CN106967292A - A kind of nylon heat conduction new material and preparation method thereof - Google Patents
A kind of nylon heat conduction new material and preparation method thereof Download PDFInfo
- Publication number
- CN106967292A CN106967292A CN201710350925.2A CN201710350925A CN106967292A CN 106967292 A CN106967292 A CN 106967292A CN 201710350925 A CN201710350925 A CN 201710350925A CN 106967292 A CN106967292 A CN 106967292A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat conduction
- nylon
- new material
- compatilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of nylon heat conduction new material, the nylon heat conduction new material includes the component of following mass parts：15 parts of 25 35 parts of nylon, 5 10 parts of Heat Conduction Material, 5 10 parts of conductance powdered iron, 5 10 parts of silver powder, 35 parts of compatilizer, 28 parts of tackifier, 37 parts of toughener, 5 15 parts of butadiene resin, 28 parts of polyvinyl chloride, 13 parts of nano-graphite, 37 parts of antioxidant, 7 15 parts of vinyl silicone oil, 57 parts of glycerin ether and fire retardant.The invention provides a kind of nylon heat conduction new material and preparation method thereof, the new material has good function effect, and the formula of material is simple, cheap, and preparation technology is simple, realizes cost-effective and reduces labor intensity, meets actual operation requirements.
Description
Technical field
The present invention relates to a kind of nylon heat conduction new material and preparation method thereof, belong to new material and fabricating technology neck
Domain.
Background technology
New material refers to some newly-developed or researching and developing, having preeminent performance materials, with than traditional material more
For excellent performance.New material technology is then the will according to people, is processed by physical study, design of material, material, experiment is commented
A series of research process such as valency, create the technology for the new material that can meet various needs.With scientific technological advance, people
On the basis of traditional material, according to the achievement in research of modern science and technology, new material is developed.New material is metal material by component
Material, inorganic non-metallic material（Such as ceramics, gallium arsenide semiconductor）, high-molecular organic material, the major class of advanced composite material four.Press
Material property is divided into structural material and functional material.Structural material mainly uses the mechanics and physicochemical property of material, to meet
The performance requirement such as high intensity, high rigidity, high rigidity, high temperature resistant, wear-resisting, anti-corrosion, Flouride-resistani acid phesphatase；Functional material mainly uses material
The effects such as the electricity, magnetic, sound, the photo-thermal that have, to realize certain function, such as semi-conducting material, magnetic material, light-sensitive material, temperature-sensitive
Material, stealth material and manufacture atom bomb, nuclear material of hydrogen bomb etc..New material acts on great in national defense construction.For example, ultrapure
Silicon, GaAs are succeeded in developing, and cause the birth of extensive and super large-scale integration, make the operational speed of a computer from per second several
Bring up to more than 10,000,000,000 times per second for 100000 times；The operating temperature of materials for aeroengines often improves 100 DEG C, and thrust can increase 24%；
Stealth material energy electromagnetic wave absorption or the infra-red radiation for reducing weaponry, make enemy's detection system be difficult to find etc..21 generation
One of Main way of discipline development in science and technology is the development and application of new material.The research of new material, is that the mankind are recognized physical property
Know and application is marched to deeper.
The research of new material is always the main body of China's scientific research project, if it is possible to research and develop that a composition is simple, raw material is honest and clean
Valency, and the green wood material formula and the simple preparation technology of flow of good result can be reached, will be the big contribution of the mankind.
The content of the invention
The present invention exactly in view of the deficienciess of the prior art, provide a kind of nylon heat conduction new material and preparation method thereof,
The new material has good function effect, and the formula of material is simple, cheap, and preparation technology is simple, realizes section
About cost meets actual operation requirements with reducing labor intensity.
To solve the above problems, the technical solution used in the present invention is as follows：
A kind of nylon heat conduction new material, the nylon heat conduction new material includes the component of following mass parts：25-35 parts of nylon, lead
5-10 parts of hot material, 5-10 parts of conductance powdered iron, 5-10 parts of silver powder, 3-5 parts of compatilizer, 2-8 parts of tackifier, 3-7 parts of toughener, fourth
It is 5-15 parts of diene resin, 2-8 parts of polyvinyl chloride, 1-3 parts of nano-graphite, 3-7 parts of antioxidant, 7-15 parts of vinyl silicone oil, sweet
Oily ether 5-7 parts and 1-5 parts of fire retardant.
