CN106925728B - Pulping head for semi-solid pulping - Google Patents
Pulping head for semi-solid pulping Download PDFInfo
- Publication number
- CN106925728B CN106925728B CN201710265528.5A CN201710265528A CN106925728B CN 106925728 B CN106925728 B CN 106925728B CN 201710265528 A CN201710265528 A CN 201710265528A CN 106925728 B CN106925728 B CN 106925728B
- Authority
- CN
- China
- Prior art keywords
- pulping
- heat exchange
- head
- liner
- container
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
the invention discloses a pulping head for semi-solid pulping, which at least comprises an outer container inserted into the pulp to be prepared, wherein micropores with air permeability are densely distributed on at least the lower container body of the outer container. When the pulping machine works, inert gas with certain pressure is introduced into the cavity of the outer container liner, and the inert gas can uniformly permeate into slurry through the micropores densely distributed on the outer container liner and can be subjected to violent collision reaction and heat exchange with the slurry, so that the effects of slag discharge, degassing, material internal crystal structure refinement and heat exchange are achieved, the internal temperature of the slurry is uniform, and the internal crystal structure is more uniform. Meanwhile, the pulping head can not be stirred in the pulping process, so that the loss cost of the pulping head can be obviously reduced.
Description
Technical Field
The invention relates to a pulping head for semi-solid pulping.
Background
The semi-solid metal forming technology is a metal forming technology between solid forming and liquid forming, has the advantages of low liquid forming flow stress, high forming speed and capability of forming parts with complex shapes, and is widely concerned and researched by the fields of academia, manufacturing industry and the like at present. The most critical technology in the semi-solid metal forming technology is how to prepare semi-solid slurry with excellent performance.
at present, a method commonly adopted in the preparation process of the semi-solid slurry is that a mechanical stirring rod is adopted for stirring, and then the stirring rod is cooled or solid materials of the same material are added. The pulping mode has the defects of quick abrasion of a stirring rod, high cost, long stirring time, long cooling time and the like, influences the production rhythm and efficiency, has the defects of uneven temperature, uneven crystal structure and the like of the treated molten metal, and seriously influences the production cost, the production efficiency and the product quality.
Disclosure of Invention
the invention aims to overcome the defects of the prior art and provide a novel semi-solid pulping head for pulping.
In order to achieve the purpose, the invention adopts the technical scheme that: the pulping head at least comprises an outer liner which is inserted into the slurry to be prepared, and micropores with air permeability are densely distributed on at least the lower liner body of the outer liner.
preferably, the micropores are densely distributed on the whole liner body of the outer liner.
Preferably, the outer container is made of ceramic, graphite, silicon nitride, silicon carbide material or stainless steel material.
Preferably, the pulping head further comprises a connecting seat, and the connecting seat is fixed to the top of the outer container and seals the container cavity of the outer container.
Furthermore, the pulping head further comprises a heat exchange inner container, the heat exchange inner container is contained in the container cavity of the outer container, the top of the heat exchange inner container is fixedly connected with the connecting seat, a closed environment cavity is formed among the heat exchange inner container, the outer container and the connecting seat, and a closed heat exchange cavity is formed between the connecting seat and the heat exchange inner container.
Furthermore, a first medium inlet used for introducing inert gas into the environment cavity and a second medium inlet used for introducing a heat exchange medium into the heat exchange cavity are formed in the connecting seat.
Furthermore, the connecting seat is fixedly connected with an air duct, the upper part of the air duct is connected with the second medium inlet, and the air duct extends downwards into the lower part of the heat exchange cavity.
Preferably, the pulping head further comprises a cooling ring, the cooling ring is fixedly sleeved on the outer side of the connecting seat or the outer side of the top of the outer container, and an annular air outlet used for performing air blowing cooling on the periphery of the outer side of the outer container is formed in the cooling ring.
As a specific implementation manner, the top of the outer container has an annular flange protruding outward, the connecting seat is fixedly connected with the annular flange through an annular fastening member, and the cooling ring is fixedly sleeved on the outer side of the top of the outer container and located below the annular fastening member, or the cooling ring is fixedly sleeved on the annular fastening member.
preferably, the pulping head further comprises a stirring impeller fixedly sleeved at the lower part of the outer liner.
