CN107011751A - A kind of electrical equipment negative ion paint and preparation method thereof - Google Patents
A kind of electrical equipment negative ion paint and preparation method thereof Download PDFInfo
- Publication number
- CN107011751A CN107011751A CN201710272055.1A CN201710272055A CN107011751A CN 107011751 A CN107011751 A CN 107011751A CN 201710272055 A CN201710272055 A CN 201710272055A CN 107011751 A CN107011751 A CN 107011751A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative ion
- powder
- electrical equipment
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of electrical equipment negative ion paint and preparation method thereof, and the components by weight percent of raw material is：17 24 parts of polyacrylic acid, 11 18 parts of titanium dioxide, 11 17 parts of animal bone powder, 19 27 parts of calcium carbonate, 6 11 parts of zinc oxide, 7 12 parts of ten dicalcium of oxidation, 14 aluminium, 25 parts of negative ion powder, 13 parts of antistatic additive, 15 30 parts of deionized water.Raw material can not only strengthen the plasticity of negative ion paint, and can also effectively lift the anion burst size of negative ion paint, and whole operation is convenient easy, can be with further genralrlization application.
Description
Technical field
The present invention relates to paint field, and in particular to a kind of electrical equipment negative ion paint and preparation method thereof.
Background technology
With present industrialization, information-based development people pursue also more and more higher for the living standard of itself, especially
It is the contemporary society of industrialization development.According to geodesy and the reason of air joint committee of geographic physical League of Nations
By negative aeroion is the anion of debita spissitudo in OH- (H2O) n, O2- (H2O) n and CO4- (H2O) n, air to the mankind's
Health, long-lived and ecological environment have highly beneficial effect.
The existence and form of the trace harmful gases floated in air be it is complicated and various, have with gas ionization
Molecular state is present, and what is had surrounds to form cation by the positive charge absorption floated in air, and some minimum gas are in air
It is middle that to occur heterogeneous heterocoagulation process be that gas molecule deposits on the particle surface existed, condenses and form aeresols
System.
But the coating used on some present electrical equipments while production and processing to save cost, using compared with
Produced for common and easier method, the common coating of electrical equipment has a large amount of poisonous and harmful elements, for a long time
Use, can gradually discharge in the energized state, further injury can be also caused to the human body often contacted.Exist currently on the market
Negative ion paint, although containing anion composition, but when specifically used, the DeGrain of release so that promotion effect
Difference.
The content of the invention
In view of the shortcomings of the prior art, the invention provides a kind of electrical equipment negative ion paint and preparation method thereof,
It can effectively solve the problem that the problem of anion composition release of negative ion paint is difficult.
To realize object above, the present invention is achieved by the following technical programs：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：17-24 parts of polyacrylic acid, titanium dioxide 11-18
Part, 11-17 parts of animal bone powder, 19-27 parts of calcium carbonate, 6-11 parts of zinc oxide, 7-12 parts of ten dicalcium of oxidation, 14 aluminium, negative ion powder
2-5 parts, 1-3 parts of antistatic additive, 15-30 parts of deionized water.
Preferably, the components by weight percent of raw material is：19-22 parts of polyacrylic acid, 13-17 parts of titanium dioxide, animal bone powder 12-15
Part, 21-25 parts of calcium carbonate, 7-10 parts of zinc oxide, 8-10 parts of ten dicalcium of oxidation, 14 aluminium, 2-4 parts of negative ion powder, antistatic additive 1-
3 parts, 18-27 parts of deionized water.
Preferably, the components by weight percent of raw material is：21 parts of polyacrylic acid, 16 parts of titanium dioxide, 14 parts of animal bone powder, calcium carbonate 24
Part, 9 parts of zinc oxide, 9 parts of ten dicalcium of oxidation, 14 aluminium, 4 parts of negative ion powder, 3 parts of antistatic additive, 25 parts of deionized water.
Preferably, described negative ion powder is 1 in mass ratio by iron dravite powder and rare earth element powder:3 ratio is mixed
Conjunction is formed.
