CN106977971A - Polyester fiber net strengthens the preparation method of impact-resistant panels chestnut shell plastic wood sheet - Google Patents
Polyester fiber net strengthens the preparation method of impact-resistant panels chestnut shell plastic wood sheet Download PDFInfo
- Publication number
- CN106977971A CN106977971A CN201710260015.5A CN201710260015A CN106977971A CN 106977971 A CN106977971 A CN 106977971A CN 201710260015 A CN201710260015 A CN 201710260015A CN 106977971 A CN106977971 A CN 106977971A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- chestnut shell
- preparation
- consumption
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method that a kind of polyester fiber net strengthens impact-resistant panels chestnut shell plastic wood sheet, the preparation method includes:1) chestnut shell, pectase, cellulase and water are soaked, then dries, crushes that chestnut shell powder is made;2) polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell powder melted, cool and solidify that modeling reel body is made;3) when the temperature on the surface of modeling reel body is reduced to 130 145 DEG C, polyester fiber net is coated on to the surface of modeling reel body;4) surface that the anti-impacting layer material of melting is coated on into polyester fiber net forms anti-impacting layer strengthens impact-resistant panels chestnut shell plastic wood sheet so that polyester fiber net is made;Anti-impacting layer material is composed of the following components:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, lanolin magnesium soap and pentaerythrite.The plastic wood sheet has excellent shock resistance.
Description
Technical field
The present invention relates to plastic-wood material, in particular it relates to which polyester fiber net strengthens the system of impact-resistant panels chestnut shell plastic wood sheet
Preparation Method.
Background technology
Plastic-wood material, is also wood plastic composite, as the term suggests it can be regarded as mainly (polypropylene, polyethylene, poly- with plastics
The waste or used plastics of the recovery such as vinyl chloride) it is raw material, it is mixed into new wood by adding the useless string such as wood powder, rice husk, stalk
Material, then through plastic processings such as extruding, molding, injection mouldings, the sheet material or section bar produced;It is mainly used in building
The industries such as material, furniture, logistics packaging.Because plastic-wood material has both the double grading of timber and plastics, plastic-wood material and wooden material
Material is compared and had the advantage that:Water absorption rate is low, is unlikely to deform cracking, Anti-moth-eating, anti-mildew, mechanical performance high, moistureproof, acidproof
Alkali, it is corrosion-resistant, be easy to cleaning.Based on these above-mentioned characteristics cause plastic-wood material can many fields substitute log, plastics and
Aluminium alloy so that it is the following energy-conserving and environment-protective new product of new generation for substituting traditional timber, with extensive market application foreground.
Although for wood materials, the density of plastic-wood material has declined, relative to other lightweight materials
Material, the density of plastic-wood material is still difficult to meet the market demand;The shock resistance of especially existing plastic-wood material is difficult to full
Foot is required.
The content of the invention
It is an object of the invention to provide the preparation method that a kind of polyester fiber net strengthens impact-resistant panels chestnut shell plastic wood sheet, lead to
Crossing polyester fiber net enhancing impact-resistant panels chestnut shell plastic wood sheet made from this method has excellent shock resistance, while the system
Preparation Method has the advantages that process is simple and raw material is easy to get.
To achieve these goals, the invention provides a kind of polyester fiber net enhancing impact-resistant panels chestnut shell plastic wood sheet
Preparation method, the preparation method includes:
1) chestnut shell, pectase, cellulase and water are soaked, then dries, crushes that chestnut shell powder is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell
Powder is melted, cools and solidifies that modeling reel body is made;
3) when the temperature on the surface of modeling reel body is reduced to 130-145 DEG C, polyester fiber net is coated on modeling reel body
Surface;
4) surface that the anti-impacting layer material of melting is coated on into polyester fiber net forms anti-impacting layer polyester fibre is made
Dimension net enhancing impact-resistant panels chestnut shell plastic wood sheet;
Wherein, anti-impacting layer material is composed of the following components:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, sheep
Hair fat magnesium soap and pentaerythrite.
