CN106977087A - The face-down tempering processing method of glass-film - Google Patents
The face-down tempering processing method of glass-film Download PDFInfo
- Publication number
- CN106977087A CN106977087A CN201710164540.7A CN201710164540A CN106977087A CN 106977087 A CN106977087 A CN 106977087A CN 201710164540 A CN201710164540 A CN 201710164540A CN 106977087 A CN106977087 A CN 106977087A
- Authority
- CN
- China
- Prior art keywords
- glass
- film
- product
- face
- tempering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of face-down tempering processing method of glass-film, 1）, the polishing of 1000 mesh sand paper is carried out to the ceramic track of glass tempering furnace；2）, in step 1）Resistance to more than 1000 DEG C round and smooth of high-temperature resistant rubber is wound on the ceramic track polished；3）, the film surface of glass to be toughened is placed on downwards step 2）Annealing furnace is sent on ceramic track after processing.Beneficial effects of the present invention are：After glass-film placed face down, product can be even into annealing furnace, and product is crawled on the track wound, because raceway surface has round and smooth material winding, therefore, any injury will not be formed to film surface.It can ensure that film surface carries out tempering down, it is ensured that the quality of product.Technical scheme does not influence the testing result of product toughening degree, and granularity, flatness and intensity are up to state standards.
Description
Technical field
The present invention relates to glass working arts field, more particularly to a kind of face-down tempering processing method of glass-film.
Background technology
Prior art, glass film surface tempering can only be handled upward., can not be in flat steel if glass surface has the product of printing
Change and tempering processing is carried out in stove.
The content of the invention
For the problems of the prior art, the invention aims to provide a kind of glass-film face-down tempering processing side
Method.
In order to achieve the above object, the technical scheme is that：A kind of face-down tempering processing method of glass-film,
1）, the polishing of 1000 mesh sand paper is carried out to the ceramic track of glass tempering furnace；
2）, in step 1）Resistance to more than 1000 DEG C round and smooth of high-temperature resistant rubber is wound on the ceramic track polished；
3）, the film surface of glass to be toughened is placed on downwards step 2）Annealing furnace is sent on ceramic track after processing.
Further, as a preferred embodiment, the high-temperature resistant rubber is silicon rubber.
Beneficial effects of the present invention are：After glass-film placed face down, product can be even into annealing furnace, and product is crawled
On the track wound, because raceway surface has round and smooth material winding, therefore, any injury will not be formed to film surface.
It can ensure that film surface carries out tempering down, it is ensured that the quality of product.Technical scheme does not influence the inspection of product toughening degree
Result is surveyed, granularity, flatness and intensity are up to state standards.
Embodiment
Technical scheme will be clearly and completely described below, it is clear that described embodiment is this hair
Bright a part of embodiment, rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not having
There is the every other embodiment made and obtained under the premise of creative work, belong to the scope of protection of the invention.
In the description of the invention, it is necessary to explanation, term " " center ", " on ", " under ", "left", "right", " vertical ",
The orientation or position relationship of the instruction such as " level ", " interior ", " outer " be based on orientation shown in the drawings or position relationship, merely to
Be easy to the description present invention and simplify description, rather than indicate or imply signified device or element must have specific orientation,
With specific azimuth configuration and operation, therefore it is not considered as limiting the invention.In addition, term " first ", " second ",
" the 3rd " is only used for describing purpose, and it is not intended that indicating or implying relative importance.
In the description of the invention, it is necessary to illustrate, unless otherwise clearly defined and limited, term " installation ", " phase
Even ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected, or be integrally connected；Can
To be mechanical connection or electrical connection；Can be joined directly together, can also be indirectly connected to by intermediary, Ke Yishi
The connection of two element internals.For the ordinary skill in the art, with concrete condition above-mentioned term can be understood at this
Concrete meaning in invention.
Embodiment 1
A kind of face-down tempering processing method of glass-film,
1）, the polishing of 1000 mesh sand paper is carried out to the ceramic track of glass tempering furnace；
2）, in step 1）Resistance to more than 1000 DEG C round and smooth of high-temperature-resisting silicon rubber is wound on the ceramic track polished；
3）, the film surface of glass to be toughened is placed on downwards step 2）Annealing furnace is sent on ceramic track after processing.
The present invention operation principle be：After glass-film placed face down, product can be even into annealing furnace, and product is crawled
On the track wound, because raceway surface has round and smooth material winding, therefore, any wound will not be formed to glass film surface
Evil.It can ensure that film surface carries out tempering down, it is ensured that the quality of product.Technical scheme does not influence product toughening degree
Testing result, granularity, flatness and intensity are up to state standards.
All simple deformations made in the case where not departing from core of the present invention or modification each fall within the protection of the present invention
Scope.
Claims (2)
1. a kind of face-down tempering processing method of glass-film, it is characterised in that：
1）, the polishing of 1000 mesh sand paper is carried out to the ceramic track of glass tempering furnace；
2）, in step 1）Round and smooth high-temperature resistant rubber is wound on the ceramic track polished；
3）, the film surface of glass to be toughened is placed on downwards step 2）Annealing furnace is sent on ceramic track after processing.
2. the face-down tempering processing method of glass-film according to claim 1, it is characterised in that：The high-temperature resistant rubber is
At least resistance to more than 1000 DEG C of silicon rubber.