CN1069713A - The manufacture method of color quartz tlass tube - Google Patents
The manufacture method of color quartz tlass tube Download PDFInfo
- Publication number
- CN1069713A CN1069713A CN 92106107 CN92106107A CN1069713A CN 1069713 A CN1069713 A CN 1069713A CN 92106107 CN92106107 CN 92106107 CN 92106107 A CN92106107 A CN 92106107A CN 1069713 A CN1069713 A CN 1069713A
- Authority
- CN
- China
- Prior art keywords
- tube
- tlass
- base
- quartz
- manufacture method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Disclosed by the invention is the method for manufacturing technology of coloured quartz glass tube.It is that silica material and quartzy material are prepared burden by 2.5-4: 1-2 weight ratios, and being crushed to granularity 8-20 orders is base-material, gets 0.1-1% tinting material; Soak and the back oven dry that stirs with base-material 15-25% deionized water, when sending continuous induction melting furnace to be warmed up to 1800-1950 ℃ gradually, be drawn into color quartz tlass tube.Given color quartz tlass tube is owing to be the tube wall integral colouring, still kept the far-infrared radiated property that milky white quartz glass tube had, can draw out versicolor silica glass, caliber can be controlled between 5-25mm, is suitable for mass industrialized production.
Description
The present invention relates to the working method of quartz glass product, specifically the method for manufacturing technology of coloured quartz glass tube.
As everyone knows, the thermal expansivity of silica glass is little, and has high temperature resistant, saturating ultraviolet, saturating characteristics such as infrared, is applied to more and more widely on the industry and the product for civilian use.In existing transparent and two kinds of quartz glass tubes of oyster white, because milky white quartz glass tube is to be disperse phase with the bubble, its specific refractory power is 1, is much better than the specific refractory power of transparent quartz tube, but also has stronger far-infrared radiated property.Do infrared heating element with it, quick heating, good insulation preformance, but, people are far from suitable because its color dullness visually feels bad.In order to adapt to user's demand visually, the relevant personnel are seeking to make the processing method of stained glass pipe always for many years, adapt to the demand of current development in science and technology.Put down in writing in the clear 42-9888 specification sheets of disclosed Japan's special permission, it is nonmetal heating unit to be put in the mixed solution that has tinting material soak, the mixed solution that has tinting material like this enters this bar-shaped heating element center, with this heating element energising fused quartz powder, can obtain the opaque silica glass pipe of the inside band look again.With the color quartz tlass tube of this method processing owing to be that internal surface is painted, tinting material is uniformly dispersed, so bubble seldom in the goods, far-infrared radiated property in use is lower than former non-staining quartz glass tube, and its complete processing complexity, the cost height, the external diameter of pipe only limits within the 13mm, now, can not produce in enormous quantities also just at laboratory stage.
The objective of the invention is the shortcoming at above-mentioned existence, provide a kind of complete processing simple, tube wall integral colouring, far-infrared radiated property is good, the working method of the color quartz tlass tube that can produce in batches.
Technical essential of the present invention is:
Silica material and quartzy material are pressed 2.5-4: 1-2 weight ratio batching, being crushed to granularity 8-20 order is base-material, gets the weight 0.1-1% tinting material of base-material; Soak and the back oven dry that stirs with base-material weight 15-25% deionized water, when crucible oven or continuous induction melting furnace are warmed up to 1800-1950 ℃ gradually, be drawn into color quartz tlass tube.
The given color quartz tlass tube of the present invention is owing to be the tube wall integral colouring, still the far-infrared radiated property that has kept the white quartz Glass tubing to be had, pass through add tinting material variation can draw out versicolor silica glass, its caliber can be controlled between the 5-25mm as required, its complete processing is simple, is suitable for mass industrialized production.This colored quartz glass tube meets user's demand visually fully.
The present invention is 1.5-2.5 hour the said time with deionized water soaking and stirring base-material and tinting material, and drying time is 8-24 hour.Tinting material is elements such as titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, neodymium, samarium, also can be a kind of compound of element wherein.
Embodiment:
1, gets silica material and quartzy material by weight at 3: 1, be crushed to 15 orders, the 0.5% tinting material copper powder that adds above-mentioned base-material weight, soaked 2 hours and stir with its deionized water of 20%, then through oven dry in 20 hours, when sending crucible oven or continuous induction melting furnace to be warmed up to 1850 ℃, be drawn into pink silica glass tubing.
2, add with Vanadium Pentoxide in FLAKES and be crushed to that (the silica material is 4: 2 with the proportioning of quartzy material in 10 purpose silica material and the quartzy material, Vanadium Pentoxide in FLAKES be above-mentioned two material close 0.8%), deionized water with base-material weight 25% soaks, stirred 2 hours and dried 20 hours, go into crucible oven or continuous induction melting furnace then when being warmed up to 1950 ℃ gradually, be drawn into the pipes-black of certain specification.
The color quartz tlass tube that adopts aforesaid method to obtain, switch on after loading onto resistance wire in its pipe, the heating element insulating pipe that can be used as electric radiator etc. uses, it on visual sense feeling a kind of enjoyment, can be according to actual needs, select versicolor tubing for use, be suitable for people's demand, help user's physical and mental health.
Claims (3)
1, a kind of manufacture method of color quartz tlass tube is characterized in that silica material and crystal are expected by 2.5-4: 1-2 weight ratio batching, and being crushed to granularity 8-20 order is base-material, gets the weight 0.1-1% tinting material of base-material; Soak and the back oven dry that stirs with base-material weight 15-25% deionized water, when sending crucible oven or continuous induction melting furnace to be warmed up to 1800-1950 ℃ gradually, be drawn into color quartz tlass tube.
2, according to the described manufacture method of claim 1, it is characterized in that the said time with deionized water soaking and stirring base-material and tinting material is 1.5-2.5 hour, drying time is 8-24 hour.
3, according to the described manufacture method of claim 1, it is characterized in that said tinting material is elements such as titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, neodymium, samarium, also can be a kind of compound of element wherein.