CN106891227A - A kind of sander presses nog plate and preparation method thereof with fast-assembling - Google Patents
A kind of sander presses nog plate and preparation method thereof with fast-assembling Download PDFInfo
- Publication number
- CN106891227A CN106891227A CN201710102080.5A CN201710102080A CN106891227A CN 106891227 A CN106891227 A CN 106891227A CN 201710102080 A CN201710102080 A CN 201710102080A CN 106891227 A CN106891227 A CN 106891227A
- Authority
- CN
- China
- Prior art keywords
- substrate
- pad
- graphite
- groove
- nog plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of sander fast-assembling pressure nog plate and preparation method thereof is related to the abrasive band of sanding machinery to press nog plate and preparation method thereof.Pressure nog plate bonds compound composition by substrate, cushion pad, Graphite cloth.Substrate its dual side-edge is formed with tongue and groove, can be engaged with the rabbet groove of pressure nog plate base and plugged together.Substrate can be wood-fiber board, wood-plastic board, plastic plate, acrylic board or composite panel.Cushion pad can be wool felt pan, acupuncture nonwoven felt pan, artificial leather pad, resin foamed sheet or compressed sponge pad.Graphite cloth is made up of in its surface coating graphite canvas with the mixed coating of adhesive.Its making step is followed successively by：Make substrate, elastic buffering pad, Graphite cloth, by elastic buffering pad and substrate bonding it is compound, Graphite cloth is combined with being bonded with the elastic buffering pad of substrate bonding.Beneficial effect produced by the present invention：The processing request of different workpieces can be allowed to preferably be adapted to using the making substrate and elastic buffering pad of various different materials.Can draw and insert-type fast-assembling, change it is easy to use.Using novel graphite cloth, lubrication, wearability are more preferable.Can be by specialized factory's batch making low cost.
Description
Technical field：
The present invention relates to woodworking machinery, relate generally to woodenware product or other metal products are sanded the sander scraped
Tool, and more particularly to supporting with the sander pressure nog plate for the grinding belt that presses and preparation method thereof.
Background technology：
It, using one piece of pressure abrading block, is the one piece of bullet of bottom adhesive in cuboid wooden unit that prior art sander pressure nog plate is
Property cushion, then Wai Guo Graphite cloths, are fixed on two side walls of cuboid wooden unit with nail or bolt, the graphite of Wai Guo Graphite cloths
Coating down, and is pressed on cuboid pressure abrading block by pressing piece, and the pressure abrading block of Wai Guo Graphite cloths is pressed on the grinding of quick motion
The back side in abrasive band, its effect is pressure abrasive band, the grinding sand grains face in abrasive band is closely overlayed on workpiece to be machined, to carry out
Effectively grinding.Because of pressure, abrading block Wai Guo Graphite cloths have good lubricity, its back side for being pressed on grinding belt, rubbing therebetween
Resistance very little is wiped, so the resistance of motion in abrasive band is mainly grinding group power of the abrasive band front sand grains in face of workpiece, and the abrasive band back side
With the frictional resistance between pressure abrading block Graphite cloth by very little.
There are three defects in the press mold block of prior art, one is, make trouble, and inconvenience is made using various different materials,
Therefore the grinding suitability with the processing workpiece of unlike material is poor, and two are, replacing Graphite cloth is bothersome, is not easy to fast-assembling quick change, if
Pressure abrading block is integrally thrown away and renews and waste very much, three are, Graphite cloth's coating is only one layer of right Lin piece graphite linings in day, lubricity it is good but
Not wear-resisting, service life is short.
The content of the invention：
It is an object of the present invention to provide a kind of sander fast-assembling pressure nog plate and preparation method thereof, it is multiple to change existing pressure abrading block
Lamination nog plate construction is closed, various different materials is can select and is made, be suitable for being ground different workpieces object, ground effect is more preferable.Take out
The formula of inserting is changed, convenient and swift.The construction of former Graphite cloth is changed, not only lubricity is good and long service life.
