CN106905938A - Molten inert material sealing agent of part theobromine and preparation method thereof and application method - Google Patents
Molten inert material sealing agent of part theobromine and preparation method thereof and application method Download PDFInfo
- Publication number
- CN106905938A CN106905938A CN201710079440.4A CN201710079440A CN106905938A CN 106905938 A CN106905938 A CN 106905938A CN 201710079440 A CN201710079440 A CN 201710079440A CN 106905938 A CN106905938 A CN 106905938A
- Authority
- CN
- China
- Prior art keywords
- mesh
- sealing agent
- theobromine
- inert material
- material sealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It is molten inert material sealing agent of a kind of part theobromine and preparation method thereof and application method the present invention relates to drilling plugging agent technical field, the molten inert material sealing agent of the part theobromine, raw material includes the agstone of mineral fibres, quartz sand and different meshes.The leak stopping performance of theobromine molten rigid material sealing agent in part of the present invention is better than domestic common commercially available sealing agent, and the leak stopping performance with external sealing agent is suitable, because the raw material sources of the molten rigid material sealing agent of part theobromine of the present invention are extensive, low in raw material price, make the production cost of the production cost less than external sealing agent of the molten rigid material sealing agent of part theobromine of the present invention, make the cost performance of the molten rigid material sealing agent of part theobromine of the present invention better than external sealing agent, technical support is provided to improve leakage complex process efficiency.
Description
Technical field
It is a kind of molten inert material sealing agent of part theobromine and its preparation side the present invention relates to drilling plugging agent technical field
Method and application method.
Background technology
During Underwell leakage is Oil/gas Well operation process, working fluid such as drilling fluid, cement mortar, workover fluid etc. enter in pit shaft
Underground high permeability zone, hole stratum, natural or induction formation fracture phenomenon.The harm of Underwell leakage:Head of liquid reduction is made
Into blowout;Cause underground bit freezing;Aggravation reservoir damage, influences cementing quality;Extension drilling period, increases cost, severe patient oil
Well is scrapped.As a example by 2003, the whole world is costly up to 800,000,000 dollars for drilling well leak-proof leak-stopping, does not include also being leaked for treatment
Other down-hole accident expenses that mistake causes.As domestic outer portion old area oil gas field tends to exhaustion, drilling well leakage complicated phenomenon will
Can increasingly protrude.
Either in land or marine drilling operating environment, Underwell leakage is all the time common with oil drilling
Problem, especially for the hole condition that leakage is complicated.At present, commonly use sealing agent and solve the problems, such as Underwell leakage, current leak stopping
Agent species is many, according to the composition species point of sealing agent, can be divided into single dose and complexing agent, and when carrying out leak stopping using single dose, it is blocked up
Leakage effect is poor, and the leak stopping performance of domestic compound sealing agent is not good, has much room for improvement.Particularly with the leakage that leakage is complicated
Lose, existing sealing agent is difficult to reach its leak stopping requirement, so as to constrain the raising of leakage complex process efficiency, this turns into restriction oil
One of major technology bottleneck of gas exploration development rate.And the plugging effect of the sealing agent of external import is preferably, but it is produced
Relatively costly, price occupies height, makes the reduction of its cost performance, causes to increase using the leak stopping cost of external sealing agent.
The content of the invention
The invention provides molten inert material sealing agent of a kind of part theobromine and preparation method thereof and application method, overcome
The deficiency of above-mentioned prior art, the leak stopping performance that it can effectively solve existing domestic sealing agent is not good and import sealing agent is produced into
This problem higher.
One of technical scheme is realized by following measures:A kind of molten inert material leak stopping of part theobromine
Agent, raw materials by weight portion meter is 20 mesh to 10 parts to 20 parts of 40 target minreal fiber, the quartz of 20 mesh to 40 mesh including mesh number
5 parts to 20 parts of sand, 60 mesh to 10 parts to 30 parts of the agstone of 80 mesh, 20 parts to 40 parts of the agstone of 80 mesh to 120 mesh and
30 parts to 50 parts of the agstone of 120 mesh to 160 mesh.