Due to the application of the technical scheme, compared with the prior art, the invention has the following advantages:
1. in the pulping process, inert gas with certain pressure is introduced into the outer container chamber, the inert gas can uniformly permeate into the slurry through the micropores densely distributed on the outer container body, and can generate violent collision reaction with the slurry and quickly take away heat, so that the metal solution is quenched, the effects of slag discharge, degassing, refining and changing the crystal structure in the material and heat exchange are achieved, the temperature in the slurry is uniform, the crystal structure in the slurry is more uniform, and the metallographic structure of a product obtained by die-casting the prepared slurry is more uniform;
2. Stirring operation can be omitted in the pulping process, and the pulping head and the pulp are relatively static without friction, so that the abrasion of the pulping head is reduced, and the loss cost caused by the pulping head is greatly reduced;
3. The pulping process can realize automatic control, and has the advantages of short process, high speed, less peripheral supporting equipment, low energy consumption and the like.
Drawings
FIG. 1 is a schematic view showing the overall structure of a pulper used in example 1;
FIG. 2 is a schematic cross-sectional view of a pulping head used in example 1;
FIG. 3 is a schematic structural view of the inner and outer liners of the pulping head of embodiment 1;
FIG. 4 is a schematic structural view of a heat exchange liner in the pulping head of embodiment 1;
FIG. 5 is a schematic view showing the overall construction of a pulper according to embodiment 2;
FIG. 6 is a schematic cross-sectional view of a pulping head used in example 2;
FIG. 7 is a schematic view showing the overall construction of a pulper according to embodiment 3;
FIG. 8 is a schematic cross-sectional view of a pulping head used in example 3;
FIG. 9 is a top view of the agitator impeller on the slurrying head of example 3;
FIG. 10 is a gold phase diagram of an aluminum alloy solution before pulping operation of a pulping head;
FIG. 11 is a metallographic graph of an aluminum alloy solution after pulping by using the pulping head of example 1;
Wherein: 10. a machine base; 101. a base; 102. a column; 102a, a lower column; 102b, an upper column; 103. a cross beam; 104. a support; 105. an adjusting seat; 106. a first hand wheel; 107. a second hand wheel;
20. pulping head; 1. a coupling seat; 11. a first media inlet; 12. a second media inlet; 13. a first inlet fitting; 14. a second inlet fitting; 15. a first medium outlet; 16. a second medium outlet; 17. a first outlet connection; 18. a second outlet connection; 19. a temperature sensor;
2. A heat exchange inner container; 21. a thread structure; 3. an outer liner; 31. an annular flange; 4. an air duct; 5. an environmental chamber; 6. a heat exchange cavity; 7. an annular fastener; 8. a cooling ring; 81. an annular air outlet; 82. an inlet fitting; 9. a stirring impeller;
30. A support; 40. an air control system; 50. a soup container; 60. a rotary motor.
Detailed Description
the technical solution of the present invention is further explained with reference to the drawings and the specific embodiments.
example 1
Referring to fig. 1, the pulping machine includes a machine base 10, a bracket 30 disposed on the machine base 10, and a pulping head 20 mounted on the bracket 30, wherein when a soup container 50 contains semi-solid slurry, the lower portion of the pulping head 20 is inserted into the soup container 50 to prepare the pulp.
Referring to fig. 2, a pulping head 20 adopted in this embodiment is provided, where the pulping head 20 includes a heat exchange liner 2, an outer liner 3 sleeved outside the heat exchange liner 2, and a connecting seat 1 fixedly connected to the top of the heat exchange liner 2 and the top of the outer liner 3, and the connecting seat 1 is fixedly installed on a support 30. A closed environment cavity 5 is formed among the heat exchange inner container 2, the outer container 3 and the connecting seat 1, and a closed heat exchange cavity 6 is formed between the heat exchange inner container 2 and the connecting seat 1.