Strengthen impact-resistant panels chestnut shell plastic wood sheet, polyester fiber net enhancing present invention also offers a kind of polyester fiber net
Impact-resistant panels chestnut shell plastic wood sheet is prepared by above-mentioned preparation method.
By above-mentioned technical proposal, the present invention make it that obtained polyester is fine by the synergy of each step and each raw material
Dimension net enhancing impact-resistant panels chestnut shell plastic wood sheet has excellent shock resistance, at the same the preparation method have process simple and
The advantage that raw material is easy to get.
Other features and advantages of the present invention will be described in detail in subsequent embodiment part.
Embodiment
The embodiment to the present invention is described in detail below.It should be appreciated that described herein specific
Embodiment is merely to illustrate and explain the present invention, and is not intended to limit the invention.
The end points and any value of disclosed scope are not limited to the accurate scope or value herein, these scopes or
Value should be understood to comprising the value close to these scopes or value.For number range, between the endpoint value of each scope, respectively
It can be combined with each other between the endpoint value of individual scope and single point value, and individually between point value and obtain one or more
New number range, these number ranges should be considered as specific open herein.
The invention provides the preparation method that a kind of polyester fiber net strengthens impact-resistant panels chestnut shell plastic wood sheet, the preparation side
Method includes:
1) chestnut shell, pectase, cellulase and water are soaked, then dries, crushes that chestnut shell powder is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell
Powder is melted, cools and solidifies that modeling reel body is made;
3) when the temperature on the surface of modeling reel body is reduced to 130-145 DEG C, polyester fiber net is coated on modeling reel body
Surface;
4) surface that the anti-impacting layer material of melting is coated on into polyester fiber net forms anti-impacting layer polyester fibre is made
Dimension net enhancing impact-resistant panels chestnut shell plastic wood sheet;
Wherein, anti-impacting layer material is composed of the following components:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, sheep
Hair fat magnesium soap and pentaerythrite.
In the step 1 of above-mentioned preparation method) in, the actual conditions of immersion can be selected in wide scope, but in order to
Make obtained plastic wood sheet that there is more excellent shock resistance, it is preferable that in step 1) in, immersion at least meets following bar
Part:Soaking temperature is 35-45 DEG C, and soak time is 30-40h.
In the step 1 of above-mentioned preparation method) in, dry actual conditions can be selected in wide scope, but in order to
Make obtained plastic wood sheet that there is more excellent shock resistance, it is preferable that drying at least meets following condition:Drying temperature is
110-120 DEG C, drying time is 5-7h.
In the step 1 of above-mentioned preparation method) in, the grain diameter of chestnut shell powder can be selected in wide scope, still
In order that obtained plastic wood sheet has more excellent shock resistance, it is preferable that the grain diameter of chestnut shell powder is 3-7mm.
In the step 1 of above-mentioned preparation method) in, the consumption of each material can be selected in wide scope, but in order that
Obtained plastic wood sheet has more excellent shock resistance, it is preferable that in step 1) in, relative to the Chinese chestnut of 100 parts by weight
Shell, the consumption of pectase is 1-1.5 parts by weight, and the consumption of cellulase is 0.8-1.2 parts by weight, and the consumption of water is 300-500
Parts by weight.
In the step 2 of above-mentioned preparation method) in, the actual conditions of melting can be selected in wide scope, but in order to
Make obtained plastic wood sheet that there is more excellent shock resistance, it is preferable that in step 2) in, melting at least meets following bar
Part:Melting temperature is 190-205 DEG C, and the melting time is 3-4h.
