CN106893910A - 一种低稀土高强铝合金 - Google Patents
一种低稀土高强铝合金 Download PDFInfo
- Publication number
- CN106893910A CN106893910A CN201710116555.6A CN201710116555A CN106893910A CN 106893910 A CN106893910 A CN 106893910A CN 201710116555 A CN201710116555 A CN 201710116555A CN 106893910 A CN106893910 A CN 106893910A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- aluminium alloy
- strength
- low rare
- strength aluminium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种低稀土高强铝合金,由以下的质量百分比的组分组成:5.5~6.5%Cu,0.6~0.8%Mg,0.4~0.6%Ag,0.2~0.4%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。本发明的低稀土高强铝合金具有良好的室温和高温强度,室温抗拉强度不低于600MPa,250℃时抗拉强度不低于280MPa。本发明的低稀土高强铝合金具有低成本和高强度两个突出的优点,在航天航空工业中有着广阔的应用前景。
Description
技术领域
本发明涉及一种低稀土高强铝合金,属于金属材料技术领域。
背景技术
铝及铝合金是工程应用中轻质的金属结构材料,在许多领域应用都有十分显著的优势,特别是在航天航空工业中具有其他材料无法取代的优势。但是,普通铝合金的耐热性能不佳,当温度超过150℃时,铝合金的强度迅速下降,严重阻碍其在航天航空工业中的应用。虽然相继出现了一些性能较好的耐热铝合金,但是这些合金中一般都含有比例较高的稀土元素,致使合金的成本过高,应用受到限制。因此,在提高铝合金耐热性能的同时降低其成本,已成为发展铝合金材料的重要课题。
现有的耐热铝合金研究主要从限制位错运动和强化晶界入手,通过适当的合金化,通过引入热稳定性高的第二相、降低元素在铝基体中的扩散速率或者改善晶界结构状态和组织形态等手段,来实现提高铝合金高温性能的目的。目前,在所有合金元素中,稀土(RE)是提高铝合金高温性能最有效的合金元素。大部分稀土元素在铝中具有较高的固溶度极限,而且随温度下降,固溶度逐渐下降,从而在随后的时效过程中析出弥散的、高熔点的稀土化合物相;稀土元素还可以细化晶粒、提高室温强度,而且分布在晶内和晶界(主要是晶界)的弥散的、高熔点稀土化合物,在高温时仍能对晶内位错运动和晶界滑移起到钉扎作用,从而提高铝合金的高温性能;同时,稀土元素在铝基体中的扩散速率较慢,这使得含稀土铝合金适于在较高温度环境下工作。Al-Cu系合金是重要的低成本耐热铝合金系,具有良好的铸造性能和室温力学性能,加入适量稀土元素后,其高温力学性能可进一步提高。含稀土Al-Cu系成为发展低成本耐热铝合金的一个重要合金系。
作为铝和稀土资源大国,中国关于含稀土铝合金的研究近年来不断增多和深入,稀土铝合金的成功研发将有助于我们利用这一优势。目前发展较为成功的商业稀土铝合金,其存在的主要不足是稀土含量过高,导致成本过高,其应用受到严重的限制。低稀土耐热铝合金的开发具有十分重要的意义。
发明内容
本发明的目的是提供一种低稀土高强铝合金。
为了实现以上目的,本发明所采用的技术方案是:一种低稀土高强铝合金,由以下的质量百分比的组分组成:5.5~6.5%Cu,0.6~0.8%Mg,0.4~0.6%Ag,0.2~0.4%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。
所述的稀土Nd的质量百分比为0.2~0.4%。
本发明低稀土高强铝合金是由高纯Al (99.99%) 、纯Mg(99.95%)、纯Ag(99.9%)和中间合金Al-50Cu、Al-20Nd为原料熔炼铸造并经过固溶和时效热处理而成。