Here is the further optimization and/or improvements to one of foregoing invention technical scheme:
Theobromine molten inert material sealing agent in part described above is obtained as follows:By the desired amount of 20 mesh to 40 target minreals
Fiber, 20 mesh to the quartz sand of 40 mesh, the agstone of 60 mesh to 80 mesh, the agstone of 80 mesh to 120 mesh and 120 mesh extremely
The molten inert material sealing agent of part theobromine is obtained after the agstone mixing of 160 mesh.
Above-mentioned mineral fibres is one or more of asbestos, mica and vermiculite.
Above-mentioned 20 mesh to 40 target minreal fibers are obtained as follows:Mineral fibres is obtained by after drying and crushing
20 mesh to 40 target minreal fibers.
In crushing process, to the surfactant of its addition 0.1% to 0.2%, surfactant is above-mentioned mineral fibres
Nonionic surface active agent or amphoteric ionic surfactant.
The two of technical scheme are realized by following measures:A kind of described part of one of technical scheme
The preparation method of the molten inert material sealing agent of theobromine, is carried out as follows:By the desired amount of 20 mesh to 40 target minreal fibers,
The quartz sand of 20 mesh to 40 mesh, the agstone of 60 mesh to 80 mesh, the agstone of 80 mesh to 120 mesh and 120 mesh to 160 purposes
The molten inert material sealing agent of part theobromine is obtained after agstone mixing.
Here is the further optimization and/or improvements to the two of foregoing invention technical scheme:
Above-mentioned mineral fibres is one or more of asbestos, mica and vermiculite.
Above-mentioned 20 mesh to 40 target minreal fibers are obtained as follows:Mineral fibres is obtained by after drying and crushing
20 mesh to 40 target minreal fibers.
In crushing process, to the surfactant of its addition 0.1% to 0.2%, surfactant is above-mentioned mineral fibres
Nonionic surface active agent or amphoteric ionic surfactant.
The three of technical scheme are realized by following measures:A kind of molten inert material leak stopping of part theobromine
The application method of agent, is carried out as follows:Theobromine molten inert material sealing agent in part is added in drilling well base slurry and mixed
Leak stopping slurry is obtained after uniform, at leak stopping stock pump to Underwell leakage layer, wherein, theobromine molten inert material sealing agent in part exists
Mass percent in leak stopping slurry is 3% to 5%.
The leak stopping performance of theobromine molten rigid material sealing agent in part of the present invention is better than domestic common commercially available leak stopping
Agent, and it is suitable with the leak stopping performance of external sealing agent, due to the molten rigid material sealing agent of part theobromine of the present invention
Extensively, low in raw material price makes the low production cost of the molten rigid material sealing agent of part theobromine of the present invention to raw material sources
In the production cost of external sealing agent, the cost performance of the molten rigid material sealing agent of part theobromine of the present invention is set to be better than state
Outer sealing agent, technical support is provided to improve leakage complex process efficiency, is carried to accelerate Complex formation drilling and oil and gas development
Effective technical guarantee is supplied, simultaneously as the otherness of each regional geographical environment, leakage stratum has choosing to sealing agent
Selecting property, illustrates, theobromine molten rigid material sealing agent in part of the present invention is more suitable for native country stratum by testing.
Specific embodiment
The present invention is not limited by following embodiments, can technology according to the present invention scheme and actual conditions determine specifically
Implementation method.Various chemical reagent and chemical article are previously mentioned in the present invention unless otherwise specified, are known in existing technology
Public chemical reagent and chemical article;Percentage in the present invention is as without specified otherwise, being mass percent.
With reference to embodiment, the invention will be further described:
Embodiment 1:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40 purposes
10 parts to 20 parts of mineral fibres, 20 mesh are to 5 parts to 20 parts of the quartz sand of 40 mesh, 10 parts to 30 of the agstone of 60 mesh to 80 mesh
Part, 20 parts to 40 parts of the agstone and 30 parts to 50 parts of the agstone of 120 mesh to 160 mesh of 80 mesh to 120 mesh, the part
The molten inert material sealing agent of theobromine is obtained as follows:By the desired amount of 20 mesh to 40 target minreal fibers, 20 mesh to 40 mesh
Quartz sand, the agstone of 60 mesh to 80 mesh, the agstone of the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh mix
Theobromine molten inert material sealing agent in part is obtained after conjunction.
