CN106892669A - A kind of gauze screen and its production technology - Google Patents
A kind of gauze screen and its production technology Download PDFInfo
- Publication number
- CN106892669A CN106892669A CN201710028128.2A CN201710028128A CN106892669A CN 106892669 A CN106892669 A CN 106892669A CN 201710028128 A CN201710028128 A CN 201710028128A CN 106892669 A CN106892669 A CN 106892669A
- Authority
- CN
- China
- Prior art keywords
- parts
- ball
- aluminum oxide
- gauze screen
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of gauze screen, including protective layer and the metallic shield net that is spirally wound between the protective layer, described protective layer includes the composition of following mass fraction:9 15 parts of zinc chloride, 5 10 parts of heat conducting fiber, 38 parts of aluminum oxide, 57 parts of nanometer tungsten carbide, 49 parts of diatomite, 3 10 parts of strontium aluminate, 26 parts of waterglass, 57 parts of Graphene, 48 parts of diatomite, 69 parts of ceramic fibre, 48 parts of borax, 69 parts of molybdenum dioxide, 3 10 parts of feldspar, 79 parts of ferrous sulfate, 38 parts of strontium aluminate, 26 parts of polyether-ether-ketone resin, 6 10 parts of boron nitride, 15 parts of mica of calcining, 13 parts of epoxy resin, 8 13 parts of alumina silicate fibre, 11 13 parts of metallocene PE, 9 14 parts of zirconium oxide, 7 15 parts of aluminum oxide, 58 parts of potter's clay, 13 parts of cremart.The gauze screen that the present invention is provided, the material of preparation has good mechanical strength, while having good anti-seismic performance, can reduce the breakage of gauze screen, and its is durable in use.
Description
Technical field
The present invention relates to a kind of gauze screen and its production technology.
Background technology
Rail vehicle is in dither, the occasion of frequently micro stretching and compression protects what is laid using flexible nonmetallic tubing
Cable.Laying cable has EMC Requirements, and originally conventional mode is to cover layer of metal housing outside plastic film capicitor again
Pipe is solved.This mode need to be installed twice, and connector construction is complicated, easily causes and does over again.Outer layer metal shielded tube is in high frequency
The lower inside and outside of vibration is easily worn and torn, and reduces electromagnetic compatibility shielding efficiency.
The advantageous feature of gauze screen is a lot, but there are some shortcomings, such as tensile strength is relatively low, and plasticity and toughness are very
Difference.Tensile strength can be developed strong, plasticity and toughness are high, and it uses the more extensive gauze screen of scope, is technology of the invention
Main points.
The content of the invention
The technical problem to be solved in the present invention is the defect for overcoming prior art, there is provided a kind of gauze screen and its production work
Skill.
In order to solve the above-mentioned technical problem, the invention provides following technical scheme:
A kind of gauze screen of the present invention, including protective layer and the metallic shield net that is spirally wound between the protective layer, institute
The protective layer stated includes the composition of following mass fraction:Zinc chloride 9-15 parts, heat conducting fiber 5-10 parts, aluminum oxide 3-8 parts, nanometer
Tungsten carbide 5-7 parts, diatomite 4-9 parts, strontium aluminate 3-10 parts, waterglass 2-6 parts, Graphene 5-7 parts, diatomite 4-8 parts, ceramics
Fiber 6-9 parts, borax 4-8 parts, molybdenum dioxide 6-9 parts, feldspar 3-10 parts, ferrous sulfate 7-9 parts, strontium aluminate 3-8 parts, polyethers ether
Ketone resin 2-6 parts, boron nitride 6-10 parts, calcine 1-5 parts of mica, epoxy resin 1-3 parts, alumina silicate fibre 8-13 parts, metallocene
Polyethylene 11-13 parts, zirconium oxide 9-14 parts, aluminum oxide 7-15 parts, potter's clay 5-8 parts, cremart 1-3 parts.
