CN106928605A - A kind of organic carrier for solar cell positive silver paste and preparation method thereof - Google Patents
A kind of organic carrier for solar cell positive silver paste and preparation method thereof Download PDFInfo
- Publication number
- CN106928605A CN106928605A CN201710088796.4A CN201710088796A CN106928605A CN 106928605 A CN106928605 A CN 106928605A CN 201710088796 A CN201710088796 A CN 201710088796A CN 106928605 A CN106928605 A CN 106928605A
- Authority
- CN
- China
- Prior art keywords
- organic carrier
- silver paste
- solar cell
- cell positive
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of solar batteries, and in particular to a kind of organic carrier for solar cell positive silver paste and preparation method thereof;The organic carrier is the mixture of resin, solvent and auxiliary agent, and the mass ratio of the resin, solvent and auxiliary agent is 12:3‑4:0.01‑0.05;The organic carrier reasonable component formula that the present invention is provided, helps to improve the rheological property of slurry system;It can be mixed with certain proportion after being dispersed in silver paste, the linear moulding ability of grid line can be significantly improved, and then the depth-width ratio of electrode and grid line after silk-screen quality of the silver paste on silicon chip and sintering is improve, reduce shared light-receiving area, so as to lift the efficiency of solar cell.
Description
Technical field
The present invention relates to technical field of solar batteries, and in particular to a kind of for the organic of solar cell positive silver paste
Carrier and preparation method thereof.
Background technology
Organic carrier is the important component of silver paste, is the second largest composition in silver paste, for solar battery front side
The silver paste of grid line usually contains the organic carrier of 10-20 wt%.It is that a kind of auxiliary agent by each tool function is dissolved in organic solvent
In organic polymer solution.It has been the fortune of the glass dust (or oxide) of the metal-powder and a cementation of electric action
Carrier, plays the viscosity of regulation charging, controls the effect of the rheological characteristic of slurry.The various powder mixtures of solid-state are made to be dispersed into tool
There is the slurry of fluid behaviour, in order to be printed onto on matrix at a high speed, accurately by screen process press, the line required for being formed
Bar.Organic carrier is typically mainly made up of organic solvent and thickener, in addition, in order to improve its levelability, often adding appropriate
Surfactant, levelling agent;In order to improve the thixotropy of beam material, thixotropic agent or gelling agent are also added;In order to subtract as far as possible
The stomata that few slurry is produced after printing-sintering, improves electric conductivity, also usually adds defoamer.Therefore solvent and various auxiliary agents
Selection and proportioning just seem increasingly important.In the prior art, the composition of organic carrier is required further improvement, and is existed with improving silver paste
Silk-screen quality on silicon chip, and then lift the efficiency of solar cell.
The content of the invention
The technical problem to be solved in the invention is a kind of efficiency that can lift solar cell of offer for too
The organic carrier of positive energy battery positive silver paste, additionally, present invention also offers its preparation method.
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin, solvent and auxiliary agent
Mixture, the mass ratio of the resin, solvent and auxiliary agent is 1-2:3-4:0.01-0.05.
Further, the described organic carrier for solar cell positive silver paste, the organic carrier is resin, molten
Agent and the mixture of auxiliary agent, the mass ratio of the resin, solvent and auxiliary agent is 1-1.6:3.2-3.4:0.01-0.03.
Further, the described organic carrier for solar cell positive silver paste, the resin is selected from epoxy resin
One of which in modified cellulose diacetate, polyester modification acrylic resin, polyvinyl butyral resin.
Further, the described organic carrier for solar cell positive silver paste, the solvent is selected from nylon acid two
Methyl esters, polyamide modified rilanit special, atoleine, at least one in hexylene glycol, carbitol, turpentine oil.
Further, the described organic carrier for solar cell positive silver paste, the auxiliary agent is thickener and table
Face activating agent.
Further, the described organic carrier for solar cell positive silver paste, the thickener is Abietyl modified
Its in methylcellulose, Abietyl modified ethyl cellulose, Abietyl modified carboxymethylcellulose calcium, Abietyl modified carboxyethyl cellulose
Middle one kind.
Further, the described organic carrier for solar cell positive silver paste, the surfactant is alkyl
Ammonium salt type cationic surface active agent, betaine type amphoteric ionic surface active agent, C8-C10 fatty acid glycerine ester type it is non-from
One of which in sub- surfactant.