Specifically, as shown in fig. 2 and 4, the heat exchange liner 2 is a cylindrical structure having an opening at the upper part and a spherical lower part, a thread structure 21 is provided at the periphery of the top outer side, the heat exchange liner 2 is fixed at the bottom of the coupling seat 1 through the thread structure 21, and the top of the heat exchange liner 2 is hermetically connected with the coupling seat 1 by a sealing ring, so that a closed heat exchange cavity 6 is formed between the heat exchange liner 2 and the coupling seat 1. In this embodiment, the heat exchange liner 2 may be an aluminum alloy heat exchange liner made of an aluminum alloy material.
referring to fig. 2 and 3, the outer container 3 is also a cylindrical structure having an opening at the upper part and a spherical lower part, and the diameter of the cross section of the outer container 3 is larger than that of the heat exchange inner container 2. The top of the outer liner 3 is provided with an annular flange 31 which protrudes outwards along the radial direction, the connecting seat 1 is fixedly connected with the annular flange 31 through an annular fastener 7, and the top of the outer liner 3 is hermetically connected with the bottom of the connecting seat 1 through a sealing ring, so that the connecting seat 1 seals the liner cavity of the outer liner 3 at the top of the outer liner 3. Thus, a closed environment cavity 5 is formed among the heat exchange inner container 2, the outer container 3 and the connecting seat 1.
at least the lower liner body of the outer liner 3 is densely provided with micropores with ventilation function, the aperture of the micropores is between 0.5 and 25 mu m, and the porosity is 45 to 55 percent, so that inert gas with certain pressure introduced into the environment cavity 5 can overflow through the micropores, and thus, when the pulping head 20 is inserted into semi-solid slurry for pulping, the inert gas introduced into the environment cavity 5 can uniformly permeate into the semi-solid solution through the micropores on the outer liner 3 to generate violent collision reaction with the semi-solid solution and rapidly take away heat, and the metal solution is rapidly cooled, thereby achieving the effects of slag removal, degassing, refining, changing the crystal structure in the material and heat exchange.
In this embodiment, the outer container 3 is made of ceramic, graphite, silicon nitride, silicon carbide, stainless steel, etc. and the pores with air permeability are densely arranged on the whole container body of the outer container 3, and when the outer container 3 is made of the above materials, the gaps among the molecules form a densely distributed capillary pore structure, so that the whole outer container 3 has air permeability.
Referring to fig. 2, on the pulping head 20, a first medium inlet 11 for introducing inert gas into the environmental chamber 5 is formed on the connecting seat 1, and a first inlet joint 13 is arranged at the upper part of the first medium inlet 11; the coupling seat 1 is further provided with a second medium inlet 12 for introducing a heat exchange medium into the heat exchange cavity 6, the heat exchange medium may be cooling liquid or cooling gas, the heat exchange medium is compressed air, and the upper portion of the second medium inlet 12 is provided with a second inlet joint 14. The connecting seat 1 is also provided with a second medium outlet 16 communicated with the heat exchange cavity 6 for the outflow of the heat exchanged gas.
referring to fig. 2, the connection base 1 is further fixedly connected with an air duct 4, the air duct 4 extends in the up-down direction, the upper portion of the air duct 4 is connected with the lower portion of the second medium inlet 12, and the air duct 4 extends downwards into the lower portion of the heat exchange cavity 6, so that introduced compressed air can be uniformly and effectively distributed in the heat exchange cavity 6, and the heat exchange efficiency is improved.
Referring to fig. 2, the pulping head 20 further comprises a temperature sensor 19 for detecting the ambient temperature in the ambient chamber 5, so as to facilitate the control of the heat exchange medium feeding state in the heat exchange chamber 6 according to the ambient temperature in the ambient chamber 5.
referring to fig. 2, the pulping head 20 further comprises a cooling ring 8, wherein the cooling ring 8 is relatively fixedly arranged on the top of the outer liner 2 or the coupling seat 1, and the cooling ring 8 is fixedly sleeved on the annular fastener 7. Offer on this cooling ring 8 and be used for carrying out the annular venthole 81 that blows air cooling to the outside week portion of outer courage 3, still offer the air inlet that is linked together with this annular venthole 81 on the cooling ring 8, this air inlet is located the upper portion of annular venthole 81, and be equipped with entry joint 82 on it, in order to let in cooling gas to this annular venthole 81, after slurrying head 20 finishes slurrying work like this, cooling down can be realized fast to outer courage 3 with the cooling gas that annular venthole 81 let in, can also make the thick liquids that adhere on the outer wall of outer courage 3 blow off in order to clear up the outer courage wall of outer courage 3 simultaneously.
the pulper further comprises a first gas source device (not shown) for supplying low-temperature inert gas into the environment chamber 5, a second gas source device (not shown) for supplying heat exchange gas into the heat exchange chamber 6, and a gas control system 40 for controlling the working state of the first gas source device and the second gas source device, wherein the inert gas is preferably nitrogen or argon. In this embodiment, the pneumatic control system 40 is further electrically connected or signal-connected to the temperature sensor 19, and when the temperature sensor 19 detects that the temperature in the environmental chamber 5 exceeds the preset temperature, the pneumatic control system 40 controls the operating state of the second air source device to supply low-temperature compressed air for heat exchange into the heat exchange chamber 6 to accelerate heat exchange, and controls the environmental temperature in the environmental chamber 5 within a set range, so as to ensure that the temperature of the inert gas entering the slurry through the environmental chamber 5 is maintained within the set range.
