CN106930111A - A kind of transmission belt infantees - Google Patents
A kind of transmission belt infantees Download PDFInfo
- Publication number
- CN106930111A CN106930111A CN201710103425.9A CN201710103425A CN106930111A CN 106930111 A CN106930111 A CN 106930111A CN 201710103425 A CN201710103425 A CN 201710103425A CN 106930111 A CN106930111 A CN 106930111A
- Authority
- CN
- China
- Prior art keywords
- transmission belt
- infantees
- polyurethane
- treatment
- belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to transmission belt technical field, and in particular to a kind of transmission belt infantees, the infantees is processed using the composite or polyurethane for including polyurethane.The quality of the infantees is improved, and after being applied to transmission belt, preferably, long-term use is difficult wear damage to the transmission belt wearability being prepared into, and improves the service life of transmission belt.
Description
Technical field
The present invention relates to transmission belt technical field, and in particular to a kind of transmission belt infantees.
Background technology
Transmission belt is the power for producing the motor of prime mover or engine rotation, and machinery is transmitted to by adhesive tape by belt wheel
In equipment, therefore also referred to as powered belt.It is the core coupling component of electromechanical equipment, and species is extremely various, and purposes is extremely wide.
From greatly to the huge motor of several megawatts, the small micromachine to less than kilowatt, or even including household electrical appliances, computer, machine
The precision optical machineries such as people all be unable to do without transmission belt interior.Its maximum feature can be free speed change, distance transmission, simple structure,
Change convenient.So, there is the figure of transmission belt to modern automatic equipment from original mechanical, product is after repeatedly differentiation, technology
It is ripe day by day.
Transmission belt mainly includes flat belt（Flat board band, flat rubber belting）, V-belt（V bands）, circular strip, tooth-like belt（Including many wedges
Band）And the species such as metal tape, most transmission belt is infantees all with protective layer, and certainly, infantees includes bead flipper and outsourcing
Cloth, and be integrally formed with the various pieces of the excellent retractility of infantees and frictional property connection conveyer belt, infantees protects conveyer belt not
Frayed, etch.
Most infantees based on duck, for requiring that anti-wear performance and resistance to bend(ing) transmission belt can preferably can make
Cotton blend canvas is used, or uses fully synthetic fiber canvas；Cog belt（Timing Belt, including polywedge bet）In order to protect cog belt
Teeth portion and heart yearn, can be used the synthetic fibers of high-performance strong, especially based on nylon canvas.
Current infantees is typically with the gasoline solution of natural gum（Soaking paste）Impregnation process, determines transmission belt service life
One of principal element be infantees quality, the quality of infantees directly affects the service life of transmission belt.Current transmission belt
Service life it is low, easily abrasion, its one of the main reasons is infantees poor quality, thus improve infantees quality for carrying
The service life for rising transmission belt has very important meaning.
The content of the invention
It is specifically a kind of high-quality the invention aims to solve the above problems, there is provided a kind of transmission belt infantees
Transmission belt infantees.
Infantees of the invention is processed using polyurethane, and processing mode mainly has painting to scrape mode, impregnation method or painting way
Or spraying method or spin coating mode or several ways are used in combination.
In order to reach foregoing invention purpose, the present invention uses following technical scheme：
A kind of transmission belt infantees, its material is the base fabric being made up of natural fiber or chemical fibre or the two blending, and is being prepared
Before into transmission belt or after being prepared into transmission belt, specifically, transmission belt infantees is using polyurethane or includes the composite wood of polyurethane
Material is processed.
Used as preferred scheme, the treatment is before preparing as transmission belt.
Used as preferred scheme, the treatment includes that surface treatment, inter-process or the interior surface of infantees are processed simultaneously.
Used as preferred scheme, the treatment is scraped including painting, impregnated, brushing, spraying or spin coating.
Used as preferred scheme, the wrap material is duck, tarare, canvas of chemical fibre or blending canvas.
Used as preferred scheme, the transmission belt is flat belt, V-belt, circular strip, cog belt or triangular belt.
Used as preferred scheme, the polyurethane is modified polyurethane or unmodified polyurethane, and the modified polyurethane is
Chemical modification polyurethane, physical modification polyurethane or the two mixture.
Used as preferred scheme, the polyurethane is the organic solution of polyurethane body, aqueous polyurethane or polyurethane.