Further, described protective layer includes the composition of following mass fraction:10 parts of zinc chloride, 8 parts of heat conducting fiber, oxygen
Change 6 parts of aluminium, 6 parts of nanometer tungsten carbide, 6 parts of diatomite, 6 parts of strontium aluminate, 4 parts of waterglass, 6 parts of Graphene, 5 parts of diatomite, ceramics
7 parts of fiber, 5 parts of borax, 7 parts of molybdenum dioxide, 5 parts of feldspar, 8 parts of ferrous sulfate, 7 parts of strontium aluminate, 5 parts of polyether-ether-ketone resin, nitrogen
Change 7 parts of boron, calcine 3 parts of mica, 2 parts of epoxy resin, 10 parts of alumina silicate fibre, 12 parts of metallocene PE, 12 parts of zirconium oxide, oxygen
Change 10 parts of aluminium, 6 parts of potter's clay, 2 parts of cremart.
Further, described protective layer includes the composition of following mass fraction:9 parts of zinc chloride, 5 parts of heat conducting fiber, oxygen
Change 8 parts of aluminium, 5 parts of nanometer tungsten carbide, 9 parts of diatomite, 3 parts of strontium aluminate, 2 parts of waterglass, 5 parts of Graphene, 4 parts of diatomite, ceramics
6 parts of fiber, 4 parts of borax, 6 parts of molybdenum dioxide, 3 parts of feldspar, 7 parts of ferrous sulfate, 3 parts of strontium aluminate, 2 parts of polyether-ether-ketone resin, nitrogen
Change 6 parts of boron, calcine 1 part of mica, 1 part of epoxy resin, 8 parts of alumina silicate fibre, 11 parts of metallocene PE, 9 parts of zirconium oxide, oxidation
7 parts of aluminium, 5 parts of potter's clay, 1 part of cremart.
Further, described protective layer includes the composition of following mass fraction:15 parts of zinc chloride, 10 parts of heat conducting fiber,
8 parts of aluminum oxide, 7 parts of nanometer tungsten carbide, 9 parts of diatomite, 10 parts of strontium aluminate, 6 parts of waterglass, 7 parts of Graphene, 8 parts of diatomite, pottery
9 parts of porcelain fiber, 8 parts of borax, 9 parts of molybdenum dioxide, 10 parts of feldspar, 9 parts of ferrous sulfate, 8 parts of strontium aluminate, 6 parts of polyether-ether-ketone resin,
10 parts of boron nitride, calcines 5 parts of mica, 3 parts of epoxy resin, 13 parts of alumina silicate fibre, 13 parts of metallocene PE, zirconium oxide 14
Part, 15 parts of aluminum oxide, 8 parts of potter's clay, 3 parts of cremart.
Further, the α phase chlorinations Zn content in the zinc chloride is 99 parts, and oxygen content is less than 1 part;The zinc chloride
Microscopic appearance is spherical particle, d50=4.5 ± 0.8 μm.
Further, the purity of the heat conducting fiber is 99.99%, and its microscopic appearance is irregular lamellar particle.
A kind of preparation method of gauze screen, it is comprised the following steps:
(1) raw material is put into ball mill by formula, abrading-ball selects the aluminum oxide abrading-ball of a diameter of 5-15mm, aluminum oxide abrading-ball
It is 3-7 with the mass ratio of material:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein propylene
The mass fraction of acid amides and methylene-bisacrylamide is respectively 1-2 parts, 2-3 parts, is then stirred with constant temperature blender with magnetic force,
Speed of agitator is 300-400r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 120-150r/min, ball milling
Time is 4-6h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3-5;
(4) after the completion of ball milling, it is degasification 10-20min under -10000Pa that mixed slurry is placed in into vacuum, excludes mixing slurry
Bubble in material;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, treats
Mixed slurry surface is put into graphite jig in continuing to dry 1-3h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 15-30 DEG C/min, pressurize 25MPa, insulation
Pressurize 0.5-3h, hot pressed sintering system;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
Further, comprise the following steps:
(1) raw material is put into ball mill by proportioning mixing, abrading-ball selects the aluminum oxide abrading-ball of a diameter of 10mm, aluminum oxide mill
The mass ratio of ball and material is 3:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein propylene
The mass fraction of acid amides and methylene-bisacrylamide is respectively 1.3 parts, 2.5 parts, is then stirred with constant temperature blender with magnetic force,
Speed of agitator is 350r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 135r/min, Ball-milling Time
It is 4.5h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3.5;
(4) after the completion of ball milling, it is degasification 15min under -10000Pa that mixed slurry is placed in into vacuum, excludes mixed slurry
In bubble;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, treats
Mixed slurry surface is put into graphite jig in continuing to dry 2h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 20 DEG C/min, pressurize 25MPa, heat-insulation pressure keeping
1h, hot pressed sintering;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
Further, in step (3), on ball mill, rotating speed is 120r/min.
