CN106928781A - A kind of nanometer anti-nuclear radiation coating - Google Patents
A kind of nanometer anti-nuclear radiation coating Download PDFInfo
- Publication number
- CN106928781A CN106928781A CN201511015249.0A CN201511015249A CN106928781A CN 106928781 A CN106928781 A CN 106928781A CN 201511015249 A CN201511015249 A CN 201511015249A CN 106928781 A CN106928781 A CN 106928781A
- Authority
- CN
- China
- Prior art keywords
- nuclear radiation
- water
- added
- minutes
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry, the coating that the slurry is made can according to demand have insulation, sound-absorbing, the whole of anti-nuclear radiation function or its combination.The base-material of the slurry is aqueous nanometer anti-nuclear radiation material, consisting of water-based emulsion, blanc fixe, nano-tourmaline powder, nanometer scale graphite, water and various auxiliary agents;The material radiation protection ability is strong, and class coating material is firmly combined with matrix each other, and can coordinate with expanded perlite, expanded vermiculite, cement etc. and be made water paste(Putty), thicker nano thermal insulation sound-absorbing anti-nuclear radiation coating can be manufactured in wall.
Description
Technical field
The present invention relates to water paint manufacturing technology field, especially a kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry.
Background technology
The blast and nuclear leakage of the Chernobyl Plant of the former Soviet Union make people not yet recovered from a fright, the Fukushima nuclear power station of Japan
Bad dream again reappears!Anti-nuclear radiation has turned into the thing of everybody attention.
The content of the invention
To solve the deficiency of prior art, a kind of nanometer anti-nuclear radiation coating of the invention.A kind of anti-core of nano thermal insulation sound-absorbing
Radiation slurry, can be subdivided into aqueous anti-nuclear radiation coating and water paste(Putty), and water paste is using aqueous anti-core spoke
Penetrate coating addition lightweight feature aggregate, cement.
Described aqueous anti-nuclear radiation coating, its composition includes the component of following mass percent number:
The mesh 30~50 of blanc fixe 300
Nano-tourmaline powder < 200nm 2~4
Nanometer scale graphite powder < 200nm 0.3~1
Water-based emulsion(Phenylpropyl alcohol, pure third, fluorocarbon resin emulsion or its combination)50% solid part 10~20
Toning mill base 3~8
Dispersant NNO 0.5~3
Appropriate defoamer
Thickener HE2 is appropriate
Ethylene glycol 0.2-0.8
Epoxy silane coupling 0.3-0.8
Water 40-55
Its technique, preparation method are comprised the following steps:
(1)Water is put into dispersion tank, rotating speed is controlled at 300~500 revs/min;
(2)Then defoamer, dispersant and other auxiliary agents are added in dispersion tank successively, are stirred 3 ± 1 minutes;
(3)Blanc fixe, nano-tourmaline powder, nanometer scale graphite powder are added in dispersion tank, raising rotating speed to 1200~
1800 revs/min, disperse 15 ± 3 minutes at a high speed;
(4)Rotating speed is dropped after disperseing at a high speed to 600~800 revs/min, water is added, stirred 3 ± 1 minutes;
(5)Water-based emulsion is slowly added to, is stirred 5 ± 2 minutes;
(6)Epoxy silane coupling is subsequently added into, is stirred 3 ± 1 minutes;
(7)Adjustment viscosity;
(8) sieve and pack.
A kind of described nano thermal insulation sound-absorbing anti-nuclear radiation slurry(Putty), constituent mass ratio and manufacturing process are:
By above-mentioned 100 parts of aqueous anti-nuclear radiation coating, the swelling perlite powder of 80 mesh, expanded vermiculite powder or its mixture are added
100-300 powder, No. 500 cement 30-80 parts, appropriate cement water reducing agent and water, uniform paste is mixed into kneader.
Outstanding feature of the invention is:The blanc fixe for having good barrier to act on to nuclear radiation wide spectrum electromagnetic wave has been used,
The nanometer scale graphite powder for having coordinated the Mineral with Polar Electricity tourmaline nano powder being electromagnetically shielded, anti-nuclear radiation to work well, makes
The anti-nuclear radiation function of product is excellent and insulation, sound insulation, environment-friendly.
Specific embodiment
Formula and technological process with reference to specific implementation, are expanded on further the present invention:
A kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry, can be subdivided into aqueous anti-nuclear radiation coating and water paste(Putty), and
Water paste is using aqueous anti-nuclear radiation coating addition lightweight feature aggregate, cement.
