CN106977197A - Oxide yellow zirconia material - Google Patents
Oxide yellow zirconia material Download PDFInfo
- Publication number
- CN106977197A CN106977197A CN201611056175.XA CN201611056175A CN106977197A CN 106977197 A CN106977197 A CN 106977197A CN 201611056175 A CN201611056175 A CN 201611056175A CN 106977197 A CN106977197 A CN 106977197A
- Authority
- CN
- China
- Prior art keywords
- parts
- yellow
- oxide powder
- sintering
- zirconium oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides the zirconia material that yellow is directly presented after a kind of sintering, includes the raw material of following parts by weight:Zirconium oxide powder:20 ~ 120 parts;Praseodymium oxide:1 ~ 3 part;Dispersant:0.1 ~ 2 part;Binding agent:0.2 2 parts.The oxide yellow zirconia material that the present invention is provided, can be applied to apply on wrist-watch accessory, Cellphone Accessories, various china ornaments, color is beautiful, will never fade.
Description
Technical field
The present invention relates to Material Field, and in particular to the zirconia material directly in yellow and its preparation side after a kind of sintering
Method.
Technical background
The light that our naked eyes can be seen is visible ray, between 380 ~ 780 nanometers, can produce what is become clear in vision system
Color perception, through radiation of visible light, the light of the material meeting some wave bands of selective absorbing, and shows the face of the light of its commplementary wave length
Color.In the range of visible ray, wavelength is different, produces different colour visions.Color shown by material is that it absorbs minimum that
The color of a part of visible ray.
Zirconia ceramics has high intensity, high rigidity, and good toughness is corrosion-resistant to wait premium properties, is widely applied to each
Field., can be with if colorful translucent polycrystalline zirconia material is made because zirconia ceramics has higher refractive index
It is beautiful as heaven and earth jewel.As people improve constantly to the demand of ornament, colored zirconia ceramics are with its excellent machine
Tool performance, chromatic colour, metallic luster and the features such as acted on without allergy, the new material as top grade decoration.But production at present
Colored zirconia ceramics color it is more dull, mostly black and white, thus colored zirconia ceramics research and development have it is wide
Market prospects.
The preparation of common color ceramics is usually that colouring agent or colorant are added in ceramic idiosome or glaze, passes through high temperature
Burn till(General temperature is less than 1300 DEG C)And obtain.And the sintering temperature of zirconia ceramics is higher, 1400 ~ 1650 are commonly reached
℃.At this temperature, most colorant or colouring agent can decompose, volatilize and no longer develop the color or color reduction.Therefore, simply add
The method of additive color material or colouring agent, it is difficult to the bright-coloured colored zirconia ceramics of colour generation are made.
The content of the invention
It is an object of the invention to provide zirconia material that yellow is directly presented after a kind of sintering and preparation method thereof.
In order to solve problem above, adopt the technical scheme that:
The zirconia material of yellow is directly presented after a kind of sintering, includes the raw material of following parts by weight:
Zirconium oxide powder:20 ~ 120 parts;Praseodymium oxide:1 ~ 3 part;Dispersant:0.1 ~ 2 part;Binding agent:0.2-2 parts.
Preferably, the zirconia material of yellow is directly presented after a kind of sintering, includes the raw material of following parts by weight:
Zirconium oxide powder:100 parts;Praseodymium oxide:1-2 parts;Dispersant:0.1 ~ 2 part;Binding agent:0.2-2 parts.
Preferably, the zirconia material of yellow is directly presented after a kind of sintering, includes the raw material of following parts by weight:
Zirconium oxide powder:100 parts;Praseodymium oxide:2-3 parts;Dispersant:0.1 ~ 2 part;Binding agent:0.2-2 parts.
Described zirconium oxide powder is micron order powder, and purity is more than 99.5%.
Described praseodymium oxide powder is micron order powder, and purity is more than 99.5%.
Described dispersant is the fourth fat of phosphoric acid four.
Described binding agent is the PVA aqueous solution, and concentration is 10%.
Directly it is in the preparation method of the zirconia material of yellow after a kind of sintering, comprises the following steps:
(1)The raw material of corresponding number is weighed by weight, and zirconium oxide powder and praseodymium oxide powder are mixed in ball mill
Close, while addition 1:1 part of pure water is solvent, and adds dispersant progress ball milling, obtains component A.
(2)After ball milling 24 hours, slurry is taken to carry out testing graininess, control centre granularity D(50)In 0.5um, rear add is glued
Tie agent and continue ball milling 2 hours.
(3)Dries pulverizing is carried out after slurry is taken out, material powder is obtained.
(4)Powder is pressed into required shape and carries out dry-pressing formed rear sintering, sintering temperature is 1480 degrees Celsius, obtains ceramics
Crude green body.
(5)Crude green body surface is processed, the zirconia material of yellow is can obtain after polishing.
Beneficial effect
Zirconia material made by the present invention, goes for dry-pressing formed, makes Ceramic fitting, effect can meet decoration
With the requirement of ceramics, and with the increase of praseodymium oxide addition, color developing effect more and more substantially can accordingly make a variety of
The different oxide yellow zirconia material of the depth.
Embodiment
Below by instantiation, make further specific description to technical scheme, but the present invention is not limited
In these examples.