The beneficial effect that is reached of the present invention is:
The gauze screen that the present invention is provided, the material of preparation has good mechanical strength, while having good shock resistance
Can, the breakage of gauze screen can be reduced, its is durable in use, and the material light weight of preparation is flexible, waterproof and dampproof, tear-resistant, chemically-resistant
Reagent, oil resistant is fire-retardant, long service life, disclosure satisfy that specific use environment condition, and market application foreground is wide.
Brief description of the drawings
Accompanying drawing is used for providing further understanding invention, and constitutes a part for specification, with inventive embodiment
It is used to explain together and invents, does not constitute the limitation to inventing.In the accompanying drawings:
Fig. 1 is the schematic flow sheet of invention.
Specific embodiment
The preferred embodiment invented is illustrated below in conjunction with accompanying drawing, it will be appreciated that described herein to be preferable to carry out
Example is merely to illustrate and explains invention, is not used to limit invention.
Embodiment 1
A kind of gauze screen of the present invention, including protective layer and the metallic shield net that is spirally wound between the protective layer, institute
The protective layer stated includes the composition of following mass fraction:Zinc chloride 9-15 parts, heat conducting fiber 5-10 parts, aluminum oxide 3-8 parts, nanometer
Tungsten carbide 5-7 parts, diatomite 4-9 parts, strontium aluminate 3-10 parts, waterglass 2-6 parts, Graphene 5-7 parts, diatomite 4-8 parts, ceramics
Fiber 6-9 parts, borax 4-8 parts, molybdenum dioxide 6-9 parts, feldspar 3-10 parts, ferrous sulfate 7-9 parts, strontium aluminate 3-8 parts, polyethers ether
Ketone resin 2-6 parts, boron nitride 6-10 parts, calcine 1-5 parts of mica, epoxy resin 1-3 parts, alumina silicate fibre 8-13 parts, metallocene
Polyethylene 11-13 parts, zirconium oxide 9-14 parts, aluminum oxide 7-15 parts, potter's clay 5-8 parts, cremart 1-3 parts.
α phase chlorinations Zn content in the zinc chloride is 99 parts, and oxygen content is less than 1 part;The microscopic appearance of the zinc chloride
It is spherical particle, d50=4.5 ± 0.8 μm.
The purity of the heat conducting fiber is 99.99%, and its microscopic appearance is irregular lamellar particle.
Embodiment 2
A kind of gauze screen, including protective layer and the metallic shield net that is spirally wound between the protective layer, described guarantor
Sheath includes the composition of following mass fraction:10 parts of zinc chloride, 8 parts of heat conducting fiber, 6 parts of aluminum oxide, 6 parts of nanometer tungsten carbide, silicon
6 parts of diatomaceous earth, 6 parts of strontium aluminate, 4 parts of waterglass, 6 parts of Graphene, 5 parts of diatomite, 7 parts of ceramic fibre, 5 parts of borax, molybdenum dioxide 7
Part, 5 parts of feldspar, 8 parts of ferrous sulfate, 7 parts of strontium aluminate, 5 parts of polyether-ether-ketone resin, 7 parts of boron nitride calcines 3 parts of mica, asphalt mixtures modified by epoxy resin
2 parts of fat, 10 parts of alumina silicate fibre, 12 parts of metallocene PE, 12 parts of zirconium oxide, 10 parts of aluminum oxide, 6 parts of potter's clay, cremart 2
Part.
α phase chlorinations Zn content in the zinc chloride is 99 parts, and oxygen content is less than 1 part;The microscopic appearance of the zinc chloride
It is spherical particle, d50=4.5 ± 0.8 μm.