Present disclosure is that a kind of sander fast-assembling presses nog plate 1 successively by substrate 2, elastic buffering pad 5, Graphite cloth 6
To each other compound composition is bonded through binding agent.Its dual side-edge of the substrate 2 can grind with tongue and groove 2 ' or convex-concave tongue and groove is inclined with pressure
The corresponding inclination rabbet groove 7 ' of plate base 7 or concavo-convex rabbet groove are engaged and plug together.
Further embodiment of the present invention is that the substrate 2 can be wood-fiber board or wood-plastic board or plastic plate or Asia
Gram force plate or composite panel, its thickness are 5-8mm.Can also be steel belt plate, its thickness is 0.5-1mm.The elastic buffering pad
4 can be wool felt pan or acupuncture nonwoven felt pan or artificial leather pad or resin foamed sheet or compressed sponge pad, and its thickness is
3-5mm.The Graphite cloth 6 is by the canvas 8 of thick 0.4-0.5mm in its surface coating 1.5-1.8mm thick graphite and adhesive
Mixed coating is constituted, and wherein graphite linings include one layer of artificial stone layer of ink 9 and one layer of natural stone layer of ink 9 '.
The preparation method that the sander presses nog plate with fast-assembling, its making step is followed successively by：Make substrate 2, make elasticity
Cushion pad 4, make Graphite cloth 6, by elastic buffering pad 4 and substrate 2 bond it is compound, by Graphite cloth 6 with bonded with substrate 2 it is compound
Elastic buffering pad 4 bond it is compound.
The invention has the advantages that：
It is layer structure that the present invention changes former pressure abrading block, and substrate can need to be made using multiple material according to application, two sides
While being formed with contract mouthful, can be engaged with the corresponding rabbet groove of pressure nog plate base 7 and plugged together.The pressure nog plate can pull and push fast-assembling, change
It is convenient.Elastic buffering pad can need to be made using multiple material according to different.Its equadag coating right graphite linings on another day of Graphite cloth are
One layer of Delanium coating covers one layer of native graphite coating again thereon.The outstanding advantages of the pressuring diaphragm are：1st, can be right according to processing
The difference of elephant makes substrate and elastic buffering pad using various different materials, and selection range is wide, can make its hard soft elasticity and be added
The suitability of workpiece is stronger, and sanding effect is more preferable.2nd, the pressure nog plate can draw and insert-type fast-assembling, change it is easy to use.3rd, the pressure nog plate
Constructed using novel graphite cloth, existing more preferable lubricity, and wear-resisting long service life.4th, different user can be pressed by specialized factory
The pressuring template of batch making different materials, different size is needed, cost, price are low, user need to only be needed to change at any time by processing
Different pressure nog plates.
Brief description of the drawings：
The present invention of accompanying drawing 1 is loaded on (substrate dual side-edge is formed with inclination tongue and groove) front view on pressure nog plate base
The Graphite cloth's profile of the present invention of accompanying drawing 2
The present invention of accompanying drawing 3 is sanded machining sketch chart for sander
The present invention of accompanying drawing 4 is loaded on (substrate dual side-edge is formed with convex-concave tongue and groove) front view on pressure nog plate base
Specific embodiment：
A kind of sander fast-assembling presses nog plate 1 successively by substrate 2, elastic buffering pad 4, Graphite cloth 6 to each other through binding agent
Bond compound composition.Its dual side-edge of the substrate 2, can be relative with pressure nog plate base 7 with tongue and groove 2 ' or convex-concave tongue and groove is inclined
The inclination rabbet groove 7 ' or concavo-convex rabbet groove answered are engaged and plug together.