Embodiment 2:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40
10 parts or 20 parts of target minreal fiber, 5 parts or 20 parts of the quartz sand of 20 mesh to 40 mesh, 10 parts of the agstone of 60 mesh to 80 mesh or
30 parts, 30 parts or 50 parts of the agstone of 20 parts or 40 parts of the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh, the portion
The molten inert material sealing agent of theobromine is divided to obtain as follows:By the desired amount of 20 mesh to 40 target minreal fibers, 20 mesh to 40
Purpose quartz sand, 60 mesh to the agstone, the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh of 80 mesh agstone
Theobromine molten inert material sealing agent in part is obtained after mixing.
Embodiment 3:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40
10 parts of target minreal fiber, 20 mesh to 40 mesh 5 parts of quartz sand, 10 parts of the agstone of 60 mesh to 80 mesh, 80 mesh to 120 purposes
50 parts of the agstone of 20 parts of agstone and 120 mesh to 160 mesh, the molten inert material sealing agent of part theobromine presses following sides
Method is obtained:By the desired amount of 20 mesh to 40 target minreal fibers, the quartz sand of 20 mesh to 40 mesh, 60 mesh to 80 mesh lime stone
Powder, 80 mesh obtain the molten inert material of part theobromine after mixing to the agstone of 160 mesh to the agstone and 120 mesh of 120 mesh
Sealing agent.
Embodiment 4:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40
20 parts of target minreal fiber, 20 mesh to 40 mesh 20 parts of quartz sand, 30 parts of the agstone of 60 mesh to 80 mesh, 80 mesh to 120 mesh
40 parts of agstone and 120 mesh to 160 mesh 30 parts of agstone, the molten inert material sealing agent of part theobromine is by following
Method is obtained:By the desired amount of 20 mesh to 40 target minreal fibers, the quartz sand of 20 mesh to 40 mesh, 60 mesh to 80 mesh lime stone
Powder, 80 mesh obtain the molten inert material of part theobromine after mixing to the agstone of 160 mesh to the agstone and 120 mesh of 120 mesh
Sealing agent.
Embodiment 5:Used as the optimization of above-described embodiment, mineral fibres is one or more of asbestos, mica and vermiculite.
Embodiment 6:Used as the optimization of above-described embodiment, 20 mesh to 40 target minreal fibers are obtained as follows:By ore deposit
Fibres are by obtaining 20 mesh to 40 target minreal fibers after drying and crushing.
Embodiment 7:Used as the optimization of above-described embodiment, mineral fibres adds 0.1% to 0.2% in crushing process to it
Surfactant, surfactant be nonionic surface active agent or amphoteric ionic surfactant.
Embodiment 8:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40
Target minreal fiber(Asbestos and vermiculite)15 parts, 15 parts of the quartz sand of 20 mesh to 40 mesh, 20 parts of the agstone of 60 mesh to 80 mesh,
40 parts of the agstone of 30 parts of the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh, the molten inert material of part theobromine
Sealing agent is obtained as follows:By the asbestos and vermiculite of the desired amount of 20 mesh to 40 mesh, the quartz sand of 20 mesh to 40 mesh, 60 mesh
Agstone, 80 mesh to 80 mesh obtain part after mixing to the agstone of 160 mesh to the agstone and 120 mesh of 120 mesh
The molten inert material sealing agent of theobromine.
Embodiment 9:The molten inert material sealing agent of the part theobromine, raw materials by weight portion meter includes that mesh number is 20 mesh to 40
Target minreal fiber(Asbestos and vermiculite)17 parts, 10 parts of the quartz sand of 20 mesh to 40 mesh, 17 parts of the agstone of 60 mesh to 80 mesh,
43 parts of the agstone of 37 parts of the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh, the molten inert material of part theobromine
Sealing agent is obtained as follows:By the mica and vermiculite of the desired amount of 20 mesh to 40 mesh, the quartz sand of 20 mesh to 40 mesh, 60 mesh
Agstone, 80 mesh to 80 mesh obtain part after mixing to the agstone of 160 mesh to the agstone and 120 mesh of 120 mesh
The molten inert material sealing agent of theobromine.