In the step 2 of above-mentioned preparation method) in, the consumption of each material can be selected in wide scope, but in order that
Obtained plastic wood sheet has more excellent shock resistance, it is preferable that in step 2) in, relative to the polychlorostyrene of 100 parts by weight
Ethene, the consumption of polyvinyl alcohol is 40-60 parts by weight, and the consumption of alumina powder is 4-8 parts by weight, diisooctyl phthalate
Consumption be 26-38 parts by weight, the consumption of castor oil is 42-55 parts by weight, and the consumption of silicone oil is 10-17 parts by weight, chestnut shell
The consumption of powder is 70-88 parts by weight.
In the step 3 of above-mentioned preparation method) in, the specification of polyester fiber net can be selected in wide scope, but be
Make obtained plastic wood sheet that there is more excellent shock resistance, it is preferable that in step 3) in, polyester fiber net at least meets
Following condition:String diameter is 1.5-2.5mm, and the distance between adjacent two polyester fibers silk is 2-5cm.
In the step 4 of above-mentioned preparation method) in, the temperature of the anti-impacting layer material of melting can be selected in wide scope
Select, but in order that obtained plastic wood sheet has more excellent shock resistance, it is preferable that in step 4) in, melting it is anti-
The temperature for impacting layer material is 178-186 DEG C.
In the step 4 of above-mentioned preparation method) in, the consumption of material can be selected in wide scope, but in order that system
The plastic wood sheet obtained has more excellent shock resistance, it is preferable that in step 4) in, relative to the asphalt mixtures modified by epoxy resin of 100 parts by weight
Fat, the consumption of carbon fiber is 14-19 parts by weight, and the consumption of nanomete talc powder is 5-10 parts by weight, and the consumption of konjaku flour is 40-48
Parts by weight, the consumption of lanolin magnesium soap is 22-31 parts by weight, and the consumption of pentaerythrite is 35-49 parts by weight.
In the step 4 of above-mentioned preparation method) in, the thickness of anti-impacting layer can be selected in wide scope, but in order to
Make obtained plastic wood sheet that there is more excellent shock resistance, it is preferable that in step 4) in, the thickness of anti-impacting layer is 2-
3mm。
Strengthen impact-resistant panels chestnut shell plastic wood sheet, polyester fiber net enhancing present invention also offers a kind of polyester fiber net
Impact-resistant panels chestnut shell plastic wood sheet is prepared by above-mentioned preparation method.
The present invention will be described in detail by way of examples below.
Embodiment 1
1) by chestnut shell, pectase, cellulase and water according to 100:1.2:1.0:400 weight ratio is in immersion at 40 DEG C
35h, then in dry 6h, crushing at 115 DEG C so that chestnut shell powder of the grain diameter as 5mm is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell
Powder is according to 100:50:6:33:48:15:758 weight ratio is in melting 5h, cooling and solidifying at 200 DEG C with the obtained modeling reel
Body;
3) when the temperature on the surface of the modeling reel body is reduced to 130-145 DEG C, by polyester fiber net, (string diameter is 2mm, phase
The distance between adjacent two polyester fibers silk is 3cm) it is coated on the surface of the modeling reel body;
4) surface that 180 DEG C of anti-impacting layer material is coated on into polyester fiber net forms the shock resistance that thickness is 2.5mm
Layer strengthens impact-resistant panels chestnut shell plastic wood sheet A1 so that the polyester fiber net is made;Wherein, the anti-impacting layer material is by following
Component is constituted:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, lanolin magnesium soap and pentaerythrite and weight ratio is followed successively by
100:16:8:44:28:42.
