CN107011796A CN201710236932.XA CN201710236932A CN107011796A CN 107011796 A CN107011796 A CN 107011796A CN 201710236932 A CN201710236932 A CN 201710236932A CN 107011796 A CN107011796 A CN 107011796A
- Authority
- CN
- China
- Prior art keywords
- parts
- preparation
- tung oil
- coating
- subbing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of coating of the present invention and preparation method thereof, belongs to technical field of coatings, and wherein coating includes subbing and investment precoat, and the subbing is made up of the component of following parts by weight：25 ~ 35 parts of quick lime, breaking bar/15 ~ 25 parts of dry cow dung, 40 ~ 50 parts of tung oil；The investment precoat is made up of the component of following parts by weight：Tung oil：80 ~ 90 parts, 5 ~ 20 parts of pigment, the preparation method of the coating include the preparation of subbing and the preparation of investment precoat.Simple production process of the present invention, colouring effect is good, especially be surface irregularity material surface application effect it is good, require higher field available for environmental-protecting performances such as various packagings for foodstuff, tableware for daily use, toys for children.
Description
Technical field
The invention belongs to technical field of coatings, and in particular to a kind of coating and preparation method thereof.
Background technology
Various coating emerge in an endless stream in recent years, and manufacturer attracts the eye of consumer in color, material and safety, respectively
The material that kind gets close to human body is very high to the quality requirement of coating, and such as toy for children, children are during playing with toys, constantly
Touch toy, or even can also put into the mouth, and coating typically applies the toy watch face that is located at, if quality is not with child getting in contact closely
Reach a standard, have a strong impact on the healthy of children.
Existing coating, in use, is typically easy to problems with occur：Manufacturing procedure complexity, price are big first
More costly；Next material surface to be painted is textured, then extremely influence colouring effect if out-of-flatness；Generally exist again
Admixed in coating with the organic medicament of corrosion-resistant, organic medicament more or less there are some toxicity, unfavorable to health；And
Most of water-resistant coatings are poor, and inconvenience is brought to consumer；Environmental-protecting performance is poor, wherein containing certain formaldehyde, waving
The harmful substances such as hair property organic matter, it will usually give off an unpleasant smell for a long time, the body given people brings lasting harm.
The content of the invention
Technical problem solved by the invention is to provide a kind of coating and preparation method thereof, added with solving existing coating
Work is complicated, surface irregularity is then painted, and effect is undesirable, the problem of be not carried out really environment-protecting and non-poisonous.
Technical problem solved by the invention is realized using following technical scheme：
A kind of coating, including subbing and investment precoat, the subbing are made up of the component of following parts by weight：Quick lime
25 ~ 35 parts, breaking bar/15 ~ 25 parts of dry cow dung, 40 ~ 50 parts of tung oil；The investment precoat is made up of the component of following parts by weight：
Tung oil：80 ~ 90 parts, 5 ~ 20 parts of pigment.
Preferably, the coating include subbing and investment precoat, the subbing by following parts by weight component group
Into：30 parts of quick lime, breaking bar/20 parts of dry cow dung, 50 parts of tung oil；The investment precoat is made up of the component of following parts by weight：
Tung oil：85 parts, 15 parts of pigment.
Further, the pigment is inorganic pigment, and it is selected from, and titanium yellow, titanium chromium palm fibre, cobalt green, cobalt blue, siderochrome be black, iron zinc
Chromium palm fibre, copper-chrome black, bismuth are yellow, compound titan yellow or composite titanium it is red in one kind.
Further, the pigment is pig blood.
A kind of preparation method of coating, the preparation method of the coating uses the raw material of above-mentioned each parts by weight, and it is prepared
Step is as follows：
（1）The preparation of subbing：Quick lime, breaking bar/dry cow dung, tung oil are weighed in proportion, and load weighted each component is mixed
Merging is packed after stirring；
（2）The preparation of investment precoat：Tung oil and pigment are weighed in proportion, and tung oil is heated to after 60 ~ 70 DEG C, added while stirring
Inorganic pigment, cools down after stirring, packs.Further, a kind of preparation method of coating, the preparation method of the coating is used
To the raw material of above-mentioned each parts by weight, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, breaking bar/dry cow dung, tung oil are weighed in proportion, and load weighted each component is mixed
Merging is packed after stirring；
（2）The preparation of investment precoat：Tung oil and fresh pig blood are weighed in proportion, and tung oil and fresh pig blood are poured into reactor, side
Heating side is stirred untill water content is less than 1%, cooling, packaging.
Beneficial effect：A kind of coating of the present invention, meets European Union's RoHS standards, EN71-3 standards, U.S. through SGS detections
State's ASTM F963 standards, US FDA standard, will available for environmental-protecting performances such as various packagings for foodstuff, tableware for daily use, toys for children
Ask higher field, and simple production process of the present invention, colouring effect is good, be especially that the material surface of surface irregularity should
It is good with effect, with preferably practicality and promotional value.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below
One step illustrates the present invention.
Specific embodiment 1
The present embodiment includes subbing and investment precoat, and subbing includes following components：Quick lime 30kg, breaking bar
20kg, tung oil 50kg；Investment precoat includes following components：Tung oil：85 parts, 15 parts of pig blood.
The preparation method of coating based on said components, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, breaking bar, tung oil are weighed by as above weight, load weighted each component is mixed simultaneously
Packed after stirring；
（2）The preparation of investment precoat：Tung oil and fresh pig blood are weighed by as above weight, load weighted tung oil and fresh pig blood are fallen
Enter reactor, heat while stirring untill water content is less than 1%, now substantially without white haze, cooling, packaging in reactor.
