CN106883487A - It is a kind of to can be used for the laminated film and its manufacture method of equipment heat-sealing - Google Patents
It is a kind of to can be used for the laminated film and its manufacture method of equipment heat-sealing Download PDFInfo
- Publication number
- CN106883487A CN106883487A CN201710152689.3A CN201710152689A CN106883487A CN 106883487 A CN106883487 A CN 106883487A CN 201710152689 A CN201710152689 A CN 201710152689A CN 106883487 A CN106883487 A CN 106883487A
- Authority
- CN
- China
- Prior art keywords
- parts
- laminated film
- layer
- raw material
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of laminated film that can be used for equipment heat-sealing is provided, it is characterised in that:The laminated film is three-layer extrusion film, and outer layer includes the raw material of following parts by weight:18~21 parts of PN resins, 0.6 1 parts of silicone, 0.1 0.3 parts of antioxidant;Intermediate layer includes the raw material of following parts by weight:52~58 parts of PE resins, 2.2 2.6 parts of silicone, 0.4 0.8 parts of antioxidant;Internal layer includes the raw material of following parts by weight:18~21 parts of POE plastics, 0.6~1 part of silicone, 0.1~0.3 part of antioxidant;The fusing point of outer layer is more than the fusing point of internal layer, the maximum temperature when fusing point of internal layer is sealed more than equipment.This can be used to not crease easily, damage and encapsulate firmly when the laminated film high temperature resistant of equipment heat-sealing, encapsulation.A kind of manufacture method of the above-mentioned laminated film that can be used for equipment heat-sealing is also provided in addition.
Description
Technical field
Can be used for the laminated film and its manufacture method of equipment heat-sealing the present invention relates to a kind of.
Background technology
Currently used for the appendicle material of packaging household appliances, such as sterilized net, remote controller bracket, specification and guarantee card
Deng generally using PE films.When being sealed using equipment, because longitudinal sealing temperature is 90 DEG C, horizontal sealing temperature is 85 to PE films
DEG C, temperature higher easily causes to be shrinked into ridges during PE thin-film packages, even damages, if turning down package temperature, cannot encapsulate
Firmly.
The content of the invention
The technical problem to be solved in the present invention is:Jail is not creased easily, damages and encapsulates when a kind of high temperature resistant, encapsulation are provided
Solid can be used for equipment heat-sealing laminated film.
Technical solution of the invention is:A kind of laminated film that can be used for equipment heat-sealing, it is characterised in that:It is described multiple
Conjunction film is three-layer extrusion film, including outer layer, intermediate layer and the internal layer being combined with each other, the outer layer includes following parts by weight
Raw material:18~21 parts, silicone 0.6-1 parts, antioxidant 0.1-0.3 parts of PN resins;The intermediate layer includes following parts by weight
Raw material:52~58 parts, silicone 2.2-2.6 parts, antioxidant 0.4-0.8 parts of PE resins;The internal layer includes following parts by weight
Raw material:18~21 parts of POE plastics, 0.6~1 part of silicone, 0.1~0.3 part of antioxidant;The fusing point of the outer layer is more than internal layer
Fusing point, the maximum temperature when fusing point of the internal layer is sealed more than equipment.
After said structure, the present invention has advantages below:
The present invention can be used for the laminated film of equipment heat-sealing, and PN resin outer layers and POE plastics are additionally arranged on PE resin beds
Internal layer;Because the fusing point of outer layer and internal layer is all higher than maximum temperature when equipment is sealed, therefore laminated film will not in heat-sealing
Shrink into ridges or damage;Secondly, internal layer POE plastics performances more softness, good toughness, adhesion strength is high, tensile strength and tear
Intensity is protruded, and puncture-resistant, hence in so that the product after heat-sealing is bonded more firmly, heat sealability is more preferable;Again, with heat-sealing
The outer layer PN resin beds of equipment directly contact not only high temperature resistant, and hardness is higher, so as to more be not easy to shrink into ridges or damage
It is bad;Finally, using three-layer extrusion film heat sealability more preferably, mechanical strength higher, puncture resistant and tear resistance is stronger, resistance to height
Temperature simultaneously can anti-oxidation, waterproof, protection against the tide.
