CN106892625A - 一种大体积混凝土施工的混凝土拌合物 - Google Patents

一种大体积混凝土施工的混凝土拌合物 Download PDF

Info

Publication number
CN106892625A
CN106892625A CN201710228070.6A CN201710228070A CN106892625A CN 106892625 A CN106892625 A CN 106892625A CN 201710228070 A CN201710228070 A CN 201710228070A CN 106892625 A CN106892625 A CN 106892625A
Authority
CN
China
Prior art keywords
parts
concrete
cement
concrete mix
mass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710228070.6A
Other languages
English (en)
Inventor
刘树科
苗增刚
石富财
丛国良
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Rongtai Construction Group Co., Ltd.
Original Assignee
Jia Maolai
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jia Maolai filed Critical Jia Maolai
Priority to CN201710228070.6A priority Critical patent/CN106892625A/zh
Publication of CN106892625A publication Critical patent/CN106892625A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种大体积混凝土施工的混凝土拌合物，包括下列重量份数的组分：水泥0.3‑0.8份，细骨料5‑9份，粗骨料3‑8份，水0.5‑2份，聚羧酸减水剂0.5‑1份，十二烷基磺酸钠0.5‑1份，高岭土0.5‑1份，氧化铝0.5‑1份。在本发明提供的用于大体积混凝土施工的混凝土拌合物中，在现有技术的基础上，改进配方，进一步减少了水泥的用量，改善了混凝土拌合物的性能，使混凝土建筑物的结构强度、耐久性、和易性和坍落度进一步增强，产生裂缝的几率大大降低。

Description

一种大体积混凝土施工的混凝土拌合物
技术领域
本发明涉及一种大体积混凝土施工的混凝土拌合物，属于混凝土建筑施工领域。
背景技术
在进行大体积混凝土施工时，按照常规，为了满足建筑物的结构强度，混凝土拌合物中水泥的用量需大于等于300千克每平方米（kg/m3），掺有活性掺和料时水泥用量需大于等于280kg/m3。而在实际施工中，水泥的用量过大往往会使混凝土水化热过高，导致建筑物出现温度裂缝，影响施工质量。因此，为了最大限度地降低水化热，混凝土拌合物既要选用低热水泥又要降低水泥用量。
中国专利CN201310343069.X公开了一种大体积混凝土施工的混凝土拌合物，本发明是在其基础上进行的改进。
发明内容
本发明所要解决的技术问题是：提供一种用于大体积混凝土施工的混凝土拌合物，以在保证混凝土建筑物结构强度的基础上，提高其耐久性，减少其裂缝的产生。
为解决上述技术问题，本发明采用的技术方案是：
本发明的大体积混凝土施工的混凝土拌合物，包括下列重量份数的组分：.水泥0.3-0.8份，细骨料5-9份，粗骨料3-8份，水0.5-2份，聚羧酸减水剂0.5-1份，十二烷基磺酸钠0.5-1份，高岭土0.5-1份，氧化铝0.5-1份。
优选的，本发明的水泥为矿渣硅酸盐水泥，进一步的，矿渣硅酸盐水泥采用低热矿渣硅酸盐水泥。
优选的，细骨料为中砂，细度模数为1.5-2.0，含泥量小于等于1%。粗骨料为石子，石子的直径为10-25毫米，含泥量小于等于0.5%。
优选的，本发明采用的高岭土的粒径是100-200目。氧化铝的粒径是50-100目。
本发明是在现有技术的基础上进行的改进，在配方中增加了高岭土和氧化铝，申请人通过大量实验证明，这这两种组分可以明显改善混凝土水化热过高的问题，解决建筑物出现温度裂缝的缺陷。
现有技术相比，本发明具有以下有益效果：
在本发明提供的用于大体积混凝土施工的混凝土拌合物中，在现有技术的基础上，改进配方，进一步减少了水泥的用量，改善了混凝土拌合物的性能，使混凝土建筑物的结构强度、耐久性、和易性和坍落度进一步增强，产生裂缝的几率大大降低。
具体实施方式
实施例1
本实施例提供的大体积混凝土施工的混凝土拌合物，包括下列重量份数的组分：.水泥0.8份，细骨料9份，粗骨料8份，水2份，聚羧酸减水剂1份，十二烷基磺酸钠1份，高岭土1份，氧化铝1份。
水泥为低热矿渣硅酸盐水泥。
细骨料为中砂，细度模数为2.0，含泥量小于等于1%。粗骨料为石子，石子的直径为25毫米，含泥量小于等于0.5%。
高岭土的粒径是200目。氧化铝的粒径是100目。
实施例2
本实施例的大体积混凝土施工的混凝土拌合物，包括下列重量份数的组分：.水泥0.3份，细骨料5份，粗骨料3份，水0.5份，聚羧酸减水剂0.5份，十二烷基磺酸钠0.5份，高岭土0.5份，氧化铝0.5份。
水泥为低热矿渣硅酸盐水泥。
细骨料为中砂，细度模数为1.5，含泥量小于等于1%。粗骨料为石子，石子的直径为10毫米，含泥量小于等于0.5%。
高岭土的粒径是100目。氧化铝的粒径是50目。
性能测试：
对实施例1的混凝土拌合物进行实际应用测试，结构强度优，和易性优，坍落度在50-60之间，没有产生裂缝。

Claims (6)

1.一种大体积混凝土施工的混凝土拌合物，其特征在于，包括下列重量份数的组分：.水泥0.3-0.8份，细骨料5-9份，粗骨料3-8份，水0.5-2份，聚羧酸减水剂0.5-1份，十二烷基磺酸钠0.5-1份，高岭土0.5-1份，氧化铝0.5-1份。
2.根据权利要求1所述的大体积混凝土施工的混凝土拌合物，其特征在于，水泥为矿渣硅酸盐水泥。
3.根据权利要求1所述的大体积混凝土施工的混凝土拌合物，其特征在于，所述细骨料为中砂，细度模数为1.5-2.0，含泥量小于等于1%。
4.根据权利要求1所述的大体积混凝土施工的混凝土拌合物，其特征在于，述粗骨料为的石子，石子的直径为10-25毫米，含泥量小于等于0.5%。
5.根据权利要求1所述的大体积混凝土施工的混凝土拌合物，其特征在于，高岭土的粒径是100-200目。
6.根据权利要求1所述的大体积混凝土施工的混凝土拌合物，其特征在于，氧化铝的粒径是50-100目。
CN201710228070.6A 2017-04-10 2017-04-10 一种大体积混凝土施工的混凝土拌合物 Pending CN106892625A (zh)