Specific embodiment 2
The present embodiment includes subbing and investment precoat, and subbing includes following components：Quick lime 25kg, dry cow dung
25kg, tung oil 50kg；Investment precoat includes following components：Tung oil：80 parts, 20 parts of pig blood.
The preparation method of coating based on said components, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, breaking bar, tung oil are weighed by as above weight, load weighted each component is mixed simultaneously
Packed after stirring；
（2）The preparation of investment precoat：Tung oil and fresh pig blood are weighed by as above weight, load weighted tung oil and fresh pig blood are fallen
Enter reactor, heat while stirring untill water content is less than 1%, now substantially without white haze, cooling, packaging in reactor.
Specific embodiment 3
The present embodiment includes subbing and investment precoat, and subbing includes following components：Quick lime 30kg, dry cow dung
20kg, tung oil 50kg；Investment precoat includes following components：Tung oil：85 parts, 15 parts of inorganic pigment titanium yellow.
The preparation method of coating based on said components, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, dry cow dung, tung oil are weighed by as above weight, load weighted each component is mixed simultaneously
Packed after stirring；
（2）The preparation of investment precoat：Tung oil and inorganic pigment titanium yellow are weighed by as above weight, tung oil is heated to 60 ~ 70 DEG C
Afterwards, inorganic pigment titanium yellow is added while stirring, is cooled down, is packed after stirring.
Specific embodiment 4
The present embodiment includes subbing and investment precoat, and subbing includes following components：Quick lime 35kg, dry cow dung
15kg, tung oil 50kg；Investment precoat includes following components：Tung oil：90 parts, 10 parts of inorganic pigment cobalt blue, inorganic pigment cobalt blue by
Hunan Ju Fa Science and Technology Ltd.s produce.
The preparation method of coating based on said components, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, dry cow dung, tung oil are weighed by as above weight, load weighted each component is mixed simultaneously
Packed after stirring；
（2）The preparation of investment precoat：Tung oil and inorganic pigment titanium yellow are weighed by as above weight, tung oil is heated to 60 ~ 70 DEG C
Afterwards, inorganic pigment cobalt blue is added while stirring, is cooled down, is packed after stirring.
Specific embodiment 5
The present embodiment includes subbing and investment precoat, and subbing includes following components：Quick lime 35kg, breaking bar
25kg, tung oil 40kg；Investment precoat includes following components：Tung oil：80 parts, 20 parts of inorganic pigment iron zinc chrome palm fibre, inorganic pigment iron
Zinc chrome palm fibre is produced by Hunan Ju Fa Science and Technology Ltd.s.
The preparation method of coating based on said components, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, dry cow dung, tung oil are weighed by as above weight, load weighted each component is mixed simultaneously
Packed after stirring；
（2）The preparation of investment precoat：Tung oil and inorganic pigment titanium yellow are weighed by as above weight, tung oil is heated to 60 ~ 70 DEG C
Afterwards, inorganic pigment iron zinc chrome palm fibre is added while stirring, is cooled down, is packed after stirring.
Coating in specific embodiment 1 ~ 5 uses subbing bottoming when in use, first, and the surface of material to be processed is filled
Investment precoat is coated with after smooth again, in practice it has proved that, its colouring effect and color developing effect are superior to these coating in use
General coating, and it is environmentally friendly.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (6)
1. a kind of coating, it is characterised in that including subbing and investment precoat, the subbing by following parts by weight group
It is grouped into：25 ~ 35 parts of quick lime, breaking bar/15 ~ 25 parts of dry cow dung, 40 ~ 50 parts of tung oil；The investment precoat is by following weight
The component composition of part：Tung oil：80 ~ 90 parts, 10 ~ 20 parts of pigment.
2. a kind of coating, it is characterised in that including subbing and investment precoat, the subbing by following parts by weight group
It is grouped into：30 parts of quick lime, breaking bar/20 parts of dry cow dung, 50 parts of tung oil；The investment precoat by following parts by weight component
Composition：Tung oil：85 parts, 15 parts of pigment.
3. a kind of coating according to claim 1 or 2, it is characterised in that the pigment is inorganic pigment, it is selected from titanium nickel
Huang, titanium chromium palm fibre, cobalt green, cobalt blue, black siderochrome, iron zinc chrome palm fibre, copper-chrome black, bismuth are yellow, compound titan yellow or composite titanium it is red in one kind.
4. a kind of coating according to right 1 or 2, it is characterised in that the pigment is pig blood.
5. a kind of preparation method of coating, it is characterised in that the preparation method of the coating uses as described in claim 3
The raw material of each parts by weight, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, breaking bar/dry cow dung, tung oil are weighed in proportion, and load weighted each component is mixed
Merging is packed after stirring；
（2）The preparation of investment precoat：Tung oil and pigment are weighed in proportion, and tung oil is heated to after 60 ~ 70 DEG C, added while stirring
Inorganic pigment, cools down after stirring, packs.
6. a kind of preparation method of coating, it is characterised in that the preparation method of the coating uses as described in claim 4
The raw material of each parts by weight, its preparation process is as follows：
（1）The preparation of subbing：Quick lime, breaking bar/dry cow dung, tung oil are weighed in proportion, and load weighted each component is mixed
Merging is packed after stirring；
（2）The preparation of investment precoat：Tung oil and fresh pig blood are weighed in proportion, and tung oil and fresh pig blood are poured into reactor, side
Heating side is stirred untill water content is less than 1%, cooling, packaging.