Further embodiment is, the substrate 2 can be for wood-fiber board or for wood-plastic board or for plastic plate or be sub- gram
Power plate is composite panel, and its thickness is 5-8mm.Can also be steel belt plate, its thickness is 0.5-1mm.The elastic buffering pad
4 can be wool felt pan or acupuncture nonwoven felt pan or artificial leather pad or resin foamed sheet or compressed sponge pad, and its thickness is
3-5mm.The Graphite cloth 6 is by the canvas 8 of thick 0.4-0.5mm in its surface coating 1.5-1.8mm thick graphite and adhesive
Mixed coating is constituted, and wherein graphite linings include one layer of artificial stone layer of ink 9 and one layer of natural stone layer of ink 9 '.
Substrate 2 described in present embodiment is Midst density wood-fiber board, and its thickness is 5mm.The elastic buffering pad 4 is compression
Foam-rubber cushion, thickness is 4mm.The Graphite cloth 6 is by the canvas 8 of thick 0.5mm, in its surface coating 1.6mm thickness graphite and gluing
The mixed coating of agent is constituted, and the mixed coating includes the thick artificial stone layer of ink 9 of 1mm and natural stone layer of ink 9 ' 0.2mm thick thereon.
The preparation method of sander fast-assembling pressure nog plate its step is successively：
(1) substrate 2, is made：It is the wood-fiber board or wood-plastic board or plastic plate or acrylic of 5-8mm from thickness
Each 5-8mm in the side of lath two edges of boards wide are made as inclining by the one kind in plate or composite panel, beam into the lath of 50-150mm wide
Oblique tongue and groove 2 ' or convex-concave tongue and groove, corresponding is pressing nog plate base 7 to be made the inclination tongue and groove that can be engaged with substrate tongue and groove and plugged together
Groove 7 ' or concavo-convex rabbet groove.
Or from the steel band that thickness is 0.5-1mm, a width of 50-150mm, the band edge each 5-8mm in the side of steel band two wide is plug tenon,
Corresponding is pressing nog plate base 7 to make the plug tenon groove that can be engaged with steel band plug tenon and plugged together.
(2) elastic buffering pad 4, is made：From thickness for the wool felt or acupuncture nonwoven felt or artificial leather of 3-5mm or
One kind in resin foamed sheet or compressed sponge, is cut into and does not include the wide strip pad of the substrate strip of two side tongue and grooves.
(3) Graphite cloth 6, is made：By first 5 points of the kiering in 100 DEG C ± 20 DEG C of hot water kettle of 0.4-0.5mm thick canvas
Clock, then takes out draining, drying, ironing, and then uniform coating a layer thickness is 1.5-1.8mm graphite and high score subtree thereon
The mixed coating of fat adhesive.It comprises the concrete steps that first uniform brushing a layer thickness is the macromolecule resin gluing of 0.2-0.3mm
Agent, it is 0.8-1mm Delanium particulate powder that a layer thickness is dispensed thereon, by 10 minutes adhesives to pre-hardening state, then two
Secondary coating 0.2-0.3mm thickness macromolecule resin gluing agent, it is the natural graphite powder of 0.2-0.3mm then to dispense a layer thickness, quiet
Put 48 hours and solidify completely, be cut into the strip Graphite cloth wide with elastic buffering pad 4.
(4), elastic buffering pad 4 and substrate 2 are bonded compound：Operated at room temperature at 15-35 DEG C, in the basal surface of substrate 2
A floor height molecule Resin adhesive is applied, elastic buffering pad is alignd (with part in substrate tongue and groove) with substrate 2, be laid in institute's gluing
In glutinous agent, then rolled by rubber roll, stand 24 hours.
(5), by Graphite cloth 6 with bonded with substrate 2 compound elastic buffering pad 4 bond it is compound：By elastic buffering pad 4
Basal surface applies a floor height molecule Resin adhesive, and Graphite cloth 6 is alignd with elastic buffering pad 4, is laid on applied adhesive, so
Afterwards by rubber roll roll, stand 24 hours, finished product sander with fast-assembling press nog plate.
Claims (3)
1. a kind of sander presses nog plate and preparation method thereof with fast-assembling, it is characterized in that, pressure nog plate (1) is successively by substrate (2), elasticity
Cushion pad (4), Graphite cloth (6) bond compound composition through binding agent to each other；Described its dual side-edge of substrate (2) has inclination tongue and groove
(2 ') or convex-concave tongue and groove, can be engaged slotting with corresponding inclination rabbet groove (7 ') of pressure nog plate base (7) or concavo-convex rabbet groove
Close.