Preferably, the outer layer includes the raw material of following parts by weight:20 parts of PN resins, 0.8 part of silicone, antioxidant
0.2 part;The intermediate layer includes the raw material of following parts by weight:55 parts of PE resins, 2.4 parts of silicone, 0.6 part of antioxidant;It is described
Internal layer includes the raw material of following parts by weight:20 parts of POE plastics, 0.8 part of silicone, 0.2 part of antioxidant.This is set to each component
Preferred scheme, can be optimal the performance of laminated film.
Preferably, the PE resins in the intermediate layer are LDPE resin.LDPE resin is one kind of PE resins, and performance is soft
Various moulding process that are soft, being adapted to thermoplastic molding's processing, molding processibility is good, impact resistance and toughness are preferable.
Another technical problem to be solved by the present invention is that:A kind of high degree of automation, easily manufactured, precision machining is provided
Manufacture method for manufacturing the above-mentioned laminated film that can be used for equipment heat-sealing.
Technical solution of the invention is:A kind of manufacture method of the laminated film that can be used for equipment heat-sealing, its feature
It is:It is comprised the following steps:
(1) three layers of raw material are configured:Mechanical mixture is carried out by with comparison raw material, is mixed with obtaining outer layer mixed material, intermediate layer
Compound material and internal layer mixed material;
(2) automatic blanking:PC control automatic blanking system is entered automatically in the ratio shared by outer layer, intermediate layer, internal layer
Row blanking;
(3) fusion plastification:Each layer mixed material enters fusion plastification in respective extruder through hopper, and PC control is squeezed
The plasticization temperature gone out in machine is 170 DEG C~220 DEG C;
(4) blow molding:The melt of each layer mixed material is imported into die head by respective runner carries out three layers of bonding
And blow molding, the outflow of die lip that process can be adjusted, blow temperatures in PC control extruder die head for 165 DEG C~
180℃;
(5) cooling and shaping:By the laminated film of die lip outflow to chill roll or vane cooling and shaping, then by PC control
Automatic trailer system draws laminated film with the speed for setting;
(6) splitting winding and packaging and storage.
After the above method, the present invention has advantages below:
The manufacture method that the present invention can be used for the laminated film of equipment heat-sealing uses automatic blanking system by three layers of mixture
Material is automatically added in each extruder respectively by proportioning, and the process of fusion plastification and blow molding is automatically performed by extruder, and
The laminated film after cooling and shaping is drawn by automatic trailer system, above-mentioned automatic blanking system, extruder and automatic traction
System is uniformly coordinated by host computer and automatically controlled, whole process high degree of automation, easily manufactured, precision machining, is manufactured
Laminated film have high temperature resistant, encapsulation when do not crease easily, damage and encapsulate firm advantage.
Preferably, also by the total thickness of the laminated film after measuring thickness device on-line checking cooling and shaping in step (5)
The thickness information of the thickness of degree and each layer, the gross thickness of the laminated film and each layer feeds back to host computer for controlling to squeeze
Go out the screw speed of machine and the hauling speed of trailer system.By the gross thickness and the thickness of each layer of on-line checking laminated film
Carry out the rotating speed and hauling speed of adjusting bolt, can more be accurately controlled the quality of film forming.
Brief description of the drawings:
Fig. 1 is the structural representation of the laminated film that the present invention can be used for equipment heat-sealing;
In figure of the present invention:1- outer layers, 2- intermediate layers, 3- internal layers.
Specific embodiment
Below in conjunction with the accompanying drawings, and in conjunction with the embodiments the present invention is described further.
Embodiment 1:
As shown in figure 1, a kind of laminated film that can be used for equipment heat-sealing, the laminated film is three-layer extrusion film, including
Outer layer 1, intermediate layer 2 and the internal layer 3 being combined with each other, the outer layer 1 include the raw material of following parts by weight:PN resins 18~21
Part, silicone 0.6-1 parts, antioxidant 0.1-0.3 parts;The intermediate layer 2 include 52~58 parts of PE resins, silicone 2.2-2.6 part, resist
0.4-0.8 parts of oxygen agent;The internal layer 3 includes the raw material of following parts by weight:It is 18~21 parts of POE plastics, 0.6~1 part of silicone, anti-
0.1~0.3 part of oxygen agent;PN resins are propylene-ethylene block copolymer;POE materials are ethylene-octene copolymer;The outer layer 1
Fusing point more than internal layer 3 fusing point, the maximum temperature when fusing point of the internal layer 3 is sealed more than equipment.