The purity of the heat conducting fiber is 99.99%, and its microscopic appearance is irregular lamellar particle.
Embodiment 3
A kind of gauze screen, including protective layer and the metallic shield net that is spirally wound between the protective layer, described guarantor
Sheath includes the composition of following mass fraction:9 parts of zinc chloride, 5 parts of heat conducting fiber, 8 parts of aluminum oxide, 5 parts of nanometer tungsten carbide, diatom
9 parts of soil, 3 parts of strontium aluminate, 2 parts of waterglass, 5 parts of Graphene, 4 parts of diatomite, 6 parts of ceramic fibre, 4 parts of borax, molybdenum dioxide 6
Part, 3 parts of feldspar, 7 parts of ferrous sulfate, 3 parts of strontium aluminate, 2 parts of polyether-ether-ketone resin, 6 parts of boron nitride calcines 1 part of mica, asphalt mixtures modified by epoxy resin
1 part of fat, 8 parts of alumina silicate fibre, 11 parts of metallocene PE, 9 parts of zirconium oxide, 7 parts of aluminum oxide, 5 parts of potter's clay, 1 part of cremart.
α phase chlorinations Zn content in the zinc chloride is 99 parts, and oxygen content is less than 1 part;The microscopic appearance of the zinc chloride
It is spherical particle, d50=4.5 ± 0.8 μm.
The purity of the heat conducting fiber is 99.99%, and its microscopic appearance is irregular lamellar particle.
Embodiment 4
A kind of gauze screen, including protective layer and the metallic shield net that is spirally wound between the protective layer, described guarantor
Sheath includes the composition of following mass fraction:15 parts of zinc chloride, 10 parts of heat conducting fiber, 8 parts of aluminum oxide, 7 parts of nanometer tungsten carbide, silicon
9 parts of diatomaceous earth, 10 parts of strontium aluminate, 6 parts of waterglass, 7 parts of Graphene, 8 parts of diatomite, 9 parts of ceramic fibre, 8 parts of borax, molybdenum dioxide
9 parts, 10 parts of feldspar, 9 parts of ferrous sulfate, 8 parts of strontium aluminate, 6 parts of polyether-ether-ketone resin, 10 parts of boron nitride calcines 5 parts of mica, ring
3 parts of oxygen tree fat, 13 parts of alumina silicate fibre, 13 parts of metallocene PE, 14 parts of zirconium oxide, 15 parts of aluminum oxide, 8 parts of potter's clay, careless amine
3 parts of phosphorus.
α phase chlorinations Zn content in the zinc chloride is 99 parts, and oxygen content is less than 1 part;The microscopic appearance of the zinc chloride
It is spherical particle, d50=4.5 ± 0.8 μm.
The purity of the heat conducting fiber is 99.99%, and its microscopic appearance is irregular lamellar particle.
Embodiment 5
Shown in Fig. 1, a kind of preparation method of gauze screen, it is comprised the following steps:
(1) raw material is put into ball mill by formula, abrading-ball selects the aluminum oxide abrading-ball of a diameter of 5-15mm, aluminum oxide abrading-ball
It is 3-7 with the mass ratio of material:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein propylene
The mass fraction of acid amides and methylene-bisacrylamide is respectively 1-2 parts, 2-3 parts, is then stirred with constant temperature blender with magnetic force,
Speed of agitator is 300-400r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 120-150r/min, ball milling
Time is 4-6h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3-5;
(4) after the completion of ball milling, it is degasification 10-20min under -10000Pa that mixed slurry is placed in into vacuum, excludes mixing slurry
Bubble in material;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, treats
Mixed slurry surface is put into graphite jig in continuing to dry 1-3h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 15-30 DEG C/min, pressurize 25MPa, insulation
Pressurize 0.5-3h, hot pressed sintering system;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
Embodiment 6
A kind of preparation method of gauze screen, it is comprised the following steps:
(1) raw material is put into ball mill by proportioning mixing, abrading-ball selects the aluminum oxide abrading-ball of a diameter of 10mm, aluminum oxide mill
The mass ratio of ball and material is 3:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein propylene
The mass fraction of acid amides and methylene-bisacrylamide is respectively 1.3 parts, 2.5 parts, is then stirred with constant temperature blender with magnetic force,
Speed of agitator is 350r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 135r/min, Ball-milling Time
It is 4.5h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3.5;
(4) after the completion of ball milling, it is degasification 15min under -10000Pa that mixed slurry is placed in into vacuum, excludes mixed slurry
In bubble;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, treats
Mixed slurry surface is put into graphite jig in continuing to dry 2h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 20 DEG C/min, pressurize 25MPa, heat-insulation pressure keeping
1h, hot pressed sintering system;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
Finally it should be noted that:The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention,
Although being described in detail to the present invention with reference to the foregoing embodiments, for a person skilled in the art, it still may be used
Modified with to the technical scheme described in foregoing embodiments, or equivalent is carried out to which part technical characteristic.