2. a kind of sander presses nog plate and preparation method thereof with fast-assembling according to claim 1, it is characterized in that, the substrate
(2) can be wood-fiber board or wood-plastic board or plastic plate or acrylic board or composite panel, its thickness is 5-8mm；May be used also
It is steel belt plate, its thickness is 0.5-1mm；
The elastic buffering pad (4) can for wool felt pan or acupuncture nonwoven felt pan or artificial leather pad or resin foamed sheet or
It is compressed sponge pad, its thickness is 3-5mm；
The Graphite cloth (6) is by the canvas (8) of thick 0.4-0.5mm in its surface coating 1.5-1.8mm thick graphite and adhesive
Mixed coating constitute, wherein graphite linings include one layer of artificial stone layer of ink (9) and one layer of natural stone layer of ink (9 ').
3. the preparation method that a kind of sander according to claim 1 or claim 2 presses nog plate with fast-assembling, it is characterized in that, making step
It is followed successively by：
(1) substrate (2) is made：From thickness for the wood-fiber board or wood-plastic board or plastic plate or acrylic board of 5-8mm or
Be made as each 5-8mm in the side of lath two edges of boards wide to incline tongue and groove into the lath of 50-150mm wide by the one kind in composite panel, beam
(2 ') or convex-concave tongue and groove, corresponding is pressing nog plate base (7) to be made the inclination rabbet groove that can be engaged with substrate tongue and groove and plugged together
(7 ') or concavo-convex rabbet groove；
Or from the steel band that thickness is 0.5-1mm, a width of 50-150mm, the band edge each 5-8mm in the side of steel band two wide is plug tenon, relatively
That answers is pressing nog plate base 7 to make the plug tenon groove that can be engaged with steel band plug tenon and plugged together.
(2) elastic buffering pad (4) is made：The wool felt or acupuncture nonwoven felt or artificial leather for 3-5mm or tree from thickness
One kind in fat foam sheet or compressed sponge, is cut into and does not include the wide strip pad of the substrate strip of two side tongue and grooves.
(3) Graphite cloth (6) is made：By first kiering 5 minutes in 100 DEG C ± 20 DEG C of hot water kettle of 0.4-0.5mm thick canvas,
Draining, drying, ironing are then taken out, then uniform coating a layer thickness is 1.5-1.8mm graphite and macromolecule resin thereon
The mixed coating of adhesive, comprises the concrete steps that, first uniform brushing a layer thickness is the macromolecule resin gluing agent of 0.2-0.3mm,
It is 0.8-1mm Delanium particulates powder (9) to dispense a layer thickness thereon, by 10 minutes adhesives to pre-hardening state, then two
Secondary coating 0.2-0.3mm thick macromolecule resin gluing agent, it is the natural graphite powder of 0.2-0.3mm then to dispense a layer thickness
(9 '), standing solidifies for 48 hours completely, is cut into the strip Graphite cloth wide with elastic buffering pad (4).
(4) elastic buffering pad (4) and substrate (2) are bonded compound：Operated at room temperature at 15-35 DEG C, in the bottom table of substrate (2)
Face applies floor height molecule Resin adhesive (3), and elastic buffering pad (4) is alignd (with part in substrate tongue and groove) with substrate (2), puts down
It is laid on applied adhesive, is then rolled by rubber roll, stands 24 hours.
(5) Graphite cloth (6) is combined with compound elastic buffering pad (4) bonding is bonded with substrate (2)：By elastic buffering pad
(4) basal surface applies floor height molecule Resin adhesive (5), and Graphite cloth (6) is alignd with elastic buffering pad (4), is laid in and is applied
On adhesive, then by rubber roll roll, stand 24 hours, finished product sander with fast-assembling press nog plate.