The present invention can be used for the laminated film of equipment heat-sealing, and PN resin outer layers 1 and POE plastics are additionally arranged on PE resin beds
Internal layer 3, due to the fusing point of outer layer 1 and internal layer 3 be all higher than equipment seal when maximum temperature, therefore laminated film heat-sealing when not
Can shrink into ridges or damage;Secondly, internal layer 3POE plastics performances more softness, good toughness, adhesion strength is high, tensile strength and tear
Resistance to spalling is protruded, and puncture-resistant, hence in so that the product after heat-sealing is bonded more firmly, heat sealability is more preferable;Again, with heat
The outer layer 1PN resin beds of envelope equipment directly contact not only high temperature resistant, and hardness is higher, thus be more not easy to shrink into ridges or
Damage;Finally, using three-layer extrusion film heat sealability more preferably, mechanical strength higher, puncture resistant and tear resistance is stronger, resistance to height
Temperature simultaneously can anti-oxidation, waterproof, protection against the tide.
Preferably, the outer layer 1 includes the raw material of following parts by weight:20 parts of PN resins, 0.8 part of silicone, antioxidant
0.2 part;The intermediate layer 2 includes the raw material of following parts by weight:55 parts of PE resins, 2.4 parts of silicone, 0.6 part of antioxidant;It is described
Internal layer 3 includes the raw material of following parts by weight:20 parts of POE plastics, 0.8 part of silicone, 0.2 part of antioxidant.This is set to each component
Preferred scheme, can be optimal the performance of laminated film.
Preferably, the PE resins in the intermediate layer 2 are LDPE resin, LDPE is low density polyethylene (LDPE).LDPE resin is
One kind of PE resins, performance is soft, be adapted to the various moulding process of thermoplastic molding's processing, and molding processibility is good, shock resistance energy
Power and toughness are preferable.
Embodiment 2:
A kind of manufacture method of the laminated film that can be used for equipment heat-sealing, it is characterised in that:It is comprised the following steps:
(1) three layers of raw material are configured:Mechanical mixture is carried out by with comparison raw material, to obtain the mixed material of outer layer 1, intermediate layer 2
Mixed material and the mixed material of internal layer 3, the mixed material of the outer layer 1 include:20 parts of PN resins, 0.8 part of silicone, antioxidant 0.2
Part, the mixed material of the intermediate layer 2 includes:55 parts of LDPE resin, 2.4 parts of silicone, 0.6 part of antioxidant, the mixture of the internal layer 3
Material includes:20 parts of POE plastics, 0.8 part of silicone, 0.2 part of antioxidant;
(2) automatic blanking:PC control automatic blanking system is automatic in the ratio shared by outer layer 1, intermediate layer 2, internal layer 3
Blanking is carried out, the ratio shared by the outer layer 1 isRatio shared by the intermediate layer 2 isRatio shared by the internal layer 3 is
(3) fusion plastification:Each layer mixed material enters fusion plastification in respective extruder through hopper, and PC control is squeezed
The plasticization temperature gone out in machine is 170 DEG C~220 DEG C;
(4) blow molding:The melt of each layer mixed material is imported into die head by respective runner carries out three layers of bonding
And blow molding, the outflow of die lip that process can be adjusted, blow temperatures in PC control extruder die head for 165 DEG C~
180℃;
(5) cooling and shaping:By the laminated film of die lip outflow to chill roll or vane cooling and shaping, then by PC control
Automatic trailer system draws laminated film with the speed for setting;
(6) splitting winding and packaging and storage.
Above-mentioned host computer, automatic blanking system, extruder, automatic trailer system and host computer to automatic blanking system,
The control of extruder and automatic trailer system uses prior art, and above-mentioned automatic control equipment is not in itself hair of the invention
Bright, inventive point of the invention is the manufacture method that above-mentioned automatic control equipment is applied to laminated film of the present invention.
The manufacture method that the present invention can be used for the laminated film of equipment heat-sealing uses automatic blanking system by three layers of mixture
Material is automatically added in each extruder respectively by proportioning, and the process of fusion plastification and blow molding is automatically performed by extruder, and
The laminated film after cooling and shaping is drawn by automatic trailer system, above-mentioned automatic blanking system, extruder and automatic traction
System is uniformly coordinated by host computer and automatically controlled, whole process high degree of automation, easily manufactured, precision machining, is manufactured
Laminated film have high temperature resistant, encapsulation when do not crease easily, damage and encapsulate firm advantage.