As the improvement of above-mentioned technical proposal, the component of the nylon heat conduction new material mass parts is 30 parts of nylon, heat conduction
8 parts of material, 7 parts of conductance powdered iron, 8 parts of silver powder, 4 parts of compatilizer, 5 parts of tackifier, 5 parts of toughener, 10 parts of butadiene resin, polychlorostyrene
3 parts of 5 parts of ethene, 2 parts of nano-graphite, 5 parts of antioxidant, 11 parts of vinyl silicone oil, 6 parts of glycerin ether and fire retardant.
Specifically, a kind of preparation method of nylon heat conduction new material is as follows：
Step（1）：By above-mentioned conductance powdered iron, silver powder, compatilizer, tackifier, butadiene resin, polyvinyl chloride, nano-graphite, anti-
Oxidant, vinyl silicone oil, glycerin ether and fire retardant are proportionally added into homogenizer, are added in two times in whipping process
With the toughener got ready, mixer rotating speed 600-800rpm makes mixing material temperature be raised to 130 DEG C；
Step（2）：By step（1）Material in high speed mixer is released, and is added in low-speed mixer and is cooled, and is added simultaneously
The nylon and Heat Conduction Material of preheated processing, compatilizer is added when temperature drops to 65 degree, is stirred for 15-25 minutes, and mixing is equal
Discharged after even；
Step（3）：To step（2）Obtained mixture carries out plasma-induced；
Wherein, it is described plasma-induced to be：By step（2）The mixture of acquisition inserts the bottom electrode medium of plasma device
On, voltage 24kV is irradiated 35~45 seconds under electric current 1.8mA, gap 3mm operating condition；
Step（4）：By step（3）Mixture is put into single screw extrusion machine after processing, 130-170 DEG C of rotating speed 28- of plasticization temperature
36rpm, material of the present invention is produced by hot-forming twice, then through air-cooled.
Compared with prior art, implementation result of the invention is as follows by the present invention：
The invention provides a kind of nylon heat conduction new material and preparation method thereof, electrode-induced causes material molecule has very good
Selective penetrated property, and then greatly enhance the good function effect that nylon Heat Conduction Material has, the formula of material is simple, valency
Lattice are cheap, and preparation technology is simple, realize cost-effective and reduce labor intensity, meet actual operation requirements.
Note：Nylon Heat Conduction Material produced by the present invention tool extremely excellent ultraviolet resistance, resistance to ozone and chemical-resistant characteristic and
Tensile strength and fracture elongation are big.
Embodiment
Illustrate present disclosure below in conjunction with specific embodiments.
Embodiment 1
A kind of nylon heat conduction new material, the nylon heat conduction new material includes the component of following mass parts：25 parts of nylon, heat conduction material
5 parts of material, 5 parts of conductance powdered iron, 5 parts of silver powder, 3 parts of compatilizer, 2 parts of tackifier, 3 parts of toughener, 5 parts of butadiene resin, polychlorostyrene second
1 part of 2 parts of alkene, 1 part of nano-graphite, 3 parts of antioxidant, 7 parts of vinyl silicone oil, 5 parts of glycerin ether and fire retardant.
Specifically, a kind of preparation method of nylon heat conduction new material is as follows：
Step（1）：By above-mentioned conductance powdered iron, silver powder, compatilizer, tackifier, butadiene resin, polyvinyl chloride, nano-graphite, anti-
Oxidant, vinyl silicone oil, glycerin ether and fire retardant are proportionally added into homogenizer, are added in two times in whipping process
With the toughener got ready, mixer rotating speed 600rpm makes mixing material temperature be raised to 130 DEG C；
Step（2）：By step（1）Material in high speed mixer is released, and is added in low-speed mixer and is cooled, and is added simultaneously
The nylon and Heat Conduction Material of preheated processing, compatilizer is added when temperature drops to 65 degree, is stirred for 15 minutes, after being well mixed
Discharging；
Step（3）：To step（2）Obtained mixture carries out plasma-induced；
Wherein, it is described plasma-induced to be：By step（2）The mixture of acquisition inserts the bottom electrode medium of plasma device
On, voltage 24kV is irradiated 35 seconds under electric current 1.8mA, gap 3mm operating condition；
Step（4）：By step（3）Mixture is put into single screw extrusion machine after processing, 130 DEG C of rotating speed 28rpm of plasticization temperature, warp
It is hot-forming after twice, then produce material of the present invention through air-cooled.