Used as preferred scheme, the treatment processes with rubber soaking paste and combines or individually carry out, and is processed with rubber soaking paste and tied
During conjunction, after treatment opportunity is for rubber soaking paste before processing or rubber soaking paste treatment.
Used as preferred scheme, the composite is counted including following components by weight：40 parts of aqueous polyurethane, third
5-10 parts of olefin(e) acid ester gum breast, titanium dioxide 1-3 parts, sodium acid carbonate 2-5 parts, unsaturated polyester (UP) 3-5 parts, gathers by resorcinol 1-3 parts
PAA 1-3 parts, trifluoroethyl methacrylate 2-5 parts.
A kind of transmission belt, is prepared from using any of the above-described kind of transmission belt infantees.
Compared with prior art, beneficial effect is the present invention：The quality of infantees is improved, and is applied to wear-resisting after transmission belt
Property preferably, long-term use is difficult wear damage, improves the service life of transmission belt.
Specific embodiment
Explanation is further described to technical scheme below by specific embodiment.
If without specified otherwise, the raw material employed in embodiments of the invention is raw material commonly used in the art, implements
Method employed in example, is the conventional method of this area.
Embodiment 1：
By duck first with rubber soaking paste routine impregnation process, then apply on one face again and scrape a strata urethane（Herein refer to bag
Composite containing polyurethane, or polyurethane body, or aqueous polyurethane, or polyurethane organic solution）, finally at drying
Reason, obtains product.
Embodiment 2：
On the basis of embodiment 1, after rubber routine impregnation process, rolling process is first passed through.
Embodiment 3-4：
The painting of embodiment 1-2 is scraped and replaces with brushing.
Embodiment 5-6：
The painting of embodiment 1-2 is scraped and replaces with dipping.
Embodiment 7-12：
On the basis of embodiment 1-6, the two-sided of duck is carried out by painting scrapes or impregnation process.
Embodiment 13：
To be applied on a face of duck first and scrape a strata urethane and herein refer to include the composite of polyurethane, polyurethane sheet
Body, aqueous polyurethane, or polyurethane organic solution）, conventional impregnation process then is carried out with rubber soaking paste again, finally at drying
Reason, obtains product.
Embodiment 14：
Duck in any of the above-described embodiment is changed to synthetic fibers canvas.
Embodiment 15：
Duck in any of the above-described embodiment is changed to cotton blend canvas.
Embodiment 16：
Being prepared using the infantees in any of the above-described embodiment turns into rubber V-belt.
Embodiment 17：
Being prepared using the infantees in any of the above-described embodiment turns into rubber flat belt.
Embodiment 18：
Being prepared using the infantees in any of the above-described embodiment turns into plantation rubber shape band.
Embodiment 19：
Being prepared using the infantees in any of the above-described embodiment turns into rubber teeth shape band（Including triangular belt）.
Embodiment 20：
A kind of infantees is processed with polyurethane body, and its proportioning is as follows：TDI+PPG（Molecular weight 1000）+ TMP is made
The base polyurethane prepolymer for use as double centner of-NCO=4.7%, MOCA14.5 kilograms.
Embodiment 20：
A kind of infantees is processed with polyurethane body, and its proportioning is as follows：TDI+PTMG（Molecular weight 1000）+ TMP is made
The base polyurethane prepolymer for use as double centner of-NCO=4.7%, MOCA14.5 kilograms of.
Embodiment 20：
A kind of infantees is processed with polyurethane organic solution, and its proportioning is as follows：TDI+PPG（Molecular weight 1000）+ TMP is made
The base polyurethane prepolymer for use as double centner of-NCO=4.7%, MOCA14.5 kilograms, 20 kilograms of ethyl acetate.
Embodiment 20：
A kind of infantees is processed with compound polyurethane material, and its proportioning is as follows：40 kilograms of aqueous polyurethane, acrylate latex 5,000
Gram, 3 kilograms of resorcinol, 1 kilogram of titanium dioxide, 5 kilograms of sodium acid carbonate, 3 kilograms of unsaturated polyester (UP), 3 kilograms of Sodium Polyacrylate,
2 kilograms of trifluoroethyl methacrylate.
After raw material is ready to, stirred at 40-50 DEG C, and boil holding 20-30 minutes, regulation pH is 7.5-8.
Under mild alkaline conditions, more conducively treatment of the composite to infantees, it is possible to increase infiltration speed of the composite to infantees
Rate, accelerates treatment effeciency.