Further, the described organic carrier for solar cell positive silver paste, the surfactant is alkyl
Ammonium salt type cationic surface active agent.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, the slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out to slurry in device;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Further, the preparation method of the described organic carrier for solar cell positive silver paste, the step(2)
In mixing speed be 2500-3000r/min;Jitter time is 30min;The step(3)In milling time be 10-
20min。
The beneficial effect of protrusion that the present invention has compared with prior art is:
The organic carrier reasonable component formula that the present invention is provided, helps to improve the rheological property of slurry system.By it with certain
After ratio mixing is dispersed in silver paste, the linear moulding ability of grid line can be significantly improved, and then improve silver paste on silicon chip
The depth-width ratio of electrode and grid line after silk-screen quality and sintering, reduces shared light-receiving area, so as to lift the efficiency of solar cell.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment 1:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:Polyester modification acrylic acid tree
Fat, solvent:Polyamide modified rilanit special and auxiliary agent:Thickener:Abietyl modified methylcellulose, surfactant:Alkyl
Ammonium salt type cationic surface active agent, wherein, thickener and surfactant are with arbitrary proportion interworking, the resin, solvent
It is 2 with the mass ratio of auxiliary agent:3:0.05.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 2500r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 10min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Embodiment 2:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:The vinegar of epoxy resin modification two
One of which, solvent in acid cellulose, polyester modification acrylic resin, polyvinyl butyral resin:Nylon acid dimethyl ester,
Polyamide modified rilanit special and auxiliary agent:Thickener:Abietyl modified carboxyethyl cellulose, surfactant:Isooctyl acid glycerine
Ester type nonionic surfactant, wherein, thickener and surfactant the resin, solvent and are helped with arbitrary proportion interworking
The mass ratio of agent is 1-:4:0.01.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 3000r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 15min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Embodiment 3:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:Polyvinyl butyral resin tree
Fat, solvent:Polyamide modified rilanit special, atoleine and auxiliary agent:Thickener:Abietyl modified carboxymethylcellulose calcium, surface
Activating agent:Alkylammonium salt form cationic surface active agent, wherein, thickener and surfactant are with arbitrary proportion interworking, institute
The mass ratio for stating resin, solvent and auxiliary agent is 1.2:3.4:0.02.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 2500r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 20min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Embodiment 4:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:The vinegar of epoxy resin modification two
Acid cellulose, solvent:Turpentine oil and auxiliary agent:Thickener:Abietyl modified methylcellulose, surfactant:2- isodecyl acid glycerols
Ester type nonionic surfactant;Wherein, thickener and surfactant be with arbitrary proportion interworking, the resin, solvent and helps
The mass ratio of agent is 1:3.4:0.01.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 2500r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 20min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Embodiment 5:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:Polyester modification acrylic acid tree
Fat, solvent:Carbitol and auxiliary agent:Thickener:Abietyl modified ethyl cellulose, surfactant:Betaine type amphoteric ion table
Face activating agent, wherein, with arbitrary proportion interworking, the mass ratio of the resin, solvent and auxiliary agent is for thickener and surfactant
1.6:3.2:0.03.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 3000r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 10min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Embodiment 6:
A kind of organic carrier for solar cell positive silver paste, the organic carrier is resin:Polyester modification acrylic acid tree
Fat, solvent:Polyamide modified rilanit special and auxiliary agent:Thickener:Abietyl modified methylcellulose, surfactant:Alkyl
Ammonium salt type cationic surface active agent, wherein, thickener and surfactant are with arbitrary proportion interworking, the resin, solvent
It is 1.8 with the mass ratio of auxiliary agent:3.5:0.03.
A kind of preparation method of the described organic carrier for solar cell positive silver paste, comprises the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, mixing speed is 2500r/min;Jitter time is 30min;The slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out in device to slurry, milling time is 10min;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
Presently preferred embodiments of the present invention is the foregoing is only, is not intended to limit the invention, it is all in essence of the invention
Any modification, equivalent and improvement made within god and principle etc., should be included within the scope of the present invention.
Claims (10)
1. a kind of organic carrier for solar cell positive silver paste, it is characterised in that the organic carrier is resin, solvent
With the mixture of auxiliary agent, the mass ratio of the resin, solvent and auxiliary agent is 1-2:3-4:0.01-0.05.
2. the organic carrier for solar cell positive silver paste according to claim 1, it is characterised in that described organic
Carrier is the mixture of resin, solvent and auxiliary agent, and the mass ratio of the resin, solvent and auxiliary agent is 1-1.6:3.2-3.4:
0.01-0.03。
3. the organic carrier for solar cell positive silver paste according to claim 1, it is characterised in that the resin
Selected from wherein in epoxy resin modification cellulose diacetate, polyester modification acrylic resin, polyvinyl butyral resin
Kind.
4. the organic carrier for solar cell positive silver paste according to claim 1, it is characterised in that the solvent
Selected from nylon acid dimethyl ester, polyamide modified rilanit special, atoleine, in hexylene glycol, carbitol, turpentine oil at least one
Kind.
5. the organic carrier for solar cell positive silver paste according to claim 1, it is characterised in that the auxiliary agent
It is thickener and surfactant.
6. the organic carrier for solar cell positive silver paste according to claim 5, it is characterised in that the thickening
Agent is Abietyl modified methylcellulose, Abietyl modified ethyl cellulose, Abietyl modified carboxymethylcellulose calcium, Abietyl modified carboxyethyl
One of which in cellulose.
7. the organic carrier for solar cell positive silver paste according to claim 5, it is characterised in that the surface
Activating agent is alkylammonium salt form cationic surface active agent, betaine type amphoteric ionic surface active agent, C8-C10 aliphatic acid
One of which in glycerine ester type nonionic surfactant.
8. the organic carrier for solar cell positive silver paste according to claim 7, it is characterised in that the surface
Activating agent is alkylammonium salt form cationic surface active agent.
9. the preparation of a kind of organic carrier for solar cell positive silver paste according to any one of claim 1-8
Method, it is characterised in that comprise the following steps:
(1)Each raw material is measured respectively by proportioning;
(2)According to first solubilizer, again plus resin, the order of last adding assistant successively will raw material put into dispersed with stirring device in carry out
Preliminary mixing, the slurry that formation can continuously be flowed;
(3)While being kept stirring for dispersal device and continuously running, above-mentioned slurry is delivered to by grinding distribution by the circulatory system
Fine gtinding is carried out to slurry in device;
(4)Flowed back to again in dispersed with stirring device after slurry is finer ground and continue dispersed with stirring;
(5)Slurry is circulated between dispersed with stirring device and apparatus for grinding and dispersing, until particle diameter distribution≤3 micron of slurry.
10. the preparation method of the organic carrier for solar cell positive silver paste according to claim 9, its feature exists
In the step(2)In mixing speed be 2500-3000r/min;Jitter time is 30min;The step(3)In grind
It is 10-20min to consume time.