Referring to fig. 1, in the pulping apparatus of the present embodiment, a support 30 is liftably disposed on a machine base 10, and a lifting driving mechanism for driving the support 30 to lift in a vertical direction is further disposed on the pulping apparatus, so that a pulping head 20 can be conveniently inserted into a soup container 50 for pulping and lifted from the soup container 50 after pulping. Specifically, the machine base 10 includes a base 101, a vertical column 102 erected upward from the base 101, and a cross beam 103 installed on the upper portion of the vertical column 102 and extending in a horizontal direction, a support 104 is further fixedly provided on an end portion of the cross beam 103, the support 30 is vertically arranged on the support 104, and the air control system 40 is fixedly arranged on the cross beam 103.
In this embodiment, the support 104 is provided with a guide rail (not shown) extending in the up-down direction to provide sliding guidance for the support 30 up and down, and the lifting driving mechanism is a screw-nut driving mechanism disposed between the support 104 and the support 30, so as to achieve precise lifting of the pulping head 20. Specifically, the nut may be fixed to the bracket 30, the screw may be rotatably disposed on the support 104 around its own axis, and the nut may be linearly moved along the screw by rotating the screw using the motor, so that the bracket 30 is lifted up and down relative to the support 104. In the specific arrangement, the bracket 30 may be configured to have an L-shaped structure with a horizontal plate portion and a vertical plate portion, the connecting seat 1 of the pulping head 20 is fixed at the bottom of the horizontal plate portion, and the vertical plate portion is connected with the support 104 in a relatively sliding manner. Of course, the lifting driving mechanism may be configured by a cylinder, a rack and pinion, or the like.
The following takes semi-solid casting slurry of aluminum alloy as an example to illustrate the specific working process of the embodiment:
Referring to fig. 1, after the semi-solid aluminum alloy slurry is contained in the soup container 50, the soup container moves to a position below the slurrying head 20, the slurrying machine is started, the air control system 40 works first, so that the environment cavity 5 is filled with low-temperature inert gas, i.e., nitrogen or argon, with a certain pressure, and then the bracket 30 is driven to descend along the support 104, so that the lower portion of the slurrying head 20 is inserted into the semi-solid aluminum alloy slurry in the soup container 50. In the pulping process, a first gas source device continuously introduces low-temperature inert gas-nitrogen or argon into the environmental cavity 5; the second air source device leads to low-temperature compressed air in the heat exchange cavity 6 to exchange heat in the environment cavity 5, so that heat transmitted by the aluminum alloy solution is rapidly taken away, the environment temperature in the environment cavity 5 is kept in a set range, and the temperature inside and outside the pulping head 20 is always in a stable range.
The low temperature inert gas-nitrogen or argon gas that lets in the environment chamber 5 permeates in the thick liquids evenly through the micropore on the outer courage 3 courage body, and make produce a plurality of micro-bubble in the thick liquids and take away the heat with aluminum alloy solution collision reaction and rapidly, quench the metal solution, thereby make the internal crystal structure of thick liquids take place from dendritic crystal tissue (dendritic crystal tissue) to the change of granular spherical crystal tissue (non-dendritic crystal tissue) in the hot water container 50, as shown in figure 10, 11, and then improve comprehensive mechanical properties such as mechanical strength and elongation of material tissue, finally reach the purpose that needs slurrying.
after the pulping is completed, the bracket 30 is lifted to lift the pulping head 20 from the pulp, and cooling gas is introduced into the cooling ring 8 in the process to rapidly cool the pulping head 20. The slurry in the soup container 50 is sent to a die casting machine for die casting.