Embodiment 21：
A kind of infantees composite, its proportioning is as follows：40 kilograms of aqueous polyurethane, 10 kilograms of acrylate latex, isophthalic two
1 kilogram of phenol, 3 kilograms of titanium dioxide, 2 kilograms of sodium acid carbonate, 5 kilograms of unsaturated polyester (UP), 1 kilogram of Sodium Polyacrylate, trifluoroethyl
5 kilograms of methacrylate.
After raw material is ready to, stirred at 40-50 DEG C, and boil holding 20-30 minutes, regulation pH is 7.5-8.
Under mild alkaline conditions, more conducively treatment of the composite to infantees, it is possible to increase infiltration speed of the composite to infantees
Rate, accelerates treatment effeciency.
Embodiment 22：
A kind of production technology of infantees, specifically includes following steps：
（1）Pending duck is pre-processed on dryer, baking oven steam pressure is set in 0.5MPa, setting is led
Draw motor speed and be adjusted to 200r/min, duck moisture is fully volatilized；
（2）Dipping process is carried out with rubber solutions：
Drying alley steam pressure in leaching cloth machine is set to 0.5MPa, guiding motor speed is more than 500r/min, master control roller
Away from according to being actually adjusted, specially it is adjusted according to the spread of 80g/m, after the completion of gluing, carries out drying and processing, is dried
Dry temperature is 40-50 DEG C, and drying time is 30-60min, and secondary gluing is then carried out again, wherein, drying alley steam pressure is
0.7MPa, guiding motor speed be 400r/min, master control roll spacing according to being actually adjusted, specially according to the upper of 50-60g/m
Glue amount is adjusted, and after the completion of gluing, is cleaned using ethylene glycol, then 40-50 DEG C of drying；
（3）The infantees processed by rubber solutions is impregnated using the composite of embodiment 20 or embodiment 21, is applied and is scraped, applies
Brush or other coating processings；
（4）The infantees for obtaining will be processed carries out other conventional treatments, obtains product.
Embodiment 23：
On the basis of embodiment 22, in its step（3）Impregnation process during, add 1-3 in every 100 parts of composite
The fourth pyrrole latex of part.
The service life change of V-belt, flat belt, circular strip and the cog belt scraped using dipping, painting, brushed see the table below：
（Artificial limit aging condition）
In embodiment 21-22, processing speed 5-10% can be improved after composite treating agent is adjusted into weak base.
In embodiment 23, after adding fourth pyrrole latex, using dipping, apply scrape, the V-belt brushed, flat belt, circular strip and
The service life of cog belt can also increase 1-2%.
Claims (10)
1. a kind of transmission belt infantees, its material is the base fabric being made up of natural fiber or chemical fibre or the two blending, is treated
Journey is after being prepared into before transmission belt or being prepared into transmission belt, it is characterised in that transmission belt infantees is using polyurethane or includes poly-
The composite of urethane is processed.
2. a kind of transmission belt infantees according to claim 1, it is characterised in that the treatment turns into transmission belt preparing
Before.
3. a kind of transmission belt infantees according to claim 2, it is characterised in that the treatment is included at the surface of infantees
Reason, inter-process or interior surface are processed simultaneously.
4. a kind of transmission belt infantees according to claim 3, it is characterised in that the treatment is scraped including painting, impregnates, applied
Brush, spraying or spin coating or several ways are used in combination.
5. a kind of transmission belt infantees according to claim 4, it is characterised in that the wrap material is duck, numb sail
Cloth, canvas of chemical fibre or blending canvas.
6. a kind of transmission belt infantees according to claim 1 or 2 or 3 or 4, it is characterised in that the transmission belt is flat skin
Band, V-belt, circular strip, cog belt or triangular belt.
7. a kind of transmission belt infantees according to claim 6, it is characterised in that the polyurethane is modified polyurethane or not
Modified polyurethane, the modified polyurethane is chemical modification polyurethane, physical modification polyurethane or the two mixture.
8. a kind of transmission belt infantees according to claim 7, it is characterised in that the polyurethane is polyurethane body, water
The organic solution of property polyurethane or polyurethane.
9. a kind of transmission belt infantees according to claim 8, it is characterised in that the treatment is processed with rubber soaking paste and combined
Or individually carry out, when being combined with rubber soaking paste treatment, after treatment opportunity is for rubber soaking paste before processing or rubber soaking paste treatment.
10. a kind of transmission belt, it is characterised in that be prepared from using the transmission belt infantees described in claim 1-9.