The preparation method of described electrical equipment negative ion paint, operating procedure is as follows：
1) raw material polyacrylic acid, zinc oxide, oxidation ten dicalcium 14 aluminium, negative ion powder, antistatic additive, deionized water are pressed
Parts by weight are mixed, and it is 0.5-0.7mpa to control reaction pressure, react 1-2h, standby；
2) in step 1) processing after raw material in addition titanium dioxide, animal bone powder, calcium carbonate, controlling reaction temperature is 40-
50 DEG C, the stirring reaction time is 3-4h, and adjusts pressure for normal pressure, standby；
3) by step 2) raw material after processing takes out, then defibrination, and fineness control is less than 10um, and regulation is to needing viscosity i.e.
Can.
Preferably, described step 2) processing after raw material addition titanium dioxide, animal bone powder, calcium carbonate addition when, it is necessary to
It is slowly added after mixing under stirring.
The invention provides a kind of electrical equipment negative ion paint and preparation method thereof, the titanium dioxide added in raw material,
Animal bone powder, calcium carbonate, zinc oxide and negative ion powder composition can not only strengthen the plasticity of negative ion paint, and can also effectively carry
Rise the anion burst size of negative ion paint, with curing rate is fast, environmental protection, energy-conservation.Whole raw material is easily obtained, and can be easy to processing
Production, and the first carry out compressive reaction used in preparation method, then by add titanium dioxide, animal bone powder, calcium carbonate and bear from
Sub- powder, then defibrination so that raw material reaches effectively good anion burst size effect, it is to avoid cause to mix in other raw materials
Afterwards, it is difficult so that negative ion powder fully discharges anion.Whole operation is convenient easy, can other further genralrlization application.
Embodiment
To make the purpose, technical scheme and advantage of the embodiment of the present invention clearer, below in conjunction with the implementation of the present invention
Example, the technical scheme in the embodiment of the present invention is clearly and completely described.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of creative work is not made, belongs to protection of the present invention
Scope.
Embodiment 1：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：It is 21 parts of polyacrylic acid, 16 parts of titanium dioxide, dynamic
14 parts of thing bone meal, 24 parts of calcium carbonate, 9 parts of zinc oxide, 9 parts of oxidation ten dicalcium 14 aluminium, 4 parts of negative ion powder, 3 parts of antistatic additive,
25 parts of deionized water.
Embodiment 2：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：It is 17 parts of polyacrylic acid, 13 parts of titanium dioxide, dynamic
12 parts of thing bone meal, 21 parts of calcium carbonate, 6 parts of zinc oxide, 9 parts of oxidation ten dicalcium 14 aluminium, 5 parts of negative ion powder, 1 part of antistatic additive,
27 parts of deionized water.
Embodiment 3：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：It is 24 parts of polyacrylic acid, 18 parts of titanium dioxide, dynamic
11 parts of thing bone meal, 25 parts of calcium carbonate, 11 parts of zinc oxide, 9 parts of oxidation ten dicalcium 14 aluminium, 3 parts of negative ion powder, 2 parts of antistatic additive,
18 parts of deionized water.
Embodiment 4：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：It is 22 parts of polyacrylic acid, 17 parts of titanium dioxide, dynamic
15 parts of thing bone meal, 27 parts of calcium carbonate, 10 parts of zinc oxide, 9 parts of oxidation ten dicalcium 14 aluminium, 3 parts of negative ion powder, 2 parts of antistatic additive,
30 parts of deionized water.
Embodiment 5：
A kind of electrical equipment negative ion paint, the components by weight percent of raw material is：It is 19 parts of polyacrylic acid, 11 parts of titanium dioxide, dynamic
17 parts of thing bone meal, 19 parts of calcium carbonate, 7 parts of zinc oxide, 7 parts of oxidation ten dicalcium 14 aluminium, 2 parts of negative ion powder, 1 part of antistatic additive,
15 parts of deionized water.