All any modification, equivalent substitution and improvements within the spirit and principles in the present invention, made etc., should be included in of the invention
Within protection domain.
Claims (9)
1. a kind of gauze screen, it is characterised in that including protective layer and the metallic shield net being spirally wound between the protective layer,
Described protective layer includes the composition of following mass fraction:Zinc chloride 9-15 parts, heat conducting fiber 5-10 parts, aluminum oxide 3-8 parts, receive
5-7 parts of tungsten carbide of rice, diatomite 4-9 parts, strontium aluminate 3-10 parts, waterglass 2-6 parts, Graphene 5-7 parts, diatomite 4-8 parts, pottery
6-9 parts of porcelain fiber, borax 4-8 parts, molybdenum dioxide 6-9 parts, feldspar 3-10 parts, ferrous sulfate 7-9 parts, strontium aluminate 3-8 parts, polyethers
2-6 parts of ether ketone resin, calcines 1-5 parts of mica, epoxy resin 1-3 parts, alumina silicate fibre 8-13 parts, cyclopentadienyl gold by boron nitride 6-10 parts
11-13 parts, zirconium oxide 9-14 parts, aluminum oxide 7-15 parts, potter's clay 5-8 parts, cremart 1-3 parts of polyethylene of category.
2. a kind of gauze screen according to claim 1, it is characterised in that described protective layer includes following mass fraction
Composition:10 parts of zinc chloride, 8 parts of heat conducting fiber, 6 parts of aluminum oxide, 6 parts of nanometer tungsten carbide, 6 parts of diatomite, 6 parts of strontium aluminate, water glass
4 parts of glass, 6 parts of Graphene, 5 parts of diatomite, 7 parts of ceramic fibre, 5 parts of borax, 7 parts of molybdenum dioxide, 5 parts of feldspar, ferrous sulfate 8
Part, 7 parts of strontium aluminate, 5 parts of polyether-ether-ketone resin, 7 parts of boron nitride calcines 3 parts of mica, 2 parts of epoxy resin, alumina silicate fibre 10
Part, 12 parts of metallocene PE, 12 parts of zirconium oxide, 10 parts of aluminum oxide, 6 parts of potter's clay, 2 parts of cremart.
3. a kind of gauze screen according to claim 1, it is characterised in that described protective layer includes following mass fraction
Composition:9 parts of zinc chloride, 5 parts of heat conducting fiber, 8 parts of aluminum oxide, 5 parts of nanometer tungsten carbide, 9 parts of diatomite, 3 parts of strontium aluminate, waterglass
2 parts, 5 parts of Graphene, 4 parts of diatomite, 6 parts of ceramic fibre, 4 parts of borax, 6 parts of molybdenum dioxide, 3 parts of feldspar, 7 parts of ferrous sulfate,
3 parts of strontium aluminate, 2 parts of polyether-ether-ketone resin, 6 parts of boron nitride calcines 1 part of mica, 1 part of epoxy resin, 8 parts of alumina silicate fibre, cyclopentadienyl
11 parts of metal polyethylene, 9 parts of zirconium oxide, 7 parts of aluminum oxide, 5 parts of potter's clay, 1 part of cremart.