Preferably, also by the total thickness of the laminated film after measuring thickness device on-line checking cooling and shaping in step (5)
The thickness information of the thickness of degree and each layer, the gross thickness of the laminated film and each layer feeds back to host computer for controlling to squeeze
Go out the screw speed of machine and the hauling speed of trailer system, the measuring thickness device is prior art, for example near infrared technology.
By on-line checking to the gross thickness of laminated film and the thickness of each layer come the rotating speed and hauling speed of adjusting bolt, can be more
Plus it is accurately controlled the quality of film forming.
The laminated film product cross directional stretch force value >=22N for finally being manufactured with proportioning as stated above, extensibility >=
500%, tensile strength >=30Mpa;Longitudinal stretching force value >=18N, extensibility >=500%, tensile strength >=24Mpa, integrated machine
Tool intensity, tensile strength and extensibility are higher;And longitudinal sealing temperature be 90 DEG C, horizontal sealing temperature be 85 DEG C at a high temperature of carry out
During heat-sealing, will not wrinkle, damage and encapsulate very firm.
Claims (5)
- It is 1. a kind of to can be used for the laminated film that equipment is sealed, it is characterised in that:The laminated film is three-layer extrusion film, including again Outer layer (1), intermediate layer (2) and the internal layer (3) being combined, the raw material of the outer layer (1) including following parts by weight:PN resins 18~21 parts, silicone 0.6-1 parts, antioxidant 0.1-0.3 parts;The raw material of the intermediate layer (2) including following parts by weight:PE trees 52~58 parts, silicone 2.2-2.6 parts, antioxidant 0.4-0.8 parts of fat;The raw material of the internal layer (3) including following parts by weight: 18~21 parts of POE plastics, 0.6~1 part of silicone, 0.1~0.3 part of antioxidant;The fusing point of the outer layer (1) is more than internal layer (3) Fusing point, the maximum temperature when fusing point of the internal layer (3) is sealed more than equipment.
- 2. it is according to claim 1 it is a kind of can be used for equipment heat-sealing laminated film, it is characterised in that:The outer layer (1) Raw material including following parts by weight:20 parts of PN resins, 0.8 part of silicone, 0.2 part of antioxidant;The intermediate layer (2) is including following The raw material of parts by weight:55 parts of PE resins, 2.4 parts of silicone, 0.6 part of antioxidant;The internal layer (3) includes following parts by weight Raw material:20 parts of POE plastics, 0.8 part of silicone, 0.2 part of antioxidant.
- 3. it is according to claim 1 it is a kind of can be used for equipment heat-sealing laminated film, it is characterised in that:The intermediate layer (2) PE resins are LDPE resin.
- 4. it is a kind of can be used for equipment heat-sealing laminated film manufacture method, it is characterised in that:It is comprised the following steps:(1) three layers of raw material are configured:Mechanical mixture is carried out by with comparison raw material, to obtain outer layer (1) mixed material, intermediate layer (2) Mixed material and internal layer (3) mixed material;(2) automatic blanking:PC control automatic blanking system in the ratio shared by outer layer (1), intermediate layer (2), internal layer (3) from It is dynamic to carry out blanking;(3) fusion plastification:Each layer mixed material enters fusion plastification, PC control extruder in respective extruder through hopper Interior plasticization temperature is 170 DEG C~220 DEG C;(4) blow molding:The melt of each layer mixed material is imported into die head by respective runner and carries out three layers and bond and blow Type is moulded, the die lip outflow that process can be adjusted, the blow temperatures in PC control extruder die head are 165 DEG C~180 DEG C;(5) cooling and shaping:The laminated film flowed out by die lip is to chill roll or vane cooling and shaping then automatic by PC control Trailer system draws laminated film with the speed for setting;(6) splitting winding and packaging and storage.
- 5. it is according to claim 4 it is a kind of can be used for equipment heat-sealing laminated film manufacture method, it is characterised in that: Also by the gross thickness and the thickness of each layer of the laminated film after measuring thickness device on-line checking cooling and shaping, institute in step (5) The thickness information of the gross thickness and each layer of stating laminated film feeds back to host computer for controlling the screw speed of extruder and leading Draw the hauling speed of system.