taking a case product with an aluminum alloy mark of 375-T6 as an example, the slurry head and the slurry method of the embodiment are adopted to perform semi-solid molding and conventional die-casting molding, and the performance parameters of the obtained products are compared as shown in the following table:
It can be seen that the semi-solid die-casting adopted in the embodiment has the following advantages:
(1) the forming is convenient and the forming speed is high;
(2) the slurry does not splash during molding, the compactness is improved, and the air doping is reduced;
(3) No macrosegregation exists, and the comprehensive mechanical property of the material is improved;
(4) The heat preservation temperature of the metal solution is low, so that the energy is saved;
(5) the addition phase can be conveniently added in the forming process;
(6) high automation is convenient to realize, and the productivity is improved;
(7) The environment is improved, and the operation is safe;
(8) The quality and the reliability of a formed piece are obviously improved;
(9) The semi-solid die cast parts may be heat treated (T5, T6);
(10) the semisolid forming stress is obviously reduced, the thermal shock to a forming die is greatly reduced, and the service life of the die is prolonged;
(11) The forming precision is high, the processing amount of the part blank is greatly reduced, and the cost is reduced.
In summary, when the pulping head 20 of this embodiment is used for pulping, inert gas such as nitrogen is introduced into the chamber of the outer container 3, so that the inert gas permeates into the slurry through the micropores densely distributed on the container body of the outer container 3 and reacts with the slurry through violent collision and heat exchange, thereby achieving the effects of slag discharge, degassing, refining the internal crystal structure of the material and heat exchange, making the internal temperature of the slurry uniform and the internal crystal structure more uniform, and making the metallographic structure of the product obtained by die-casting the prepared slurry more uniform. Meanwhile, because the pulping head 20 does not need to be stirred in the pulping process, the pulping head 20 and the pulp are relatively static without friction, the abrasion of the pulping head 20 is reduced, and the loss cost caused by the pulping head 20 is greatly reduced.
Example 2
Referring to the pulping machine shown in fig. 5 and the pulping head shown in fig. 6, the design concept of the pulping head is basically consistent with that of embodiment 1, and the following differences mainly exist in structure:
Referring to fig. 5, the stand 10 of the pulper comprises a base 101, a vertical column 102 erected upwards from the base 101, and a beam 103 installed on the upper part of the vertical column 102 through an adjusting seat 105 and extending in the horizontal direction, wherein a support 104 is fixedly arranged on the end of the beam 103, a bracket 30 is arranged on the support 104 in a way of ascending and descending, and a pulping head 20 is fixedly installed on the bracket 30.
The upright post 102 includes a lower post 102a and an upper post 102b which are slidably disposed in the vertical direction to adjust the height, the cross beam 103 is slidably disposed in the longitudinal direction and rotatably connected to the adjusting base 105 around the axial line of the upright post 102, the cross beam 103 is provided with a first hand wheel 106 for adjusting the horizontal position of the cross beam 103 relative to the upright post 102, the top of the upright post 102 is provided with a second hand wheel 107 for adjusting the height of the upright post 102, and the upright post 102 is further provided with a third hand wheel (not shown) for adjusting the rotation angle of the cross beam 103 relative to the upright post 102. Through the height adjustment of the upright post 102, the horizontal position adjustment and the rotation angle adjustment of the cross beam 103, the position of the pulping head 20 can be well corresponding to the position of the soup container 50.
referring to fig. 6, the first inlet joint 13 of the pulping head 20 is connected to an inert gas source and a cooling medium source through a solenoid valve, so that the inert gas can be supplied into the environment cavity 5 when the pulping head 20 performs pulping operation, and the cooling medium can be supplied into the environment cavity 5 after the pulping head 20 finishes pulping operation, so that the pulping head 20 can be cooled quickly after pulping operation.
The pulping head 20 is further provided with a first medium outlet 15, a first outlet joint 17 is arranged on the first medium outlet 15, and the first medium outlet 15 is closed during pulping so that the inert gas introduced into the environmental chamber 5 enters the pulp through the micropores on the outer liner 3. The second medium outlet 16 of the pulping head 20 is also provided with a second outlet joint 18, which can recycle the cooling medium introduced into the heat exchange cavity 6 after heat exchange and flow out for recycling.
On this slurrying head 20, outer courage 3 is big-end-up and has certain tapering tubular structure, and cooling ring 8 cover is established at the top of outer courage 3 and is located the below of cyclic annular buckle spare 7, can form even air current and make the outside courage wall rapid cooling of outer courage 3 on the outside courage wall of outer courage 3 like this when letting in high-pressure cooling gas to cyclic annular venthole 81.