Compared with prior art, implementation result of the invention is as follows by the present invention：
The electrode-induced that the present invention is set is so that material molecule has extraordinary selective penetrated property, and then greatly enhances nylon
The good function effect that Heat Conduction Material has, the formula of material is simple, cheap, and preparation technology is simple, realizes section
About cost meets actual operation requirements with reducing labor intensity.
Note：Nylon Heat Conduction Material produced by the present invention tool extremely excellent ultraviolet resistance, resistance to ozone and chemical-resistant characteristic and
Tensile strength and fracture elongation are big.
Embodiment 2
A kind of nylon heat conduction new material, the nylon heat conduction new material includes the component of following mass parts：30 parts of nylon, heat conduction material
7 parts of material, 8 parts of conductance powdered iron, 7 parts of silver powder, 4 parts of compatilizer, 5 parts of tackifier, 5 parts of toughener, 10 parts of butadiene resin, polychlorostyrene second
3 parts of 5 parts of alkene, 2 parts of nano-graphite, 5 parts of antioxidant, 11 parts of vinyl silicone oil, 6 parts of glycerin ether and fire retardant.
Specifically, a kind of preparation method of nylon heat conduction new material is as follows：
Step（1）：By above-mentioned conductance powdered iron, silver powder, compatilizer, tackifier, butadiene resin, polyvinyl chloride, nano-graphite, anti-
Oxidant, vinyl silicone oil, glycerin ether and fire retardant are proportionally added into homogenizer, are added in two times in whipping process
With the toughener got ready, mixer rotating speed 700rpm makes mixing material temperature be raised to 130 DEG C；
Step（2）：By step（1）Material in high speed mixer is released, and is added in low-speed mixer and is cooled, and is added simultaneously
The nylon and Heat Conduction Material of preheated processing, compatilizer is added when temperature drops to 65 degree, is stirred for 20 minutes, after being well mixed
Discharging；
Step（3）：To step（2）Obtained mixture carries out plasma-induced；
Wherein, it is described plasma-induced to be：By step（2）The mixture of acquisition inserts the bottom electrode medium of plasma device
On, voltage 24kV is irradiated 40 seconds under electric current 1.8mA, gap 3mm operating condition；
Step（4）：By step（3）Mixture is put into single screw extrusion machine after processing, 150 DEG C of rotating speed 32rpm of plasticization temperature, warp
It is hot-forming after twice, then produce material of the present invention through air-cooled.
Compared with prior art, implementation result of the invention is as follows by the present invention：
The electrode-induced that the present invention is set is so that material molecule has extraordinary selective penetrated property, and then greatly enhances nylon
The good function effect that Heat Conduction Material has, the formula of material is simple, cheap, and preparation technology is simple, realizes section
About cost meets actual operation requirements with reducing labor intensity.
Note：Nylon Heat Conduction Material produced by the present invention tool extremely excellent ultraviolet resistance, resistance to ozone and chemical-resistant characteristic and
Tensile strength and fracture elongation are big.
Embodiment 3
A kind of nylon heat conduction new material, the nylon heat conduction new material includes the component of following mass parts：35 parts of nylon, heat conduction material
It is 10 parts of material, 10 parts of conductance powdered iron, 10 parts of silver powder, 5 parts of compatilizer, 8 parts of tackifier, 7 parts of toughener, 15 parts of butadiene resin, poly-
5 parts of 8 parts of vinyl chloride, 3 parts of nano-graphite, 7 parts of antioxidant, 15 parts of vinyl silicone oil, 7 parts of glycerin ether and fire retardant.