Embodiment 10:The application method of the molten inert material sealing agent of part theobromine described in above-described embodiment, by following sides
Method is carried out:By the molten inert material sealing agent of part theobromine be added in drilling well base slurry and it is well mixed after obtain leak stopping slurry, will be stifled
At spillage pump to Underwell leakage layer, wherein, mass percent of the theobromine molten inert material sealing agent in part in leak stopping slurry
For 3% to 5%.
Blocked up according to the molten inert material of part theobromine that embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9 are obtained
Leak the technical indicator and existing domestic common commercially available sealing agent of agent(It is common commercially available)Technical indicator it is as shown in table 1.
Be can be seen that by the data in table 1 and obtained according to embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9
To the molten inert material sealing agent of part theobromine relative to the acid-soluble ratio of common commercially available sealing agent, temperature resistance, compressive resistance ability, ooze
Saturating rate recovery rate is increased, and blocking time and leak stopping discharge are reduced, then according to embodiment 1, embodiment 3, embodiment
The technical indicator of the molten inert material sealing agent of part theobromine that the 4th, embodiment 8, embodiment 9 are obtained(Acid-soluble ratio, temperature resistance, compressive resistance
Ability, resume permeability rate, blocking time and leak stopping discharge)The technical indicator of domestic common commercially available sealing agent is superior to,
Illustrate the molten inert material sealing agent of part theobromine obtained according to embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9
Leak stopping performance of the leak stopping performance better than domestic common commercially available sealing agent.
Blocked up according to the molten inert material of part theobromine that embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9 are obtained
Leakage agent is to drilling fluid(Base is starched)Influence as shown in table 2, existing domestic common commercially available sealing agent (common commercially available) is to drilling fluid
Influence as shown in table 2, while single dose(40 mesh walnut shells)Influence to drilling fluid is as shown in table 2.In process of the test, with 1mm
Seam plate carries out static simulation leak stopping, and concentration 5%, simulated pressure 3.0MPa, 60 DEG C of test temperature, base is starched to be from scene and fetches
Well slurry.
Addition embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9 are can be seen that by the data of table 2 to obtain
The molten inert material sealing agent of part theobromine after base slurry indices numerical value be respectively smaller than in acceding state it is common commercially available stifled
The numerical value of each index of the base slurry of leakage agent or single dose, then embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9 are obtained
Influence of the molten inert material sealing agent of part theobromine for arriving to drilling fluid is respectively less than domestic common commercially available sealing agent and single dose
Influence to drilling fluid, it is possible thereby to illustrate, is obtained using embodiment 1, embodiment 3, embodiment 4, embodiment 8, embodiment 9
Influence of the theobromine molten inert material sealing agent in part to property of drilling fluid is smaller, for existing sealing agent, is more suitable for
In drillng operation.
The molten inert material sealing agent of part theobromine that embodiment 8 is obtained, the sealing agent of Halliburton Company are applied respectively
In Chinese parasol tree ditch group with overlying strata DX1473 wells, DX1804 wells, the sealing agent of An Dong oil companies and embodiment 9 are obtained
Theobromine molten inert material sealing agent in part is respectively applied to eight road gulf groups with overlying strata b1272 wells, b1289 wells, after
Equivalent drilling fluid density it is as shown in table 3.
The molten inert material of part theobromine described in Application Example 8 is can be seen that by the equal yield density raising amount in table 3
Equivalent drilling fluid density raising amount after sealing agent and the equivalent drilling fluid density raising amount using Halliburton Company's sealing agent
Quite, equivalent drilling fluid density raising amount after the molten inert material sealing agent of part theobromine and application described in Application Example 9
The equivalent drilling fluid density raising amount of An Dong oil companies sealing agent quite, illustrates that the part that embodiment 8 and embodiment 9 are obtained can
The molten inert material sealing agent of acid is suitable with the leak stopping performance of above-mentioned two sealing agents.