Embodiment 2
1) by chestnut shell, pectase, cellulase and water according to 100:1:0.8:300 weight ratio is in immersion at 35 DEG C
30h, then in dry 5-7h, crushing at 110 DEG C so that chestnut shell powder of the grain diameter as 3mm is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell
Powder is according to 100:40:4:26:42:10:70 weight ratio moulds reel body in melting 3h, cooling and solidifying at 190 DEG C to be made described;
3) when the temperature on surface of the modeling reel body is reduced to 130-145 DEG C, by polyester fiber net (string diameter is 1.5mm,
The distance between adjacent two polyester fibers silk is 2cm) it is coated on the surface of the modeling reel body;
4) surface that 178 DEG C of anti-impacting layer material is coated on into polyester fiber net forms the anti-impacting layer that thickness is 2mm
So that the polyester fiber net enhancing impact-resistant panels chestnut shell plastic wood sheet A2 is made;Wherein, the anti-impacting layer material is by with the following group
It is grouped into:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, lanolin magnesium soap and pentaerythrite and weight ratio is followed successively by
100:14:5:40:22:35.
Embodiment 3
1) by chestnut shell, pectase, cellulase and water according to 100:1.5:1.2:500 weight ratio is in immersion at 45 DEG C
40h, then in dry 7h, crushing at 120 DEG C so that chestnut shell powder of the grain diameter as 7mm is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and chestnut shell
Powder is according to 100:60:8:38:55:17:88 weight ratio moulds reel body in melting 4h, cooling and solidifying at 205 DEG C to be made described;
3) when the temperature on surface of the modeling reel body is reduced to 130-145 DEG C, by polyester fiber net (string diameter is 2.5mm,
The distance between adjacent two polyester fibers silk is 5cm) it is coated on the surface of the modeling reel body;
4) surface that 186 DEG C of anti-impacting layer material is coated on into polyester fiber net forms the anti-impacting layer that thickness is 3mm
So that the polyester fiber net enhancing impact-resistant panels chestnut shell plastic wood sheet A3 is made;Wherein, the anti-impacting layer material is by with the following group
It is grouped into:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, lanolin magnesium soap and pentaerythrite and weight ratio is followed successively by
100:19:10:48:31:49.
Comparative example 1
Method according to embodiment 1 carries out that plastic wood sheet B1 is made, unlike, step 1 is not carried out).
Comparative example 2
Method according to embodiment 1 carries out that plastic wood sheet B2 is made, unlike, step 2) chestnut shell powder is not used.
Comparative example 3
Method according to embodiment 1 carries out that plastic wood sheet B3 is made, unlike, step 3 is not carried out).
Comparative example 4
Method according to embodiment 1 carries out that plastic wood sheet B4 is made, unlike, step 4) in carbon fiber is not used.
Comparative example 5
Method according to embodiment 1 carries out that plastic wood sheet B5 is made, unlike, step 4) in nano-talc is not used
Powder.
Comparative example 6
Method according to embodiment 1 carries out that plastic wood sheet B6 is made, unlike, step 4) in konjaku flour is not used.
Comparative example 7
Method according to embodiment 1 carries out that plastic wood sheet B7 is made, unlike, step 4) in lanolin magnesium is not used
Soap.
Detect example 1
The normal temperature ball falling impact time for detecting above-mentioned plastic wood sheet according to the GB/T24508-2009 methods recorded, (standard will
Seeking Truth pit diameter≤12mm), concrete outcome is shown in Table 1.
Table 1
Pit diameter/mm | |
Embodiment 1 | 5 |
Embodiment 2 | 6 |
Embodiment 3 | 7 |
Comparative example 1 | 11 |
Comparative example 2 | 12 |
Comparative example 3 | 13 |
Comparative example 4 | 12 |
Comparative example 5 | 11 |
Comparative example 6 | 10 |
Comparative example 7 | 10 |
By above-described embodiment, comparative example and detection example, the polyester fiber net enhancing impact-resistant panels that the present invention is provided
Chestnut shell plastic wood sheet has excellent shock resistance.
The preferred embodiment of the present invention described in detail above, still, the present invention are not limited in above-mentioned embodiment
Detail, in the range of the technology design of the present invention, a variety of simple variants can be carried out to technical scheme, this
A little simple variants belong to protection scope of the present invention.
It is further to note that each particular technique feature described in above-mentioned embodiment, in not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to it is various can
The combination of energy no longer separately illustrates.