Example 3
referring to the pulper shown in fig. 7, the structural arrangement of the stand 10 is the same as that of the stand 10 in the pulper of embodiment 2, and the description thereof is omitted. The main difference from embodiment 2 is that the coupling base 1 of the pulping head 20 is rotatably connected to the support 30 by a rotating shaft (not shown) whose axis extends along the vertical direction, and the support 30 is further provided with a rotating motor 60 for driving the coupling base 1 to rotate around the axis of the rotating shaft.
referring to fig. 8 and 9, in the embodiment, the lower liner body of the outer liner 3 of the pulping head 20 is further fixedly sleeved with the stirring impeller 9, and the stirring impeller 9 is provided with a plurality of blades uniformly distributed at intervals along the circumferential direction, so as to stir the pulp in the pulping process.
therefore, in the process that the pulping head 20 is inserted into the pulp to prepare the pulp, the pulping head 20 also carries out violent stirring operation while introducing the inert gas, and further shears and breaks all dendritic crystal tissue structures of the pulp, so that the tissue structure of spherical primary grains is formed, the inert gas can be further uniformly mixed in the pulp, the spherical crystal tissue structure and the temperature in the pulp solution are more uniform, the pulp temperature can be rapidly reduced, the pulping time can be greatly shortened, and the performance of the prepared pulp is more ideal.
In conclusion, the pulping head 20 of the invention has a simple structure, can realize automatic control of the pulping process when being installed on the pulping machine base 10 for pulping, has the advantages of short process, high speed, less peripheral supporting equipment, low energy consumption and the like, and is particularly suitable for semi-solid pulping of aluminum alloy, magnesium alloy and aluminum-magnesium alloy solution.
the above embodiments are merely illustrative of the technical ideas and features of the present invention, and the purpose thereof is to enable those skilled in the art to understand the contents of the present invention and implement the present invention, and not to limit the protection scope of the present invention. All equivalent changes and modifications made according to the spirit of the present invention should be covered within the protection scope of the present invention.
Claims (6)
1. a pulping head for semi-solid pulping is characterized in that: the pulping head at least comprises an outer liner which is inserted into slurry to be prepared, micropores with a ventilation function are densely arranged on at least the lower liner body of the outer liner, the outer liner is of a cylindrical structure with a large upper part and a small lower part and tapered, the pulping head also comprises a stirring impeller which is fixedly sleeved at the lower part of the outer liner, and the pulping head also comprises a connecting seat which is fixed at the top of the outer liner and seals the liner cavity of the outer liner; the pulping head further comprises a heat exchange inner container, the heat exchange inner container is contained in a container cavity of the outer container, the top of the heat exchange inner container is fixedly connected with the connecting seat, a closed environment cavity is formed among the heat exchange inner container, the outer container and the connecting seat, a closed heat exchange cavity is formed between the connecting seat and the heat exchange inner container, and a first medium inlet used for introducing inert gas into the environment cavity and a second medium inlet used for introducing heat exchange medium into the heat exchange cavity are formed in the connecting seat.
2. The semi-solid pulping head of claim 1, wherein: the micropores are densely arranged on the whole liner body of the outer liner.
3. The semi-solid pulping head of claim 1, wherein: the outer container is made of one of ceramic, graphite, silicon nitride, silicon carbide material and stainless steel material.
4. The semi-solid pulping head of claim 1, wherein: the connecting seat is fixedly connected with an air duct, the upper part of the air duct is connected with the second medium inlet, and the air duct extends downwards into the lower part of the heat exchange cavity.
5. The semi-solid pulping head of claim 1, wherein: the pulping head further comprises a cooling ring, the cooling ring is fixedly sleeved on the outer side of the connecting seat or the outer side of the top of the outer container, and an annular air outlet used for performing air blowing cooling on the periphery of the outer side of the outer container is formed in the cooling ring.
6. The semi-solid pulping head of claim 5, wherein: the top of the outer container is provided with an annular flange protruding outwards, the connecting seat is fixedly connected with the annular flange through an annular clamping piece, and the cooling ring is fixedly sleeved on the outer side of the top of the outer container and positioned below the annular clamping piece or is fixedly sleeved on the annular clamping piece.