In sum, the leak stopping performance of the molten rigid material sealing agent of part theobromine of the present invention is better than domestic common city
The sealing agent sold, and it is suitable with the leak stopping performance of external sealing agent, due to theobromine molten rigid material in part of the present invention
Extensively, low in raw material price makes the life of the molten rigid material sealing agent of part theobromine of the present invention to the raw material sources of sealing agent
Production cost of the cost less than external sealing agent is produced, makes the sexual valence of the molten rigid material sealing agent of part theobromine of the present invention
Than better than external sealing agent, technical support being provided to improve leakage complex process efficiency, to accelerate Complex formation drilling and oil
Gas exploitation provides effective technical guarantee, simultaneously as the otherness of each regional geographical environment, leakage stratum is to leak stopping
Agent has selectivity, is illustrated by testing, and theobromine molten rigid material sealing agent in part of the present invention is more suitable for this soil
Layer.
Above technical characteristic constitutes embodiments of the invention, and it has stronger adaptability and implementation result, can basis
The non-essential technical characteristic of increase and decrease is actually needed to meet the demand of different situations.
Claims (9)
1. the molten inert material sealing agent of a kind of part theobromine, it is characterised in that raw materials by weight portion meter include mesh number be 20 mesh extremely
40 10 parts to 20 parts of target minreal fibers, 5 parts to 20 parts of the quartz sand of 20 mesh to 40 mesh, 10 parts of the agstone of 60 mesh to 80 mesh
To 30 parts, 20 parts to 40 parts of the agstone and 30 parts to 50 parts of the agstone of 120 mesh to 160 mesh of 80 mesh to 120 mesh.
2. the molten inert material sealing agent of part theobromine according to claim 1, it is characterised in that the part theobromine is molten lazy
Property material sealing agent is obtained as follows:By the desired amount of 20 mesh to 40 target minreal fibers, the quartz sand of 20 mesh to 40 mesh,
Obtained after the agstone mixing of the agstone, the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh of 60 mesh to 80 mesh
The molten inert material sealing agent of part theobromine.
3. the molten inert material sealing agent of part theobromine according to claim 1 and 2, it is characterised in that mineral fibres is stone
One or more of cotton, mica and vermiculite.
4. the molten inert material sealing agent of part theobromine according to claim 1 and 2, it is characterised in that the ore deposit of 20 mesh to 40 mesh
Fibres are obtained as follows:By mineral fibres by obtaining 20 mesh to 40 target minreal fibers after drying and crushing.
5. the molten inert material sealing agent of part theobromine according to claim 3, it is characterised in that 20 mesh to 40 target minreals
Fiber is obtained as follows:By mineral fibres by obtaining 20 mesh to 40 target minreal fibers after drying and crushing.
6. the molten inert material sealing agent of part theobromine according to claim 4, it is characterised in that mineral fibres was being crushed
Cheng Zhong, 0.1% to 0.2% surfactant is added to it, and surfactant is nonionic surface active agent or amphion
Type surfactant.
7. the molten inert material sealing agent of part theobromine according to claim 6, it is characterised in that mineral fibres was being crushed
Cheng Zhong, 0.1% to 0.2% surfactant is added to it, and surfactant is nonionic surface active agent or amphion
Type surfactant.
8. the preparation side of the molten inert material sealing agent of a kind of part theobromine according to claim 1 or 3 or 4 or 5 or 6 or 7
Method, it is characterised in that carry out as follows:By the desired amount of 20 mesh to 40 target minreal fibers, the quartz of 20 mesh to 40 mesh
After sand, 60 mesh to the agstone mixing of the agstone, the agstone of 80 mesh to 120 mesh and 120 mesh to 160 mesh of 80 mesh
To the molten inert material sealing agent of part theobromine.
9. the use of the molten inert material sealing agent of a kind of part theobromine according to claim 1 or 2 or 3 or 4 or 5 or 6 or 7
Method, it is characterised in that carry out as follows:Theobromine molten inert material sealing agent in part is added in drilling well base slurry and mixed
Leak stopping slurry is obtained after closing uniformly, at leak stopping stock pump to Underwell leakage layer, wherein, the molten inert material sealing agent of part theobromine
Mass percent in leak stopping slurry is 3% to 5%.