Embodiment one:
100 parts of zirconium oxide powder is taken, zirconium oxide powder is added 1 by powder original particle size in 100um or so:1 pure water, in ball
Pre-grinding in grinding machine, ratio of grinding media to material is 3:1,0.1 part of dispersant is added, after zirconium oxide powder is completely dispersed in water, 1 part is added
Praseodymium oxide powder, 24 hours rear center's granularities of ball milling can reach in 0.5um.1 part of binding agent is now added, ball milling mixing is further continued for
2 hours, Zirconium oxide powder is can obtain after discharging drying, yellow zirconium oxide idiosome is can obtain after being sintered through 1480 DEG C.Make after polishing
It is that 88.92, a values are that -76.6, b values are 65.6 that can measure L values with colour developing instrument, is visually observed to be faint yellow.Use universal material
Tester can measure three-point bending resistance intensity for 1400MPA, can meet the use requirement of accessories class ceramic member.
Embodiment two:
100 parts of zirconium oxide powder is taken, zirconium oxide powder is added 1 by powder original particle size in 100um or so:1 pure water, in ball
Grinding machine kind pre-grinding, ratio of grinding media to material is 3:1,1 part of dispersant is added, after zirconium oxide powder is completely dispersed in water, 2 parts of oxygen is added
Change praseodymium powder, 24 hours rear center's granularities of ball milling can reach 0.3um. and now add 1.5 parts of binding agent, be further continued for ball milling mixing 2
Hour, Zirconium oxide powder is can obtain after discharging drying, yellow zirconium oxide idiosome can be obtained after being sintered through 1480 DEG C.Using aobvious after polishing
It is that 90.62, a values are that -72.3, b values are 79.2 that color instrument, which can measure L values,.Three-point bending resistance can be measured using universal material tester
Intensity is 1382MPA, can meet the use requirement of accessories class ceramic member.
Embodiment three:
80 parts of zirconium oxide powder is taken, zirconium oxide powder is added 1 by powder original particle size in 100um or so:1 pure water, in ball milling
Machine pre-grinding, ratio of grinding media to material is 3:1,2 parts of dispersants are added, after zirconium oxide powder is completely dispersed in water, 3 parts of oxidation are added
Praseodymium powder, 24 hours rear center's granularities of ball milling can reach 0.10um. and now add 1.5 parts of binding agent, be further continued for ball milling mixing 2 small
When, Zirconium oxide powder is can obtain after discharging drying, yellow zirconium oxide idiosome can be obtained after being sintered through 1480 DEG C.Colour developing is used after polishing
It is that 90.65, a values are that -70.2, b values are 82.3 that instrument, which can measure L values,.It is strong that three-point bending resistance can be measured using universal material tester
Spend for 1290MPA, the use requirement of accessories class ceramic member can be met.
Finally it should be noted that the above embodiments are merely illustrative of the technical solutions of the present invention rather than the present invention is protected
The limitation of scope, although being elaborated with reference to preferred embodiment to the present invention, one of ordinary skill in the art should manage
Solution, can modify or equivalent substitution to technical scheme, without departing from the essence and model of technical solution of the present invention
Enclose.
Claims (5)
1. directly it is in the zirconia material of yellow after a kind of sintering, it is characterised in that include the raw material of following parts by weight:
Zirconium oxide powder:20 ~ 120 parts;Praseodymium oxide:1 ~ 3 part;Dispersant:0.1 ~ 2 part;Binding agent:0.2-2 parts.
2. the zirconia material of direct yellow after a kind of sintering according to claim 1, it is characterised in that comprising following heavy
Measure the raw material of part:
Zirconium oxide powder:50-100 parts;Praseodymium oxide:2-3 parts;Dispersant:0.5-2 parts;Binding agent:0.2-1 parts.
3. after a kind of sintering according to claims 1 directly be in yellow zirconia material, it is characterised in that including with
The raw material of lower parts by weight:
Zirconium oxide powder:100 parts;Praseodymium oxide:2.5 part;Dispersant:0.5 part;Binding agent:0.5 part.
4. directly it is in the zirconia material of yellow after a kind of sintering according to claim 1 or 2 or 3, it is characterised in that institute
Zirconia material is stated for micron order zirconium oxide powder, purity with the addition of yittrium oxide modification more than 99.5%, and dispersant is
The fourth fat of phosphoric acid four, binding agent is the 10%PVA aqueous solution.
5. directly it is in the preparation method of the zirconia material of yellow after a kind of sintering, it is characterised in that comprise the following steps:
(1)The raw material of corresponding number is weighed by weight, and zirconium oxide powder is mixed with praseodymium oxide powder in ball mill,
Addition 1 simultaneously:1 part of pure water is solvent, and adds dispersant progress ball milling, obtains component A;
(2)After ball milling 24 hours, slurry is taken to carry out testing graininess, control centre granularity D(50)In 0.5um, binding agent is added afterwards
Continue ball milling 2 hours;
(3)Dries pulverizing is carried out after slurry is taken out, material powder is obtained;
(4)Powder is pressed into required shape and carries out dry-pressing formed rear sintering, sintering temperature is 1480 degrees Celsius, obtains ceramic crude green body;
(5)Crude green body surface is processed, the zirconia material of yellow is can obtain after polishing.