In addition, various embodiments of the present invention can be combined randomly, as long as it is without prejudice to originally
The thought of invention, it should equally be considered as content disclosed in this invention.
Claims (10)
1. a kind of polyester fiber net strengthens the preparation method of impact-resistant panels chestnut shell plastic wood sheet, it is characterised in that the preparation side
Method includes:
1) chestnut shell, pectase, cellulase and water are soaked, then dries, crushes that chestnut shell powder is made;
2) by polyvinyl chloride, polyvinyl alcohol, alumina powder, diisooctyl phthalate, castor oil, silicone oil and the chestnut shell
Powder is melted, cools and solidifies that the modeling reel body is made;
3) when the temperature on the surface of the modeling reel body is reduced to 130-145 DEG C, polyester fiber net is coated on the modeling reel
The surface of body;
4) surface that the anti-impacting layer material of melting is coated on into the polyester fiber net forms anti-impacting layer to be made described poly-
Ester fiber net strengthens impact-resistant panels chestnut shell plastic wood sheet;
Wherein, the anti-impacting layer material is composed of the following components:Epoxy resin, carbon fiber, nanomete talc powder, konjaku flour, sheep
Hair fat magnesium soap and pentaerythrite.
2. preparation method according to claim 1, wherein, in step 1) in, the immersion at least meets following condition:Leaching
It is 35-45 DEG C to steep temperature, and soak time is 30-40h;
Preferably, the drying at least meets following condition:Drying temperature is 110-120 DEG C, and drying time is 5-7h;
It is highly preferred that the grain diameter of the chestnut shell powder is 3-7mm.
3. preparation method according to claim 1 or 2, wherein, in step 1) in, relative to the plate of 100 parts by weight
Chestnut shell, the consumption of the pectase is 1-1.5 parts by weight, and the consumption of the cellulase is 0.8-1.2 parts by weight, the water
Consumption is 300-500 parts by weight.
4. preparation method according to claim 3, wherein, in step 2) in, the melting at least meets following condition:It is molten
Melt temperature for 190-205 DEG C, the melting time is 3-4h.
5. preparation method according to claim 4, wherein, in step 2) in, relative to the polychlorostyrene second of 100 parts by weight
Alkene, the consumption of the polyvinyl alcohol is 40-60 parts by weight, and the consumption of the alumina powder is 4-8 parts by weight, the O-phthalic
The consumption of sour two isodecyl esters is 26-38 parts by weight, and the consumption of the castor oil is 42-55 parts by weight, and the consumption of the silicone oil is
10-17 parts by weight, the consumption of the chestnut shell powder is 70-88 parts by weight.
6. the preparation method according to claim 3 or 4, wherein, in step 3) in, the polyester fiber net at least meet with
Lower condition:String diameter is 1.5-2.5mm, and the distance between adjacent two polyester fibers silk is 2-5cm.
7. preparation method according to claim 6, wherein, in step 4) in, the temperature of the anti-impacting layer material of the melting
Spend for 178-186 DEG C.
8. preparation method according to claim 6, wherein, in step 4) in, relative to the asphalt mixtures modified by epoxy resin of 100 parts by weight
Fat, the consumption of the carbon fiber is 14-19 parts by weight, and the consumption of the nanomete talc powder is 5-10 parts by weight, the konjaku flour
Consumption be 40-48 parts by weight, the consumption of the lanolin magnesium soap is 22-31 parts by weight, and the consumption of the pentaerythrite is 35-
49 parts by weight.
9. the preparation method according to claim 7 or 8, wherein, in step 4) in, the thickness of the anti-impacting layer is 2-
3mm。
10. a kind of polyester fiber net strengthens impact-resistant panels chestnut shell plastic wood sheet, it is characterised in that the polyester fiber net enhancing is anti-
Impact chestnut shell plastic wood sheet is prepared by the preparation method described in any one in claim 1-9.