4. a kind of gauze screen according to claim 1, it is characterised in that described protective layer includes following mass fraction
Composition:15 parts of zinc chloride, 10 parts of heat conducting fiber, 8 parts of aluminum oxide, 7 parts of nanometer tungsten carbide, 9 parts of diatomite, 10 parts of strontium aluminate, water
6 parts of glass, 7 parts of Graphene, 8 parts of diatomite, 9 parts of ceramic fibre, 8 parts of borax, 9 parts of molybdenum dioxide, 10 parts of feldspar, ferrous sulfate
9 parts, 8 parts of strontium aluminate, 6 parts of polyether-ether-ketone resin, 10 parts of boron nitride calcines 5 parts of mica, 3 parts of epoxy resin, alumina silicate fibre 13
Part, 13 parts of metallocene PE, 14 parts of zirconium oxide, 15 parts of aluminum oxide, 8 parts of potter's clay, 3 parts of cremart.
5. a kind of gauze screen according to claim 1, it is characterised in that the α phase chlorination Zn contents in the zinc chloride are
99 parts, oxygen content is less than 1 part;The microscopic appearance of the zinc chloride is spherical particle, d50=4.5 ± 0.8 μm.
6. a kind of gauze screen according to claim 1, it is characterised in that the purity of the heat conducting fiber is 99.99%, its
Microscopic appearance is irregular lamellar particle.
7. the preparation method of a kind of gauze screen according to claim 1 to 6 any one, it is characterised in that including following
Step:
(1) raw material is put into ball mill by formula, abrading-ball selects the aluminum oxide abrading-ball of a diameter of 5-15mm, aluminum oxide abrading-ball and thing
The mass ratio of material is 3-7:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein acrylamide
And the mass fraction of methylene-bisacrylamide is respectively 1-2 parts, 2-3 parts, then stirred with constant temperature blender with magnetic force, stirring
Rotating speed is 300-400r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 120-150r/min, Ball-milling Time
It is 4-6h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3-5;
(4) after the completion of ball milling, it is degasification 10-20min under -10000Pa that mixed slurry is placed in into vacuum, in exclusion mixed slurry
Bubble;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, to be mixed
Pulp surface is put into graphite jig in continuing to dry 1-3h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 15-30 DEG C/min, pressurize 25MPa, heat-insulation pressure keeping
0.5-3h, hot pressed sintering;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
8. the preparation method of gauze screen according to claim 7, it is characterised in that comprise the following steps:
(1) raw material is put into ball mill by proportioning mixing, abrading-ball from a diameter of 10mm aluminum oxide abrading-ball, aluminum oxide abrading-ball and
The mass ratio of material is 3:1;
(2) organic monomer acrylamide and crosslinking agent methylene-bisacrylamide are dissolved in deionized water, wherein acrylamide
And the mass fraction of methylene-bisacrylamide is respectively 1.3 parts, 2.5 parts, then stirred with constant temperature blender with magnetic force, stirring
Rotating speed is 350r/min, and stirring 5-6min forms uniform auxiliary agent slurry;
(3) it is fixed on ball mill after auxiliary agent slurry being injected into ball grinder and sealing, rotating speed is 135r/min, and Ball-milling Time is
4.5h, forms mixed slurry, wherein, auxiliary agent slurry is 1 with the mass ratio of zinc chloride:3.5;
(4) after the completion of ball milling, it is degasification 15min under -10000Pa that mixed slurry is placed in into vacuum, in exclusion mixed slurry
Bubble;
(5) mixed slurry after degasification is poured out, is put into heat drying in vacuum drying oven, initial temperature is set to 60 DEG C, to be mixed
Pulp surface is put into graphite jig in continuing to dry 2h again at 100 DEG C after drying regime after drying;
(6) under N2 atmosphere protections, 1250 DEG C are heated to the heating rate of 20 DEG C/min, pressurize 25MPa, heat-insulation pressure keeping 1h,
Hot pressed sintering;
(7) double screw extruder granulation is sent into after crushing, cooling is obtained final product feeding plastics spraying machine plastic-spraying to metallic shield afterwards on the net.
9. the preparation method of gauze screen according to claim 7, it is characterised in that in step (3), on ball mill, rotating speed
It is 120r/min.