Specifically, a kind of preparation method of nylon heat conduction new material is as follows：
Step（1）：By above-mentioned conductance powdered iron, silver powder, compatilizer, tackifier, butadiene resin, polyvinyl chloride, nano-graphite, anti-
Oxidant, vinyl silicone oil, glycerin ether and fire retardant are proportionally added into homogenizer, are added in two times in whipping process
With the toughener got ready, mixer rotating speed 800rpm makes mixing material temperature be raised to 130 DEG C；
Step（2）：By step（1）Material in high speed mixer is released, and is added in low-speed mixer and is cooled, and is added simultaneously
The nylon and Heat Conduction Material of preheated processing, compatilizer is added when temperature drops to 65 degree, is stirred for 25 minutes, after being well mixed
Discharging；
Step（3）：To step（2）Obtained mixture carries out plasma-induced；
Wherein, it is described plasma-induced to be：By step（2）The mixture of acquisition is put on the bottom electrode medium of plasma device,
Irradiated 45 seconds under voltage 24kV, electric current 1.8mA, gap 3mm operating conditions；
Step（4）：By step（3）Mixture is put into single screw extrusion machine after processing, 170 DEG C of rotating speed 36rpm of plasticization temperature, warp
It is hot-forming after twice, then produce material of the present invention through air-cooled.
Compared with prior art, implementation result of the invention is as follows by the present invention：
The electrode-induced that the present invention is set is so that material molecule has extraordinary selective penetrated property, and then greatly enhances nylon
The good function effect that Heat Conduction Material has, the formula of material is simple, cheap, and preparation technology is simple, realizes section
About cost meets actual operation requirements with reducing labor intensity.
Note：Nylon Heat Conduction Material produced by the present invention tool extremely excellent ultraviolet resistance, resistance to ozone and chemical-resistant characteristic and
Tensile strength and fracture elongation are big.
Above content is made for the present invention in conjunction with specific embodiments describes in detail, it is impossible to assert that the present invention is specific real
Apply and be only limitted to these explanations.For those skilled in the art, before present inventive concept is not departed from
Put, some simple deduction or replace can also be made, the scope of protection of the invention should be all considered as belonging to.
Claims (3)
1. a kind of nylon heat conduction new material, it is characterised in that：The nylon heat conduction new material includes the component of following mass parts：Buddhist nun
Imperial 25-35 parts, 5-10 parts of Heat Conduction Material, 5-10 parts of conductance powdered iron, 5-10 parts of silver powder, 3-5 parts of compatilizer, 2-8 parts of tackifier, increasing
Tough dose 3-7 parts, 5-15 parts of butadiene resin, 2-8 parts of polyvinyl chloride, 1-3 parts of nano-graphite, 3-7 parts of antioxidant, vinyl silicon
1-5 parts of oily 7-15 parts, 5-7 parts of glycerin ether and fire retardant.
2. a kind of nylon heat conduction new material according to claim 1, it is characterised in that：The nylon heat conduction new material mass parts
Component be 30 parts of nylon, 8 parts of Heat Conduction Material, 7 parts of conductance powdered iron, 8 parts of silver powder, 4 parts of compatilizer, 5 parts of tackifier, toughener 5
Part, 10 parts of butadiene resin, 5 parts of polyvinyl chloride, 2 parts of nano-graphite, 5 parts of antioxidant, 11 parts of vinyl silicone oil, glycerin ether 6
3 parts of part and fire retardant.
3. a kind of preparation method of nylon heat conduction new material according to claim 1-2, it is characterised in that：The preparation method
It is as follows：
Step（1）：By above-mentioned conductance powdered iron, silver powder, compatilizer, tackifier, butadiene resin, polyvinyl chloride, nano-graphite, anti-
Oxidant, vinyl silicone oil, glycerin ether and fire retardant are proportionally added into homogenizer, are added in two times in whipping process
With the toughener got ready, mixer rotating speed 600-800rpm makes mixing material temperature be raised to 130 DEG C；
Step（2）：By step（1）Material in high speed mixer is released, and is added in low-speed mixer and is cooled, and is added simultaneously
The nylon and Heat Conduction Material of preheated processing, compatilizer is added when temperature drops to 65 degree, is stirred for 15-25 minutes, and mixing is equal
Discharged after even；
Step（3）：To step（2）Obtained mixture carries out plasma-induced；
Wherein, it is described plasma-induced to be：By step（2）The mixture of acquisition inserts the bottom electrode medium of plasma device
On, voltage 24kV is irradiated 35~45 seconds under electric current 1.8mA, gap 3mm operating condition；
Step（4）：By step（3）Mixture is put into single screw extrusion machine after processing, 130-170 DEG C of rotating speed 28- of plasticization temperature
36rpm, material of the present invention is produced by hot-forming twice, then through air-cooled.