The preparation method of electrical equipment negative ion paint, operating procedure is as follows：
1) raw material polyacrylic acid, zinc oxide, oxidation ten dicalcium 14 aluminium, negative ion powder, antistatic additive, deionized water are pressed
Parts by weight are mixed, and it is 0.5-0.7mpa to control reaction pressure, react 1-2h, standby；
2) in step 1) processing after raw material in addition titanium dioxide, animal bone powder, calcium carbonate, controlling reaction temperature is 40-
50 DEG C, the stirring reaction time is 3-4h, and adjusts pressure for normal pressure, standby；
3) by step 2) raw material after processing takes out, then defibrination, and fineness control is less than 10um, and regulation is to needing viscosity i.e.
Can.
Step 2) raw material addition titanium dioxide after processing, animal bone powder, calcium carbonate addition when, it is necessary to stirring after mixing
Under be slowly added.
The beneficial effect provided according to the present invention, applicant makes following experimental method and verified：
Experimental group and control group, electrical equipment negative ion paint respectively choose same model and working condition good
Electrical equipment, carries out painting negative ion paint and common negative ion paint that the present invention is provided respectively to it：
Experimental group, anion-generating capacity is more than 1000/cm after testing3；
Control group, anion-generating capacity is more than 365/cm after testing3。
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
The present invention is described in detail, it will be understood by those within the art that：It still can be to foregoing each implementation
Technical scheme described in example is modified, or carries out equivalent substitution to which part technical characteristic；And these modification or
Replace, the essence of appropriate technical solution is departed from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (6)
1. a kind of electrical equipment negative ion paint, it is characterised in that the components by weight percent of raw material is：17-24 parts of polyacrylic acid, titanium
11-18 parts of white powder, 11-17 parts of animal bone powder, 19-27 parts of calcium carbonate, 6-11 parts of zinc oxide, oxidation ten dicalcium 14 aluminium 7-12
Part, 2-5 parts of negative ion powder, 1-3 parts of antistatic additive, 15-30 parts of deionized water.
2. electrical equipment negative ion paint as claimed in claim 1, it is characterised in that the components by weight percent of raw material is：Poly- third
19-22 parts of olefin(e) acid, 13-17 parts of titanium dioxide, 12-15 parts of animal bone powder, 21-25 parts of calcium carbonate, 7-10 parts of zinc oxide, oxidation 12
8-10 parts of 14 aluminium of calcium, 2-4 parts of negative ion powder, 1-3 parts of antistatic additive, 18-27 parts of deionized water.
3. electrical equipment negative ion paint as claimed in claim 2, it is characterised in that the components by weight percent of raw material is：Poly- third
It is 21 parts of olefin(e) acid, 16 parts of titanium dioxide, 14 parts of animal bone powder, 24 parts of calcium carbonate, 9 parts of zinc oxide, 9 parts of oxidation ten dicalcium 14 aluminium, negative
4 parts of ion powder, 3 parts of antistatic additive, 25 parts of deionized water.
4. the electrical equipment negative ion paint as described in claim 1-3 any of which, it is characterised in that it is described bear from
Sub- powder is 1 in mass ratio by iron dravite powder and rare earth element powder:3 ratio is mixed.
5. the preparation method of the electrical equipment negative ion paint as described in claim 1-3 any of which, it is characterised in that
Operating procedure is as follows：
1) by raw material polyacrylic acid, zinc oxide, oxidation ten dicalcium 14 aluminium, negative ion powder, antistatic additive, deionized water by weight
Part is mixed, and it is 0.5-0.7mpa to control reaction pressure, reacts 1-2h, standby；
2) in step 1) processing after raw material in addition titanium dioxide, animal bone powder, calcium carbonate, controlling reaction temperature be 40-50 DEG C,
The stirring reaction time is 3-4h, and adjusts pressure for normal pressure, standby；
3) by step 2) raw material after processing takes out, then defibrination, and fineness control is less than 10um, and regulation is to needing viscosity.
6. described in electrical equipment negative ion paint preparation method, it is characterised in that described step 2) processing after original
, it is necessary to be slowly added after mixing under stirring when material addition titanium dioxide, animal bone powder, calcium carbonate addition.