本发明合金组分为Al-Cu-Mg-Ag-Nd。本发明采用Cu为第一组分,为保证合金具有良好的铸造性能和综合力学性能,Cu的加入量定为5.5~6.5wt%。为了降低合金成本,稀土等其他元素的含量均严格控制,遵循的原则是多元微量。因此,Mg、Ag、Nd元素的含量均低于1 wt%。Nd在Al中的最大固溶度为11wt%,为保证合金得到良好的固溶强化和时效析出强化效果,同时考虑成本,Nd的加入量定为0.2~0.4wt%;采用合金元素Ag与稀土Nd组合使用,Ag可以降低Nd在Al中的固溶度,从而增加Nd的时效析出强化效应;Ag在Al中的最大固溶度为5.6wt%,为了保证强化效果而又尽量降低稀土总含量,因此本发明的Ag加入量定为0.4~0.6wt%;加入少量的Mg,可以在基体中析出热稳定性高的AlCuMgNd相,在高温下有效地强化基体,抑制高温下晶界的滑移,但Mg量会影响铸造性能和力学性能,因此本发明的Mg加入量定为0.6~0.8wt%;综合利用稀土元素Nd和其他元素Ag、Mg的强化作用,进一步提高合金的室温和高温强度。
本发明的低稀土高强铝合金经固溶和时效处理后具有优异的室温和高温强度,室温抗拉强度不低于600MPa,250℃时抗拉强度不低于280MPa。可满足航天航空工业中对耐热温度要求不是很高的零部件的要求。
本发明的低稀土高强铝合金,稀土用量低于1%,成本较低,室温和高温强度较高,在航天航空工业中有着广阔的应用前景。
具体实施方式
本发明具体实施方式中涉及到的原料铝(Al),镁(Mg),银(Ag)和中间合金Al-Cu、Al-Nd均为市售产品。所述原料的纯度为99.99%的Al,99.95%的Mg,99.9%的Ag,Al-50Cu和Al-20Nd。
实施例1
本实施例的低稀土高强铝合金是由以下质量百分比的组分组成:6%Cu,0.7%Mg,0.5%Ag,0.3%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。稀土Nd的质量百分比为0.3%。按上述成分配制合金,其熔铸工艺为:采用石墨坩埚、中频感应炉中熔炼,炉温升到740℃时,加入铝块;待铝全部熔化之后加入Ag和中间合金Al-50Cu、Al-20Nd,并加入溶剂覆盖,保温40min。待中间合金全部熔化之后,采用六氯乙炔除气剂进行除气,除渣后采用钟罩法加入Mg。静置10min后进行第二次除气,搅拌,扒渣,静置处理。釆用水冷铜模激冷技术进行饶铸,得到Al-6Cu-0.7Mg-0.5Ag-0.3Nd铸态合金,随后进行热处理:双级均匀化处理(420℃×6h)+(515℃×18 h)→固溶处理(525℃×2h)→时效处理(185℃×7h)。
将所得稀土铝合金进行拉伸试验,试验方法为:按照国家标准GB6397-86《金属拉伸实验试样》加工标准拉伸试样,在岛津AG-I 250kN电子拉伸试验机上进行拉伸,试验温度为室温和250℃,拉伸速率为1mm/min。
本实施例所得的稀土铝合金,室温抗拉强度为603MPa,250℃时抗拉强度为282MPa。
实施例2
本实施例的低稀土高强铝合金是由以下质量百分比的组分组成:6.5%Cu,0.8%Mg,0.6%Ag,0.4%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。稀土Nd的质量百分比为0.4%。
本实施例的低稀土高强铝合金的熔炼、铸造、热处理工艺和拉伸试验方法同实施例1。
本实施例所得的稀土铝合金,室温抗拉强度为612MPa,250℃时抗拉强度为290MPa。。
实施例3
本实施例的低稀土高强铝合金是由以下质量百分比的组分组成:5.5%Cu,0.6%Mg,0.4%Ag,0.2%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。稀土Nd的质量百分比为0.2%。
本实施例的低稀土高强铝合金的熔炼、铸造、热处理工艺和拉伸试验方法同实施例1。
本实施例所得的稀土铝合金,室温抗拉强度为601MPa,250℃时抗拉强度为280MPa。
Claims (2)
1.一种低稀土高强铝合金,其特征在于:由以下的质量百分比的组分组成:5.5~6.5%Cu,0.6~0.8%Mg,0.4~0.6%Ag,0.2~0.4%Nd,杂质元素Si、Fe、Mn、Ni总量小于0.2%,余量为Al。
2.根据权利要求1所述低稀土高强铝合金,其特征在于:所述稀土Nd的质量百分比为0.2~0.4%。