Described aqueous anti-nuclear radiation coating, its composition includes the component of following mass percent number:
The mesh 30~50 of blanc fixe 300
Nano-tourmaline powder < 200nm 2~4
Nanometer scale graphite powder < 200nm 0.3~1
Water-based emulsion(Phenylpropyl alcohol, pure third, fluorocarbon resin emulsion or its combination)50% solid part 10~20
Toning mill base 3~8
Dispersant NNO 0.5~3
Appropriate defoamer
Thickener HE2 is appropriate
Ethylene glycol 0.2-0.8
Epoxy silane coupling 0.3-0.8
Water 40-55
Its technique, preparation method are comprised the following steps:Water is put into dispersion tank, rotating speed is controlled at 300~500 revs/min
Clock;Then defoamer, dispersant and other auxiliary agents are added in dispersion tank successively, are stirred 3 ± 1 minutes;By blanc fixe,
Nano-tourmaline powder, nanometer scale graphite powder are added in dispersion tank, improve rotating speed to 1200~1800 revs/min, at a high speed
Dispersion 15 ± 3 minutes;Rotating speed is dropped after disperseing at a high speed to 600~800 revs/min, water is added, stirred 3 ± 1 minutes;It is slow
It is slow to add water-based emulsion, stir 5 ± 2 minutes;Epoxy silane coupling is subsequently added into, is stirred 3 ± 1 minutes;Adjustment viscosity,
Sieving packaging.
Described nano thermal insulation sound-absorbing anti-nuclear radiation slurry(Putty), constituent mass ratio and manufacturing process are:
By above-mentioned 100 parts of aqueous anti-nuclear radiation coating, the swelling perlite powder of 80 mesh, expanded vermiculite powder or its mixture are added
100-300 powder, No. 500 cement 30-80 parts, appropriate cement water reducing agent and water, uniform paste is mixed into kneader.
The above, implementation method is only that the preferred embodiment of the present invention is described, not to of the invention
Scope is defined, and on the premise of the spirit for not departing from the technology of the present invention, those skilled in the art are to technical side of the invention
Various modifications and improvement that case is made, all should fall into the protection domain of claims of the present invention determination.
Claims (3)
1. a kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry, can be subdivided into aqueous anti-nuclear radiation coating and water paste(Putty),
And water paste is using aqueous anti-nuclear radiation coating addition lightweight feature aggregate, cement.
2. a kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry according to claim 1, it is characterised in that:Described is aqueous
Anti-nuclear radiation coating
Its composition includes the component of following mass percent number:
The mesh 30~50 of blanc fixe 300
Nano-tourmaline powder < 200nm 2~4
Nanometer scale graphite powder < 200nm 0.3~1
Water-based emulsion(Phenylpropyl alcohol, pure third, fluorocarbon resin emulsion or its combination)50% solid part 10~20
Toning mill base 3~8
Dispersant NNO 0.5~3
Appropriate defoamer
Thickener HE2 is appropriate
Ethylene glycol 0.2-0.8
Epoxy silane coupling 0.3-0.8
Water 40-55
Its technique, preparation method are comprised the following steps:
(1)Water is put into dispersion tank, rotating speed is controlled at 300~500 revs/min;
(2)Then defoamer, dispersant and other auxiliary agents are added in dispersion tank successively, are stirred 3 ± 1 minutes;
(3)Blanc fixe, nano-tourmaline powder, nanometer scale graphite powder are added in dispersion tank, raising rotating speed to 1200~
1800 revs/min, disperse 15 ± 3 minutes at a high speed;
(4)Rotating speed is dropped after disperseing at a high speed to 600~800 revs/min, water is added, stirred 3 ± 1 minutes;
(5)Water-based emulsion is slowly added to, is stirred 5 ± 2 minutes;
(6)Epoxy silane coupling is subsequently added into, is stirred 3 ± 1 minutes;
(7)Adjustment viscosity;
(8) sieve and pack.
3. a kind of nano thermal insulation sound-absorbing anti-nuclear radiation slurry according to claim 1, it is characterised in that:Described nanometer
Heat-insulating and sound-absorbing anti-nuclear radiation slurry, is the swelling perlite powder that above-mentioned 100 parts of aqueous anti-nuclear radiation coating is added 80 mesh, swollen
Swollen vermiculite power or its mixture 100-300 powder, No. 500 cement 30-80 parts, appropriate cement water reducing agent and water, it is mixed in kneader
Synthesize uniform paste.